WO2001040363A1 - Mousse polystyrene extrudee a temperature de vicat superieure a 100 °c - Google Patents

Mousse polystyrene extrudee a temperature de vicat superieure a 100 °c Download PDF

Info

Publication number
WO2001040363A1
WO2001040363A1 PCT/US2000/031147 US0031147W WO0140363A1 WO 2001040363 A1 WO2001040363 A1 WO 2001040363A1 US 0031147 W US0031147 W US 0031147W WO 0140363 A1 WO0140363 A1 WO 0140363A1
Authority
WO
WIPO (PCT)
Prior art keywords
blowing agent
foam
mixture
pressure
foam product
Prior art date
Application number
PCT/US2000/031147
Other languages
English (en)
Inventor
Larry M. Miller
Raymond M. Breindel
Mitchell Z. Weekley
Thomas E. Cisar
Original Assignee
Owens Corning
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Owens Corning filed Critical Owens Corning
Priority to AU17633/01A priority Critical patent/AU1763301A/en
Priority to EP00980360A priority patent/EP1246866A1/fr
Publication of WO2001040363A1 publication Critical patent/WO2001040363A1/fr

Abstract

La présente invention concerne un procédé de préparation d'un produit mousse consistant (A) à former un mélange expansible constitué (1) d'au moins un polymère de styrène linéaire ayant une température de ramollissement Vicat supérieure à 100 °C (212°F) au moins, et (2) d'un agent d'expansion comprenant une quantité majeure d'un agent d'expansion inorganique, à une pression suffisante pour empêcher le prémoussage du mélange et (B) à mousser le mélange dans une région sous pression réduite pour former le produit mousse. Dans un autre mode de réalisation, l'invention concerne un procédé de préparation d'un produit mousse consistant (A) à former un mélange expansible constitué (1) d'au moins un polystyrène linéaire ayant une température de ramollissement Vicat supérieure à 100 °C (212°F) au moins, et (2) d'un agent d'expansion comprenant une quantité majeure d'un agent d'expansion inorganique, à une pression suffisante pour empêcher le prémoussage du mélange, et (B) à mousser le mélange à travers une filière dans une région sous pression réduite pour former le produit mousse, ledit procédé étant caractérisé en ce que la pression de l'opération (A) équivaut à deux fois au moins la pression au niveau de la filière. L'invention concerne également des panneaux de mousse fabriqués conformément à ces procédés. L'invention concerne notamment des panneaux de mousse exempts d'halogènes. Les mousses ainsi produites présentent une résistance à la compression améliorée et possèdent une certaine stabilité dimensionnelle.
PCT/US2000/031147 1999-11-30 2000-11-14 Mousse polystyrene extrudee a temperature de vicat superieure a 100 °c WO2001040363A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
AU17633/01A AU1763301A (en) 1999-11-30 2000-11-14 Extruded polystyrene foam with vicat temperature over 100 degreesc
EP00980360A EP1246866A1 (fr) 1999-11-30 2000-11-14 Mousse polystyrene extrudee a temperature de vicat superieure a 100 c

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US45161799A 1999-11-30 1999-11-30
US09/451,617 1999-11-30

Publications (1)

Publication Number Publication Date
WO2001040363A1 true WO2001040363A1 (fr) 2001-06-07

Family

ID=23792972

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2000/031147 WO2001040363A1 (fr) 1999-11-30 2000-11-14 Mousse polystyrene extrudee a temperature de vicat superieure a 100 °c

Country Status (3)

Country Link
EP (1) EP1246866A1 (fr)
AU (1) AU1763301A (fr)
WO (1) WO2001040363A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5772830A (en) * 1980-10-23 1982-05-07 Asahi Chem Ind Co Ltd Foamed plate of styrene-based resin
US5182308A (en) * 1990-07-04 1993-01-26 Basf Aktiengesellschaft Production of foam sheets of high compressive strength
DE4402909A1 (de) * 1994-02-01 1995-08-03 Basf Ag Unter Verwendung halogenfreier Treibmittel hergestellte Schaumstoffplatten
US5576094A (en) * 1993-05-27 1996-11-19 Basf Aktiengesellschaft Foam boards produced using halogen-free blowing agents
JPH1053662A (ja) * 1997-05-28 1998-02-24 Sekisui Plastics Co Ltd 加熱成形用スチレン系樹脂発泡シート

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5772830A (en) * 1980-10-23 1982-05-07 Asahi Chem Ind Co Ltd Foamed plate of styrene-based resin
US5182308A (en) * 1990-07-04 1993-01-26 Basf Aktiengesellschaft Production of foam sheets of high compressive strength
US5576094A (en) * 1993-05-27 1996-11-19 Basf Aktiengesellschaft Foam boards produced using halogen-free blowing agents
DE4402909A1 (de) * 1994-02-01 1995-08-03 Basf Ag Unter Verwendung halogenfreier Treibmittel hergestellte Schaumstoffplatten
JPH1053662A (ja) * 1997-05-28 1998-02-24 Sekisui Plastics Co Ltd 加熱成形用スチレン系樹脂発泡シート

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
D. BENDER: "Kunststoff Handbuch 4", 1996, HANSER, MÜNCHEN, XP002158358, 952216 *
PATENT ABSTRACTS OF JAPAN vol. 006, no. 157 (M - 150) 18 August 1982 (1982-08-18) *
PATENT ABSTRACTS OF JAPAN vol. 1998, no. 06 30 April 1998 (1998-04-30) *

Also Published As

Publication number Publication date
AU1763301A (en) 2001-06-12
EP1246866A1 (fr) 2002-10-09

Similar Documents

Publication Publication Date Title
CA2344338C (fr) Procede de production de mousse extrudee avec du co2 comme agent porogene
EP1124887B1 (fr) Procede de production de mousse extrudee
US6123881A (en) Process for producing extruded foam products having polystyrene blends with high levels of CO2 as a blowing agent
CA2399239C (fr) Produit de mousse extrudee a defauts de surface reduits
KR100626135B1 (ko) 스티렌계 발포물의 제조 방법
WO1996016111A1 (fr) Mousse en resine de polystyrene et procede pour produire la mousse
WO1998003581A1 (fr) Mousses thermoplastiques a alveoles fermees contenant hfc-134
EP1246866A1 (fr) Mousse polystyrene extrudee a temperature de vicat superieure a 100 c
JP2001055463A (ja) ポリプロピレン系樹脂押出発泡シート
CA3198253A1 (fr) Agents gonflants pour mousse de polystyrene extrude et mousse de polystyrene extrude et procedes de moussage

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2000980360

Country of ref document: EP

AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWP Wipo information: published in national office

Ref document number: 2000980360

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWW Wipo information: withdrawn in national office

Ref document number: 2000980360

Country of ref document: EP