WO1998032433A9 - Structures de forme adaptable - Google Patents
Structures de forme adaptableInfo
- Publication number
- WO1998032433A9 WO1998032433A9 PCT/US1998/001355 US9801355W WO9832433A9 WO 1998032433 A9 WO1998032433 A9 WO 1998032433A9 US 9801355 W US9801355 W US 9801355W WO 9832433 A9 WO9832433 A9 WO 9832433A9
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- gel
- responsive
- incorporated
- responsive gel
- temperature
- Prior art date
Abstract
L'invention concerne des structures de forme adaptable comprenant un gel réagissant à l'environnement qui constitue une partie desdites structures. Le gel réagit à des conditions extérieures telles que la température en changeant d'état de manière réversible. Il est préférable de placer le gel dans un récipient étanche. Dans un mode de réalisation, le gel est constitué par un gel thermique à action inverse qui se trouve à l'état liquide à des températures peu élevées et devient visqueux à température corporelle. Les objets que l'on met en contact avec le corps s'adaptent au corps et gardent leur forme sous l'effet de la température corporelle. Parmi les structures en question, on peut citer des articles vestimentaires tels que les chapeaux, les casques et les soutien-gorge. D'autres objets à forme adaptable comprennent des chaises et des canapés.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU61342/98A AU6134298A (en) | 1997-01-24 | 1998-01-23 | Conformable structures |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US78727897A | 1997-01-24 | 1997-01-24 | |
US08/787,278 | 1997-01-24 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO1998032433A1 WO1998032433A1 (fr) | 1998-07-30 |
WO1998032433A9 true WO1998032433A9 (fr) | 1999-02-18 |
Family
ID=25140965
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US1998/001355 WO1998032433A1 (fr) | 1997-01-24 | 1998-01-23 | Structures de forme adaptable |
Country Status (2)
Country | Link |
---|---|
AU (1) | AU6134298A (fr) |
WO (1) | WO1998032433A1 (fr) |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE10058830B4 (de) * | 2000-11-27 | 2005-01-27 | 3M Espe Ag | Verwendung von verzweigten Polysäuren in Dentalmassen und Dentalmassen enthaltend verzweigte Polysäuren |
US8320191B2 (en) | 2007-08-30 | 2012-11-27 | Infineon Technologies Ag | Memory cell arrangement, method for controlling a memory cell, memory array and electronic device |
DE102009023302B3 (de) * | 2009-05-29 | 2010-12-02 | Siemens Medical Instruments Pte. Ltd. | Wieder verwendbares Ohranpassstück zur Erstellung eines Ohrabdrucks |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5252318A (en) * | 1990-06-15 | 1993-10-12 | Allergan, Inc. | Reversible gelation compositions and methods of use |
JPH06506384A (ja) * | 1992-01-31 | 1994-07-21 | リーボック インターナショナル リミテッド | 運動靴の甲革及びその製造方法 |
US5407445A (en) * | 1992-05-20 | 1995-04-18 | Cytrx Corporation | Gel composition for implant prosthesis and method of use |
-
1998
- 1998-01-23 AU AU61342/98A patent/AU6134298A/en not_active Abandoned
- 1998-01-23 WO PCT/US1998/001355 patent/WO1998032433A1/fr active Application Filing
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO1996028056A9 (fr) | Structures adaptables | |
EP0759710A1 (fr) | Structures adaptables | |
TW524828B (en) | Impact energy absorbent medium; energy absorbent and form compliant article for impact absorption and dissipation; method for forming viscoelastic, compliant, energy absorbent composition; self-conforming, compliant energy absorbent medium | |
US5766704A (en) | Conforming shoe construction and gel compositions therefor | |
US5985383A (en) | Conforming shoe construction and gel compositions therefor | |
US6093468A (en) | Flexible lightweight protective pad with energy absorbing inserts | |
US9315648B2 (en) | Gel putties, articles comprising same, and methods of forming such gel putties and articles | |
US6231423B1 (en) | Malleable bra pad | |
US20140223649A1 (en) | Impact-resistant pad and method of manufacturing | |
KR100825493B1 (ko) | 경량 실리콘 보형물 및 이의 제조방법 | |
WO1998032433A9 (fr) | Structures de forme adaptable | |
WO1998032433A1 (fr) | Structures de forme adaptable | |
US6443986B1 (en) | Self-forming prosthetic device and method of making the same | |
AU5252996A (en) | Conforming shoe construction and gel compositions therefor | |
US6162250A (en) | Self-forming partial breast prosthesis with encapsulated catalyst and a method of making the same | |
WO1996028057A1 (fr) | Construction de chaussure adaptable a base de gels et procede de fabrication de cette chaussure | |
US9000059B2 (en) | Heat moldable gel and foam composition | |
WO1996028057A9 (fr) | Construction de chaussure adaptable a base de gels et procede de fabrication de cette chaussure | |
US5245938A (en) | Solid, pliable organic compound for hot/cold thermal padding material | |
CN107880348A (zh) | 一种改性花生壳粉/epe复合材料及其制备方法 | |
EP1159352B1 (fr) | Systeme de rembourrage intelligent comprenant un materiau amortisseur, et articles pouvant etre obtenus a partir dudit systeme | |
CN208625160U (zh) | 一种脑部降温枕头 | |
CN213881817U (zh) | 一种保暖棉服 | |
WO2013039945A1 (fr) | Amortisseurs résistant aux impacts et procédé de fabrication | |
CN205549490U (zh) | 一种一体式滑雪护具 |