WO1999006481A1 - Elastomeric material for rubber articles - Google Patents
Elastomeric material for rubber articles Download PDFInfo
- Publication number
- WO1999006481A1 WO1999006481A1 PCT/US1998/016022 US9816022W WO9906481A1 WO 1999006481 A1 WO1999006481 A1 WO 1999006481A1 US 9816022 W US9816022 W US 9816022W WO 9906481 A1 WO9906481 A1 WO 9906481A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer latex
- latex composition
- monomer
- glove
- weight percent
- Prior art date
Abstract
Description
Claims