WO2000078450A1

WO2000078450A1 - MANUFACTURING METHOD OF CdS PHOTOCATALYST FOR HYDROGEN PRODUCTION

Info

Publication number: WO2000078450A1
Application number: PCT/KR2000/000411
Authority: WO
Inventors: Dae Chul Park; Jin Wook Baek
Original assignee: Chonggu Co., Ltd.; Korea Research Institute Of Chemical Technology
Priority date: 1999-06-18
Filing date: 2000-05-01
Publication date: 2000-12-28
Also published as: CN1317993A; CA2340923A1; RU2238145C2; AU740440B2; EP1113876A4; KR100301281B1; CN1121271C; JP3586242B2; US6447650B1; JP2003502148A; BR0006818A; EP1113876A1; KR20010002898A; AU4616900A

Abstract

The present invention relates to a method for preparing a CdS photocatalyst (photocatalyst system) used in photolysis of water and a method for producing hydrogen in the presence of CdS photocatalyst. A method for preparing a CdS photocatalyst represented by general formula (I): m(a)/Cd[M(b)]S, comprising the steps of: dissolving Cd-containing and M-containing compounds in water in such an amount that the mol % of M ranges from 0.001 to 20.00; adding one H2S or Na2S as a reactant in the solution with stirring to precipitate Cd[M]S; washing the precipitate with water and vacuum-drying the precipitate in a nitrogen and thermostat at 105-150 °C for 1.5-3.0 hours; doping a liquid m-containing compound to this precipitate in such an amount that the % by weight of m ranges from 0.10 to 5.00. In said formula m represents a doped metal element as an electron acceptor selected from the group of Ni, Pd, Pt, Fe, Ru, Co or an oxidized compound of these metals; a represents a percentage by weight of m, ranging from 0.10 to 5.00; M is a promoter selected from the group consisting of V, Cr, Al, P, As, Sb and Pb; b represents mol % of M/(M+Cd), ranging from 0.001 to 20.00. In accordance with a further aspect of the present invention, there is provided a method for producing hydrogen, in which visible light adjusted by light filter or sunlight is irradiated onto a suspension of the photocatalyst in water to which 0.05-1.00 mol of Na2S (as an electron donor) and 0.05-1.00 mol of Na2SO3 (as a reducing agent) are added.

Description

MANUFACTURING METHOD OF CdS PHOTOCATALYST FOR HYDROGEN PRODUCTION

Technical Field

The present invention relates, in general, to a method for preparing a photocatalyst for hydrogen production and a method 10 for producing hydrogen by use of the same, more particularly, to a method for preparing a CdS photocatalyst for the use of hydrogen production and to a photoreaction in which hydrogen is efficiently produced from water in the presence of the CdS photocatalyst.

15 Background Art

In general, hydrogen is used to produce ammonia and methanol in the chemical industry. Hydrogen is also an essential material for hydrogenation in which unsaturated compounds are 20 converted into saturated ones and for hydrotreating processes, including hydrogen addition, desulfurization, denitrogenation and demetallization. Another example for the use of hydrogen is contact hydrogenation of carbon dioxide which causes global warming. In addition, hydrogen is viewed as a pollution-free,

25 clear energy source substituting for existing fossil fuels.

Conventional techniques for obtaining hydrogen include extraction from fossil fuels, such as naphtha, modification of natural gas, reaction of vapor with iron at a high temperature, 30 reaction of water with alkaline metal, electrolysis of water, etc.

However, the said conventional methods are not economically favorable because immense heat or electric energy is required. Regarding modification of fossil fuels, the conventional methods have another disadvantage of generating a large quantity of by-products, such as carbon dioxide. In case of electrolysis, problems, such as a short electrode lifetime and generation of by-products, should be solved to purify hydrogen more easily. Thus the cost of facilities for hydrogen production is economically unfavorable due to the noted problems.

In the nature, some of hydrogen exists in various compounds forms, particularly in inorganic forms but most of it exists in water. Only a small quantity of hydrogen exists in the atmosphere because it is of low specific gravity. It is also very difficult and economically unfavorable to purify hydrogen existing in inorganic forms.

Therefore, a method to produce hydrogen from water will be a very meaningful technique in near future. Recently, hydrogen producing techniques have been developed in which photocatalysts are used to decompose water into hydrogen and oxygen. However, little has been published in prior art relating to photocatalysts for producing hydrogen. Representative examples are Japanese Pat. Laid-Open

Publication Nos. Sho 62-191045 and Sho 63-107815 and a couple of Korean Patent applications by the present inventors as described as below.

Japanese Pat. Laid-Open Publication No. Sho 62-191045 relates to generating hydrogen from an aqueous Na₂S solution in the presence of a rare earth element compound by a photolysis reaction. The rare earth element compound has an advantage of exhibiting optical activity in the range of visible light.

Japanese Pat. Laid-Open Publication No. Sho 63-107815 concerns a photolysis reaction in which a composite oxide of niobium and alkaline earth metal is used as a photocatalyst to generate hydrogen from a methanol solution in water. This photocatalyst likewise has an advantage of being active in the range of visible light.

However, both of the said prior arts are disadvantageous because the amount of hydrogen generated is as little as 10 ml/0.5g hr.

Korean Pat. Application No. 95-7721 applied by the present inventors solve the above problems to some degree by suggesting a photocatalyst represented by the following formula I-

Cs(a)/K Nb₆O₇ I

This technique has little affect on the environment and generates hydrogen at room temperature but the oxygen-containing organic compounds is needed as hydrogen-generating promoters.

Korean Pat. Application No. 95-30416 suggests a photocatalyst represented by the following formula II:

Cs(a)H(c)/S(b) π

This technique has little affect on the environment and generates hydrogen without an oxygen-containing organic compounds as a hydrogen-generating promoter at room temperature, but encounters a problem with the life time and the stability of the photocatalyst. For example, when an alkali metal, such as cesium, is impregnated into a photo-carrier, the amount of generated hydrogen is increased outstandingly but the stability of the catalyst is decreased.

Similarly, Korean Pat. Application No. 96-44214 suggests a photocatalyst represented by the following formula EL Pt(A)/Zn[M(B)]S m

This technique also has little affect on the environment. This compound shows not only the optical activity of photocatalyst in some degree but also the preparation is relatively simple and the stability of photocatalyst is superior. The life time of said compound is longer which depends on electron donors and reducing agents and the amount of generated hydrogen is larger than that of prior arts. When doping with Pt instead of Cs, the stability of the catalyst is improved but still the amount of generated hydrogen is not enough in the economic point of view.

Korean Pat. Application No. 98-37179 suggests a photocatalyst represented by the following formula IV:

Pt(a)/Zn[M(b)]S IV

This technique also has little affect on the environment and the said photocatalyst has optical activity in some degree in the range of visible light. The preparation of the said photocatalyst is more simpler and by-products are much less produced.

To solve the above problem, Korean Pat. Application 98-37180 by present inventors suggests a photocatalyst represented by the following formula V:

m(A)/Cd[M(B)]S V

The said photocatalyst shows an optical activity in the range of visible light adjusted by light filter as well as sun light. The amount of generated hydrogen is much larger and the life time of the said photocatalyst is semi-infinitive. By introducing various doping metals and promoters and other new methods, the said application solves the restricted activity to the light source and suggests more simple preparation process. Likewise, the life time of photocatalyst is also longer and the amount of generated hydrogen from water is remarkably larger than that of prior art. However, this technique shows limited hydrogen activity only to one reducing agent.

Disclosure of the Invention

Therefore, it is an object of the present invention to overcome the previously-noted problems encountered in prior art, and to provide economical reduction system which remarkably improves the restricted activity of photocatalysts of prior art. It is an another object of the present invention to provide that the preparation of the photocatalyst in the present invention is more simple and has little affect on the environment.

It is an another object of the present invention to provide that the photocatalyst in the present invention has an optical activity in the range of visible light adjusted by light filter as well as sun light and thus the amount of generated hydrogen is much larger.

It is an further object of the present invention to provide the life time of the photocatalyst in the present invention being semi-infinitive.

Best Mode for Carrying Out the Invention

A photocatalyst in accordance with the present invention represented by the following formula VI: m(A)/Cd[M(B)]S VI

wherein m represents a doped metal element as an electron acceptor selected from the group of Ni, Pd, Pt, Fe, Ru, Co or an oxidized compound of these metals; a represents a percentage by weight of m, ranging from 0.10 to 5.00; M is a promoter selected from the group consisting of V, Cr, Al, P, As, Sb and Pb; b represents mole% of M/(M+Cd), ranging from 0.001 to 20.00. A method for preparing the said photocatalyst of formula VI, comprising the steps of : dissolving Cd-containing and M-containing compounds in water in such an amount that the mol % of M ranges from 0.001 to 20.00; adding H2S or Na₂S as a reactant in the solution with stirring to precipitate Cd[M]S; washing the precipitate with water and vacuum-drying the precipitate in a nitrogen and thermostat at

105-150 "C for 1.5-3.0 hours; doping a liquid m-containing compound to this precipitate in such amount that the % by weight of m ranges from 0.10 to 5.00.

Likewise prior art of present inventors, hydrogen is produced by a method in which visible light adjusted by a light filter or sun light is irradiated onto a suspension of the said photocatalyst in water to which Na2S as a electron donor and NaH2PO2 or Na2Sθ3 as a reducing agent have been added.

In detail, the present invention will be described as below. In the formula VI, m represents a doped metal element as an electron acceptor selected from the group of Ni, Pd, Pt, Fe, Ru, Co or an oxidized compound of these metals; a represents a percentage by weight of m, ranging from 0.10 to 5.00. Below 0.10 % by weight, the amount of generated hydrogen is decreased, and the stability of the photocatalyst is also reduced. On the other hand, over 5.00 % by weight, the amount of generated hydrogen is decreased, and the cost of production of photocatalyst is also increased. M is a promoter selected from the group consisting of V, Cr, Al,

P, As, Sb and Pb; b represents mole% of M/(M+Cd), ranging from 0.001 to 20.00. Incase of less than 0.001 mole % of M, the function of photocatalyst is lost, and in case of over 20.00 mole % of M, the amount of generated hydrogen is decreased. The appropriate molar ratio of Cd/S is from 1:0.1 to 1:2.8, and more desirably from 1:0.6 to 1:1.4. Within said molar ratio, the effectiveness of the photocatalyst is improved.

In the preparation of the said photocatalyst, if m is platinum(pt) as a doping element, it is preferable for Pt to be illuminated with UV in a nitrogen atmosphere and doped on the Cd[M]S by sintering. More preferably, hydrogen hexachloroplatinatedV) (H2PtClθ) is added to the Cd[M]S precipitate and irradiated with UV light in a nitrogen atmosphere to impregnate the carrier at such an amount that the value of A for Pt(A) ranges from 0.10 to 5.00. The precipitate thus obtained is washed with water until the wash water pH reaches 7, vacuum-dried at 105 to 130 °C for 1.5 to 3.0 hours, oxidation-sintered at 300 to 400 °C for 1.0 to 5.0 hours and then reduction- sintered at 300 to 400 °C for 1.0 to 5.0 hours.

In case of other doping elements except Pt, the preferable preparation example of the photocatalyst comprises the steps of : adding an m-containing compound other than platinum to the Cd[M]S precipitate obtained to reach the value of m ranging from 0.10 to 5.00; adding slowly 6 or 7 drops of cone, hydrochloric acid with stirring; applying ultrasonication to the obtained slurry for 1.0 to 5.0 minutes; drying at 110 to 130 °C for 1.5 to 3.0 hours in vacuo; oxidation- sintering at 300 to 400 °C for 1.0 to 5.0 hours and then reduction-sintering at 300 to 400 ^°C for 1.0 to 5.0 hours.

In the preparation of photocatalyst doped with Pt, the reason why it is dried and sintered at oxidation/reduction state after the pH reaches 7 is to keep electron acceptor, Pt, in pure state. As well known, when Pt in HaPtClβ is irradiated with UV, Pt activates the surface of CdS and makes a bond with separated S to form PtS and therefore a Wurzite structure is obtained by sintering under oxidation and reduction states at a temperature of 300 to 400 °C for 1.0 to 5.0 hours, Pt as an electron acceptor can be transferred to pure state of Pt(0). More preferably, it should be sintered at a temperature of from 320 to 390 ^°C and beyond this temperature range, the lifetime and optical activity of said photocatalyst is decreased.

Examples of the Cd-containing compounds include CdCl₂, CdBr2, Cdl₂, Cd(CH3CO₂)₂ xH₂O, CdSO xH₂O and Cd(NO₃)₂ 24H₂O and examples of the M-containing compounds include K₂Cr₂θ7, Cr(NO₃)3, A1(N0₃)₃, AlC , Hs PO_2> NaH₂ P0₂, As₂0₅, SbCls, MnCls, KMn0 ,

Pb(N0₃)₂, Pb(CH3CO₂) , RuCb, VCls, VOSO , VOCI3, etc. And examples of the m-containing compounds include FeC , H^PtCle, RuCk, Co(NO₃)₂, CoCl₂, Co(CH3CO₂)₂, NiSO₄, Ni(NO₃)₂, Ni(CHsCO₂)₂, NiC , NiBr₂, Nil₂, Pd(No₃)₂, etc. In Korean Pat. Application No. 96-44214 of present inventors, etching with acid is required after the primary sintering, but in the present invention, only the procedure of drying the precipitate in vacuo in a nitrogen atmosphere is needed, so procedures for the primary sintering and etching with acid can be canceled.

However, according to the present invention hydrogen is produced by dissolving from 0.15 to 1.00 mol of Na₂S as an electron donor and from 0.15 to 1.00 mol of H2PO₂ or SO₃ as a reducing agent in primary and/or secondary distilled water or in the previously treated water, and adding the photocatalyst of the present invention thereto.

Then, the thus-obtained suspension is irradiated with visible light adjusted by a light filter or sunlight with stirring at a temperature of from 5 to 85 ^°C under from 0.1 up to 5 atm. to produce hydrogen from water in a high degree of efficiency.

In addition, it is an important step to keep the concentration range of electron donor and reducing agent within the noted limits. If it is below the lower limit, the amount of hydrogen generated is decreased; if it is excess, the amount of hydrogen generated can not be increased further and the optimal reaction condition is at a temperature of from 10 to 60 "C in from a vacuum to 2 atm.

The photocatalyst of the present invention has an semi-infinitive lifetime if the electron donor and reducing agents are added repeatedly to the reaction. The reaction time of ZnS photocatalyst in prior art is only 6 to 8 hours, but, surprisingly, the reaction time of photocatalyst of the present invention is from 20 to 25 hours, which means that said photocatalyst has continuously kept its activity well.

PREPARATION EXAMPLE I to VII

Admix with 125 ml of water, CdSO₄ H₂O, K₂Cr₂0₇ as a promoter and H₂S as a reactant in accordance with each of Table I until a precipitate appears. Stir the resulting admixture wherein the precipitate is CdCrS. Wash this precipitate with wash water until the pH of the wash water reaches 7. Vacuum-dry the thus-washed precipitate in a nitrogen atmosphere at a temperature of 130 °C for 2 hours to yield a CdCrS powder. Add Ni(NO₃) 26H₂O to impart 1% by weight of Ni to the yielded CdCrS powder. Then slowly add 6 to 7 drops of cone, hydrochloric acid with stirring, followed by ultrasonication of the obtained product for 3 minutes, drying at a temperature of 130 °C for 2 hours, and finally oxidation sintering at a temperature of 360 ^°C for 4 hours and again reduction sintering at a temperature of 360 °C for 4 hours to yield a final Ni(l wt. %)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE Vm

Repeat Preparation Example I, except: follow the oxidation sintering at a temperature of 360 °C for 2 hours and again reduction sintering at a temperature of 360 °C for 2 hours to yield a final Ni(l wt. %)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE IX

Repeat Preparation Example I, except: follow the oxidation sintering at a temperature of 360 °C for 2.5 hours and again reduction sintering at a temperature of 360 °C for 2.5 hours to yield a final Ni(l wt. %)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE X

Repeat Preparation Example I, except: follow the oxidation sintering at a temperature of 360 ^°C for 3 hours and again reduction sintering at a temperature of 360 °C for 3 hours to yield a final Ni(l wt. %)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE XI

Repeat Preparation Example I, except: follow the oxidation sintering at a temperature of 360 ^°C for 3.5 hours and again reduction sintering at a temperature of 360 °C for 3.5 hours to yield a final Ni(l wt. %)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE XII

Repeat Preparation Example I except substitute 0.05 mol % for 0.2 mol % of Cr to yield a final Ni(l wt. %)/Cd[Cr(0.05)]S photocatalyst.

PREPARATION EXAMPLE Xm

Repeat Preparation Example I except substitute 0.1 mol % for 0.2 mol % of Cr to yield a final Ni(l wt. %)/Cd[Cr(0.1)]S photocatalyst.

PREPARATION EXAMPLE XIV

Repeat Preparation Example I except substitute 0.5 mol % for 0.2 mol % of Cr to yield a final Ni(l wt. %)/Cd[Cr(0.5)]S photocatalyst.

PREPARATION EXAMPLE XV

Repeat Preparation Example I except substitute 1.0 mol % for 0.2 mol % of Cr to yield a final Ni(l wt. %)/Cd[Cr(1.0)]S photocatalyst. PREPARATION EXAMPLE XVI

Repeat Preparation Example I except substitute RuCb 3H₂O for the Ni(N0₃)₂ 6H₂O to impart 1.0 weight % of Ru to the precipitate and thus yield a final Ru(l wt.%)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE XVII

Repeat Preparation Example XVI except cancel the procedure of the reduction sintering and thus yield a final RuO₂(l wt.%)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE X IX

Repeat Preparation Example I except substitute Co(NO₃)₂ 6H₂O for the Ni(NO₃)₂ 6H₂O to impart 1.0 weight % of Co to yield a final Co(l wt.%)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE XX

Repeat Preparation Example I except substitute Pd(NO₃)₂ for the Ni(N0₃)₂ 6H₂0 to impart 1.0 weight % of Pd to yield a final Co(l wt.%)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE XXI

Repeat Preparation Example I except substitute HzPtClβ for the Ni(NO₃)₂ 6H₂O to impart 1.0 weight % of Pt to the precipitate and thus yield a final Pt(l wt. )/Cd[Cr(0.2)]S photocatalyst. PREPARATION EXAMPLE XXII

Repeat Preparation Example I except substitute

for the Ni(N0₃)₂ 6H₂O to impart 1.0 weight % of Pt to the precipitate and irradiate with UV light in a nitrogen environment for 0.5 hour and wash the precipitate with water until pH 7 reaches and dry at 130 °C for 2 hours and oxidation sintering at 360 ^°C for 4 hours, reduction sintering at 360 °C for 4 hours, and thus yield a final Pt(l wt.%)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE XXIH

Admix with 125 ml of water, CdSO H₂O, 5 mol% of HsPO₂ as a promoter and H₂S as a reactant with stirring until a precipitate appears. Stir the resulting admixture wherein the precipitate is CdPS. Wash this precipitate with wash water until the pH of the wash water reaches 7. Vacuum-dry the thus-washed precipitate in a nitrogen atmosphere at a temperature of 130 °C for 2 hours to yield a CdPS powder. Repeat Preparation Example I except substitute

for the Ni(NO₃)₂ 6H₂O to impart 1.0 weight % of Pt to the obtained CdPS powder and thus yield a final Pt(l wt.%)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE XXIV

Repeat Preparation XX π, except substitute HsPO₂ for K₂Cr₂0₇ as a promoter, to yield a final Pt(l wt.%)/Cd[Cr(0.2)]S photocatalyst.

PREPARATION EXAMPLE XXV

Repeat Preparation Example XX HI except substitute Ni(NO₃)₂ 6H₂O for H2PtCl₆ to impart 1.0 weight % of Ni, to yield a final Ni(l wt.%)/Cd[P(5.0)]S photocatalyst.

PREPARATION EXAMPLE XXVI

Repeat Preparation I, except substitute Al(NO3)3 for K₂Cr₂O₇ as a promoter, to yield a final Ni(l wt.%)/Cd[Al(0.5)]S photocatalyst.

PREPARATION EXAMPLE XXVR

Repeat Preparation I, except substitute As₂Os 2H₂O for K₂Cr₂O₇ as a promoter, to yield a final Ni(l wt.%)/Cd[As(0.5)]S photocatalyst.

PREPARATION EXAMPLE XXVIR

Repeat Preparation XXVII, except impart 2.0 mol % of As as a promoter instead of 0.5 mol % of As, to yield a final Ni(l wt.%)/Cd[As(2.0)]S photocatalyst.

PREPARATION EXAMPLE XXIX

Repeat Preparation I, except substitute MnC for K₂Cr₂O₇ as a promoter, to yield a final Ni(l wt.%)/Cd[Mn(0.2)]S photocatalyst.

PREPARATION EXAMPLE XXX

Repeat Preparation XXIX, except impart 0.5 mol % of Mn instead of 0.2 mol % of Mn as a promoter, to yield a final Ni(l wt.%)/Cd[As(2.0)]S photocatalyst.

PREPARATION EXAMPLE XXXI Repeat Preparation I, except substitute SbCb for K₂Cr₂O7 as a promoter, to yield a final Ni(l wt.%)/Cd[Sb(0.5)]S photocatalyst.

PREPARATION EXAMPLE XXXR

Repeat Preparation XXXI, except impart 2.0 mol % of Sb instead of 0.2 mol % of Sb as a promoter, to yield a final Ni(l wt.%)/Cd[Sb(2.0)]S photocatalyst.

PREPARATION EXAMPLE XXXm

Repeat Preparation I, except impart 2.0 mol % of Sb as a promoter, to yield a final Ni(l wt.%)/Cd[Pb(0.01)]S photocatalyst.

PREPARATION EXAMPLE XXXIV

Repeat Preparation I, except impart 2.0 mol % of Sb as a promoter, to yield a final Ni(l wt.%)/Cd[Pb(0.1)]S photocatalyst.

PREPARATION EXAMPLE XXXV

Repeat Preparation I, except impart 2.0 mol % of Sb as a promoter, to yield a final Ni(l wt.%)/Cd[Pb(0.5)]S photocatalyst.

PREPARATION EXAMPLE XXXVI

Repeat Preparation I, except substitute VCI3 for K₂Cr₂0₇ as a promoter, to yield a final Ni(l wt.%)/Cd[V(0.5)]S photocatalyst.

COMPARATIVE PREPARATION EXAMPLE I

Repeat Preparation I, except impart 3 % by weight of Ni, to yield a final Ni(3wt.%)/Cd[Cr(0.2)]S photocatalyst.

COMPARATIVE PREPARATION EXAMPLE π

Repeat Preparation I, except impart 3 % by weight of Fe, to yield a final Fe(3wt.%)/Cd[Cr(0.2)]S photocatalyst.

EXAMPLE I

Suspend 0.5g of the photocatalyst, obtained in accordance with

Preparation Example I, in 500 ml of water which contains 0.24 mol 1 of Na₂S and 0.36 mol 1 Na₂SO3 and stir the resulting suspension at a speed of 300 rpm in a photo reactor of a closed gas circulation system. Illuminate the resulting suspension with visible light (500 W Xe lamp with an optical filter which passes light with a wavelength over 400nm, with sample 4cm from light source) at room temperature and at 1 atm. On analysis by gas chromatography and Burette the amounts of produced hydrogen thus obtained are reflected in Table I below.

EXAMPLE π

Repeat Example I with 0.5g of the photocatalyst obtained in accordance Preparation Example -Q except impart the molar ratio of

Na₂S : Na SO₃ to be 0.24 mol/1 : 0.36 mol/1 in 500 ml water. On analysis by gas chromatography and Burette the amounts of produced hydrogen thus obtained are reflected in Table I below.

EXAMPLE in

Repeat Example I with 0.5g of the photocatalyst obtained in accordance Preparation Example DI except impart the molar ratio of

Na₂S : Na₂SO₃ to be 048 mol 1 : 0.36 mol/1 in 500 ml water. On analysis by gas chromatography and Burette the amounts of produced hydrogen thus obtained are reflected in Table I below.

EXAMPLE IV

Repeat Example I with 0.5g of the photocatalyst obtained in accordance Preparation Example IV except impart the molar ratio of Na₂S : Na₂SO₃ to be 0.36 mol/1 : 0.24 mol/1 in 500 ml water. On analysis by gas chromatography and Burette the amounts of produced hydrogen thus obtained are reflected in Table I below.

EXAMPLE V

Repeat Example I with 0.5g of the photocatalyst obtained in accordance Preparation Example V except impart the molar ratio of

Na₂S : Na₂SO₃ to be 0.36 mol/1 : 0.48 mol/1 in 500 ml water. On analysis by gas chromatography and Burette the amounts of produced hydrogen thus obtained are reflected in Table I below.

EXAMPLE VI

Repeat Example I with 0.5g of the photocatalyst obtained in accordance Preparation Example VI except impart the molar ratio of

Na₂S : Na₂SO₃ to be 0.24 mol/1 : 0.24 mol/1 in 500 ml water. On analysis by gas chromatography and Burette the amounts of produced hydrogen thus obtained are reflected in Table I below. EXAMPLE Vπ

Repeat Example I with 0.5g of the photocatalyst obtained in accordance Preparation Example VU except impart the molar ratio of Na₂S : Na₂S0₃ to be 0.48 mol/1 : 0.48 mol/1 in 500 ml water. On analysis by gas chromatography and Burette the amounts of produced hydrogen thus obtained are reflected in Table I below.

EXAMPLE Vm TO XXXVI & COMPARATIVE EXAMPLE I TO II

Repeat Example I with 0.5g of the photocatalyst obtained in accordance Preparation Example V-H to XXXVI & Comparative Preparation Example I to π, respectively, except impart the molar ratio of Na₂S : Na₂S0₃ to be 0.36 mol/1 : 0.36 mol/1 in 500 ml water. On analysis by gas chromatography and Burette the amounts of produced hydrogen thus obtained are reflected in Table I below.

EXAMPLE XXXVπ

This procedure measures the lifetime of photocatalyst obtained in accordance with Preparation Example XVQ. Suspend 0.5g of photocatalyst obtained in accordance with Preparation Example XVII in 500 ml of water which contains 0.36 mol/1 of Na₂S and 0.36 mol/1 of Na₂SO₃ and thereafter add a further 0.36 mol/1 of Na₂S and 0.36 mol/1 of

Na2SO₃ into the above solution each subsequent period of 20 hours for total 100 hours, and measure the amount of produced hydrogen. As a result, the average value of the amount of produced gas during this procedure is 260 ml/hr, which is similar to the result (262ml/hr) of Example H Thus, the results of this procedure establishes that the lifetime of the photocatalyst is almost infinite.

TABLE I

Industrial Applicability

As apparent from the data according to Table I, the photocatalysts in accordance with the present invention show various kinds of transition metal included as a promoter and new addition technique thereof, optimal sintering time to enhance the effectiveness of photocatalysts, new contrived reduction system with sulfite in much less cost, improvement of the limited activity of photocatalysts of prior art, more simple preparation having little affect environment and much longer lifetime.

Furthermore, the amount of produced hydrogen increases remarkably as the highest reaction condition and optimal ratio of reducing agents are introduced in this present invention.

Claims

WHAT IS CLAIMED IS:

1. A method for preparing a CdS photocatalyst, represented by the following general formula VI, comprising the steps of: dissolving Cd-containing and M-containing compounds in water in such an amount that the mol % of M ranges from 0.001 to 20.00; adding H₂S or Na₂S as a reactant in the solution with stirring to precipitate Cd[M]S; washing the precipitate with water and vacuum-drying the precipitate in a nitrogen and thermostat at 105-150 ^°C for 1.5-3.0 hours; doping a liquid m-containing compound to this precipitate in such amount that the

% by weight of m ranges from 0.10 to 5.00.

m(a)/Cd[M(b)]S

wherein m represents a doped metal element as an electron acceptor selected from the group of Ni, Pd, Pt, Fe, Ru, Co or an oxidized compound of these metals; a represents a percentage by weight of m, ranging from 0.10 to 5.00; M is a promoter selected from the group consisting of V, Cr, Al, P, As, Sb and Pb; b represents mole% of

M/(M+Cd), ranging from 0.001 to 20.00.

2. A method for preparing said photocatalyst in accordance with claim 1, in which the doing includes sintering after UV illumination or acid treatment and ultrasonication.

3. A method for preparing said photocatalyst in accordance with claim 1, wherein M-containing compounds include K₂Cr2θ7, Cr(NO₃)₃, Al(NO₃)₃, AlCb, H3PO2. NaH₂PO₂, As O₅, SbCls, MnCls, KMnO₄, Pb(NO₃)₂, Pb(CHsCO₂) , RuCls, VCls, VOSO , VOCls.

4. A method for preparing said photocatalyst in accordance with claim 1, wherein m-containing compounds include FeCb, H2PtCl6, RuCb, Co(NO₃)₂, C0CI2,

NiSO , Ni(NO₃)₂, Ni(CH₃CO₂)₂. NiCl₂, NiBr₂, Nil₂, Pd(No₃)₂.

5. A method for preparing said photocatalyst in accordance with claim 1, in which oxidation and reduction sintering at a temperature of 300 to 400 ^°C after doping with UV illumination in a nitrogen environment when m is a platinum.

6. A method for preparing said photocatalyst in accordance with claim 1, wherein Cd- containing compounds include CdCl₂, CdBr₂, Cdl₂, Cd(CH₃CO₂ )₂ xH₂0, CdSO xH₂0 and Cd(NO₃)₂ 24H₂O.

7. A method for preparing said photocatalyst in accordance with claim 1, in which additional hydrochloric acid and ultrasonication treatments before drying are included when m is not a platinum.

8. A method for producing hydrogen, which comprises irradiating with visible light adjusted by a light filter or with sun light, an aqueous suspension of said photocatalyst in Claim 1, while stirring, which aqueous suspension comprises from 0.05 to 1.00 mol/1 of Na₂SO₃ as a reducing agent and from 0.05 to 1.00 mol/1 of Na₂S as an electron donor.

9. A method for producing hydrogen in accordance with Claim 8, which comprises producing hydrogen at a temperature of from 10 to 60 ^°C in from vacuo up to 2 atm. AMENDED CLAIMS

[received by the International Bureau on 26 September 2000 (26.09.00); original claims 1 and 34 amended; other claims unchanged (2 pages)]

1. A method for preparing a CdS photocatalyst, represented by the following general formula VI, comprising the steps of: dissolving Cd-containing and M-containing compounds in water in such an amount that the mol % of M ranges from 0.001 to 20.00 ; adding H₂S or Na₂S as a reactant in the solution with stirring to precipitate Cd[M]S ; washing the precipitate with water and vacuum- drying the precipitate in a nitrogen and thermostat at 105-150 °C for 1.5 ~ 3.0 hours ; doping a liquid m-containing compound to this precipitate in such amount that the % by weight of m ranges from 0.10 to 5.00.

m(a)/Cd[M(b)]S I

wherein m represents a doped metal element as an electron acceptor selected from the group of Fe or an oxidized compound of Fe ; a represents a percentage by weight of m, ranging from 0.10 to 5.00 ; M is a promoter selected from the group consisting of As, Sb and Pd ; b represents mole% of M/(M+Cd), ranging from 0.001 to 20.00.

3. A method for preparing said photocatalyst in accordance with claim 1, wherein M-containing compounds include As₂O₅, SbCl₃, Pd(NO₃)₂, Pd(CH₃CO₂)₄.

AMENDED SHEET /ARTICLE 19)

4. A method for preparing said photocatalyst in accordance with claim 1, wherein m-containing compounds include FeCl₃.

5. A method for preparing said photocatalyst in accordance with claim 1,

in which oxidation and reduction sintering at a temperature of 300 to 400 °C after

doping with UV illumination in a nitrogen environment when m is a platinum.

6. A method for preparing said photocatalyst in accordance with claim 1, wherein Cd-containing compounds include CdCl₂, CdBr₂, Cdl₂, Cd(CH₃CO₂)₂ • xH₂O, CdSO₄ • xH₂O and Cd(NO₃)₂ • 4H₂O.

9. A method for producing hydrogen in accordance with Claim 8, which comprises producing hydrogen at a temperature of from 10 to 60 ^°C in from vacuo up to 2 atm. STATEMENT UNDER ARTICLE 19

According to the International Search Report, we would like to request amendment of claims in this present patent application as attached sheet of amended pages 22&23.

Please refer to the explanation of correction as below.

1. In claim 1, " the group of Ni, Pd, Pt, Fe, Ru, Co or an oxidized compound of these metals " in line 17&18 page 22 of Specification is replaced with " Fe or an oxidized compound of Fe ".

2. In claim 1, " V, Cr, Al, P, As, Sb and Pb " in line 20 page 22 of Specification is replaced with " As, Sb and Pd ".

3. In claim 3, " K₂Cr₂O₇, Cr(NO₃)₃, Al(NO₃)₃, A1C1₃, H₃PO₂, NaH₂PO₂, As₂O₅, SbCl₃, MnCl₃, KMnO₄, Pb(NO₃)₂, Pb(CH₃CO₂)₄, RuCl₃, VC1₃, VOSO₄, VOCl₃ " in line 28-30 page 22 is replaced with "As₂O₅, SbCl₃, Pd(NO₃)₂, Pd(CH₃CO₂)₄".

4. In claim 4, " FeCl₃, H₂PtCl₆, RuCl₃, Co(NO₃)₂, CoCl₂, Co(CH₃CO₂)₂, NiSO₄, Ni(NO₃)₂, Ni(CH₃CO₂)₂, NiCl₂, NiBr₂, Nil₂, Pd(NO₃)₂" in line 2-4 page 23 is replaced with " FeCl₃ ".