WO2004099529A1 - Bande et joint pour cloison seche - Google Patents

Bande et joint pour cloison seche Download PDF

Info

Publication number
WO2004099529A1
WO2004099529A1 PCT/IB2003/002226 IB0302226W WO2004099529A1 WO 2004099529 A1 WO2004099529 A1 WO 2004099529A1 IB 0302226 W IB0302226 W IB 0302226W WO 2004099529 A1 WO2004099529 A1 WO 2004099529A1
Authority
WO
WIPO (PCT)
Prior art keywords
tape
drywall
drywall tape
coating
web
Prior art date
Application number
PCT/IB2003/002226
Other languages
English (en)
Inventor
Mark Joseph Newton
David Geraint Roberts
Original Assignee
Saint-Gobain Technical Fabrics Canada, Ltd.
Certainteed Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to CA002427514A priority Critical patent/CA2427514A1/fr
Application filed by Saint-Gobain Technical Fabrics Canada, Ltd., Certainteed Corporation filed Critical Saint-Gobain Technical Fabrics Canada, Ltd.
Priority to JP2004571534A priority patent/JP2007516366A/ja
Priority to EP03727793A priority patent/EP1620613A1/fr
Priority to BRPI0318297-5A priority patent/BR0318297A/pt
Priority to CA002525971A priority patent/CA2525971C/fr
Priority to AU2003232993A priority patent/AU2003232993A1/en
Priority to CNA038265796A priority patent/CN1788130A/zh
Priority to PCT/IB2003/002226 priority patent/WO2004099529A1/fr
Publication of WO2004099529A1 publication Critical patent/WO2004099529A1/fr

Abstract

L'invention concerne des bandes et des joints pour cloison sèche ainsi que leurs procédés de fabrication. La bande pour cloison sèche décrite dans la présente invention comporte une nappe de fibres de verre (10) et un revêtement (14) disposé sur une partie desdites fibres. Ce revêtement renferme un liant résineux qui est au moins partiellement soluble ou dispersible dans le mélange de jointoiement. Le lien résineux permet de former une liaison adhésive avec le mélange de jointoiement lors de la prise.
PCT/IB2003/002226 2003-05-06 2003-05-06 Bande et joint pour cloison seche WO2004099529A1 (fr)

Priority Applications (8)

Application Number Priority Date Filing Date Title
CA002427514A CA2427514A1 (fr) 2003-05-06 2003-05-01 Ruban et joint a cloison seche
JP2004571534A JP2007516366A (ja) 2003-05-06 2003-05-06 ドライウォールテープとジョイント
EP03727793A EP1620613A1 (fr) 2003-05-06 2003-05-06 Bande et joint pour cloison seche
BRPI0318297-5A BR0318297A (pt) 2003-05-06 2003-05-06 fita e junta e drywall
CA002525971A CA2525971C (fr) 2003-05-06 2003-05-06 Bande et joint pour cloison seche
AU2003232993A AU2003232993A1 (en) 2003-05-06 2003-05-06 Drywall tape and joint
CNA038265796A CN1788130A (zh) 2003-05-06 2003-05-06 干墙带和接缝
PCT/IB2003/002226 WO2004099529A1 (fr) 2003-05-06 2003-05-06 Bande et joint pour cloison seche

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IB2003/002226 WO2004099529A1 (fr) 2003-05-06 2003-05-06 Bande et joint pour cloison seche

Publications (1)

Publication Number Publication Date
WO2004099529A1 true WO2004099529A1 (fr) 2004-11-18

Family

ID=34385732

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2003/002226 WO2004099529A1 (fr) 2003-05-06 2003-05-06 Bande et joint pour cloison seche

Country Status (7)

Country Link
EP (1) EP1620613A1 (fr)
JP (1) JP2007516366A (fr)
CN (1) CN1788130A (fr)
AU (1) AU2003232993A1 (fr)
BR (1) BR0318297A (fr)
CA (2) CA2427514A1 (fr)
WO (1) WO2004099529A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010512478A (ja) * 2006-12-12 2010-04-22 ユナイテッド・ステイツ・ジプサム・カンパニー 低水分伸張特性を有する不織布ジョイントテープ及びその使用方法
WO2010099563A1 (fr) * 2009-03-05 2010-09-10 Csr Building Products Limited Système amélioré de jonction de plaque de plâtre
EP2433772A1 (fr) 2006-10-20 2012-03-28 Dow Global Technologies LLC Dispersions aqueuses disposées sur des fibres à base de verre et des substrats contenant du verre
WO2014075188A1 (fr) * 2012-11-16 2014-05-22 Shawcor Ltd. Ruban ou feuille renforcé(e) de fibres pour le renforcement d'un tuyau
US8828892B2 (en) 2007-01-18 2014-09-09 Saint-Gobain Adfors Canada, Ltd. Drywall tape and drywall joint
US11066576B2 (en) 2015-09-21 2021-07-20 United States Gypsum Company Drywall joint tape with dual purpose adhesive backing

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2953531B1 (fr) * 2009-12-07 2012-03-02 Ahlstroem Oy Support non tisse pour bande a joint et bande a joint stable dimensionnellement et pliable sans perte de resistance mecanique comprenant ledit support
CN103643516B (zh) * 2013-12-02 2016-01-20 山东永泰化工有限公司 一种玻璃纤维壁布涂层的制备方法
CN107905407A (zh) * 2017-12-01 2018-04-13 中冶天工集团天津有限公司 一种防火石膏墙板接缝抗震防裂的方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3391037A (en) * 1964-10-12 1968-07-02 Joseph D. Mcnulty Method of covering joints in interior wall construction
FR2123259A1 (en) * 1971-01-28 1972-09-08 Nat Gypsum Co Wall joint - between chamfered panels concealing a melt mesh and resin joint

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3391037A (en) * 1964-10-12 1968-07-02 Joseph D. Mcnulty Method of covering joints in interior wall construction
FR2123259A1 (en) * 1971-01-28 1972-09-08 Nat Gypsum Co Wall joint - between chamfered panels concealing a melt mesh and resin joint

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2433772A1 (fr) 2006-10-20 2012-03-28 Dow Global Technologies LLC Dispersions aqueuses disposées sur des fibres à base de verre et des substrats contenant du verre
JP2010512478A (ja) * 2006-12-12 2010-04-22 ユナイテッド・ステイツ・ジプサム・カンパニー 低水分伸張特性を有する不織布ジョイントテープ及びその使用方法
JP2015038302A (ja) * 2006-12-12 2015-02-26 ユナイテッド・ステイツ・ジプサム・カンパニー 低水分伸張特性を有する不織布ジョントテープ及びその使用方法
US9376824B2 (en) 2006-12-12 2016-06-28 United States Gypsum Company Nonwoven joint tape having low moisture expansion properties and method for using same
JP2018135519A (ja) * 2006-12-12 2018-08-30 ユナイテッド・ステイツ・ジプサム・カンパニー 低水分伸張特性を有する不織布ジョントテープ
US10352050B2 (en) 2006-12-12 2019-07-16 United States Gypsum Company Nonwoven joint tape having low moisture expansion properties and method for using same
US8828892B2 (en) 2007-01-18 2014-09-09 Saint-Gobain Adfors Canada, Ltd. Drywall tape and drywall joint
WO2010099563A1 (fr) * 2009-03-05 2010-09-10 Csr Building Products Limited Système amélioré de jonction de plaque de plâtre
US8257526B2 (en) 2009-03-05 2012-09-04 Csr Building Products Limited Plasterboard jointing system
AU2017204076B2 (en) * 2009-03-05 2019-02-14 Csr Building Products Limited Improved Plaster Board Jointing System
WO2014075188A1 (fr) * 2012-11-16 2014-05-22 Shawcor Ltd. Ruban ou feuille renforcé(e) de fibres pour le renforcement d'un tuyau
US11066576B2 (en) 2015-09-21 2021-07-20 United States Gypsum Company Drywall joint tape with dual purpose adhesive backing

Also Published As

Publication number Publication date
CN1788130A (zh) 2006-06-14
BR0318297A (pt) 2006-07-11
AU2003232993A1 (en) 2004-11-26
CA2525971A1 (fr) 2004-11-18
JP2007516366A (ja) 2007-06-21
AU2003232993A8 (en) 2004-11-26
EP1620613A1 (fr) 2006-02-01
CA2427514A1 (fr) 2004-11-01
CA2525971C (fr) 2008-11-18

Similar Documents

Publication Publication Date Title
US7141284B2 (en) Drywall tape and joint
US10352050B2 (en) Nonwoven joint tape having low moisture expansion properties and method for using same
AU2006240151B2 (en) Interior wallboard and method of making same
US8828892B2 (en) Drywall tape and drywall joint
KR101953694B1 (ko) 습윤 지역 또는 습한 지역에 적합한 매트 및 석고 보드
US7482291B2 (en) Low profile reinforcing tape
EP1800853A1 (fr) Matériau pour plaque
CA2525971C (fr) Bande et joint pour cloison seche
JP2007513816A (ja) １つの不織ライナーおよび改善された靱性を有する石膏ボード
JP4779366B2 (ja) 壁紙
JP4779367B2 (ja) 壁紙
US20040203307A1 (en) Wallcovering for use on irregular surfaces
JP7099390B2 (ja) 粘着層付壁紙
TW201540915A (zh) 具有增加之表面強度的建築用板

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SC SD SE SG SK SL TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2525971

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 2004571534

Country of ref document: JP

Ref document number: 2003232993

Country of ref document: AU

WWE Wipo information: entry into national phase

Ref document number: 2003727793

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 20038265796

Country of ref document: CN

WWP Wipo information: published in national office

Ref document number: 2003727793

Country of ref document: EP

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
ENP Entry into the national phase

Ref document number: PI0318297

Country of ref document: BR

WWW Wipo information: withdrawn in national office

Ref document number: 2003727793

Country of ref document: EP

DPE2 Request for preliminary examination filed before expiration of 19th month from priority date (pct application filed from 20040101)