WO1989010997A1 - Perspiration-absorbing materials - Google Patents
Perspiration-absorbing materials Download PDFInfo
- Publication number
- WO1989010997A1 WO1989010997A1 PCT/AT1989/000043 AT8900043W WO8910997A1 WO 1989010997 A1 WO1989010997 A1 WO 1989010997A1 AT 8900043 W AT8900043 W AT 8900043W WO 8910997 A1 WO8910997 A1 WO 8910997A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- leather
- materials
- sweat
- carrier
- hydrophilic substances
- Prior art date
Abstract
The materials described consist of a combination of conventional textile, leather, plastic or artificial leather materials, possibly in composite form, as carrier material with high molecular weight hydrophilic substances as active agent. The use of the new materials as lining leather, automobile seat covers, artificial leather or the like substantially improves the perspiration-regulating properties.
Description
Schweißabieitende Materlallen Sweat-wicking materials
Die Erfindung betrifft Materialien, die eine schnelle und wiederholbare Schweißableitung bewirken. Diese Materialien zeichnen sich im wesentlichen durch eine Komposition von herkömmlichen Textil-, Lederoder Kunstlederstoffen oder deren Kombinationen, gegebenenfalls in Verbundausführung (z.B. Textilgewebe mit Schaumstoffrücken), mit höhermolekularen hydrophilen Substanzen (HMHS) aus.The invention relates to materials that cause rapid and repeatable sweat wicking. These materials are essentially characterized by a composition of conventional textile, leather or synthetic leather materials or their combinations, possibly in a composite design (e.g. textile fabric with a foam backing), with higher molecular weight hydrophilic substances (HMHS).
Materialien für Artikel des persönlichen Komforts, wie z.B. für Schuhe, Sitze, Liegen usw. sind des öfteren hydrophob oder nur gering feuchtigkeitsleitend. Sehr häufig führen sie zu einem lokalen Wärmestau und verursachen fast immer das Problem der sich leicht bildenden Schweißansammlung an den einschlägigen Körperstellen.Materials for items of personal comfort, such as for shoes, seats, loungers etc. are often hydrophobic or only slightly moisture-conducting. Very often they lead to a local build-up of heat and almost always cause the problem of the easily forming sweat accumulation on the relevant parts of the body.
Bekannterweise ist dieses Phänomen störend, unangenehm und geruchsbelästigend. Darüberhinaus verursacht es leicht Hautreizungen, bakterielle Erkrankungen sowie Pilzinfektionen und kann sich auch mechanisch sehr unvorteilhaft auswrir-ken.As is known, this phenomenon is annoying, uncomfortable and unpleasant. In addition, it easily causes skin irritation, bacterial diseases and fungal infections and can also be mechanically very disadvantageous.
Die zufriedenstellende Beseitigung dieses Phänomens ist seit langem trotz zahlreicher Bemühungen ein praktisch ungelöstes Problem. Es wurden z.B. Materialien mit Perforierungen, schwei .ßaufnehmende Einlagen aus Papier oder Schaumstoff, schweißsaugende Füllungen oder Beschichtungen aus z.B. Ca- und Mg-Oxid mit Gummi arabicum bzw. aus Dextran oder perspirationshemmende Verbindungen vorgeschlagen.Despite numerous efforts, the satisfactory elimination of this phenomenon has long been a practically unsolved problem. For example, Materials with perforations, sweat-absorbing inserts made of paper or foam, sweat-absorbent fillings or coatings made of e.g. Ca and Mg oxide with gum arabic or from dextran or antiperspirant compounds proposed.
Derartige Lösungsvorschläge sind jedoch ineffektiv, funktionieren langsam und weisen eine nur begrenzte Schweißaufnahme<apazitat auf. So absorbieren beispielsweise Schuheinlagen aus Papier, aus Stoff mit Aktivkohle usw. den Schweiß. Dies erfolgt jedoch langsam und relativ kurzzeitig, da es bei einigermaßen intensiverer Schweißabsonderung zu schneller Sättigung und somit zum Verlust der weiteren Schweißeliniinierung kommt.However, such proposed solutions are ineffective, work slowly and have only a limited sweat absorption capacity. For example, shoe inserts made of paper, fabric with activated carbon, etc. absorb sweat. However, this takes place slowly and relatively briefly, since with somewhat more intensive sweating, rapid saturation occurs and thus further welding lines are lost.
