WO1998009141A2 - Infrared radiation-detecting device - Google Patents
Infrared radiation-detecting device Download PDFInfo
- Publication number
- WO1998009141A2 WO1998009141A2 PCT/US1997/015188 US9715188W WO9809141A2 WO 1998009141 A2 WO1998009141 A2 WO 1998009141A2 US 9715188 W US9715188 W US 9715188W WO 9809141 A2 WO9809141 A2 WO 9809141A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- well
- layer
- bound
- quantum well
- energy
- Prior art date
Abstract
Description
Claims