WO1999060066A1 - Compositions de revetement en poudre de polymere fluore - Google Patents

Compositions de revetement en poudre de polymere fluore Download PDF

Info

Publication number
WO1999060066A1
WO1999060066A1 PCT/US1998/027269 US9827269W WO9960066A1 WO 1999060066 A1 WO1999060066 A1 WO 1999060066A1 US 9827269 W US9827269 W US 9827269W WO 9960066 A1 WO9960066 A1 WO 9960066A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder coating
coating composition
diol
hydroxyl functional
functional fluoropolymer
Prior art date
Application number
PCT/US1998/027269
Other languages
English (en)
Inventor
Robert B. Barbee
Original Assignee
Eastman Chemical Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Eastman Chemical Company filed Critical Eastman Chemical Company
Priority to PCT/US1998/027269 priority Critical patent/WO1999060066A1/fr
Publication of WO1999060066A1 publication Critical patent/WO1999060066A1/fr

Abstract

L'invention concerne des compositions de revêtement en poudre thermodurcissables qui contiennent des mélanges d'un polymère fluoré à fonction hydroxyle et d'un polyester aliphatique hydroxylé solide ou cristallin obtenu à partir d'un diacide cycloaliphatique et d'un diol combinés à un agent de réticulation. Lesdites compositions, lorsqu'elles sont appliquées sur un substrat et chauffées, donnent des revêtements réticulés combinant des propriétés souhaitables, telles qu'une bonne résistance au choc, la souplesse, la stabilité aux rayons ultraviolets et la brillance.
PCT/US1998/027269 1998-12-22 1998-12-22 Compositions de revetement en poudre de polymere fluore WO1999060066A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/US1998/027269 WO1999060066A1 (fr) 1998-12-22 1998-12-22 Compositions de revetement en poudre de polymere fluore

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US1998/027269 WO1999060066A1 (fr) 1998-12-22 1998-12-22 Compositions de revetement en poudre de polymere fluore

Publications (1)

Publication Number Publication Date
WO1999060066A1 true WO1999060066A1 (fr) 1999-11-25

Family

ID=22268526

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1998/027269 WO1999060066A1 (fr) 1998-12-22 1998-12-22 Compositions de revetement en poudre de polymere fluore

Country Status (1)

Country Link
WO (1) WO1999060066A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1443086A1 (fr) * 2001-09-27 2004-08-04 Asahi Glass Company Ltd. Composition pour materiau de revetement a base de poudre de resine fluoree
US7498385B2 (en) * 2006-09-28 2009-03-03 Gore Enterprise Holdings Polyester compositions, methods of manufacturing said compositions, and articles made therefrom
CN103154415A (zh) * 2010-08-19 2013-06-12 骊住株式会社 室外使用的粉末涂装铝建筑材料
EP2627719A1 (fr) * 2010-10-13 2013-08-21 Akzo Nobel Powder Coatings (Ningbo) Co. Ltd Composition de revêtement en poudre de polyester-fluorocarbone hybride et son procédé de fabrication
EP2868724A4 (fr) * 2012-06-29 2016-02-17 Asahi Glass Co Ltd Composition de revêtement en poudre, procédé de production d'un film durci, et article revêtu
WO2016037807A1 (fr) * 2014-09-11 2016-03-17 Evonik Degussa Gmbh Traitement de surface par fluoration à base de résines polyester saturées réticulables et de fluoropolymères
EP3307802B1 (fr) 2015-06-09 2019-11-06 PPG Industries Ohio, Inc. Compositions de revêtement douces au toucher et résistantes aux taches, et revêtements formés à partir de ces compositions
EP3670570A1 (fr) * 2018-12-21 2020-06-24 Arkema France Composition de résine pour revêtements de poudre
WO2023094570A1 (fr) 2021-11-26 2023-06-01 Tiger Coatings Gmbh & Co. Kg Poudre de revêtement thermodurcissable convenant à une application en extérieur

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0371599A2 (fr) * 1988-11-28 1990-06-06 The Glidden Company Compositions d'enduction pulvérisables en fluorocarbone
EP0416501A2 (fr) * 1989-09-01 1991-03-13 Daicel Chemical Industries, Ltd. Composition de revêtement
EP0487485A2 (fr) * 1990-11-21 1992-05-27 U C B, S.A. Compositions de revêtement pulvérulentes résistant aux intempéries

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0371599A2 (fr) * 1988-11-28 1990-06-06 The Glidden Company Compositions d'enduction pulvérisables en fluorocarbone
EP0416501A2 (fr) * 1989-09-01 1991-03-13 Daicel Chemical Industries, Ltd. Composition de revêtement
EP0487485A2 (fr) * 1990-11-21 1992-05-27 U C B, S.A. Compositions de revêtement pulvérulentes résistant aux intempéries

Non-Patent Citations (4)

* Cited by examiner, † Cited by third party
Title
CHEMICAL ABSTRACTS, vol. 124, no. 12, 18 March 1996, Columbus, Ohio, US; abstract no. 147468, PIOTROWSKA, ZOFIA: "Synthesis of unsaturated polyester resins with the use of anhydrides of cyclic non-aromatic dicarboxylic acids" XP002114923 *
CHEMICAL ABSTRACTS, vol. 67, no. 16, 16 October 1967, Columbus, Ohio, US; abstract no. 74061, ARKDZHOVSKII, V. N.: "Effect of polyester composition on the light resistance of polyester resins" XP002114924 *
POLYMERY (WARSAW), vol. 40, no. 11/12, 1995, pages 669 - 671 *
SB. TR. - VSES. NAUCHNO-ISSLED. INST. NOV. STROIT. MATER., vol. 7, 1966, pages 110 - 120 *

Cited By (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1443086A1 (fr) * 2001-09-27 2004-08-04 Asahi Glass Company Ltd. Composition pour materiau de revetement a base de poudre de resine fluoree
EP1443086A4 (fr) * 2001-09-27 2008-06-18 Asahi Glass Co Ltd Composition pour materiau de revetement a base de poudre de resine fluoree
EP2045301A1 (fr) * 2001-09-27 2009-04-08 Asahi Glass Company, Limited Composition pour matériau de revêtement à base de poudre de résine fluorée
US7498385B2 (en) * 2006-09-28 2009-03-03 Gore Enterprise Holdings Polyester compositions, methods of manufacturing said compositions, and articles made therefrom
CN103154415A (zh) * 2010-08-19 2013-06-12 骊住株式会社 室外使用的粉末涂装铝建筑材料
EP2627719A4 (fr) * 2010-10-13 2014-05-21 Akzo Nobel Powder Coatings Ningbo Co Ltd Composition de revêtement en poudre de polyester-fluorocarbone hybride et son procédé de fabrication
US8853320B2 (en) 2010-10-13 2014-10-07 Akzo Nobel Powder Coatings (Ningbo) Co., Ltd. Hybrid polyester fluorocarbon powder coating composition and process for manufacture thereof
EP2627719B1 (fr) 2010-10-13 2015-09-16 Akzo Nobel Powder Coatings (Ningbo) Co. Ltd Composition de revêtement en poudre de polyester-fluorocarbone hybride et son procédé de fabrication
EP2627719A1 (fr) * 2010-10-13 2013-08-21 Akzo Nobel Powder Coatings (Ningbo) Co. Ltd Composition de revêtement en poudre de polyester-fluorocarbone hybride et son procédé de fabrication
EP3722384A1 (fr) * 2012-06-29 2020-10-14 Agc Inc. Composition de revêtement de poudre, procédé de production d'un film durci et article revêtu
EP2868724A4 (fr) * 2012-06-29 2016-02-17 Asahi Glass Co Ltd Composition de revêtement en poudre, procédé de production d'un film durci, et article revêtu
US11286399B2 (en) 2012-06-29 2022-03-29 AGC Inc. Powder coating composition, process for producing cured film and coated article
JPWO2014002964A1 (ja) * 2012-06-29 2016-06-02 旭硝子株式会社 粉体塗料組成物、硬化膜の製造方法、および塗装物品
US9714360B2 (en) 2012-06-29 2017-07-25 Asahi Glass Company, Limited Powder coating composition, process for producing cured film and coated article
CN106687539A (zh) * 2014-09-11 2017-05-17 赢创德固赛有限公司 基于可交联的饱和聚酯树脂和含氟聚合物的表面涂层
US10745580B2 (en) 2014-09-11 2020-08-18 Evonik Operations Gmbh Surface-finishing on the basis of cross-linkable, saturated polyester resins and fluoropolymers
CN106687539B (zh) * 2014-09-11 2020-08-25 赢创运营有限公司 基于可交联的饱和聚酯树脂和含氟聚合物的表面涂层
AU2015314514B2 (en) * 2014-09-11 2018-10-04 Evonik Operations Gmbh Surface-finishing on the basis of cross-linkable, saturated polyester resins and fluoropolymers
WO2016037807A1 (fr) * 2014-09-11 2016-03-17 Evonik Degussa Gmbh Traitement de surface par fluoration à base de résines polyester saturées réticulables et de fluoropolymères
DE102014218188B4 (de) 2014-09-11 2023-01-19 Evonik Operations Gmbh Formulierung zur Beschichtung von Substraten, Verfahren zur Beschichtung von Substraten, beschichtete Substrate sowie Verwendung der Formulierung
EP3307802B1 (fr) 2015-06-09 2019-11-06 PPG Industries Ohio, Inc. Compositions de revêtement douces au toucher et résistantes aux taches, et revêtements formés à partir de ces compositions
EP3670570A1 (fr) * 2018-12-21 2020-06-24 Arkema France Composition de résine pour revêtements de poudre
WO2020127938A1 (fr) * 2018-12-21 2020-06-25 Arkema France Composition de résine destinée à des revêtements en poudre
CN113227199A (zh) * 2018-12-21 2021-08-06 阿科玛法国公司 用于粉末涂料的树脂组合物
CN113227199B (zh) * 2018-12-21 2024-02-13 阿科玛法国公司 用于粉末涂料的树脂组合物
WO2023094570A1 (fr) 2021-11-26 2023-06-01 Tiger Coatings Gmbh & Co. Kg Poudre de revêtement thermodurcissable convenant à une application en extérieur

Similar Documents

Publication Publication Date Title
US5710214A (en) Thermosetting powder coating compositions
US5028682A (en) Oxime-blocked polysicyanates and polyester and powder coating compositions containing such oxide-blocked polyisocyanates
EP0706546A1 (fr) Compositions de revetement en poudre
US5614323A (en) Powder coating compositions
US5160792A (en) Thermosetting powder coating compositions
EP0649452B1 (fr) Compositions de revetement par poudre thermodurcissables
WO1991000306A1 (fr) Nouveaux polyesters semi-cristallins, leurs melanges avec des polyesters amorphes et compositions de revetement pulverulentes a base de ces melanges
WO1991015532A1 (fr) Compositions de poudres pour revetement
WO1993004102A1 (fr) Compositions pulverulentes pour revetements thermodurcissables
US4988793A (en) Powder coating compositions
WO1999060066A1 (fr) Compositions de revetement en poudre de polymere fluore
CA2066638C (fr) Compositions de revetements en poudre
US5625028A (en) Thermosetting powder coating compositions
EP0775166B1 (fr) Poudres de revetement de polyurethane
US4957814A (en) Powder coating compositions
EP0572520A1 (fr) Compositions d'enduits en poudre
US5095087A (en) Oxime-blocked polyisocyanates and polyester and powder coating compositions containing such oxime-blocked polyisocyanates

Legal Events

Date Code Title Description
AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE

121 Ep: the epo has been informed by wipo that ep was designated in this application
WA Withdrawal of international application