WO2003062920A2 - Pochoirs elastomeriques pour cellules de microstructuration - Google Patents

Pochoirs elastomeriques pour cellules de microstructuration Download PDF

Info

Publication number
WO2003062920A2
WO2003062920A2 PCT/US2002/026003 US0226003W WO03062920A2 WO 2003062920 A2 WO2003062920 A2 WO 2003062920A2 US 0226003 W US0226003 W US 0226003W WO 03062920 A2 WO03062920 A2 WO 03062920A2
Authority
WO
WIPO (PCT)
Prior art keywords
stencil
article
mold
precursor
substrate
Prior art date
Application number
PCT/US2002/026003
Other languages
English (en)
Other versions
WO2003062920A3 (fr
Inventor
Mehmet Toner
Albert Folch
David J. Beebe
Original Assignee
The General Hospital Corporation
The Board Of Trustees Of The University Of Illinois
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by The General Hospital Corporation, The Board Of Trustees Of The University Of Illinois filed Critical The General Hospital Corporation
Priority to AU2002365249A priority Critical patent/AU2002365249A1/en
Publication of WO2003062920A2 publication Critical patent/WO2003062920A2/fr
Publication of WO2003062920A3 publication Critical patent/WO2003062920A3/fr

Abstract

La présente invention concerne de nouveaux procédés et techniques de fabrication permettant de produire et d'utiliser des pochoirs afin de microstructurer des cellules. Ces techniques autorisent la fabrication de pochoirs plus minces. L'invention concerne également un système d'application sélective de cellules sur des zones préétablies d'un substrat. Un pochoir est à proximité d'un substrat, de manière à couvrir quelques parties du substrat tout en laissant d'autres parties du substrat à découvert. Le pochoir peut être traversé d'un ou de plusieurs canaux et, dans certains cas, ces canaux peuvent présenter une dimension de section transversale inférieure à 1 mm. Le pochoir peut être appliqué sur un substrat de culture cellulaire de manière à former une structure cellulaire microscopique sur le substrat, et le pochoir peut former un joint d'étanchéité ou autre contact étanche avec le substrat dans certains cas. Dans un mode de réalisation, le pochoir peut être appliqué sur un substrat avant ensemencement. Des cellules sont appliquées sur les parties découvertes de la surface, et le pochoir peut être retiré, selon que de besoin. Le pochoir peut être fabriqué, par exemple, par injection d'un précurseur élastomérique dans un moule, ou par polymérisation d'un précurseur élastomérique par application d'une pression. Dans quelques modes de réalisation, la surface du pochoir peut également être oxydée, ou être traitée de façon à rendre la surface du pochoir plus hydrophile, par exemple par traitement de la surface à l'oxygène et au plasma.
PCT/US2002/026003 2001-08-15 2002-08-15 Pochoirs elastomeriques pour cellules de microstructuration WO2003062920A2 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU2002365249A AU2002365249A1 (en) 2001-08-15 2002-08-15 Elastomeric stencils for micropatterning cells

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US31240501P 2001-08-15 2001-08-15
US60/312,405 2001-08-15

Publications (2)

Publication Number Publication Date
WO2003062920A2 true WO2003062920A2 (fr) 2003-07-31
WO2003062920A3 WO2003062920A3 (fr) 2003-10-09

Family

ID=27613173

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2002/026003 WO2003062920A2 (fr) 2001-08-15 2002-08-15 Pochoirs elastomeriques pour cellules de microstructuration

Country Status (2)

Country Link
AU (1) AU2002365249A1 (fr)
WO (1) WO2003062920A2 (fr)

Cited By (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6893850B2 (en) 2000-03-17 2005-05-17 President And Fellows Of Harvard College Method for cell patterning
US7070701B2 (en) 2002-10-08 2006-07-04 Seiko Epson Corporation Manufacturing method of fine structure, optical element, integrated circuit, and electronic instrument
EP2161043A1 (fr) * 2008-09-05 2010-03-10 Ecole Polytechnique Federale De Lausanne (Epfl) Dispositif médical revêtu et procédé de revêtement d'un dispositif médical
WO2014184687A1 (fr) * 2013-05-17 2014-11-20 Indian Institute Of Technology Kanpur Matrices à base de microbes pour impression par microcontact et procédé de préparation et d'utilisation de ces dernières
US20150004358A1 (en) * 2012-02-09 2015-01-01 Wonjae Jung Free-standing polymer membrane having through-holes and method for manufacturing same
WO2016149394A1 (fr) 2015-03-17 2016-09-22 President And Fellows Of Harvard College Système automatisé de fabrication de membrane
US10605805B2 (en) 2015-09-14 2020-03-31 Essenlix Corporation Device and system for analyzing a sample, particularly blood, as well as methods of using the same
US10628693B2 (en) 2016-12-21 2020-04-21 Essenlix Corporation Devices and methods for authenticating a sample and use of the same
US10807095B2 (en) 2017-10-26 2020-10-20 Essenlix Corporation Making and tracking assay card
US10830761B2 (en) 2015-09-14 2020-11-10 Essenlix Corporation Device and system for collecting and analyzing vapor condensate, particularly exhaled breath condensate, as well as method of using the same
US10948389B2 (en) 2015-08-10 2021-03-16 Essenlix Corporation Bio/chemical assay devices and methods for simplified steps, small samples, accelerated speed, and ease-of-use
US11156606B2 (en) 2018-01-11 2021-10-26 Essenlix Corporation Homogeneous assay (II)
US11237113B2 (en) 2017-10-26 2022-02-01 Essenlix Corporation Rapid pH measurement
US11243201B2 (en) 2017-08-01 2022-02-08 Essenlix Corporation Sample collection, holding and assaying
US11274996B2 (en) 2017-02-07 2022-03-15 Essenlix Corporation Compressed open flow assay and use
US11280706B2 (en) 2017-08-01 2022-03-22 Essenlix Corporation Dilution calibration
US11393561B2 (en) 2017-10-13 2022-07-19 Essenlix Corporation Devices and methods for authenticating a medical test and use of the same
US11510608B2 (en) 2017-12-14 2022-11-29 Essenlix Corporation Devices, systems, and methods for monitoring hair
US11523752B2 (en) 2017-02-16 2022-12-13 Essenlix Corporation Assay for vapor condensates
US11604148B2 (en) 2017-02-09 2023-03-14 Essenlix Corporation Colorimetric assays
US11609224B2 (en) 2017-10-26 2023-03-21 Essenlix Corporation Devices and methods for white blood cell analyses
US11648551B2 (en) 2017-12-12 2023-05-16 Essenlix Corporation Sample manipulation and assay with rapid temperature change
US11725227B2 (en) 2017-08-01 2023-08-15 Essenlix Corporation Devices and methods for examining drug effects on microorganisms
US11883824B2 (en) 2017-02-09 2024-01-30 Essenlix Corporation Assay using different spacing heights
US11885952B2 (en) 2018-07-30 2024-01-30 Essenlix Corporation Optics, device, and system for assaying and imaging
US11927560B2 (en) 2017-02-08 2024-03-12 Essenlix Corporation Bio/chemical material extraction and assay
US11940382B2 (en) 2017-02-09 2024-03-26 Essenlix Corporation Assay with amplification
US12007315B2 (en) 2017-02-08 2024-06-11 Essenlix Corporation Sample collection and handling for delayed analysis
US12066434B2 (en) 2017-02-08 2024-08-20 Essenlix Corporation QMAX assays and applications

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4022521A (en) * 1974-02-19 1977-05-10 Honeywell Inc. Microscope slide
US5324591A (en) * 1987-03-06 1994-06-28 Geo-Centers, Inc. Deep ultraviolet photolithographically defined ultra-thin films for selective cell adhesion and outgrowth and method of manufacturing the same and devices containing the same
US5512131A (en) * 1993-10-04 1996-04-30 President And Fellows Of Harvard College Formation of microstamped patterns on surfaces and derivative articles
US5593814A (en) * 1989-06-03 1997-01-14 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Control of cell arrangement

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4022521A (en) * 1974-02-19 1977-05-10 Honeywell Inc. Microscope slide
US5324591A (en) * 1987-03-06 1994-06-28 Geo-Centers, Inc. Deep ultraviolet photolithographically defined ultra-thin films for selective cell adhesion and outgrowth and method of manufacturing the same and devices containing the same
US5593814A (en) * 1989-06-03 1997-01-14 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Control of cell arrangement
US5512131A (en) * 1993-10-04 1996-04-30 President And Fellows Of Harvard College Formation of microstamped patterns on surfaces and derivative articles

Cited By (39)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6893850B2 (en) 2000-03-17 2005-05-17 President And Fellows Of Harvard College Method for cell patterning
US7070701B2 (en) 2002-10-08 2006-07-04 Seiko Epson Corporation Manufacturing method of fine structure, optical element, integrated circuit, and electronic instrument
EP2161043A1 (fr) * 2008-09-05 2010-03-10 Ecole Polytechnique Federale De Lausanne (Epfl) Dispositif médical revêtu et procédé de revêtement d'un dispositif médical
WO2010026557A3 (fr) * 2008-09-05 2010-08-19 Ecole Polytechnique Federale De Lausanne (Epfl) Dispositif médical revêtu et procédé de revêtement d’un dispositif médical destiné à réduire la fibrose et la formation de capsules
JP2012501716A (ja) * 2008-09-05 2012-01-26 エコール ポリテクニック フェデラル ド ローザンヌ（ウーペーエフエル） コーティングした医療用器具、ならびに線維症および被膜形成を低減するための医療用器具のコーティング方法
US20150004358A1 (en) * 2012-02-09 2015-01-01 Wonjae Jung Free-standing polymer membrane having through-holes and method for manufacturing same
WO2014184687A1 (fr) * 2013-05-17 2014-11-20 Indian Institute Of Technology Kanpur Matrices à base de microbes pour impression par microcontact et procédé de préparation et d'utilisation de ces dernières
EP3271127A4 (fr) * 2015-03-17 2018-11-21 President and Fellows of Harvard College Système automatisé de fabrication de membrane
WO2016149394A1 (fr) 2015-03-17 2016-09-22 President And Fellows Of Harvard College Système automatisé de fabrication de membrane
US11654399B2 (en) 2015-03-17 2023-05-23 President And Fellows Of Harvard College Method for micromolding a polymeric membrane having a pore array
AU2016233335B2 (en) * 2015-03-17 2021-03-25 President And Fellows Of Harvard College Automated membrane fabrication system
US10948389B2 (en) 2015-08-10 2021-03-16 Essenlix Corporation Bio/chemical assay devices and methods for simplified steps, small samples, accelerated speed, and ease-of-use
US11385143B2 (en) 2015-08-10 2022-07-12 Essenlix Corporation Bio/chemical assay devices and methods for simplified steps, small samples, accelerated speed, and ease-of-use
US10605805B2 (en) 2015-09-14 2020-03-31 Essenlix Corporation Device and system for analyzing a sample, particularly blood, as well as methods of using the same
US10830761B2 (en) 2015-09-14 2020-11-10 Essenlix Corporation Device and system for collecting and analyzing vapor condensate, particularly exhaled breath condensate, as well as method of using the same
US11543408B2 (en) 2015-09-14 2023-01-03 Essenlix Corporation Device and system for analyzing a sample, particularly blood, as well as methods of using the same
US11415570B2 (en) 2015-09-14 2022-08-16 Essenlix Corporation Rapid vapor condensate collection and analysis
US10628693B2 (en) 2016-12-21 2020-04-21 Essenlix Corporation Devices and methods for authenticating a sample and use of the same
US11274996B2 (en) 2017-02-07 2022-03-15 Essenlix Corporation Compressed open flow assay and use
US12066434B2 (en) 2017-02-08 2024-08-20 Essenlix Corporation QMAX assays and applications
US12007315B2 (en) 2017-02-08 2024-06-11 Essenlix Corporation Sample collection and handling for delayed analysis
US11927560B2 (en) 2017-02-08 2024-03-12 Essenlix Corporation Bio/chemical material extraction and assay
US11940382B2 (en) 2017-02-09 2024-03-26 Essenlix Corporation Assay with amplification
US11604148B2 (en) 2017-02-09 2023-03-14 Essenlix Corporation Colorimetric assays
US11883824B2 (en) 2017-02-09 2024-01-30 Essenlix Corporation Assay using different spacing heights
US11523752B2 (en) 2017-02-16 2022-12-13 Essenlix Corporation Assay for vapor condensates
US11725227B2 (en) 2017-08-01 2023-08-15 Essenlix Corporation Devices and methods for examining drug effects on microorganisms
US11243201B2 (en) 2017-08-01 2022-02-08 Essenlix Corporation Sample collection, holding and assaying
US11280706B2 (en) 2017-08-01 2022-03-22 Essenlix Corporation Dilution calibration
US11796538B2 (en) 2017-08-01 2023-10-24 Essenlix Corporation Sample collection, holding and assaying
US11393561B2 (en) 2017-10-13 2022-07-19 Essenlix Corporation Devices and methods for authenticating a medical test and use of the same
US10807095B2 (en) 2017-10-26 2020-10-20 Essenlix Corporation Making and tracking assay card
US11609224B2 (en) 2017-10-26 2023-03-21 Essenlix Corporation Devices and methods for white blood cell analyses
US11237113B2 (en) 2017-10-26 2022-02-01 Essenlix Corporation Rapid pH measurement
US11648551B2 (en) 2017-12-12 2023-05-16 Essenlix Corporation Sample manipulation and assay with rapid temperature change
US11696723B2 (en) 2017-12-14 2023-07-11 Essenlix Corporation Devices, systems, and methods for monitoring hair
US11510608B2 (en) 2017-12-14 2022-11-29 Essenlix Corporation Devices, systems, and methods for monitoring hair
US11156606B2 (en) 2018-01-11 2021-10-26 Essenlix Corporation Homogeneous assay (II)
US11885952B2 (en) 2018-07-30 2024-01-30 Essenlix Corporation Optics, device, and system for assaying and imaging

