WO1996026237A1 - Materiau composite ameliore - Google Patents

Materiau composite ameliore Download PDF

Info

Publication number
WO1996026237A1
WO1996026237A1 PCT/US1996/002062 US9602062W WO9626237A1 WO 1996026237 A1 WO1996026237 A1 WO 1996026237A1 US 9602062 W US9602062 W US 9602062W WO 9626237 A1 WO9626237 A1 WO 9626237A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
fibers
filler particles
section
filler
Prior art date
Application number
PCT/US1996/002062
Other languages
English (en)
Inventor
Paul R. Chalifoux
Original Assignee
Wellesley Research Associates, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wellesley Research Associates, Inc. filed Critical Wellesley Research Associates, Inc.
Publication of WO1996026237A1 publication Critical patent/WO1996026237A1/fr

Abstract

L'invention décrit une composition composite résistant aux fissures qui comprend une résine polymère matrice et entre 2 et 75 pour cent, en volume, de particules de charge mises en forme sur la base du volume de la composition (15). Les particules ou fibres de charge sont mises en forme de façon à minimaliser les fissures ou à les empêcher de se propager à travers la résine matrice.
PCT/US1996/002062 1995-02-21 1996-02-15 Materiau composite ameliore WO1996026237A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US39157295A 1995-02-21 1995-02-21
US08/391,572 1995-02-21

Publications (1)

Publication Number Publication Date
WO1996026237A1 true WO1996026237A1 (fr) 1996-08-29

Family

ID=23547135

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1996/002062 WO1996026237A1 (fr) 1995-02-21 1996-02-15 Materiau composite ameliore

Country Status (1)

Country Link
WO (1) WO1996026237A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000025729A1 (fr) * 1998-11-03 2000-05-11 New Age Biomaterials, Inc. Charge amelioree destinee aux materiaux composites dentaires
DE10253481A1 (de) * 2002-11-13 2004-06-03 Voco Gmbh Kompositmaterial und Verwendung eines Kompositmaterials
US7393883B2 (en) 2002-07-03 2008-07-01 New Age Biomaterials, Inc. Filler for dental composite materials
AU2007200795B2 (en) * 1998-11-03 2009-05-07 New Age Biomaterials, Inc. Improved filler for dental composite materials
US20120053692A1 (en) * 2010-08-26 2012-03-01 University Of Louisville Research Foundation, Inc. Compositions and methods for treating bone defects

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4879324A (en) * 1986-11-29 1989-11-07 Basf Aktiengesellschaft Thermoplastic molding compositions based on polycarbonates, polyesters and polyamides

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4879324A (en) * 1986-11-29 1989-11-07 Basf Aktiengesellschaft Thermoplastic molding compositions based on polycarbonates, polyesters and polyamides

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000025729A1 (fr) * 1998-11-03 2000-05-11 New Age Biomaterials, Inc. Charge amelioree destinee aux materiaux composites dentaires
JP2002528474A (ja) * 1998-11-03 2002-09-03 ニュー エイジ バイオマテリアルズ，インコーポレーテッド 歯科複合材料用の改良型フィラー
AU2007200795B2 (en) * 1998-11-03 2009-05-07 New Age Biomaterials, Inc. Improved filler for dental composite materials
US7393883B2 (en) 2002-07-03 2008-07-01 New Age Biomaterials, Inc. Filler for dental composite materials
DE10253481A1 (de) * 2002-11-13 2004-06-03 Voco Gmbh Kompositmaterial und Verwendung eines Kompositmaterials
DE10253481B4 (de) * 2002-11-13 2007-11-15 Voco Gmbh Kompositmaterial und Verwendung eines Kompositmaterials
US20120053692A1 (en) * 2010-08-26 2012-03-01 University Of Louisville Research Foundation, Inc. Compositions and methods for treating bone defects
US9072720B2 (en) * 2010-08-26 2015-07-07 University Of Louisville Research Foundation, Inc. Compositions and methods for treating bone defects
US20150283292A1 (en) * 2010-08-26 2015-10-08 University Of Louisville Research Foundation, Inc. Compositions and methods for treating bone defects
US10543294B2 (en) * 2010-08-26 2020-01-28 University Of Louisville Research Foundation, Inc. Compositions and methods for treating bone defects

Similar Documents

Publication Publication Date Title
DE3708618C2 (fr)
CA1107879A (fr) Element de raidissement, d'armature ou de retenue
WO2003050854A3 (fr) Gabarits de reacteur chimique: fabrication de couche sacrificielle et utilisation de gabarits
US5707231A (en) Orthodontic assembly with reinforcement structure
DE69926816T2 (de) Dental-Wiederherstellungskomposit
EP0810850B1 (fr) Preimpregne a fibres de polymere, son procede de preparation et d'utilisation
US5861445A (en) Reinforcement of dental and other composite materials
EP0047971B1 (fr) Particules minérales, leur procédé de préparation et matériaux dentaires les contenant
JP2001507719A (ja) 粉砕した、高密度化、脆化ガラスファイバフィラーを含む歯科用複合物
DK0828772T4 (da) Slagstyrkemodificerede (meth)acrylpolymerer
WO1996026237A1 (fr) Materiau composite ameliore
EP0429556B1 (fr) Resine composite renforcee
EP1243679A3 (fr) Fibres de carbone et matériau composite les utilisant
EP0648484B1 (fr) Procédé de préparation d'une matière de change ayant des rétentions et son utilisation
EP1124529B1 (fr) Charge amelioree destinee aux materiaux composites dentaires
US7393883B2 (en) Filler for dental composite materials
US20160374905A1 (en) Medium for a dental structure and a method of producing a medium for a dental structure
DE3610808A1 (de) Dental-klebmittel
EP1560557B1 (fr) Materiau composite et utilisation d'un materiau composite
DE69917458T2 (de) Mit komposit überzogenes gegossenes glas-keramik-dentalkonstrukt
Zhang et al. Bottom‐up Assembling Hierarchical Enamel‐like Bulk Materials with Excellent Optical and Mechanical Properties for Tooth Restoration
DE3826233C1 (en) Plastic denture
McDonald Advances in operative dentistry and fixed prosthodontics
JPWO2006085682A1 (ja) 歯科用修復材組成物
DD293487A5 (de) Dentalkomposite

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): CA JP KR MX

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase