WO2000064666A1 - Optical recording media having increased erasability - Google Patents
Optical recording media having increased erasability Download PDFInfo
- Publication number
- WO2000064666A1 WO2000064666A1 PCT/US1999/008861 US9908861W WO0064666A1 WO 2000064666 A1 WO2000064666 A1 WO 2000064666A1 US 9908861 W US9908861 W US 9908861W WO 0064666 A1 WO0064666 A1 WO 0064666A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- optical
- phase
- recording medium
- data storage
- change
- Prior art date
Abstract
Description
Claims