WO2004083348A2 - Non-volatile lubricant system for medical devices - Google Patents
Non-volatile lubricant system for medical devices Download PDFInfo
- Publication number
- WO2004083348A2 WO2004083348A2 PCT/US2004/007419 US2004007419W WO2004083348A2 WO 2004083348 A2 WO2004083348 A2 WO 2004083348A2 US 2004007419 W US2004007419 W US 2004007419W WO 2004083348 A2 WO2004083348 A2 WO 2004083348A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- siloxane polymer
- film
- composition
- forming composition
- centistokes
- Prior art date
Abstract
Description
Claims