WO2004069453A2 - Refractory metal annealing bands - Google Patents
Refractory metal annealing bands Download PDFInfo
- Publication number
- WO2004069453A2 WO2004069453A2 PCT/US2004/002695 US2004002695W WO2004069453A2 WO 2004069453 A2 WO2004069453 A2 WO 2004069453A2 US 2004002695 W US2004002695 W US 2004002695W WO 2004069453 A2 WO2004069453 A2 WO 2004069453A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- annealing
- powder
- band
- annealing band
- component
- Prior art date
Abstract
Description
Claims