Perspirationshemmende Systeme hingegen führen zwar zur Herabsetzung der Schweißansammlung an der relevanten Hautfläche, sind aber physiologisch ungünstig, da sie die hauteigene Funktion der Absonderung von unerwünschten Stoffen und die Wärmeregulierung stören.
Aufgabe der vorliegenden Erfindung ist es, neue Materialien zur Verfügung zu stellen, die eine schnelle und effiziente Entfernung des Schweißes von den relevanten Körperkontaktzonen gewährleisten und die unerwünschten Folgewirkungen verhindern.Perspiration-inhibiting systems, on the other hand, reduce sweat accumulation on the relevant skin area, but are physiologically unfavorable because they interfere with the skin's own function of secreting unwanted substances and regulating heat. The object of the present invention is to provide new materials which ensure a quick and efficient removal of sweat from the relevant body contact zones and prevent the undesirable secondary effects.
Diese Aufgabe wird erfindungsgemäß durch Kompositionen aus Textil-, Leder-, Kunststoff- oder Kunstledermaterialien mit permanenter und/oder Quellungsporosität oder deren Kombinationen, gegebenenfalls in Verbundausführung als Trägermaterial, mit in der Regel höhermolekularen hydrophilen Substanzen als Agens der lipophil-hydrophilen Zwitterbauweise gelöst.This object is achieved according to the invention by compositions of textile, leather, plastic or synthetic leather materials with permanent and / or swelling porosity or combinations thereof, optionally in a composite design as a carrier material, with generally higher molecular weight hydrophilic substances as agents of the lipophilic-hydrophilic hermaphrodite construction.
Statt die Schweißabsonderung chemisch zu unterdrücken oder mittels einschlägigen Absorbentien zu binden, wie dies die Funktionsweise der konventionellen Systeme ist, wird sie hier erfindungsgemäß einfach abgeleitet. Dies erfolgt durch die Diffusion des Schweißes durch das Trägermaterial als Folge der Auswirkung der hydrophilen Substanzen, der Porosität und der Oberflächenkräfte sowie der Konzentrationsgradienten des Agens. Agentien, die eine solche effiziente Diffusion ermöglichen, können dabei in feuchtem Zustand immobil, mobil oder gemischter Natur sein. Immobile Substanzen in diesem Sinne bilden praktisch nicht wandernde Depositionen an Trägern. Die Diffusion des Schweißes erfolgt hier als Wanderung der H2O-Moleküle sowie deren Agglomerate und Solutionen im Sinne der Hydratisierung dieser' Deposition und als Auswirkung der Oberflächenspannungen. Die Deposition bleibt dabei weitgehend erhalten. Lediglich die Beweglichkeit ihrer hydrophilen Segmente ist gestiegen. Nach vollendeter Hydratisierung läuft die Diffusion über die freie Beweglichkeit der hydrophilen Einheiten im hydrophilen Milieu weiter,. Als treibende Kraft tritt der Konzentrationsgradient auf.Instead of chemically suppressing sweat secretion or binding it by means of relevant absorbents, as is the way the conventional systems work, it is simply derived here according to the invention. This takes place through the diffusion of sweat through the carrier material as a result of the effect of the hydrophilic substances, the porosity and the surface forces as well as the concentration gradients of the agent. Agents that enable such efficient diffusion can be immobile, mobile or mixed in the wet state. In this sense, immobile substances form practically non-migrating depositions on carriers. The diffusion of sweat takes place here as a migration of the H 2 O molecules as well as their agglomerates and solutions in the sense of hydrating these 'depositions and as an effect of the surface tensions. The deposition is largely preserved. Only the mobility of their hydrophilic segments has increased. After hydration is complete, the diffusion continues via the free mobility of the hydrophilic units in the hydrophilic environment. The concentration gradient acts as the driving force.
Mobile Agentien werden gegenüber den immobilen infolge der Hydratisierung beweglich und wandern, ähnlich den Vorgängen bei der Chromatographie, in Richtung des fortschreitenden Lösungsmittels, des Schweißes.Mobile agents become mobile compared to the immobile ones as a result of hydration and, similar to the processes in chromatography, migrate in the direction of the progressive solvent, sweat.
Analog den vorbeschriebenen Agensformen am Trägermaterial verhalten sich Agentien gemischter Natur, jedoch mit dem Vorteil, daß auch bei totaler Diffusion stets eine dem immobilen Anteil äquivalente
Menge an hydrophilen Gruppen der Trägermasse bzw. dem Schweißangebot zur Verfügung steht.Agents of mixed nature behave analogously to the above-described forms of agents on the carrier material, but with the advantage that, even with total diffusion, there is always an equivalent to the immobile part Amount of hydrophilic groups of the carrier mass or the sweat supply is available.
Die Schweißableitung verläuft prinzipiell in Gradientrichtung (Naß—> Trocken) und dauert bis zur Erreichung des Systemgleichgewichts. Die Leistungsfähigkeit des schweißableitenden Materials ist vor allem durch seine durch das Agens aktivierte Masse und ihre Oberfläche gegeben. Der Prozeßablauf ist durch eine hohe Geschwindigkeit charakterisiert und erfolgt im Sinne der Entropie-Erhöhung.The perspiration is principally in the gradient direction (wet—> dry) and lasts until the system reaches equilibrium. The performance of the sweat-wicking material is given above all by its mass activated by the agent and its surface. The process flow is characterized by a high speed and takes place in the sense of increasing the entropy.
Die Regenerierung erfolgt bei relativer Feuchtigkeit < 100% spontan und praktisch sofort und insbesondere nach Unterbrechung der Schweißzufuhr.Regeneration takes place spontaneously and at relative humidity <100% and practically immediately and especially after the sweat supply is interrupted.
Bei schweißableitenden Materialien mit mobilen Agentien wandern diese während der Regenerierung zu der Oberfläche und bewirken somit eine besondere Aktivierung der Oberfläche der schweißableitendenMaterialien.In the case of sweat-wicking materials with mobile agents, these migrate to the surface during regeneration and thus bring about a special activation of the surface of the sweat-wicking materials.
Das in dem erfindungsgemäßen Material aufgenommene und transportierte H2O wird während der Regenerierung in Form von Wasserdampf in die umgebende uft abgegeben.The H 2 O taken up and transported in the material according to the invention is released into the surrounding air in the form of water vapor during the regeneration.
Das Verfahren zur Herstellung des erfindungsgemäßen schweißableitenden Materials beruht darauf, daß ein vorzugsweise reines Textilmaterial, Leder, Kunstleder sowie Kunststoffgebilde mit permanenter und/oder Quellungsporosität oder deren Kombinationen, vorzugsweise in Bahnenform, durch ein Tränk-, Spritz-, Übertragungs- oder Taucbverfahren mit einer vorteilhafterweise verdünnten Hydrophiliersubstanz imprägniert und gegebenenfalls anschließend in einen trockenen Zustand übergeführt wird. Das Imprägnieren kann auch in einer ein- oder mehrstufigen Vorgangsweise und gegebenenfalls mit zwischengeschaltetern Verdünn-Waschprozeß erfolgen.The process for producing the sweat-wicking material according to the invention is based on the fact that a preferably pure textile material, leather, synthetic leather and plastic structures with permanent and / or swelling porosity or combinations thereof, preferably in sheet form, by an impregnation, spraying, transferring or dewing process with a advantageously impregnated with diluted hydrophilizing substance and optionally subsequently converted into a dry state. The impregnation can also be carried out in a one- or multi-stage procedure and, if necessary, with an intermediate dilution-washing process.
Das Imprägnieren sei beispielhaft an Hand eines Tauch/erfahrens näher erläutert. Danach wird der Träger in die Agenslösung eingelegt. Nach einer Einwirkphase wird der imprägnierte Träger entnommen und ausgepreßt. An ein Auswaschen, Nachbehandeln und Kalibrieren
schließt ein Trocknen an, wonach die imprägnierte Ware lager- bzw. versandfertig ist. kontinuierliche Als besonders vorteilhaft erweist sich eine zweistufig/ Verfahrensführung, die im wesentlichen aus einer Vorbehandlung des Trägers mit etwas konzentrierterem Agens und seiner anschließenden Verdünnung durch einen Waschprozeß und einer Nachbehandlung mit vorzugsweise höhermolekularem Agens besteht.The impregnation is explained in more detail using an immersion method. The carrier is then placed in the agent solution. After an exposure phase, the impregnated carrier is removed and pressed out. Washing, post-treatment and calibration This is followed by drying, after which the impregnated goods are ready for storage or dispatch. Continuous A two-stage / process control, which essentially consists of pretreating the carrier with somewhat more concentrated agent and then diluting it with a washing process and post-treatment with preferably higher molecular weight agent, has proven particularly advantageous.
Die erfindungsgemäße Lehre wird an Hand der folgenden Beispiele erläutert:The teaching of the invention is illustrated by the following examples:
BEISPIEL 1EXAMPLE 1
Träger: Chromgare Narbenfutterleder Vorbehandlung: - 3-stündiges Tauchen in ein Agensgemisch, bestehend aus: 10,0 GT AlkylsulfonatCarrier: Chrome-grain grain leather Pretreatment: - 3 hours of immersion in an agent mixture consisting of: 10.0 GT alkyl sulfonate
0,5 GT Na-Stearat 3,0 GT Polyethylenglykol 86,5 GT DEMI ( demineralisiertes Wasser)0.5 GT Na stearate 3.0 GT polyethylene glycol 86.5 GT DEMI (demineralized water)
- Verdünnung durch Waschvorgang mit DEMI- Dilution by washing with DEMI
- Auspreß- bzw. Kalibrierungs- und Vortrocknungsprozeß- Squeezing or calibration and predrying process
Nachbehandlung: - Deposition eines Agens am Träger durch Spritzverf^hrenAftertreatment: - Deposition of an agent on the carrier by spraying
Zusammensetzung der Agenslösung: 2,0 GT Polyethylenglykol MM 300 98,0 GT DEMIComposition of the agent solution: 2.0 pbw of polyethylene glycol MM 300 98.0 pbw of DEMI
- Trocknung mit auf 40°C vorgewärmter Luft- Drying with air preheated to 40 ° C
Die relevanten Eigenschaften des behandelten Futterleders im Vergleich zu unbehandeltem sind in Tabelle 1 angeführt.
The relevant properties of the treated lining leather compared to untreated leather are listed in Table 1.
BEISPIEL 2EXAMPLE 2
Träger: Autositzbezugsstoff aus Wolle/Baumwolle, aufkaschiert auf Schaumstoff mit Gewirkunterlage, und Autositzbezugsstoff aus reinem Gewebe .Carrier: Car seat cover made of wool / cotton, laminated onto a foam with a knitted backing, and car seat cover made of pure fabric.
Vorbehandlung: - 20-minütiges Tränken mit einer Agenslösung, bestehend ausPretreatment: - Soak for 20 minutes with an agent solution consisting of
10 GT Alkylsulfonat 1 GT Natriumpalmitat 1 GT Polyethylenglykolmonostearat10 pbw alkyl sulfonate 1 pbw sodium palmitate 1 pbw polyethylene glycol monostearate
88 GT DEMI - Waschvorgang mit deionisiertem Wasser - Auspressen und Vortrocknung88 GT DEMI - washing process with deionized water - squeezing and predrying
Nachbehandlung:Post-treatment:
Deposition von etwa 0,5 Gew - Agens am Träger durch ÜbertragungDeposition of approximately 0.5% by weight on the carrier by transfer
Zusammensetzung der Agensmischung:Composition of the agent mixture:
1,0 GT Polyethylenglykol MM 3001.0 GT polyethylene glycol MM 300
1,0 GT H MM 8001.0 GT H MM 800
98,0 GT DEMI und anschließende - Trocknung im Luftstrom
Der Grad der erzielten ableitenden Eigenschaften und der erreichten Veränderungen der einschlägigen Kenndaten der Autositzbezugsstoffe ist der nachfolgenden Tabelle 2 zu entnehmen.98.0 GT DEMI and subsequent - drying in an air stream The degree of the dissipative properties achieved and the changes achieved in the relevant characteristics of the car seat upholstery is shown in Table 2 below.
- Die Wasseraufnahme nach DIN 53 923 wird durch die Ausrüstung verdoppelt.- The water absorption according to DIN 53 923 is doubled by the equipment.
- Die Feuchtigkeitsaufnahme nach TL-VW 52 081 wird bis zu 50% erhöht.- The moisture absorption according to TL-VW 52 081 is increased by up to 50%.
