WO2004097073A1 - Bipolar plate comprising metal wire - Google Patents
Bipolar plate comprising metal wire Download PDFInfo
- Publication number
- WO2004097073A1 WO2004097073A1 PCT/EP2003/050130 EP0350130W WO2004097073A1 WO 2004097073 A1 WO2004097073 A1 WO 2004097073A1 EP 0350130 W EP0350130 W EP 0350130W WO 2004097073 A1 WO2004097073 A1 WO 2004097073A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer wall
- metal wire
- electrode
- bipolar plate
- wire knitted
- Prior art date
Abstract
Description
Claims