WO2005013873A1 - Toile de formation pour procede de fabrication par voie aeraulique et produits ainsi fabriques - Google Patents

Toile de formation pour procede de fabrication par voie aeraulique et produits ainsi fabriques Download PDF

Info

Publication number
WO2005013873A1
WO2005013873A1 PCT/US2004/025527 US2004025527W WO2005013873A1 WO 2005013873 A1 WO2005013873 A1 WO 2005013873A1 US 2004025527 W US2004025527 W US 2004025527W WO 2005013873 A1 WO2005013873 A1 WO 2005013873A1
Authority
WO
WIPO (PCT)
Prior art keywords
base section
forming wire
recessed
topographical
forming
Prior art date
Application number
PCT/US2004/025527
Other languages
English (en)
Inventor
Brian E. Boehmer
Original Assignee
Bki Holding Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bki Holding Corporation filed Critical Bki Holding Corporation
Publication of WO2005013873A1 publication Critical patent/WO2005013873A1/fr

Abstract

L'invention concerne un certain nombre de toiles de formation selon divers modes de réalisation que l'on utilise dans une machine de formation de bandes par voie aéraulique. Dans un mode de réalisation exemplaire, la toile de formation (130) comporte une caractéristique (200) qui amène la bande aéraulique (140) résultante ainsi formée à être texturée et à présenter une masse surfacique et une aire superficielle différentielles. Plus précisément, une toile de formation exemplaire (130) comporte une section de base (132) et une caractéristique topographique (200) solidaire de ladite section de base (132), ladite caractéristique topographique (200) étant alors surélevée par rapport à ladite section de base (132). La caractéristique topographique (200) étant surélevée par rapport aux zones avoisinantes de la section de base, la toile de formation (130) présente donc une épaisseur non uniforme qui amène les fibres à se déposer d'une manière non uniforme, le résultat étant une bande aéraulique (140) dont les zones ont une épaisseur et une masse surfacique variables.
PCT/US2004/025527 2003-08-08 2004-08-06 Toile de formation pour procede de fabrication par voie aeraulique et produits ainsi fabriques WO2005013873A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US49387503P 2003-08-08 2003-08-08
US60/493,875 2003-08-08

Publications (1)

Publication Number Publication Date
WO2005013873A1 true WO2005013873A1 (fr) 2005-02-17

Family

ID=34135293

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2004/025527 WO2005013873A1 (fr) 2003-08-08 2004-08-06 Toile de formation pour procede de fabrication par voie aeraulique et produits ainsi fabriques

Country Status (1)

Country Link
WO (1) WO2005013873A1 (fr)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2011062227A (ja) * 2009-09-15 2011-03-31 Kochi Prefecture 吸収性物品
EP2628837A1 (fr) 2005-04-01 2013-08-21 Buckeye Technologies Inc. Matériau non tissé pour isolation acoustique et procédé de fabrication
EP2660377A1 (fr) * 2012-05-03 2013-11-06 Chen-Cheng Huang Procédé de fabrication d'un tissu non tissée gaufrée double face
US9175428B2 (en) 2012-04-30 2015-11-03 Chen-Cheng Huang Method of making a double-sided embossed non-woven fabric
WO2016020230A1 (fr) * 2014-08-07 2016-02-11 Voith Patent Gmbh Bande de tissu servant à fabriquer un matériau de bande, en particulier servant à fabriquer un non-tissé filé-lié
WO2018153576A1 (fr) * 2017-02-24 2018-08-30 Voith Patent Gmbh Procédé et dispositif pour produire une bande de matière fibreuse dans une machine à papier
WO2018153577A1 (fr) * 2017-02-24 2018-08-30 Voith Patent Gmbh Procédé et dispositif pour produire une bande de matière fibreuse dans une machine à papier
US10617576B2 (en) 2012-05-21 2020-04-14 Kimberly-Clark Worldwide, Inc. Process for forming a fibrous nonwoven web with uniform, directionally-oriented projections
US11077224B2 (en) 2015-02-02 2021-08-03 Coloplast A/S Ostomy device
US11160681B2 (en) 2015-04-10 2021-11-02 Coloplast A/S Ostomy device
WO2024091219A1 (fr) * 2022-10-24 2024-05-02 Kimberly-Clark Worldwide, Inc. Fil de formation à motifs segmenté et rigide

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2827666A (en) * 1955-01-11 1958-03-25 Dayton Rubber Company Method for manufacture of fiber reinforced articles
US4741941A (en) * 1985-11-04 1988-05-03 Kimberly-Clark Corporation Nonwoven web with projections

