WO2003006364A2 - Zeolite ssz-59 - Google Patents

Zeolite ssz-59 Download PDF

Info

Publication number
WO2003006364A2
WO2003006364A2 PCT/US2002/021019 US0221019W WO03006364A2 WO 2003006364 A2 WO2003006364 A2 WO 2003006364A2 US 0221019 W US0221019 W US 0221019W WO 03006364 A2 WO03006364 A2 WO 03006364A2
Authority
WO
WIPO (PCT)
Prior art keywords
methyl
zeolite
catalyst
cation
oxide
Prior art date
Application number
PCT/US2002/021019
Other languages
English (en)
Other versions
WO2003006364A3 (fr
Inventor
Saleh Elomari
Original Assignee
Chevron U.S.A. Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US09/905,461 external-priority patent/US6464956B1/en
Priority claimed from US09/905,353 external-priority patent/US6461578B1/en
Priority claimed from US09/905,351 external-priority patent/US6547958B1/en
Application filed by Chevron U.S.A. Inc. filed Critical Chevron U.S.A. Inc.
Priority to JP2003512143A priority Critical patent/JP4383856B2/ja
Priority to EP02748044A priority patent/EP1409402A4/fr
Priority to AU2002318478A priority patent/AU2002318478A1/en
Publication of WO2003006364A2 publication Critical patent/WO2003006364A2/fr
Publication of WO2003006364A3 publication Critical patent/WO2003006364A3/fr

Abstract

L'invention concerne une nouvelle zéolite cristalline SSZ-59 préparée au moyen d'un agent matriciel à cation N-méthyl-N-[(1-phénylcyclopentyl)méthyl]heptaméthylèneiminium, à cation N-méthyl-N-[(1-(4-chlorophenyl)cyclopentyl)méthyl]heptaméthylèneiminium, à cation N-méthyl-N-[1-(4-chlorophenyl)cyclopentyl)méthyl]hexaméthylèneiminium, à cation N-méthyl-N-[(1-phénylcyclopentyl)méthyl]hexaméthylèneiminium, à cation N-méthyl-N-[(1-phénylcyclopentyl)méthyl]piperidinium ou à cation N-méthyl-N-[(1-(4-chlorophényl)cyclopentyl)méthyl]piperidinium. L'invention concerne également des procédés qui utilisent SSZ-59 dans un catalyseur.
PCT/US2002/021019 2001-07-13 2002-07-03 Zeolite ssz-59 WO2003006364A2 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
JP2003512143A JP4383856B2 (ja) 2001-07-13 2002-07-03 ゼオライトｓｓｚ−５９
EP02748044A EP1409402A4 (fr) 2001-07-13 2002-07-03 Zeolite ssz-59
AU2002318478A AU2002318478A1 (en) 2001-07-13 2002-07-03 Zeolite ssz-59

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US09/905,461 US6464956B1 (en) 2001-07-13 2001-07-13 Zeolite SSZ-59 composition of matter and synthesis thereof
US09/905,461 2001-07-13
US09/905,353 US6461578B1 (en) 2001-07-13 2001-07-13 Using zeolite SSZ-59 for reduction of oxides of nitrogen in a gas stream
US09/905,351 US6547958B1 (en) 2001-07-13 2001-07-13 Hydrocarbon conversion using zeolite SSZ-59
US09/905,351 2001-07-13
US09/905,353 2001-07-13

Publications (2)

Publication Number Publication Date
WO2003006364A2 true WO2003006364A2 (fr) 2003-01-23
WO2003006364A3 WO2003006364A3 (fr) 2003-09-25

Family

ID=27420606

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2002/021019 WO2003006364A2 (fr) 2001-07-13 2002-07-03 Zeolite ssz-59

Country Status (4)

Country Link
EP (1) EP1409402A4 (fr)
JP (1) JP4383856B2 (fr)
AU (1) AU2002318478A1 (fr)
WO (1) WO2003006364A2 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007536252A (ja) * 2004-05-07 2007-12-13 インサイト・コーポレイション アミド化合物およびその医薬としての使用
WO2023154656A1 (fr) * 2022-02-10 2023-08-17 ExxonMobil Technology and Engineering Company Utilisation de cations choisis parmi 1,2,3,5-tétraméthylbenzimidazolium, et 1,2,3,4,5-pentaméthylbenzimidazolium en tant qu'agents d'orientation de structure pour la préparation de tamis moléculaires et tamis moléculaires obtenus à l'aide de ceux-ci

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8647602B2 (en) * 2012-06-08 2014-02-11 Chevron U.S.A. Inc. Method for making aluminosilicate zeolite SSZ-56

