WO1996035478A1 - Plaques d'elements excitateurs basse temperature, leur preparation et leur application medicale - Google Patents

Plaques d'elements excitateurs basse temperature, leur preparation et leur application medicale Download PDF

Info

Publication number
WO1996035478A1
WO1996035478A1 PCT/CN1995/000037 CN9500037W WO9635478A1 WO 1996035478 A1 WO1996035478 A1 WO 1996035478A1 CN 9500037 W CN9500037 W CN 9500037W WO 9635478 A1 WO9635478 A1 WO 9635478A1
Authority
WO
WIPO (PCT)
Prior art keywords
temperature
low
element plate
excitation element
adhesive
Prior art date
Application number
PCT/CN1995/000037
Other languages
English (en)
Chinese (zh)
Inventor
Dang Wang
Original Assignee
Dang Wang
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dang Wang filed Critical Dang Wang
Priority to PCT/CN1995/000037 priority Critical patent/WO1996035478A1/fr
Priority to AU24049/95A priority patent/AU2404995A/en
Publication of WO1996035478A1 publication Critical patent/WO1996035478A1/fr

Abstract

L'invention porte sur des plaques d'éléments excitateurs basse température destinées à un usage physiothérapeutique, ainsi que sur leur préparation et leur application médicale. Cette invention permet de fabriquer une poudre de revêtement à partir de matières que l'on a préparées en faisant fondre des oxydes traités chimiquement et des composés d'éléments inorganiques. On fait ensuite adhérer la poudre à un substrat. En réajustant la formulation d'oxydes et de composés d'éléments inorganiques, on diminue l'écart entre la valeur de crête de l'onde électromagnétique excitatrice et la valeur d'absorption de pointe du corps humain à température normale, ce qui permet d'améliorer l'effet du traitement.
PCT/CN1995/000037 1995-05-09 1995-05-09 Plaques d'elements excitateurs basse temperature, leur preparation et leur application medicale WO1996035478A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
PCT/CN1995/000037 WO1996035478A1 (fr) 1995-05-09 1995-05-09 Plaques d'elements excitateurs basse temperature, leur preparation et leur application medicale
AU24049/95A AU2404995A (en) 1995-05-09 1995-05-09 Low temperature exciting element plates, their preparation a nd medical application

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CN1995/000037 WO1996035478A1 (fr) 1995-05-09 1995-05-09 Plaques d'elements excitateurs basse temperature, leur preparation et leur application medicale

Publications (1)

Publication Number Publication Date
WO1996035478A1 true WO1996035478A1 (fr) 1996-11-14

Family

ID=4574936

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN1995/000037 WO1996035478A1 (fr) 1995-05-09 1995-05-09 Plaques d'elements excitateurs basse temperature, leur preparation et leur application medicale

Country Status (2)

Country Link
AU (1) AU2404995A (fr)
WO (1) WO1996035478A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN85100830A (zh) * 1985-04-01 1986-06-10 重庆市硅酸盐研究所 能引起生物效应的搪瓷板及其制造方法
CN1069897A (zh) * 1991-09-05 1993-03-17 管新凯 高血压、心脏病理疗器
CN1098954A (zh) * 1993-08-17 1995-02-22 王荡 低温激发元素板及其制作方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN85100830A (zh) * 1985-04-01 1986-06-10 重庆市硅酸盐研究所 能引起生物效应的搪瓷板及其制造方法
CN1069897A (zh) * 1991-09-05 1993-03-17 管新凯 高血压、心脏病理疗器
CN1098954A (zh) * 1993-08-17 1995-02-22 王荡 低温激发元素板及其制作方法

Also Published As

Publication number Publication date
AU2404995A (en) 1996-11-29

Similar Documents

Publication Publication Date Title
DE69815554T2 (de) Purinderivate und antagonisten des adenosin-a2-rezeptors, welche zur vorsorge oder heilung von diabetes dienen
EP0588950B1 (fr) Procede de traitement de verres a fluoroaluminosilicates
CZ20002587A3 (en) Bicyclic heteroaromatic compounds
EP0533585B1 (fr) Appareil pour la régulation et pour améliorer l'état de développementet de survie d'organismes vivants
EP0145210A2 (fr) Particules-supports revêtues de précurseurs pour verre biologiquement actif
WO1996035478A1 (fr) Plaques d'elements excitateurs basse temperature, leur preparation et leur application medicale
KR20020097322A (ko) 바이오 세라믹 볼의 제조방법
CN102167571A (zh) 宽谱远红外陶瓷材料及其制备方法和应用
JPH08104609A (ja) 遠赤外線放射体及び遠赤外線を放射する組成物
KR100296885B1 (ko) 원적외선 방사체 세라믹스 및 그 제조방법
KR100563558B1 (ko) 자기질 옥 타일 제조방법 및 자기질 옥 타일
US6605291B2 (en) Therapeutic pad and a method for treatment of common illnesses
CN112439132B (zh) 使用陶瓷组合物和低强度超声波改善关节炎的装置
CN1037822C (zh) 低温激发元素板及其制作方法
KR20230067304A (ko) 원적외선 방사 기능을 가지는 블랙 알루미나 세라믹 매트리스
CN87103603A (zh) 人体频谱匹配效应场治疗装置及生产方法
DD283819A5 (de) Verfahren zur herstellung von substituierten dibenzothiophenen
KR100359430B1 (ko) 원적외선 방사체 및 이의 제조방법
KR100783486B1 (ko) 사각돔형 원적외선과 음이온 방사 세라믹스 플레이트
CN1230402C (zh) 一种远红外功能砖及其制作方法
KR102297627B1 (ko) 원적외선 방출 세라믹 조성물(ndc)과 초음파를 이용한 염증 완화 및 개선용 장치
KR102339100B1 (ko) 염증 완화 또는 개선용 세라믹 조성물(ndc) 및 이의 제조방법
KR100563559B1 (ko) 도기질 옥 타일 제조방법 및 도기질 타일 유약
KR101245634B1 (ko) 적외선 집광 조성물
CN108992244A (zh) 磁性远红外能量眼罩

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AM AT AU BB BG BR BY CA CH CN CZ DE DK EE ES FI GB GE HU JP KE KG KP KR KZ LK LR LT LU LV MD MG MN MW MX NO NZ PL PT RO RU SD SE SG SI SK TJ TT UA US UZ VN

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): KE MW SD SZ UG AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA