WO2001095377A2 - Methods for forming and integrated circuit structures containing enhanced-surface-area conductive layers - Google Patents
Methods for forming and integrated circuit structures containing enhanced-surface-area conductive layers Download PDFInfo
- Publication number
- WO2001095377A2 WO2001095377A2 PCT/US2001/018583 US0118583W WO0195377A2 WO 2001095377 A2 WO2001095377 A2 WO 2001095377A2 US 0118583 W US0118583 W US 0118583W WO 0195377 A2 WO0195377 A2 WO 0195377A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- ruthenium
- forming
- conductive
- oxide
- Prior art date
Abstract
Description
Claims