WO1999065093A1 - Battery separator - Google Patents
Battery separator Download PDFInfo
- Publication number
- WO1999065093A1 WO1999065093A1 PCT/NL1999/000344 NL9900344W WO9965093A1 WO 1999065093 A1 WO1999065093 A1 WO 1999065093A1 NL 9900344 W NL9900344 W NL 9900344W WO 9965093 A1 WO9965093 A1 WO 9965093A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- polyethylene
- battery separator
- solvent
- microporous
- Prior art date
Abstract
Description
Claims