WO2003039800A1 - Improved consumable electrode arc welding - Google Patents
Improved consumable electrode arc welding Download PDFInfo
- Publication number
- WO2003039800A1 WO2003039800A1 PCT/AU2002/001510 AU0201510W WO03039800A1 WO 2003039800 A1 WO2003039800 A1 WO 2003039800A1 AU 0201510 W AU0201510 W AU 0201510W WO 03039800 A1 WO03039800 A1 WO 03039800A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- contact
- tip
- bore
- wire
- primary
- Prior art date
Abstract
Description
Claims