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5433933A (en) * 1989-12-21 1995-07-18 Toyota Jidosha Kabushiki Kaisha Method of purifying oxygen-excess exhaust gas
US5489424A (en) * 1994-08-24 1996-02-06 Board Of Regents, The University Of Texas System Synthesis of novel molecular sieves using a metal complex as a template
US5785947A (en) * 1991-12-18 1998-07-28 Chevron U.S.A. Inc. Preparation of zeolites using organic template and amine
US5965104A (en) * 1996-12-31 1999-10-12 Chevron U.S.A. Inc. Zeolite SSZ-43

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5580540A (en) * 1995-12-01 1996-12-03 Chevron U.S.A. Inc. Zeolite SSZ-44
EP0951445A1 (fr) * 1996-12-31 1999-10-27 Chevron U.S.A. Inc. Procede pour preparer des zeolites au moyen de cations de piperidine substitues
US6632417B2 (en) * 2000-03-07 2003-10-14 Chevron U.S.A. Inc. Process for preparing zeolites

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5433933A (en) * 1989-12-21 1995-07-18 Toyota Jidosha Kabushiki Kaisha Method of purifying oxygen-excess exhaust gas
US5785947A (en) * 1991-12-18 1998-07-28 Chevron U.S.A. Inc. Preparation of zeolites using organic template and amine
US5489424A (en) * 1994-08-24 1996-02-06 Board Of Regents, The University Of Texas System Synthesis of novel molecular sieves using a metal complex as a template
US5965104A (en) * 1996-12-31 1999-10-12 Chevron U.S.A. Inc. Zeolite SSZ-43

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP1409402A2 *

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007536252A (ja) * 2004-05-07 2007-12-13 インサイト・コーポレイション アミド化合物およびその医薬としての使用
US8058288B2 (en) 2004-05-07 2011-11-15 Incyte Corporation Amido compounds and their use as pharmaceuticals
JP2013151519A (ja) * 2004-05-07 2013-08-08 Incyte Corp アミド化合物およびその医薬としての使用
US9126927B2 (en) 2004-05-07 2015-09-08 Incyte Holdings Corporation Amido compounds and their use as pharmaceuticals
US9670154B2 (en) 2004-05-07 2017-06-06 Incyte Holdings Corporation Amido compounds and their use as pharmaceuticals
US9957229B2 (en) 2004-05-07 2018-05-01 Incyte Holdings Corporation Amido compounds and their use as pharmaceuticals
WO2023154656A1 (fr) * 2022-02-10 2023-08-17 ExxonMobil Technology and Engineering Company Utilisation de cations choisis parmi 1,2,3,5-tétraméthylbenzimidazolium, et 1,2,3,4,5-pentaméthylbenzimidazolium en tant qu'agents d'orientation de structure pour la préparation de tamis moléculaires et tamis moléculaires obtenus à l'aide de ceux-ci

Also Published As

Publication number Publication date
WO2003006364A3 (fr) 2003-09-25
AU2002318478A1 (en) 2003-01-29
JP2004534711A (ja) 2004-11-18
EP1409402A4 (fr) 2011-11-23
JP4383856B2 (ja) 2009-12-16
EP1409402A2 (fr) 2004-04-21

Similar Documents

Publication Publication Date Title
US6547958B1 (en) Hydrocarbon conversion using zeolite SSZ-59
US6632416B2 (en) Zeolite SSZ-53
US6080382A (en) Zeolite SSZ-48
US6616830B2 (en) Hydrocarbon conversion using zeolite SSZ-57
US6540903B2 (en) Hydrocarbon conversion with zeolite SSZ-47
CA2582295A1 (fr) Tamis moleculaire ssz-65
US6540905B1 (en) Hydrocarbon conversion using zeolite SSZ-58
WO2001066464A2 (fr) Zeolithe ssz-55
US6033643A (en) Zeolite SSZ-45
US5965104A (en) Zeolite SSZ-43
US6827843B2 (en) Hydrocarbon conversion using molecular sieve SSZ-63
US6808620B2 (en) Hydrocarbon conversion using zeolite SSZ-64
EP1409403B1 (fr) Zeolite ssz-57
EP1539642B1 (fr) Tamis moleculaire ssz-64
EP1419105B1 (fr) Zeolite ssz-60
US6540906B1 (en) Hydrocarbon conversion using zeolite SSZ-60
WO2004060794A2 (fr) Tamis moleculaire ssz-63
EP1409402A2 (fr) Zeolite ssz-59
EP1412289B1 (fr) Zeolithe ssz-58
WO2004094347A2 (fr) Tamis moleculaire ssz-65

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TN TR TT TZ UA UG UZ VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR IE IT LU MC NL PT SE SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 2002748044

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2003512143

Country of ref document: JP

WWP Wipo information: published in national office

Ref document number: 2002748044

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642