Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B22—CASTING; POWDER METALLURGY
  • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
  • B22F9/00—Making metallic powder or suspensions thereof
  • B22F9/16—Making metallic powder or suspensions thereof using chemical processes
  • B22F9/18—Making metallic powder or suspensions thereof using chemical processes with reduction of metal compounds
  • B22F9/28—Making metallic powder or suspensions thereof using chemical processes with reduction of metal compounds starting from gaseous metal compounds
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B82—NANOTECHNOLOGY
  • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
  • B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B21/00—Nitrogen; Compounds thereof
  • C01B21/06—Binary compounds of nitrogen with metals, with silicon, or with boron, or with carbon, i.e. nitrides; Compounds of nitrogen with more than one metal, silicon or boron
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
  • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
  • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
  • C04B35/62605—Treating the starting powders individually or as mixtures
  • C04B35/62625—Wet mixtures
  • C04B35/6264—Mixing media, e.g. organic solvents
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
  • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
  • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
  • C04B35/62605—Treating the starting powders individually or as mixtures
  • C04B35/62645—Thermal treatment of powders or mixtures thereof other than sintering
  • C04B35/6268—Thermal treatment of powders or mixtures thereof other than sintering characterised by the applied pressure or type of atmosphere, e.g. in vacuum, hydrogen or a specific oxygen pressure
• • C—CHEMISTRY; METALLURGY
  • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
  • C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
  • C22B34/00—Obtaining refractory metals
  • C22B34/10—Obtaining titanium, zirconium or hafnium
  • C22B34/12—Obtaining titanium or titanium compounds from ores or scrap by metallurgical processing; preparation of titanium compounds from other titanium compounds see C01G23/00 - C01G23/08
  • C22B34/1263—Obtaining titanium or titanium compounds from ores or scrap by metallurgical processing; preparation of titanium compounds from other titanium compounds see C01G23/00 - C01G23/08 obtaining metallic titanium from titanium compounds, e.g. by reduction
  • C22B34/1268—Obtaining titanium or titanium compounds from ores or scrap by metallurgical processing; preparation of titanium compounds from other titanium compounds see C01G23/00 - C01G23/08 obtaining metallic titanium from titanium compounds, e.g. by reduction using alkali or alkaline-earth metals or amalgams
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B22—CASTING; POWDER METALLURGY
  • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
  • B22F2999/00—Aspects linked to processes or compositions used in powder metallurgy
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/60—Particles characterised by their size
  • C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/60—Particles characterised by their size
  • C01P2004/62—Submicrometer sized, i.e. from 0.1-1 micrometer
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/60—Particles characterised by their size
  • C01P2004/64—Nanometer sized, i.e. from 1-100 nanometer

Definitions

• This invention relates to the Armstrong Process as described in U.S. Patent Nos. 5,779,761 , 5,958,106 and 6,409,797, the disclosures of each of which is incorporated herein by reference.
• the steady state reaction temperature could be varied depending upon the amount of excess liquid metal or the ratio of liquid metal to halide being reduced.
• the above-identified patents taught that using a greater excess of the liquid metal beyond the stoichiometric amount required for the reaction would produce a lower steady state reaction temperature and similarly, diluting or reducing the amount of halide introduced into the liquid metal would also reduce the steady state operating temperature of the process.
• powder is produced having average size distributions in the range of from about 0.1 micron to about 10 microns, in fact what was produced was not controllable but was whatever happened to be produced according to the parameters of the reaction.
• Powder morphology has been discovered to be an important factor in the production of powder.
• larger diameter powders have larger packing fractions and the control of the powder morphology has become an important aspect in the development of the Armstrong Process. It has been discovered that powder morphology is affected by a number of parameters including the temperature of the reaction zone, the length of time that the material stays in the reaction zone.
• Yet another object of the present invention is to control the temperature of reactants in the reaction zone.
• Yet another object of the present invention is to provide a method of controlling the morphology of the powder produced with the Armstrong Process in which the temperature of the reaction products in the reaction zone and the time in which the products remain in the reaction zone are manipulated to control the size of the powder produced by the reaction.
• Another object of the present invention is to control the temperature of the reaction products in the reaction zone by varying one or more of the pressure of the reaction zone, the constituents of the reaction zone and the time that the constituents remain in the reaction zone.
• Still another object of the present invention is to control the temperature of the reactants in the reaction zone by means of controlling the reactants in the reaction zone by adding a reactive gas to the reaction zone.
• Yet another object of the present invention is to provide an apparatus for controlling the morphology of the powder during the practice of the Armstrong invention in which the amount of excess liquid metal reductant is controlled during the reaction and subsequent thereto for quenching purposes.
• a final object of the present invention is to provide an apparatus of the type set forth in which a gas injection nozzle is surrounded with a sleeve forming an annulus extending axially of a conduit providing liquid metal flow so as to control the amount of liquid metal present in the reaction zone and yet provide a substantial increase in the amount of liquid metal downstream of the reaction zone.
• FIGURE 1 is a schematic representation of an apparatus for practicing the invention.
• the temperature of the reaction products can be maintained at a higher temperature for a longer period of time than possible if the reaction products are immediately exposed to large excess of sodium as soon as the reaction products are formed.
• a material such as a refractory and keeping the reaction products separated from large excess liquid metal which cools the reaction products by absorbing the heat of reaction, less cooling occurs and a longer high temperature reaction zone is obtained.
• longer high temperature reaction zone we mean a few inches where the temperatures of the reaction products are very high. Extending the high temperature zone prior to cooling the reaction products of salt and powder with additional liquid metal allows the powder particles to coalesce forming larger particles.
• reaction products could, if the excess sodium present was very small, reach very high temperatures at which steel or even titanium may fail.
• a ceramic environment can contain reaction products at high temperatures permitting larger particles to form. Any ceramic which is non-reactive with the reaction products at the reaction temperatures (for instance, such as a yttria tube or a metal tube with an interior surface of yttria, such as a tungsten tube internally coated with yttria) is applicable to the invention.
• reaction zone is a bubble containing vapor of the liquid reducing metal and liquid as well as vapor of the salt produced and the product powders.
• the upper limit of the temperature within the reaction zone is the boiling point of the salt produced by the reaction, for so long as liquid salt remains the phase change from liquid alt to vapor soaks up sufficient heat that the temperature will not exceed the salt boiling point. However, if all salt is in the vapor phase, then the temperature within the reaction zone can increase to the melting point of the produced powder.
• reaction zone temperature as well as the time at which reaction products are retained at reaction zone temperatures control to some degree, the morphology of the produced powder.
• reaction zone temperature There are a variety of conditions or combination of conditions which enable us to control reaction zone temperature and residence time of the produced powder in the reaction zone.
• the temperature of the reaction zone can be controlled by increasing the pressure at which the reaction occurs or by adding a reactive gas, such as a halide, preferably chlorine, or by limiting the amount of reducing metal in the reaction zone.
• a reactive gas such as a halide, preferably chlorine
• Duration in the reactor zone can be controlled by the length of the reaction zone, all as will be described, and various combinations may also be used.
