WO1990000940A1 - Stratifie thermotransferable - Google Patents

Stratifie thermotransferable Download PDF

Info

Publication number
WO1990000940A1
WO1990000940A1 PCT/US1989/001731 US8901731W WO9000940A1 WO 1990000940 A1 WO1990000940 A1 WO 1990000940A1 US 8901731 W US8901731 W US 8901731W WO 9000940 A1 WO9000940 A1 WO 9000940A1
Authority
WO
WIPO (PCT)
Prior art keywords
transfer
layer
oil
heat
article
Prior art date
Application number
PCT/US1989/001731
Other languages
English (en)
Inventor
Herman Abber
Robert M. Edwards
Eleanor H. Sodagar
John M. Anemaet
Richard J. Galante
Original Assignee
Dennison Manufacturing Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dennison Manufacturing Company filed Critical Dennison Manufacturing Company
Publication of WO1990000940A1 publication Critical patent/WO1990000940A1/fr

Abstract

Est décrit un système de décollage amélioré pour des stratéfiés thermotransférables, dans lequel un substrat transférable (15) renfermant une couche à motifs (30) est transféré d'une bande-support (2) à un article tel qu'une bouteille ou un récipient en plastique lors de l'application de chaleur et de pression. La bande-support (2) comporte une couche non paraffinée (5). Ce système de décollage amélioré (5) comprend une partie couche thermodurcissable, d'un alkyde non cellulosique, de la bande-support, qui est en contact avec et adhère à la partie couche de transfert non paraffinée du substrat transférable (15). La couche décollable améliorée (5) est de préférence un alkyde non cellulosique modifié par de la mélanine, qui lors du durcissement présente des caractéristiques thermodurcissables. Le substrat transférable est transféré à l'article lors de l'application de chaleur sur le support tandis que l'article vient en contact avec le stratifié. Le substrat transféré sur l'article est clair et possède une résistance améliorée à l'usure par frottement et à l'abrasion. La couche non paraffinée ne renferme pas de cire et peut présenter des caractéristiques thermoplastiques ou thermodurcissables.
PCT/US1989/001731 1988-07-22 1989-04-21 Stratifie thermotransferable WO1990000940A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US22318788A 1988-07-22 1988-07-22
US223,187 1988-07-22

Publications (1)

Publication Number Publication Date
WO1990000940A1 true WO1990000940A1 (fr) 1990-02-08

Family

ID=22835431

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1989/001731 WO1990000940A1 (fr) 1988-07-22 1989-04-21 Stratifie thermotransferable

Country Status (4)

Country Link
AU (1) AU4046089A (fr)
ES (1) ES2011565A6 (fr)
PT (1) PT91041B (fr)
WO (1) WO1990000940A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000020229A1 (fr) * 1998-10-08 2000-04-13 International Playing Card & Label Company Substrats pour etiquettes imprimees par report a chaud
US6254970B1 (en) 1998-10-08 2001-07-03 International Playing Card & Label Co. Substrates for heat transfer labels
US6376069B1 (en) 1999-06-25 2002-04-23 Avery Dennison Corporation Heat-transfer label including non-wax release layer
US6893717B1 (en) 1999-07-08 2005-05-17 Kuolih Tsai Heat-transfer label including non-wax release coating

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4117198A (en) * 1976-11-03 1978-09-26 Formica Corporation Release sheet of a cellulosic paper coated with a resin mixture
US4118541A (en) * 1976-11-03 1978-10-03 Formica Corporation Release sheet of a coated cellulose paper

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4117198A (en) * 1976-11-03 1978-09-26 Formica Corporation Release sheet of a cellulosic paper coated with a resin mixture
US4118541A (en) * 1976-11-03 1978-10-03 Formica Corporation Release sheet of a coated cellulose paper

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000020229A1 (fr) * 1998-10-08 2000-04-13 International Playing Card & Label Company Substrats pour etiquettes imprimees par report a chaud
US6254970B1 (en) 1998-10-08 2001-07-03 International Playing Card & Label Co. Substrates for heat transfer labels
US6376069B1 (en) 1999-06-25 2002-04-23 Avery Dennison Corporation Heat-transfer label including non-wax release layer
US6423406B1 (en) 1999-06-25 2002-07-23 Avery Dennison Corporation Heat-transfer label including non-wax release layer
US6893717B1 (en) 1999-07-08 2005-05-17 Kuolih Tsai Heat-transfer label including non-wax release coating

Also Published As

Publication number Publication date
PT91041B (pt) 1994-07-29
PT91041A (pt) 1990-02-08
ES2011565A6 (es) 1990-01-16
AU4046089A (en) 1990-02-19

Similar Documents

Publication Publication Date Title
US4935300A (en) Heat transferable laminate
US5104719A (en) Heat activated, quick release decals and associated methods
US4704310A (en) Heat transferable laminate
US6423406B1 (en) Heat-transfer label including non-wax release layer
US6042676A (en) Heat-transfer label including a polyester ink layer
AU719960B2 (en) Heat-transfer label including phenoxy protective lacquer layer
US4392905A (en) Method of transferring designs onto articles
US6344269B1 (en) Heat-transfer label
US8252400B2 (en) Heat-transfer label assembly and method of using the same
US4726979A (en) Heat transfer barrier label
AU719317B2 (en) Heat-transfer label and adhesive composition for use therein
US5908694A (en) Heat-transfer label
US4610744A (en) Heat transfer pad decoration and substrates therefore
US9206338B2 (en) Heat-transfer label assembly and method of using the same
WO1990000940A1 (fr) Stratifie thermotransferable
US4770733A (en) Molten heat transfer labeling process
US7364777B1 (en) Heat-transfer label assembly and method of using the same
EP0138809B1 (fr) Decoration par tampon de transfert thermique et substrats adequats
US6610397B1 (en) Heat-activatable alkali-removable labelling systems
KR100379214B1 (ko) 인조목용틱무늬패턴전이필름및그의제조방법
CA2377439A1 (fr) Systemes d'etiquettes thermocollables et detachables en milieu alcalin

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU BR DK FI JP KR NO

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE FR GB IT LU NL SE