WO2002058944A1 - Decorative laminate assembly and method of producing same - Google Patents
Decorative laminate assembly and method of producing same Download PDFInfo
- Publication number
- WO2002058944A1 WO2002058944A1 PCT/US2001/013409 US0113409W WO02058944A1 WO 2002058944 A1 WO2002058944 A1 WO 2002058944A1 US 0113409 W US0113409 W US 0113409W WO 02058944 A1 WO02058944 A1 WO 02058944A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- decorative laminate
- layer
- decorative
- laminate
- petg
- Prior art date
Abstract
Description
Claims