WO2005007727A1 - Heat stabilized moulding composition - Google Patents
Heat stabilized moulding composition Download PDFInfo
- Publication number
- WO2005007727A1 WO2005007727A1 PCT/NL2004/000507 NL2004000507W WO2005007727A1 WO 2005007727 A1 WO2005007727 A1 WO 2005007727A1 NL 2004000507 W NL2004000507 W NL 2004000507W WO 2005007727 A1 WO2005007727 A1 WO 2005007727A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- thermoplastic polymer
- mass
- polymer
- elementary iron
- Prior art date
Abstract
Description
Claims