- Ein Feuchtigkeitstransport in der Probenebene, geprüft nach dem Steighöhenverfahren nach DIN 53 924, findet in den unbehandelten Proben praktisch nicht statt. Durch die Ausrüstung wird eine rege Feuchtigkeitsweiterleitung bewirkt.- Moisture transport in the sample plane, tested according to the rising height method according to DIN 53 924, practically does not take place in the untreated samples. The equipment ensures brisk moisture transmission.
Insbesondere dieser Feuchtigkeitstransport in der Probenebene bewirkt, daß der an den Kontaktstellen aufgenommene Schweiß rasch an die Randbereiche des Sitzbezuges weitergeleitet und dort wieder in Form von Verdunstung abgegeben werden kann. Kurzfristig höhere Schweißmengen werden auf Grund der hohen Wasseraufnahme bis zur Weiterleitung zwischengespeichert (Pufferwirkung).In particular, this moisture transport in the sample plane causes the sweat absorbed at the contact points to be rapidly passed on to the edge areas of the seat cover and can be released there again in the form of evaporation. Due to the high water absorption, higher sweat quantities are temporarily stored until they are passed on (buffer effect).
Trotz dieser durch die Ausrüstung hervorgerufenen, wesentlich gesteigerten Feuchtigkeitsaufnahme quillt der Sitzbezugsstoff nicht so an, daß dadurch eine Minderung der Wasserdampfdurchlässigkeit oder eine Veränderung des Wärmedurchlaßwiderstandes gegeben wäre. Diese Meßwerte werden durch die Ausrüstung in keiner Weise verändert.Despite this significantly increased moisture absorption caused by the equipment, the seat cover material does not swell in such a way that there is a reduction in water vapor permeability or a change in the thermal resistance. These measurements are not changed in any way by the equipment.
Auch alle anderen untersuchten Eigenschaften des Sitzbezuges, wie Brennverhalten, verschiedene Farbechtheiten und Scheuerprüfungen, werden durch die Ausrüstung mit der Hydrophiliersubstanz nicht verändert.All other investigated properties of the seat cover, such as burning behavior, different color fastness and abrasion tests, are not changed by the treatment with the hydrophilizing substance.
Die Aufnahme, Zwischenspeicherung und Weiterleitung der Feuchtigkeit durch einen Autositzbezugsstoff wird durch die erfindungsgemäße Spezialausrüstung derart stark erhöht, daß in der Praxis eine wesentliche Verbesserung des Mikroklimas und damit ein hoher Grad an thermischem Wohlbefinden erreicht wird, während gleichzeitig alle anderen technischen Eigenschaften des Bezugsstoffes durch die Ausrüstung nicht verändert werden.
BEISPIEL 3The absorption, storage and transmission of moisture by a car seat cover material is increased so much by the special equipment according to the invention that in practice a substantial improvement in the microclimate and thus a high degree of thermal well-being is achieved, while at the same time all other technical properties of the cover material are achieved by the Equipment cannot be changed. EXAMPLE 3
Träger: Kunstleder, Alcantara-Trägermaterial mit Stoffrücken, reinCarrier: synthetic leather, Alcantara carrier material with fabric back, pure
Vorbehandlung: mechanische Porenbildung Nachbehandlung: Deposition von etwa 0,3 Gew.-% (trägerbezogen) eines Agens durch Tauchverfahren mit anschließendem Auspreß- und TrocknungsprozeßPretreatment: mechanical pore formation Post-treatment: deposition of about 0.3% by weight (carrier-related) of an agent by immersion, followed by a squeezing and drying process
Zusammensetzung der Agenslösung:Composition of the agent solution:
2 GT Polyethylenglykol MM 8002 pbw of polyethylene glycol MM 800
3 GT Polyethylenglykol ATT 2503 GT polyethylene glycol ATT 250
1 GT Polyethylenglykol-monostearat 0,5 GT Alkylsulfonat 95,5 GT DEMI1 pbw of polyethylene glycol monostearate 0.5 pbw of alkyl sulfonate 95.5 pbw of DEMI
Die einschlägigen Eigenschaften des behandelten Kunstledermaterials im Vergleich zu unbehandeltem sind der nachstehenden Tabelle 3 zu entnehmen:The relevant properties of the treated synthetic leather material compared to the untreated one can be found in Table 3 below:
Die permanente und/oder Quellungsporosität des Trägermaterials kann in verschiedener Weise herbeigeführt werden. Eine permanente Porosität kann beispielsweise durch mechanische Porenbildung bewirkt werden, eine Quellungsporosität kann in an sich bekannter Weise durch chemische und/oder physikalisch-chemische Vorgänge, wie Quellungs-, Fällungs- oder Extraktionsverfahren, bewirkt werden.
The permanent and / or swelling porosity of the carrier material can be brought about in various ways. Permanent porosity can be brought about, for example, by mechanical pore formation; swelling porosity can be brought about in a manner known per se by chemical and / or physicochemical processes, such as swelling, precipitation or extraction processes.
Claims
1. Schv/eißableitende Materialien, gekennzeichnet durch eine Kombination von Textil-, Leder-, Kunststoff- oder Kunstledermaterialien mit permanenter und/oder Quellungsporosität, gegebenenfalls in Verbundausführung, als Trägermaterial mit höhermolekularen hydrophilen Substanzen als wirksames Agens.1. Schv / ice-dissipating materials, characterized by a combination of textile, leather, plastic or synthetic leather materials with permanent and / or swelling porosity, optionally in composite design, as a carrier material with higher molecular weight hydrophilic substances as an effective agent.
2. Materialien nach Anspruch 1, dadurch gekennzeichnet, daß die hydrophilen Substanzen in feuchtem Zustand immobil sind.2. Materials according to claim 1, characterized in that the hydrophilic substances are immobile in the moist state.
3. Materialien nach Anspruch 1, dadurch gekennzeichnet, daß die hydrophilen Substanzen in feuchtem Zustand mobil sind.3. Materials according to claim 1, characterized in that the hydrophilic substances are mobile in the moist state.
4. Materialien nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die permanente Porosität durch mechanische Porenbildung hervorgerufen ist.4. Materials according to one of claims 1 to 3, characterized in that the permanent porosity is caused by mechanical pore formation.
5. Materialien nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die Quellungsporosität durch chemische und/oder physikalisch-chemische Vorgänge, z.B. Quellung-, Fällungs- oder Extraktionsverfahren, hervorgerufen ist.5. Materials according to one of claims 1 to 3, characterized in that the swelling porosity by chemical and / or physicochemical processes, e.g. Swelling, precipitation or extraction processes.
6. Verfahren zur Herstellung der schweißableitenden Materialien nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß ein Textilmaterial, Leder, Kunstleder oder Kunststoffgebilde oder deren Verbünde, vorzugsweise in Bahnenform, mit höhermolekularen hydrophilen Substanzen imprägniert und gegebenenfalls anschließend getrocknet werden.6. A method for producing the sweat-wicking materials according to one of claims 1 to 5, characterized in that a textile material, leather, synthetic leather or plastic structures or their composites, preferably in sheet form, impregnated with higher molecular weight hydrophilic substances and optionally subsequently dried.
7. Verfahren nach Anspruch 6, dadurch gekennzeichnet, daß das Imprägnieren ein- oder mehrstufig, gegebenenfalls mit zwischengeschalteten Verdünn-Waschprozessen, ausgeführt wird.7. The method according to claim 6, characterized in that the impregnation is carried out in one or more stages, optionally with intermediate dilution washing processes.
8. Verfahren nach Anspruch 6 oder 7, dadurch gekennzeichnet, daß das Imprägnieren zweistufig erfolgt, wobei in einer Vorbehandlungsstufe die Träger mit konzentriertem Agens behandelt und dieses anschließend durch einen Waschprozeß verdünnt wird und in einer Nachmischungsstufe der imprägnierte Träger mit höhermolekularem Agens behandelt wird.8. The method according to claim 6 or 7, characterized in that the impregnation takes place in two stages, the carrier being treated with concentrated agent in a pretreatment stage and this is then diluted by a washing process and the impregnated carrier being treated with higher molecular weight agent in a post-mixing stage.
9. Futterleder, Autositzbezugsstoff oder Kunstleder, bestehend aus einem schweißableitenden Material nach einem der Ansprüche 1 bis 5. 9. lining leather, car seat cover or synthetic leather, consisting of a sweat-wicking material according to one of claims 1 to 5.