WO1994009302A1 - Corrugated multilayer tubing having at least two dissimilar polymeric materials - Google Patents
Corrugated multilayer tubing having at least two dissimilar polymeric materialsInfo
- Publication number
- WO1994009302A1 WO1994009302A1 PCT/US1993/009850 US9309850W WO9409302A1 WO 1994009302 A1 WO1994009302 A1 WO 1994009302A1 US 9309850 W US9309850 W US 9309850W WO 9409302 A1 WO9409302 A1 WO 9409302A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tubing
- layer
- thermoplastic
- region
- essentially
- Prior art date
Abstract
Description
Claims