WO2004018115A1 - Multilayer coating system comprising thiol-functional compounds - Google Patents
Multilayer coating system comprising thiol-functional compounds Download PDFInfo
- Publication number
- WO2004018115A1 WO2004018115A1 PCT/EP2003/008503 EP0308503W WO2004018115A1 WO 2004018115 A1 WO2004018115 A1 WO 2004018115A1 EP 0308503 W EP0308503 W EP 0308503W WO 2004018115 A1 WO2004018115 A1 WO 2004018115A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- groups
- thiol
- composition
- coating system
- resin
- Prior art date
Abstract
Description
Claims