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2827666A (en) * 1955-01-11 1958-03-25 Dayton Rubber Company Method for manufacture of fiber reinforced articles
US4741941A (en) * 1985-11-04 1988-05-03 Kimberly-Clark Corporation Nonwoven web with projections

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2628837A1 (fr) 2005-04-01 2013-08-21 Buckeye Technologies Inc. Matériau non tissé pour isolation acoustique et procédé de fabrication
JP2011062227A (ja) * 2009-09-15 2011-03-31 Kochi Prefecture 吸収性物品
US9175428B2 (en) 2012-04-30 2015-11-03 Chen-Cheng Huang Method of making a double-sided embossed non-woven fabric
EP2660377A1 (fr) * 2012-05-03 2013-11-06 Chen-Cheng Huang Procédé de fabrication d'un tissu non tissée gaufrée double face
US10617576B2 (en) 2012-05-21 2020-04-14 Kimberly-Clark Worldwide, Inc. Process for forming a fibrous nonwoven web with uniform, directionally-oriented projections
EP3177459B1 (fr) 2014-08-07 2019-08-21 Voith Patent GmbH Procédé à fabriquer un non-tissé filé-lié
US10435828B2 (en) 2014-08-07 2019-10-08 Voith Patent Gmbh Fabric belt for producing web material, in particular for producing spunbonded fabric
WO2016020230A1 (fr) * 2014-08-07 2016-02-11 Voith Patent Gmbh Bande de tissu servant à fabriquer un matériau de bande, en particulier servant à fabriquer un non-tissé filé-lié
US11077224B2 (en) 2015-02-02 2021-08-03 Coloplast A/S Ostomy device
US11771798B2 (en) 2015-02-02 2023-10-03 Coloplast A/S Ostomy device with a switchable adhesive layer located between a backing layer and an absorbent adhesive layer
US11160681B2 (en) 2015-04-10 2021-11-02 Coloplast A/S Ostomy device
US11819444B2 (en) 2015-04-10 2023-11-21 Coloplast A/S Ostomy device with a switchable adhesive composition adapted to be switched by moisture activation of a switch initiator
WO2018153577A1 (fr) * 2017-02-24 2018-08-30 Voith Patent Gmbh Procédé et dispositif pour produire une bande de matière fibreuse dans une machine à papier
CN110088396A (zh) * 2017-02-24 2019-08-02 福伊特专利有限公司 在造纸机中用于制造纤维材料幅面的方法和装置
WO2018153576A1 (fr) * 2017-02-24 2018-08-30 Voith Patent Gmbh Procédé et dispositif pour produire une bande de matière fibreuse dans une machine à papier
US11261567B2 (en) 2017-02-24 2022-03-01 Voith Patent Gmbh Method and device for the production of a fibrous material web in a papermaking machine
WO2024091219A1 (fr) * 2022-10-24 2024-05-02 Kimberly-Clark Worldwide, Inc. Fil de formation à motifs segmenté et rigide

Similar Documents

Publication Publication Date Title
US11891737B2 (en) Airlaid composite sheet material and method
EP0750694B1 (fr) Voile superieur faiblement rehumidifiable et article absorbant jetable
US4425126A (en) Fibrous material and method of making the same using thermoplastic synthetic wood pulp fibers
US4081582A (en) Fibrous material and method of making the same
KR102407405B1 (ko) 비평면 부직포 직물 및 그 제조 방법
US4392861A (en) Two-ply fibrous facing material
JPH055259A (ja) 高ロフト、高強度不織布
US20170137980A1 (en) Nonwoven with improved abrasion resistance and method of making the same
CN110268113B (zh) 液压处理的非织造织物及其制造方法
PL188650B1 (pl) Struktura chłonna i sposób wytwarzania struktury chłonnej
WO2005013873A1 (fr) Toile de formation pour procede de fabrication par voie aeraulique et produits ainsi fabriques
SK163898A3 (en) Absorbent structure, and production of absorbent structure by mat formation together with adhesive-bonded layer
US6517927B2 (en) Flexible composite sheet
US11850820B2 (en) Apertured nonwoven
EP1087743A1 (fr) Structure unitaire absorbante renfermant un polymere ultra-absorbant
CA1105821A (fr) Traduction non-disponible
JP2024126768A (ja) 吸収性物品用不織布
GB2387180A (en) A lofted non-woven material with z orientated fibres
MXPA96004169A (en) Upper leaf of low rehumedment and above absorbent article

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase