WO2003018237A1 - Appareil de coulee sous pression - Google Patents

Appareil de coulee sous pression Download PDF

Info

Publication number
WO2003018237A1
WO2003018237A1 PCT/AU2002/001141 AU0201141W WO03018237A1 WO 2003018237 A1 WO2003018237 A1 WO 2003018237A1 AU 0201141 W AU0201141 W AU 0201141W WO 03018237 A1 WO03018237 A1 WO 03018237A1
Authority
WO
WIPO (PCT)
Prior art keywords
alloy
transfer vessel
vessel
gas
port
Prior art date
Application number
PCT/AU2002/001141
Other languages
English (en)
Inventor
Morris Taylor Murray
Matthew Alan Cope
Original Assignee
Commonwealth Scientific And Industrial Research Organisation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from AUPR7216A external-priority patent/AUPR721601A0/en
Application filed by Commonwealth Scientific And Industrial Research Organisation filed Critical Commonwealth Scientific And Industrial Research Organisation
Publication of WO2003018237A1 publication Critical patent/WO2003018237A1/fr

Abstract

L'invention concerne un appareil de coulée (10) d'alliages sous pression élevée comprenant un récipient de transfert (22) d'alliage fondu capable de contenir un volume d'alliage requis mesuré à transférer dans un outil matrice (14) et suffisant pour exécuter un cycle de coulée unique afin de produire au moins une coulée. Ledit récipient de transfert (22) comprend un orifice de chargement (51) commandé par une soupape (48), cet orifice situé au niveau d'une région supérieure du récipient de transfert (22) permettant de charger le volume d'alliage mesuré dans ce récipient (22), et un orifice de sortie (62) situé au niveau de la base dudit récipient (22) ou adjacente à celle-ci permettant de décharger un écoulement dans l'outil matrice (14). Le récipient de transfert (22) comprend également un orifice (70) d'alimentation de gaz, situé au niveau de la région supérieure, permettant de fournir un gaz au-dessus de la surface du volume d'alliage mesuré dans le récipient, le récipient (22) pouvant être mis sous pression afin de décharger un alliage par l'intermédiaire de l'orifice de sortie pour l'écouler dans l'outil matrice (14).
PCT/AU2002/001141 2001-08-23 2002-08-23 Appareil de coulee sous pression WO2003018237A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
AUPR7216 2001-08-23
AUPR7216A AUPR721601A0 (en) 2001-08-23 2001-08-23 Apparatus for pressure casting
AU29303/02A AU2930302A (en) 2001-08-23 2002-03-28 Apparatus for pressure casting
AU29303/02 2002-03-28

Publications (1)

Publication Number Publication Date
WO2003018237A1 true WO2003018237A1 (fr) 2003-03-06

Family

ID=25621027

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/AU2002/001141 WO2003018237A1 (fr) 2001-08-23 2002-08-23 Appareil de coulee sous pression

Country Status (2)

Country Link
AU (1) AU2930302A (fr)
WO (1) WO2003018237A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1670605A1 (fr) * 2003-08-15 2006-06-21 Commonwealth Scientific And Industrial Research Organisation Systeme d'ecoulement pour moulage sous pression
RU2680814C2 (ru) * 2015-06-17 2019-02-27 федеральное государственное бюджетное образовательное учреждение высшего образования "Нижегородский государственный технический университет им. Р.Е. Алексеева" (НГТУ) Установка для получения дисперсно-упроченного алюминиевого сплава

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3012047A1 (de) * 1980-03-28 1981-10-08 Norsk Hydro Magnesiumgesellschaft mbH, 4300 Essen Dosiereinrichtung zum foerdern von fluessigem metall
DE3050183A1 (de) * 1980-03-28 1983-01-27 Norsk Hydro Magnesiumgesellschaft mbH, 4300 Essen Dosiereinrichtung zum foerdern von fluessigem metall
JP2001121250A (ja) * 1999-10-22 2001-05-08 Toshiba Mach Co Ltd 成形機の原料注入装置

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3012047A1 (de) * 1980-03-28 1981-10-08 Norsk Hydro Magnesiumgesellschaft mbH, 4300 Essen Dosiereinrichtung zum foerdern von fluessigem metall
DE3050183A1 (de) * 1980-03-28 1983-01-27 Norsk Hydro Magnesiumgesellschaft mbH, 4300 Essen Dosiereinrichtung zum foerdern von fluessigem metall
JP2001121250A (ja) * 1999-10-22 2001-05-08 Toshiba Mach Co Ltd 成形機の原料注入装置

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
DATABASE WPI Derwent World Patents Index; Class A32, AN 2001-435974/47 *
DATABASE WPI Derwent World Patents Index; Class M22, AN 1981-75866D/42 *
DATABASE WPI Derwent World Patents Index; Class P53, AN 1983-09838K/05 *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1670605A1 (fr) * 2003-08-15 2006-06-21 Commonwealth Scientific And Industrial Research Organisation Systeme d'ecoulement pour moulage sous pression
EP1670605A4 (fr) * 2003-08-15 2006-12-06 Commw Scient Ind Res Org Systeme d'ecoulement pour moulage sous pression
RU2680814C2 (ru) * 2015-06-17 2019-02-27 федеральное государственное бюджетное образовательное учреждение высшего образования "Нижегородский государственный технический университет им. Р.Е. Алексеева" (НГТУ) Установка для получения дисперсно-упроченного алюминиевого сплава

Also Published As

Publication number Publication date
AU2930302A (en) 2003-02-27

Similar Documents

Publication Publication Date Title
US6293759B1 (en) Die casting pump
US5335711A (en) Process and apparatus for metal casting
US4874471A (en) Device for casting a metal in the pasty phase
EP0732980B1 (fr) Appareil et procede de coulage
US20070215308A1 (en) Vertical Casting Apparatus and Vertical Casting Method
US9427803B2 (en) Alloy casting apparatus
MXPA04001490A (es) Metodo y aparato para colar espuma de aluminio a baja presion.
US4153100A (en) Low-pressure or counterpressure casting apparatus
US4777998A (en) Machine for pressure casting of metal parts possibly containing fibres of ceramic materials
US3874440A (en) Moulds for producing light alloy and other castings
CA1079930A (fr) Dispositif de coulee a basse-pression ou a contre-pression
WO2003018237A1 (fr) Appareil de coulee sous pression
KR20010107613A (ko) 경금속 주물, 특히 마그네슘 및 마그네슘 합금의 부품을제조하기 위한 방법 및 장치
CN112689544B (zh) 铸造设备
JPH0245940B2 (fr)
EP1085955B1 (fr) Moulage a modele perdu avec bassin de coulee a porte d'alimentation inversee
US5385197A (en) Method and apparatus for feeding a recessed sand mold with molten metal under low pressure
US6698494B1 (en) Casting method and apparatus
JPH04231144A (ja) 金属の低圧鋳造のための方法、鋳型及び設備
EP1001861B1 (fr) Procede et systeme de moulages d'objets metalliques dans des cavites se remplissant de bas en haut
US5176196A (en) Method and apparatus for feeding liquid metal into a mold
GB2103132A (en) A method and apparatus for low pressure casting of metals
GB2206512A (en) Production of cast components having reduced porosity
JPH07112593B2 (ja) 金属の低圧多段鋳造を行うための方法、鋳型及び装置
JPH0428467B2 (fr)

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BY BZ CA CH CN CO CR CU CZ DE DM DZ EC EE ES FI GB GD GE GH HR HU ID IL IN IS JP KE KG KP KR LC LK LR LS LT LU LV MA MD MG MN MW MX MZ NO NZ OM PH PL PT RU SD SE SG SI SK SL TJ TM TN TR TZ UA UG US UZ VC VN YU ZA ZM

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ UG ZM ZW AM AZ BY KG KZ RU TJ TM AT BE BG CH CY CZ DK EE ES FI FR GB GR IE IT LU MC PT SE SK TR BF BJ CF CG CI GA GN GQ GW ML MR NE SN TD TG

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR IE IT LU MC NL PT SE SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP