Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
  • B01J20/28014—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their form
  • B01J20/28016—Particle form
  • B01J20/28019—Spherical, ellipsoidal or cylindrical
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
  • B01J20/28014—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their form
  • B01J20/28042—Shaped bodies; Monolithic structures
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
  • B29C45/16—Making multilayered or multicoloured articles
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
  • B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
  • B65D75/00—Packages comprising articles or materials partially or wholly enclosed in strips, sheets, blanks, tubes or webs of flexible sheet material, e.g. in folded wrappers
  • B65D75/28—Articles or materials wholly enclosed in composite wrappers, i.e. wrappers formed by associating or interconnecting two or more sheets or blanks
  • B65D75/30—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding
  • B65D75/32—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding one or both sheets or blanks being recessed to accommodate contents
  • B65D75/325—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding one or both sheets or blanks being recessed to accommodate contents one sheet being recessed, and the other being a flat not- rigid sheet, e.g. puncturable or peelable foil
  • B65D75/327—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding one or both sheets or blanks being recessed to accommodate contents one sheet being recessed, and the other being a flat not- rigid sheet, e.g. puncturable or peelable foil and forming several compartments
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
  • B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
  • B65D81/00—Containers, packaging elements, or packages, for contents presenting particular transport or storage problems, or adapted to be used for non-packaging purposes after removal of contents
  • B65D81/24—Adaptations for preventing deterioration or decay of contents; Applications to the container or packaging material of food preservatives, fungicides, pesticides or animal repellants
  • B65D81/26—Adaptations for preventing deterioration or decay of contents; Applications to the container or packaging material of food preservatives, fungicides, pesticides or animal repellants with provision for draining away, or absorbing, or removing by ventilation, fluids, e.g. exuded by contents; Applications of corrosion inhibitors or desiccators
  • B65D81/264—Adaptations for preventing deterioration or decay of contents; Applications to the container or packaging material of food preservatives, fungicides, pesticides or animal repellants with provision for draining away, or absorbing, or removing by ventilation, fluids, e.g. exuded by contents; Applications of corrosion inhibitors or desiccators for absorbing liquids
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
  • B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
  • B65D81/00—Containers, packaging elements, or packages, for contents presenting particular transport or storage problems, or adapted to be used for non-packaging purposes after removal of contents
  • B65D81/24—Adaptations for preventing deterioration or decay of contents; Applications to the container or packaging material of food preservatives, fungicides, pesticides or animal repellants
  • B65D81/26—Adaptations for preventing deterioration or decay of contents; Applications to the container or packaging material of food preservatives, fungicides, pesticides or animal repellants with provision for draining away, or absorbing, or removing by ventilation, fluids, e.g. exuded by contents; Applications of corrosion inhibitors or desiccators
  • B65D81/266—Adaptations for preventing deterioration or decay of contents; Applications to the container or packaging material of food preservatives, fungicides, pesticides or animal repellants with provision for draining away, or absorbing, or removing by ventilation, fluids, e.g. exuded by contents; Applications of corrosion inhibitors or desiccators for absorbing gases, e.g. oxygen absorbers or desiccants
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
  • C08J9/26—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof by elimination of a solid phase from a macromolecular composition or article, e.g. leaching out
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/10—Homopolymers or copolymers of propene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L69/00—Compositions of polycarbonates; Compositions of derivatives of polycarbonates
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L77/00—Compositions of polyamides obtained by reactions forming a carboxylic amide link in the main chain; Compositions of derivatives of such polymers
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F26—DRYING
  • F26B—DRYING SOLID MATERIALS OR OBJECTS BY REMOVING LIQUID THEREFROM
  • F26B21/00—Arrangements or duct systems, e.g. in combination with pallet boxes, for supplying and controlling air or gases for drying solid materials or objects
  • F26B21/06—Controlling, e.g. regulating, parameters of gas supply
  • F26B21/08—Humidity
  • F26B21/083—Humidity by using sorbent or hygroscopic materials, e.g. chemical substances, molecular sieves
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F26—DRYING
  • F26B—DRYING SOLID MATERIALS OR OBJECTS BY REMOVING LIQUID THEREFROM
  • F26B3/00—Drying solid materials or objects by processes involving the application of heat
  • F26B3/28—Drying solid materials or objects by processes involving the application of heat by radiation, e.g. from the sun
  • F26B3/283—Drying solid materials or objects by processes involving the application of heat by radiation, e.g. from the sun in combination with convection
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
  • B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
  • B65D75/00—Packages comprising articles or materials partially or wholly enclosed in strips, sheets, blanks, tubes or webs of flexible sheet material, e.g. in folded wrappers
  • B65D75/28—Articles or materials wholly enclosed in composite wrappers, i.e. wrappers formed by associating or interconnecting two or more sheets or blanks
  • B65D75/30—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding
  • B65D75/32—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding one or both sheets or blanks being recessed to accommodate contents
  • B65D75/34—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding one or both sheets or blanks being recessed to accommodate contents and having several recesses to accommodate a series of articles or quantities of material
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L101/00—Compositions of unspecified macromolecular compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
  • C08L23/08—Copolymers of ethene
  • C08L23/0846—Copolymers of ethene with unsaturated hydrocarbons containing atoms other than carbon or hydrogen
  • C08L23/0853—Ethene vinyl acetate copolymers
  • C08L23/0861—Saponified copolymers, e.g. ethene vinyl alcohol copolymers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L29/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an alcohol, ether, aldehydo, ketonic, acetal or ketal radical; Compositions of hydrolysed polymers of esters of unsaturated alcohols with saturated carboxylic acids; Compositions of derivatives of such polymers
  • C08L29/02—Homopolymers or copolymers of unsaturated alcohols
  • C08L29/04—Polyvinyl alcohol; Partially hydrolysed homopolymers or copolymers of esters of unsaturated alcohols with saturated carboxylic acids
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L71/00—Compositions of polyethers obtained by reactions forming an ether link in the main chain; Compositions of derivatives of such polymers
  • C08L71/02—Polyalkylene oxides
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/13—Hollow or container type article [e.g., tube, vase, etc.]
  • Y10T428/1352—Polymer or resin containing [i.e., natural or synthetic]
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/13—Hollow or container type article [e.g., tube, vase, etc.]
  • Y10T428/1352—Polymer or resin containing [i.e., natural or synthetic]
  • Y10T428/1355—Elemental metal containing [e.g., substrate, foil, film, coating, etc.]
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/13—Hollow or container type article [e.g., tube, vase, etc.]
  • Y10T428/1352—Polymer or resin containing [i.e., natural or synthetic]
  • Y10T428/1376—Foam or porous material containing

Definitions

• Medication in solid form such as tablets, pills, capsules or the like are sometimes dispensed to patients in dispensers having individually sealed compartments or blisters designed to hold a single dose of medication.
• dispensers having individually sealed compartments or blisters designed to hold a single dose of medication.
• Such packages permit the handling of only a single dose of medicine at a time, insure patient compliance, and minimize the risk of contamination of the tablet, pill or capsule.
• blister packs typically have first and second cardboard layers with a plurality of oversize aligned cutout through each layer.
• a cover portion of plastic having a plurality of blisters is placed against and laminated to the first cardboard layer with the blisters extending through the cutouts in that layer, and pills or capsules are placed within the blisters.
• a layer of foil is typically laminated to the second cardboard layer, and a peel-off backing is then removed from the foil to expose an adhesive surface upon the foil.
• the adhesive surface is typically then used to bond the first and second cardboard layers into a sandwich, thereby entrapping the pills within the blisters and creating the sealed unit dose pill package.
• a heated glue or melting techniques may also be used to seal the package.
• the present invention relates to a barrier pack.
• the barrier pack comprises a cover portion bonded to a base portion to form a sealed unit package wherein: (a) the cover portion comprises at least one cavity capable of containing and dispensing a product; (b) the base portion is in relation to the cover portion such that the cavity extends outwardly from the base portion, the base portion comprising an absorbing agent material applied to an interior of the base portion and coextensively aligned with the corresponding cavity of the cover portion.
• the barrier pack comprising a cover portion bonded to a base portion to form a sealed unit package wherein: (a) the cover portion comprises at least one cavity capable of containing and dispensing a product; the cover portion comprising an absorbing agent material applied to an interior portion of the cavity.
• the sealable portions of the cover portion are sealed , directly , or indirectly onto the sealable portions of the base portion.
• the cavities of the cover portion are extended outwardly over the product support portions of the base portion thereby forming at least one space for inserting a product.
• the product may be a medicament or pharmaceutical in the form of tablets, capsules, pills or the like.
• the base portion can be peelable or removable from the cover portion to thereby release the product within the space from the barrier pack.
• the base portion may be composed of peelable aluminum material and the cover portion may be composed of polyvinyl chloride (PVC).
• the cover portion may also be substantially transparent making the product visible to the user.
• the sealable portions of the coverportion of the present invention may be heat sealable or adhesively sealed, directly or indirectly, onto the sealable portion of the base portion.
• the cavities of the cover portion may be composed of a material that is sufficiently flexible to allow for an inverted state when a sufficient force is exerted on the cavity that results in a sufficient counter- force on the coextensive portion of the base portion to thereby allow access to the product to a user.
• the absorbing agent containing layer of the present invention contains a desiccant.
• the absorbing agent containing layer contains a material selected from the group consisting of activated carbon, carbon black, ketcham black and diamond powder.
• the absorbing agent containing layer contains a material selected from the group consisting of absorption microspheres, BaTi0 3 , SrTi0 3 , Si0 2 , A1 2 0 3 , ZnO, Ti0 2 , MnO, CuO, Sb 2 0 3 , silica, calcium oxide and ion exchange resins.
• the absorbing agent containing layer contains two or more types of absorbing agents.
• the present invention relates to a method of manufacturing the barrier pack.
• the method comprises the step of: (a) producing a coverportion comprising at least one cavity; (b) applying an absorbing agent material to an interior of the cavity; (c) placing the product within the cavity of the cover; and (d) sealing a sealable portion of the cover portion to a sealable portion of the base portion and allowing the cavities of the cover layer to be extended outwardly over the product to thereby form a sealed unit package for the product.
• FIGURE 1 is a perspective view of one embodiment of the barrier pack of the present invention.
• the term “barrier pack” means a package that includes a plurality of individually sealed blisters or compartments (e.g. sealed cavities) for containing a product to be dispensed. Such “barrier packs” are exemplified by what is sometimes referred to in the industry as “blister packs.”
• the term “substantially impermeable” layer means a layer composed of a material that is typically considered by the industry to be a barrier against the desired vapor or gas. For example, for moisture vapor, the vapor barrier of a material is typically measured by its moisture vapor transmission rate ("MVTR") and, for purposes of the present invention, material having an MVTR below about 0.25 grams of moisture/mm thick/m 2 surface area/day (measured by
• ASTM F1249 is considered to be a "substantially impermeable” material.
• the term "substantially permeable” layer means a layer composed of a material that is typically considered by the industry to transfer an acceptable amount of the desired vapor or gas through the material. For example, for moisture vapor, the MVTR above about 1.0 grams of moisture/mm thick/m 2 surface area/day (measured by ASTM - F1249) is considered to be a "substantially permeable” material.
• the term “bonded” means to hold two portions directly or indirectly together. Suitable bonding methods include gluing and heat-sealing.
• the barrier pack may have the cover portion "bonded" to the base portion by sealing (e.g. laminating) both or either portions to one or more intermediate layers and, subsequently, joining these layers to the other portion.
• the term “applied” includes coated, spread, dipped, sprayed, painted and deposited.
• the barrier pack 1 comprises a base portion 5 having an absorbing agent material applied to the base portion and coextensively aligned with the corresponding cavity of the cover portion.
• the cover portion 20 has an extendible portions (i.e. cavity) 24 wherein a product 4 such as a pharmaceutical or medicament in the form of a pill, capsule or tablet.
• a product 4 such as a pharmaceutical or medicament in the form of a pill, capsule or tablet.
• the base portion 10 can be composed of a peelable aluminum material and the coverportion 20 may be composed of polyvinyl chloride.
• the cover and base portions, 20 and 10 respectively may be heat sealable plastic .
• the cover portion 10 may be transparent making the product visible to a user.
• the cavity 24 of the cover portion 20 may be adopted to being pushed inward to an inverted state in order to separate the base portion 10 from the barrier pack 1 thereby releasing the product 4 from within the cavity 24.
• the barrier pack of the present invention may have a pull tab for separating the base portion 10 from the cover portion 20 thereby allowing the user access to the product 4.
• the cover portion 20 is overlaid by a base portion 10 which keeps the contents of the cavities in pristine condition.
• the two sheets are heat sealed completely about each cavity.
• the base portion 10 should be relatively stiff in contrast to the cover portion 20 which desirably should be somewhat pliable. The desired degrees of stiffness in the two sheets can thus be achieved by use of thicker material in the cover portion than that used in the base sheet.
• the base portion 10 is an aluminum foil. Access to the product may be achieved by applying finger pressure to the relatively thin, less rigid base sheet to urge the contained product against the foil with sufficient force to tear the foil.
• the coverportion 20 may comprise a laminate structure in which, prior to thermoforming, the lamina comprises polyvinyl chloride (PVC) about 2 mils to about 8 mils thick and a sheet of polymeric material, such as high density polyethylene (HDPE), that has been fluid compression rolled to about 2 to about 6 mils, with a preferred thickness of about 3 mils, which is about 1/3 of its original thickness. Rolling the polymeric material to 1/3 its original thickness provides the ⁇ noformability in the resulting laminate structure as compared to full fluid compression rolling which produces a non-thermoformable material. The sheets are then laminated by adhesion lamination or other suitable lamination methods.
• PVC polyvinyl chloride
• HDPE high density polyethylene
• Suitable substantially moisture vapor impermeable material may include: (1) a laminate structure comprising laminae of PVC and chlorotrifluoroethylene; and (2) a PVC/polyvinylidene chloride (PVDC) combination. It must be noted that the thickness of the above-mentioned materials may have to be increased to decrease its permeability rate and thus, achieve the desired impermeability.
• PVDC polyvinylidene chloride
• the absorbing agent material may be a monolithic composition having interconnecting channels.
• Hydrophilic agents e.g., channeling agents
• a water-insoluble polymer that is used in the formation of shaped articles.
• the water-insoluble polymer base into which the hydrophilic agent is blended includes, as examples, any polyethylene and polypropylene.
• an absorbing agent and hydrophilic agent are added to the water- insoluble polymer when the polymer is in a molten state or before the polymer is in the molten state, so that the absorbing agent and hydrophilic agent may be blended and thoroughly mixed throughout the polymer to insure that the blend is uniformly mixed before reaching the melt phase.
• a technique is useful when the absorbing agent, hydrophilic agent and polymer are all powders.
• the hydrophilic agent and polymer are mixed prior to adding the absorbing agent.
• the hydrophilic agent is added either before the polymer is in the molten state or after the polymer is in the molten state.
• the absorbing agent may be added to the polymer during the thermal process of the absorbing agent material.
• the hydrophilic agent forms interconnecting channels that act as transmission communicating passages throughout the polymer.
• the absorbing agent material is monolithic and the water-insoluble polymer, hydrophilic agent and absorbing agent form a three phase system.
• phase means a portion of a physical system that is uniform throughout, has defined boundaries and, in principle, be separated physically from other phases .
• interconnecting channels means channels that penetrate through the water- insoluble polymer and that may be interconnected to each other.
• water- insoluble polymer means a polymer having a solubility in water below about 0.1 % at 25 *C and atmospheric pressure.
• hydrophilic agent is defined as a material that is not substantially cross-linked and that has a solubility in water of at least about 1 % at 25*0 and atmospheric pressure. Suitable hydrophilic agents include "channeling" agents.
• the term "monolithic composition” means a composition that does not consist of two or more discrete macroscopic layers. Moreover, for purposes of the present invention, the term “melting point” is defined as the first order transition point of the material determined by DSC. The term “not mutually soluble” means immiscible with each other.
• suitable hydrophilic agents of the present invention include polyglycols such as poly(ethylene glycol) and poly(propylene glycol) and mixtures thereof.
• suitable materials include EVOH, glycerin, pentaerithritol, PVOH, polyvinylpyrollidine, vinylpyrollidone or poly(N-methyl pyrollidone) , and saccharide based compounds such as glucose, fructose, and their alcohols, mannitol, dextrin and hydrolyzed starch being suitable for the purposes of the present invention since they are hydrophilic compounds.
• suitable hydrophilic agents of the present invention may also include any hydrophilic material wherein, during processing, the hydrophilic agent is heated above its melt point upon melt mixing, and subsequently upon cooling separates from the polymer to form the interconnecting channeled structure of the present invention and a three phase system of a water- insoluble polymer, hydrophilic agent and the absorbing agent.
• the absorbing agent of the present invention includes a desiccating agent.
• dimer agents such as polypropylene maleic anhydride, or any plasticizer, may be optionally added to the mixture reducing viscosities and increasing the mixing compatibility of the polymer and hydrophilic agent.
• desiccating agents are selected having a polarity that causes an affinity between the desiccant and the hydrophilic agent.
• a polar desiccant is silica which is more compatible with the hydrophilic agent than it is typically with the water- insoluble polymer. For this reason, during the separating process when the interconnecting channels are formed throughout the polymer, it is believed that the desiccating agent will congregate toward the hydrophilic agent domains to which it has a greater affinity. In this manner, it is theorized that the hydrophilic agent is permitted to act as a bridge between moisture located exteriorly to the polymer structure and the desiccant that is located within the polymer.
• polar plasticizers such as glycerin may be further added to the mixture which enhance the dispersion or mixing of the desiccant into the hydrophilic agent.
• the desiccating agent which is primarily concentrated within the hydrophilic agent picks up the moisture from the transmitting hydrophilic agent and retains it therein. In this way, the moisture is quickly pulled throughout the interconnecting channels and made available to the desiccating particles or agents which are dispersed throughout the polymer.
• the water-insoluble polymer of the present invention may be any thermoplastic material.
• suitable thermoplastic materials include polyolefins such as polypropylene and polyethylene, polyisoprene, polybutadiene, polybutene, polysiloyane, polycarbonates, polyamides, ethylene-vinyl acetate copolymers, ethylene-methacrylate copolymer, poly(vinyl chloride), polystyrene, polyesters, polyanhydrides, polyacrylonitrile, polysulfones, polyacrylic ester, acrylic, polyurethane and polyacetal, or copolymers or mixtures thereof.
• the water-insoluble polymer may be an adhesive such as light curing adhesive, epoxy and/or hot melt adhesive.
• an adhesive may be selected that is ultraviolet or visible light cured.
• the UV /visible light sources may be employed to cure the polymer in seconds.
• the adhesive may be applied to the cover and/or base portion and, downstream, the adhesive is then exposed to the UV /visible light sources to cure the polymer.
• the absorbing agent material would include a desiccant such as molecular sieves, polypropylene and polyglycol.
• a desiccant such as molecular sieves, polypropylene and polyglycol.
• the amounts of the various components would be for example, from about 30-80 wt %, or from about 40-70 wt % of the desiccant, or about 60 wt %; from about 20-40 wt % of the polypropylene, e.g. polypropylene homopolymer available from Exxon [3505], having a melt flow of 400, or about 30 wt %; and from about 5-20 wt % of the polyglycol, e.g., polyfethylene propylene glycol] available from Dow (15-200), or about 10 wt %.
• the polyglycol e.g., polyfethylene propylene glycol
• the components are first dry mixed in a mixer such as a Henschel, and then fed to a compounder.
• a mixer such as a Henschel
• a Leistritz twin screw extruder, for example, or a Werner Pfleider mixer can be used to achieve a good melt mix at about
• the melt can then be either extruded to form, for example, a film or converted into pellets using dry air cooling on a vibrating conveyer.
• the formed pellets, containing channels can, for example, then be either injection molded into beads, sieves, or co-injected with polypropylene.
• the blend was then fed through a Leistritz twin screw extruder at temperatures in the sixteen zones ranging from about 145°C to about 165 °C, at a feed rate of about 50 lbs/hr at a screw speed of about 460 rpm and a six inch die.
• the extruded composition was then fed through a three roll hot press at temperatures ranging from about 85 °C to about 92 °C to produce a film of about 4 mil.
• One embodiment of the present invention includes a process for producing the absorbing agent material .
• the process comprises blending a water- insoluble polymer and a hydrophilic agent .
• the absorbing agent is blended into the polymer so that the additive is uniformly distributed within the polymer and the hydrophilic agent is distributed within the polymer.
• the hydrophilic agent forms interconnecting channels in the composition through which the desired property is transmitted through the polymer to the absorbing agent within the composition.
• the hydrophilic agent and absorbing agent are all thoroughly mixed in dry powder form, and then the polymer blend is melted and formed into a desired shape by molding. Interconnecting channels are formed in the composition through which the desired property is transmitted through the polymer to the absorbing agent within the composition.
• substantially permeable material may include a very thin (e.g. 1 mil or less) layer of the polymer such as PVC.
• the layer may be considered a coating. Consequently, for purposes of the present invention, the words "coating” and "layer” may be used interchangeably.
• the pocket or cavity draw depths are limited to about Vi inch for a 7/8 inch diameter circle, with area ratios ranging up to about 1 :3.
• Area ratio is the ratio of the initial area from which the pocket or blister 13 is drawn to the final area of the surface of the pocket or cavity).
• the draw depth and shape may be changed to fit the size and shape of the desired product.
• the plastics that are suitable for the base and coverportion of the barrier package 1 of the present invention may include, but are not limited to, thermoplastics or thermosets.
• Thermoplastics consists of long chain molecules.
• suitable thermoplastic materials include polyolefins such as polypropylene and polyethylene, polycarbonates, polyamides, ethylene-vinyl acetate copolymers , ethylene-methacrylate copolymer, polyvinyl chloride , polystyrene, polyester, polyester amide, polyacrylic ester, acrylic, polyurethane and polyacetal, or mixtures thereof.
• Thermoset plastics contain infinite three dimensional networks.
• thermosets include epoxy polyurethene and polyester.
• the absorbing agent is a desiccant
• various types of desiccating agents are known in the art and may be used with the present invention.
• the first type comprises chemical compounds that form crystals that contain water.
• Examples of such desiccant are anhydrous salts which tend to absorb water or moisture and form a stable salt. In this reaction with the moisture, a stable compound is formed within which the moisture is held and prevented from release.
• the second type of desiccant compounds are those which are considered to be reactive.
• These compounds typically undergo a chemical reaction with water or moisture and form new compounds within which the water is combined. These newly formed compounds are generally irreversible at low temperature and require a significant amount of energy to be regenerated so that they may be reused as a desiccant.
• These reactive type desiccants are mainly used in solvent drying and as additives to polymers which must themselves be maintained in a moisture reduced state .
• One application in which these reactive type compounds are particularly suitable was described above with respect to the multi-layer sheeting within which a layer of EVOH is laminated between two sheilding layers of what is normally moisture impermeable material such as polypropylene or polyethylene.
• these types of sheeting or wrap are used to package food products which must subsequently be sterilized in a retorting process wherein the packaged good is exposed to hot sterilizing steam.
• the exterior layers permit moisture to pass therethrough and compromise the oxygen barrier effectiveness of the EVOH interior layer. Because of the reactive desiccant that has been entrained that moisture is absorbed into the desiccant and retained therein away from the EVOH layer thereby allowing the EVOH layer to maintain its oxygen barrier characteristics .
• the third type of desiccants obtain their moisture absorbing capabilities through physical abso ⁇ tion.
• the abso ⁇ tion process is accomplished because of a fine capillary mo ⁇ hology of the desiccant particles which pulls moisture therethrough.
• the pore size of the capillaries, as well as the capillaries' density determine the abso ⁇ tion properties of the desiccant.
• Examples of these physical abso ⁇ tion desiccants include molecular sieves, silica gels, clays and starches. Because these types of physical abso ⁇ tion desiccants are both inert and non- water soluble, they are preferred for many applications.
• Suitable desiccating agent include silica gel, molecular sieve and naturally occurring clay compounds which would also include montmorillimite clay.
• Suitable absorbing agents may also include: (1) metals and alloys such as, but not limited to, nickel, cooper, aluminum, silicon, solder, silver, gold; (2) metal-plated paniculate such as silver- plated cooper, silver-placed nickel, silver-plated glass microspheres; (3) inorganics such as BaTi0 3 , SrTi0 3 , Si0 2 , A1 2 0 3 , ZnO, Ti0 2 , MnO, CuO, Sb 2 0 3 WC, fused silica, fumed silica, amo ⁇ hous fused silica, sol-gel silica, sol-gel titanates, mixed titanates, ion exchange resins, lithium-containing ceramics , hollow glass microspheres ; (4) carbon-based materials such as carbon, activated charcoal , carbon black, ketchem black, diamond powder; and (5) elastomers, such as polybutadiene, polysiloxane, and semi-metals, ceramic.
• metals and alloys such as
• the higher the amount of absorbing agents in the absorbing agent material the greater the abso ⁇ tion capacity will be of the portion containing the absorbing agents .
• the higher absorbing agent concentration may cause the portion to be more brittle and the mixture to be more difficult to either thermally from, extrude or injection mold.
• a maximum absorbing agent load is about 80 percent by weight with respect to the absorbing agent material.
• the desiccant loading level can range from 10% to 20%, 20% to 40% and 40% to 60% by weight with respect to the absorbing agent material.
• the portion of the barrier pack having the layer containing the absorbing agent material may be produced by placing the absorbing agent material on a first layer and thus, producing a second layer, i.e. the absorbing agent material layer. Then, a third layer is placed over the absorbing agent containing layer to produce a composite material comprising three layers.
• the second layer i.e. the absorbing agent material layer
• a third layer would then be placed on top of the side of the web having the absorbing agent material layer.
• the three layer composite produced would then be laminated together using suitable equipment such as a system of heated rollers that would both calender the composite and laminate the composite.
• the cover portion comprises the composite material
• the composite material would then be formed into individual cavities (e .g . "blisters) .
• the base portion comprises the composite material
• the base portion after the product is placed in the cavity, the base portion would then be placed over the cover portion to form a sealed unit for the product.
• the absorbing agent material may be applied to either or both the cavity and the base portion by: (a) coating the material on the cavity and/or base portion, which is co-extensive with the cavity; (b) spreading the material on the cavity and/or base portion, which is coextensive with the cavity; (c) dripping the material on the cavity and/or base portion, which is coextensive with the cavity; (d) spraying the material on the cavity and/or base portion, which is coextensive with the cavity; (e) painting the material on the cavity and/or base portion, which is coextensive with the cavity; and/or (f) depositing the material on the cavity and/or base portion, which is coextensive with the cavity.
• Suitable equipment for applying the absorbing agent material includes using a nozzle and brush.
• suitable forms of desiccants to be used in the present invention include the "raw" desiccant (e.g. powder silica gel or powder molecular sieve) , desiccant entrained in a polymer, desiccant bonded to a material, desiccant powder dispersed in a material that holds the powder together but does not substantially inhibit its moisture abso ⁇ tion capability, and other forms of desiccant products.
• suitable forms of desiccants include particles, shreds, beads, discs, fibers, slurry and film.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Organic Chemistry (AREA)
• Mechanical Engineering (AREA)
• Health & Medical Sciences (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• General Engineering & Computer Science (AREA)
• Analytical Chemistry (AREA)
• Food Science & Technology (AREA)
• Life Sciences & Earth Sciences (AREA)
• Microbiology (AREA)
• Materials Engineering (AREA)
• Manufacturing & Machinery (AREA)
• General Chemical & Material Sciences (AREA)
• Composite Materials (AREA)
• Packages (AREA)
• Laminated Bodies (AREA)
• Solid-Sorbent Or Filter-Aiding Compositions (AREA)
• Separation Of Gases By Adsorption (AREA)
• Drying Of Gases (AREA)
• Absorbent Articles And Supports Therefor (AREA)

Priority Applications (10)

Applications Claiming Priority (2)

Publications (1)

Family

ID=23303952

Family Applications (1)

Country Status (12)

Cited By (5)

Families Citing this family (55)

Citations (2)

Family Cites Families (25)

• 1999
  • 1999-06-15 US US09/333,711 patent/US6279736B1/en not_active Expired - Lifetime
• 2000
  • 2000-06-15 DE DE60044725T patent/DE60044725D1/de not_active Expired - Lifetime
  • 2000-06-15 BR BRPI0011671-8A patent/BR0011671B1/pt not_active IP Right Cessation
  • 2000-06-15 CA CA002374781A patent/CA2374781A1/en not_active Abandoned
  • 2000-06-15 WO PCT/US2000/016508 patent/WO2000076879A1/en not_active Ceased
  • 2000-06-15 EP EP00941456A patent/EP1233916B1/en not_active Revoked
  • 2000-06-15 AT AT00941456T patent/ATE474791T1/de not_active IP Right Cessation
  • 2000-06-15 JP JP2001503355A patent/JP2003520739A/ja active Pending
  • 2000-06-15 MX MXPA01012857A patent/MXPA01012857A/es active IP Right Grant
  • 2000-06-15 NZ NZ516115A patent/NZ516115A/en unknown
  • 2000-06-15 AU AU56162/00A patent/AU760090B2/en not_active Ceased
• 2001
  • 2001-12-14 NO NO20016124A patent/NO20016124L/no not_active Application Discontinuation
• 2010
  • 2010-03-24 JP JP2010068935A patent/JP2010168121A/ja active Pending

Patent Citations (2)

Also Published As

Similar Documents

Legal Events