Also Published As

Publication number Publication date
AU2002365249A1 (en) 2003-09-02
WO2003062920A3 (fr) 2003-10-09

Similar Documents

Publication Publication Date Title
WO2003062920A2 (fr) Pochoirs elastomeriques pour cellules de microstructuration
Folch et al. Microfabricated elastomeric stencils for micropatterning cell cultures
Branch et al. Microstamp patterns of biomolecules for high-resolution neuronal networks
AU2001243656B2 (en) Cell patterning technique
Kim et al. Fabrication of nanostructures of polyethylene glycol for applications to protein adsorption and cell adhesion
US8906282B2 (en) Micro-structured and nano-structured surfaces on biodegradable polymers
US6455311B1 (en) Fabrication of vascularized tissue
JP4507845B2 (ja) 細胞培養容器、及び培養細胞
US20030175824A1 (en) Drug candidate screening systems based on micropatterned hydrogels and microfluidic systems
AU2001243656A1 (en) Cell patterning technique
Folch et al. Stacks of microfabricated structures as scaffolds for cell culture and tissue engineering
WO2009086535A2 (fr) Systèmes et procédés de formation de matériaux de matrice extracellulaire comportant un motif
WO2017087693A2 (fr) Réseau de micropuits à base d'hydrogel personnalisable
US7655457B2 (en) Cell culture vessel and cultured cell
WO2011027932A1 (fr) Procédé de production de microfibres polymères à surface poreuse pour ingénierie tissulaire
EP3922431A1 (fr) Procédé de fabrication de microdispositifs pour des applications de laboratoire sur puce
US20070231850A1 (en) Patterned Cell Network Substrate Interface and Methods and Uses Thereof
US20090022896A1 (en) Method for Producing a Structured Elastomer and Elastomer
Snyder et al. Fabrication of multiple microscale features on polymer surfaces for applications in tissue engineering
KR101986016B1 (ko) 단일 세포 트래핑 장치 및 제작 방법
Snyder et al. Microscale three-dimensional polymeric platforms for in vitro cell culture systems
CN112933284A (zh) 一种用于组织粘附的仿生贴片及其制备方法
CA2565855A1 (fr) Interface de substrat de reseau cellulaire a motif et ses procedes et utilisations
KR102159231B1 (ko) 세포 배양용 용기 및 이의 제조방법
Dixon Micro-and Nano-Engineering Cellular Patterns with Plasma Technologies.

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TN TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR IE IT LU MC NL PT SE SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase in:

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP