WO1998020373A1 - Uv-cured optical elements - Google Patents
Uv-cured optical elements Download PDFInfo
- Publication number
- WO1998020373A1 WO1998020373A1 PCT/EP1997/005763 EP9705763W WO9820373A1 WO 1998020373 A1 WO1998020373 A1 WO 1998020373A1 EP 9705763 W EP9705763 W EP 9705763W WO 9820373 A1 WO9820373 A1 WO 9820373A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- groups
- optical element
- formula
- element according
- atoms
- Prior art date
Abstract
Description
Claims