WO1998053123A1 - Epitaxy boat and method for liquid phase epitaxial deposit of cdhgte - Google Patents
Epitaxy boat and method for liquid phase epitaxial deposit of cdhgte Download PDFInfo
- Publication number
- WO1998053123A1 WO1998053123A1 PCT/FR1998/001013 FR9801013W WO9853123A1 WO 1998053123 A1 WO1998053123 A1 WO 1998053123A1 FR 9801013 W FR9801013 W FR 9801013W WO 9853123 A1 WO9853123 A1 WO 9853123A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- epitaxy
- heterosubstrate
- solution
- well
- drawer
- Prior art date
Abstract
Description
Claims