WO1991002009A1 - Catalyseur de ziegler a support d'oxide de magnesium modifie par de l'acide et de l'alcanol superieur, et procede de preparation de polyethylene a haute densite a repartition etroite de la masse moleculaire - Google Patents

Catalyseur de ziegler a support d'oxide de magnesium modifie par de l'acide et de l'alcanol superieur, et procede de preparation de polyethylene a haute densite a repartition etroite de la masse moleculaire Download PDF

Info

Publication number
WO1991002009A1
WO1991002009A1 PCT/US1989/003738 US8903738W WO9102009A1 WO 1991002009 A1 WO1991002009 A1 WO 1991002009A1 US 8903738 W US8903738 W US 8903738W WO 9102009 A1 WO9102009 A1 WO 9102009A1
Authority
WO
WIPO (PCT)
Prior art keywords
acid
catalyst
alkanol
carboxylic acid
magnesium oxide
Prior art date
Application number
PCT/US1989/003738
Other languages
English (en)
Inventor
John Tai-Tung Hsieh
Original Assignee
Mobil Oil Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mobil Oil Corporation filed Critical Mobil Oil Corporation
Publication of WO1991002009A1 publication Critical patent/WO1991002009A1/fr

Abstract

On utilise du MgO traité à l'acide carboxylique, par exemple, à l'acide acétique, comme support pour un catalyseur de Ziegler Al-Ti dans lequel le composant Ti est le produit d'un alcanol contenant 5 à 12 atomes de carbone et de TiCl4 afin de produire un polyéthylène à haute densité (PEHD) présentant une répartition étroite de la masse moléculaire (RMM) ainsi qu'une grande taille de particule permettant le moulage par injection.
PCT/US1989/003738 1989-08-03 1989-08-30 Catalyseur de ziegler a support d'oxide de magnesium modifie par de l'acide et de l'alcanol superieur, et procede de preparation de polyethylene a haute densite a repartition etroite de la masse moleculaire WO1991002009A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US38920489A 1989-08-03 1989-08-03
US389,204 1989-08-03

Publications (1)

Publication Number Publication Date
WO1991002009A1 true WO1991002009A1 (fr) 1991-02-21

Family

ID=23537287

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1989/003738 WO1991002009A1 (fr) 1989-08-03 1989-08-30 Catalyseur de ziegler a support d'oxide de magnesium modifie par de l'acide et de l'alcanol superieur, et procede de preparation de polyethylene a haute densite a repartition etroite de la masse moleculaire

Country Status (4)

Country Link
EP (1) EP0436672A1 (fr)
JP (1) JPH04500830A (fr)
AU (1) AU4743090A (fr)
WO (1) WO1991002009A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995034584A1 (fr) * 1994-06-13 1995-12-21 W.R. Grace & Co.-Conn. Preparation de supports deshydroxyles

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4256865A (en) * 1975-07-30 1981-03-17 Bp Chemicals Limited Polymerization catalyst
US4311817A (en) * 1977-09-09 1982-01-19 Mitsui Petrochemical Industries Ltd. Process for polymerizing olefins and catalyst therefor

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4256865A (en) * 1975-07-30 1981-03-17 Bp Chemicals Limited Polymerization catalyst
US4311817A (en) * 1977-09-09 1982-01-19 Mitsui Petrochemical Industries Ltd. Process for polymerizing olefins and catalyst therefor

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995034584A1 (fr) * 1994-06-13 1995-12-21 W.R. Grace & Co.-Conn. Preparation de supports deshydroxyles
US5583085A (en) * 1994-06-13 1996-12-10 W. R. Grace & Co.-Conn. Preparation of dehydroxylated supports

Also Published As

Publication number Publication date
JPH04500830A (ja) 1992-02-13
EP0436672A1 (fr) 1991-07-17
AU4743090A (en) 1991-03-11

Similar Documents

Publication Publication Date Title
US5470812A (en) High activity polyethylene catalysts prepared with alkoxysilane reagents
JP2557054B2 (ja) アルフア−オレフイン重合用触媒組成物
US4719193A (en) Processes for preparing polyethylene catalysts by heating catalyst precursors
US5118648A (en) Particulate polymer-supported olefin polymerization catalyst
CA2389654C (fr) Systemes et procedes de catalyse de polymerisation utilisant des composes de lithium alkyle comme cocatalyseur
AU677145B2 (en) Catalyst composition
US4888318A (en) Catalyst composition for polymerizing alpha-olefins
JP2774807B2 (ja) 分子量分布の狭いアルファオレフィンポリマー重合用触媒組成物
US6124412A (en) Alumoxane-enhanced, supported ziegler-natta polymerization catalysts, methods of making same, processes of using same and polymers produced therefrom
EP0729478B1 (fr) Composition de catalyseur pour la copolymerisation de l'ethylene
US5260245A (en) High activity polyethylene catalysts
US5408015A (en) Mixed chromium catalyst,and alkene and alkyl aluminum hydride-modified ziegler catalyst for multimodal HDPE
EP0324588A2 (fr) Composition de catalyseur pour la préparation de polymères d'alpha-oléfines à distribution de poids moléculaire étroite
US5939348A (en) Catalyst for the manufacture of polythylene with a narrow molecular weight distribution
US5055533A (en) Process for polymerizing alpha-olefins with trimethylaluminum-activated catalyst
US4446288A (en) Polymerization method
US5232999A (en) Olefin polymerization catalyst and process
US6291384B1 (en) High activity catalyst prepared with alkoxysilanes
US5330950A (en) Mixed Ziegler and chromium catalyst and process for preparing a broad molecular weight distribution HDPE
JPH0721005B2 (ja) エチレンの（共）重合用触媒組成物
US4863886A (en) Magnesium oxide-supported ziegler catalyst modified with acid and higher alkanol, and process for preparing narrow MWD HDPE
JP4547124B2 (ja) オレフィン重合のための触媒組成物およびこの組成物を用いた方法
US5330951A (en) Catalyst composition for polymerizing alpha-olefin
WO1991002009A1 (fr) Catalyseur de ziegler a support d'oxide de magnesium modifie par de l'acide et de l'alcanol superieur, et procede de preparation de polyethylene a haute densite a repartition etroite de la masse moleculaire
US5245019A (en) Olefin polymerization catalyst and process

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU JP

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE FR GB IT LU NL SE

WWE Wipo information: entry into national phase

Ref document number: 1990901100

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1990901100

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1990901100

Country of ref document: EP