WO1985000360A1 - Hardenable dual constituent composition, and application of said composition as isophonic and isothermal coating - Google Patents
Hardenable dual constituent composition, and application of said composition as isophonic and isothermal coating Download PDFInfo
- Publication number
- WO1985000360A1 WO1985000360A1 PCT/FR1983/000135 FR8300135W WO8500360A1 WO 1985000360 A1 WO1985000360 A1 WO 1985000360A1 FR 8300135 W FR8300135 W FR 8300135W WO 8500360 A1 WO8500360 A1 WO 8500360A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- solid
- resin
- approximately
- composition according
- Prior art date
Abstract
Hardenable composition including two constituents, one of them being a liquid constituent and the other one a solid constituant in a particulate state which are mixed at the time when the composition is to be used, the liquid constituent comprising a resin and a plastifier in solution or suspension in water, while the solid constituent comprises a compound capable or causing the expansion of said resin, and fillers. Said composition is characterized in that said resin and said plastifier are respectively a modified acrylic copolymer and an acrylic plastifier, and in that the solid constituant contains plaster and cement and, as a compatibility agent between those two products, titanium oxide or aluminium oxide. Said composition is particularly convenient as an isothermal and isophonic coating.
Description
Composition durcissable à deux constituants, et application de cette composition comme revêtement isophonique et isothermique Two-component curable composition, and application of this composition as an isophonic and isothermal coating
L'invention concerne une composition durcissable à deux constituants, l'un liquide et l'autre solide à l'état de particules, notamment de poudres, que l'on mélange au moment de l'emploi, L'invention concerne également l'utilisation d'une telle composition comme revêtement isophonique et isothermique et résistant à la corrosion et aux agents chimiques.The invention relates to a curable composition with two constituents, one liquid and the other solid in the form of particles, in particular powders, which are mixed at the time of use. The invention also relates to the use of such a composition as isophonic and isothermal coating and resistant to corrosion and to chemical agents.
Dans la demande de brevet FR 79 03347, déposée le 9 Février 1979, le Demandeur a déjà proposé une composition de ce type, comprenant un composant liquide et l'autre solide, que l'on mélange au moment de l'emploi, cette composition présentant, après durcissement, des propriétés de calorifugeage et d'insonorisation.In patent application FR 79 03347, filed on February 9, 1979, the Applicant has already proposed a composition of this type, comprising a liquid component and the other solid, which is mixed at the time of use, this composition having, after hardening, thermal insulation and soundproofing properties.
Dans cette composition antérieure, la phase liquide comprend, d'une part, une résine plastique en solution ou en suspension dans de l'eau et, d'autre part, un agent anionique apte à former des bulles avec un composé du composant solide, tandis que ce composant solide comprend, outre ledit composé apte à réagir avec ledit agent anionique, un composé apte à prendre en masse au contact de l'eau.In this previous composition, the liquid phase comprises, on the one hand, a plastic resin in solution or in suspension in water and, on the other hand, an anionic agent capable of forming bubbles with a compound of the solid component, while this solid component comprises, in addition to said compound capable of reacting with said anionic agent, a compound capable of solidifying on contact with water.
La résine plastique est choisie dans le groupe comprenant les copolymères acétate de vinyl-versatate de vinyle, les terpolymères ester acrylique-versatate de vinyle-acétate de vinyle et les copolymères styrène-composé acrylique. L'agent anionique du composant liquide est le produit de condensation d'un lauryl éther sulfate de sodium et d'un alcool comprenant de 12 à 14 atomes de carbone, tandis que le composé associé du composant solide est de l'éthylhexyl sulfate de sodium. Enfin, le constituant du
composant solide apte à prendre en masse au contact de l'eau est du plâtre, éventuellement additionné d'un retardateur de prise. Des charges anti-feu peuvent aussi être prévues dans la composition.The plastic resin is chosen from the group comprising vinyl acetate-vinyl versatate copolymers, acrylic ester-vinyl versatate-vinyl acetate terpolymers and styrene-acrylic compound copolymers. The anionic agent of the liquid component is the condensation product of a sodium lauryl ether sulfate and an alcohol comprising from 12 to 14 carbon atoms, while the associated compound of the solid component is sodium ethylhexyl sulfate . Finally, the constituent of the solid component capable of solidifying on contact with water and plaster, possibly with a setting retarder. Anti-fire charges can also be provided in the composition.