• TiCI 4 from a boiler 10 flows as a vapor through a nozzle 11 into a stream 14 of sodium contained in a tubular reactor 12.
• a ceramic tube 15 or metal tube having an internal surface of ceramic or other high temperature material contains the high temperature reaction products and extends the time at which the reaction products remain at high temperature before the reaction products exit the tube 15 at the end 16 thereof to encounter a large excess of liquid sodium in a quench zone 17 formed by sodium 18 contained in a larger tube or reactor 19.
• a source 20 is in fluid communication with the chloride vapor being reduced.
• the temperature in the reaction zone is limited by the phase changes of the material in the reaction zone produced such as the salt or the reductant metal or the produced elemental material or alloy.
• the reaction product stream contains a slurry of excess liquid sodium and solid sodium chloride and solid titanium powder. While the boiling point of the sodium chloride is higher than the boiling point of the sodium and lower than the melting point of titanium, in the reaction zone, as stated, in sodium vapor. NaCI liquid and vapor and titanium solid.
• the boiling point of the sodium chloride needs to be raised so that it equals or exceeds the melting point of the titanium. If the boiling point of the reductant metal (such as sodium) and the produced salt (such as NaCI) is raised above the melting point of the produced elemental material (such as Ti) or alloy, the element material (such as Ti) or alloy or ceramic particles produced can melt and coalesce, thereby forming larger particles with smaller surface areas and higher packing fractions.
• the reductant metal such as sodium
• the produced salt such as NaCI
• the control of the reaction zone temperature is accomplished by operating the reaction zone under pressure so that the boiling point of the produced salt (NaCI) exceeds the melting point of the produced elemental material or alloy (titanium), the pressure required to increase the boiling point of NaCI above the melting point of Ti is not large. Pressures in the range of from about 14 psig to about 150 psig are useful to make powder having diameters in the 0.1 to about 20 micron range. Moreover, particularly, 2-3 atmospheres effectively -raise the boiling point of NaCI to requisite temperatures.
• the process of the present invention controls the size, surface area and packing fraction of particles produced by the method disclosed in the above identified patents by increasing the pressure in the reaction zone to control the temperature of the materials in the reaction zone so that the melting point of the produced metal is lower than the boiling point of the produced salt.
• the limit of the temperature in the reaction zone is the boiling point of the highest boiling material in the reaction zone which exists in two phases.
• the NaCI now molten
• the NaCI will begin to boil and its boiling point of 1465°C at one atm will limit the reaction zone temperature. Because the boiling point of NaCI 1465°C at one atm is lower than the melting point of Ti (1662°C), the temperature in the reaction zone will remain below the Ti melting point, as long as liquid NaCI is present. Raising the pressure in the range of from about 2 to about 3 atmospheres, increases the boiling point of the NaCI, permitting the temperature in the reaction zone to increase.
• a reactant gas such as chlorine
• chloride gas such as by combining chloride gas with the TiCI 4
• the temperature of the reaction products can be raised beyond the boiling point of sodium chloride so that the titanium particles produced will melt, coalesce and become larger.
• the reactant gas must contribute more energy to the reaction than it absorbs or the invention will not have its intended result.
• the reactant gas should be selected to avoid adding unwanted impurities to the produced elemental material or alloy thereof. Additions of chlorine in the range of from about 90 mole percent to about 200 mole percent of the halide being reduced will provide increased temperature in the reaction zone.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Organic Chemistry (AREA)
• Manufacturing & Machinery (AREA)
• Materials Engineering (AREA)
• Ceramic Engineering (AREA)
• Inorganic Chemistry (AREA)
• Environmental & Geological Engineering (AREA)
• Geology (AREA)
• Structural Engineering (AREA)
• Nanotechnology (AREA)
• Life Sciences & Earth Sciences (AREA)
• Physics & Mathematics (AREA)
• General Life Sciences & Earth Sciences (AREA)
• Mechanical Engineering (AREA)
• Composite Materials (AREA)
• General Physics & Mathematics (AREA)
• Metallurgy (AREA)
• Condensed Matter Physics & Semiconductors (AREA)
• Thermal Sciences (AREA)
• General Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Crystallography & Structural Chemistry (AREA)
• Manufacture Of Metal Powder And Suspensions Thereof (AREA)
• Manufacture And Refinement Of Metals (AREA)
• Physical Or Chemical Processes And Apparatus (AREA)
• Inorganic Compounds Of Heavy Metals (AREA)

Priority Applications (4)

Applications Claiming Priority (6)

Publications (3)

Family

ID=31982360

Family Applications (1)

Country Status (6)

Cited By (2)

Families Citing this family (13)

Family Cites Families (7)

• 2003
  • 2003-09-03 WO PCT/US2003/027391 patent/WO2004022269A2/en not_active Ceased
  • 2003-09-03 US US10/654,150 patent/US7351272B2/en not_active Expired - Fee Related
  • 2003-09-03 AU AU2003265876A patent/AU2003265876B2/en not_active Ceased
  • 2003-09-03 JP JP2004534417A patent/JP4409433B2/ja not_active Expired - Fee Related
  • 2003-09-03 CA CA002498024A patent/CA2498024A1/en not_active Abandoned
  • 2003-09-03 EA EA200500461A patent/EA009910B1/ru not_active IP Right Cessation

Also Published As

Similar Documents

Legal Events