WO1999061522A1 - Nucleation of polyamides in the presence of hypophosphite - Google Patents
Nucleation of polyamides in the presence of hypophosphite Download PDFInfo
- Publication number
- WO1999061522A1 WO1999061522A1 PCT/US1999/011610 US9911610W WO9961522A1 WO 1999061522 A1 WO1999061522 A1 WO 1999061522A1 US 9911610 W US9911610 W US 9911610W WO 9961522 A1 WO9961522 A1 WO 9961522A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nylon
- ppm
- polyamide
- phosphorous
- metal
- Prior art date
Abstract
Description
Claims