WO2001085827A2 - Temperature-controlled induction heating of polymeric materials - Google Patents
Temperature-controlled induction heating of polymeric materials Download PDFInfo
- Publication number
- WO2001085827A2 WO2001085827A2 PCT/US2001/014079 US0114079W WO0185827A2 WO 2001085827 A2 WO2001085827 A2 WO 2001085827A2 US 0114079 W US0114079 W US 0114079W WO 0185827 A2 WO0185827 A2 WO 0185827A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- particles
- composition
- heating
- matrix
- ferromagnetic
- Prior art date
Abstract
Description
Claims