Bien que satisfaisante dans son utilisation comme isolant, cette composition antérieure présente l'inconvénient, ainsi que l'a établi le Demandeur en poursuivant ses travaux, de se craqueler en vieillissant, et ce quel que soit le milieu ambiant. Du fait d'une rétraction de la résine, des fentes apparaissent en effet dans les revêtements constitués d'une telle composition, avec pour conséquence la formation de ponts thermiques et une sérieuse détérioration des propriétés de calorifugeage du revêtement.Although satisfactory in its use as an insulator, this prior composition has the disadvantage, as established by the Applicant while continuing its work, of cracking as it ages, whatever the environment. Due to a shrinkage of the resin, cracks appear in the coatings made of such a composition, with the consequence of forming thermal bridges and a serious deterioration of the thermal insulation properties of the coating.
Un autre inconvénient de la composition proposée antérieurement par le Demandeur est qu'elle ne supporte pas les températures élevées, puisque la résine fond dès 100ºC, ce qui interdit d'utiliser cette composition comme revêtement sur des machines présentant des zones très chaudes.Another drawback of the composition previously proposed by the Applicant is that it does not withstand high temperatures, since the resin melts from 100 ° C, which prohibits the use of this composition as a coating on machines with very hot zones.
La présente invention vise à remédier à ces inconvénients en proposant une composition du même type général que la composition antérieure mentionnée ci-dessus, mais qui ne présente pas de phénomène de vieillissement et qui peut être utilisée à des températures très élevées, pouvant atteindre 1000°C, sans s'altérer ni se décoller d'un support quelconque.The present invention aims to remedy these drawbacks by proposing a composition of the same general type as the previous composition mentioned above, but which does not exhibit any aging phenomenon and which can be used at very high temperatures, up to 1000 ° C, without altering or detaching from any support.
L'invention vise également à proposer une composition de ce type dans laquelle peuvent être présents simultanément du ciment et du plâtre, dont l'incompatibilité est bien connue, sans risque de voir ces deux composants se dissocier après durcissement.The invention also aims to propose a composition of this type in which cement and plaster can be present simultaneously, the incompatibility of which is well known, without the risk of these two components dissociating after hardening.
L'invention vise enfin à proposer une composition de ce type qui puisse être utilisée en couches très minces, de
l'ordre de 3 à 4 mm d'épaisseur, comme revêtement insonorisant et isothermique.The invention finally aims to propose a composition of this type which can be used in very thin layers, around 3 to 4 mm thick, as a soundproofing and isothermal covering.
A cet effet, l'invention a pour objet une composition durcissable à deux constituants, l'un liquide, l'autre solide à l'état particulaire, que l'on mélange au moment de l'emploi, le constituant liquide comprenant une résine et un plastifiant en solution ou en suspension dans de l'eau, tandis que le constituant solide comprend un composé apte à provoquer l'expansion de ladite résine, et des charges, cette composition étant caractérisée en ce que ladite résine et ledit plastifiant sont respectivement un copolymère acrylique modifié et un plastifiant acrylique, et en ce que le constituant solide contient, en % en poids, environ 30 à 60% de plâtre, environ 52 à 4% de ciment et, à titre d'agent de compatibilité entre ces deux produits, 3 à 7% d'oxyde de titane ou d'aluminium.To this end, the subject of the invention is a curable composition with two constituents, one liquid, the other solid in the particulate state, which is mixed at the time of use, the liquid constituent comprising a resin. and a plasticizer in solution or in suspension in water, while the solid component comprises a compound capable of causing the expansion of said resin, and fillers, this composition being characterized in that said resin and said plasticizer are respectively a modified acrylic copolymer and an acrylic plasticizer, and in that the solid constituent contains, in% by weight, approximately 30 to 60% of plaster, approximately 52 to 4% of cement and, as agent of compatibility between these two products, 3 to 7% of titanium or aluminum oxide.
Des additifs connus en soi pourront être incorporés dans le constituant liquide aussi bien que dans le constituant solide, par exemple, des produits antistatiques, des composés germicides et algicides, des produits anti-feu, des retardateurs de prise, etc.Additives known per se may be incorporated in the liquid component as well as in the solid component, for example, antistatic products, germicidal and algicidal compounds, fire-resistant products, setting retarders, etc.
Avantageusement, le constituant solide contiendra de la poudre d'aluminium ou du mica expansé. En effet, après mélange des deux constituants et application de la composition résultante sur le substrat à revêtir, les particules d'aluminium ou de mica expansé remontent à la surface libre, avant durcissement de la composition, pour contribuer ensuite à l'isolation thermique par réflexion du rayonnement infrarouge. Pour certaines applications particulières, par exemple pour l'industrie nucléaire, au lieu d'aluminium le constituant solide pourra contenir du plomb.Advantageously, the solid component will contain aluminum powder or expanded mica. In fact, after mixing the two constituents and applying the resulting composition to the substrate to be coated, the aluminum or expanded mica particles rise to the free surface, before the composition hardens, to then contribute to thermal insulation by reflection of infrared radiation. For certain specific applications, for example for the nuclear industry, instead of aluminum, the solid component may contain lead.
Comme copolymère acrylique modifié, on pourra avantageusement utiliser, dans le constituant liquide, un sel de
l'acide versatique. La teneur en copolymère acrylique modifié du constituant liquide sera d'environ 10 à 30% en poids, tandis que la teneur en plastifiant acrylique sera d'environ 1 à 6% . Dans ces conditions, le constituant liquide, avec ses additifs éventuels, se présentera sous la forme d'une émulsion parfaitement stable dans le temps.As a modified acrylic copolymer, it is advantageous to use, in the liquid component, a salt of versatic acid. The content of modified acrylic copolymer in the liquid component will be about 10 to 30% by weight, while the content of acrylic plasticizer will be about 1 to 6%. Under these conditions, the liquid constituent, with its possible additives, will be in the form of an emulsion which is perfectly stable over time.
Les proportions de plâtre et de ciment du constituant solide, de même que la nature de ces composés, varieront en fonction des propriétés physiques, requises du revêtement. La teneur en plâtre sera généralement de 30 à 60% en poids et la teneur en ciment de 52 à 4%, tandis que la teneur en oxyde de titane ou oxyde d'aluminium sera comprise entre 3 et 7% .The proportions of plaster and cement of the solid constituent, as well as the nature of these compounds, will vary according to the physical properties required of the coating. The plaster content will generally be 30 to 60% by weight and the cement content from 52 to 4%, while the content of titanium oxide or aluminum oxide will be between 3 and 7%.
La granulométrie des particules solides est d'environ 0,3 à 2, 5 mm.The particle size of the solid particles is approximately 0.3 to 2.5 mm.
Cette poudre, prête pour l'emploi, est également stable au stockage.This powder, ready for use, is also stable during storage.
Au moment de l'emploi, on mélange environ 100 parties en poids du constituant solide avec 140 parties en poids du constituant liquide et l'on effectue un mélange mécanique. L'application est conduite à l'aide d'une machine à projeter du type à vis sans fin, qui assure le malaxage de la pâte tout en permettant une expansion de la résine. Le mélange peut également se poser, comme un mortier, à la truelle ou tout autre appareil conventionnel de l'industrie du bâtiment.At the time of use, about 100 parts by weight of the solid component are mixed with 140 parts by weight of the liquid component and mechanical mixing is carried out. The application is carried out using a worm type spraying machine, which ensures the mixing of the paste while allowing an expansion of the resin. The mixture can also be laid, like a mortar, with a trowel or any other conventional device in the building industry.
Après application sur un substrat à calorifuger ou à isoler phoniquement, la composition conforme à l'invention durcit très rapidement, puisqu'il suffit d'un quart d'heure pour obtenir un durcissement de surface appréciable, contre deux heures et demie avec une composition selon la demande de brevet FR 79 03347 précitée.
Pour obtenir une isolation satisfaisante aux températures élevées, il suffit d'une couche d'une épaisseur beaucoup plus faible qu'avec les isolants usuels. C'est ainsi qu'avec une épaisseur de l'ordre de 3 à 4 mm sur des tuyaux métalliques à une température de 150°C, la température externe du revêtement est de 58°C. Une couche de 3,5 mm d'épaisseur assure une excellente isolation phonique de l'ordre de 20 décibels entre le médium et l'aigu.After application to a substrate to be thermally insulated or insulated, the composition according to the invention hardens very quickly, since it takes only a quarter of an hour to obtain appreciable surface hardening, against two and a half hours with a composition according to the aforementioned patent application FR 79 03347. To obtain satisfactory insulation at high temperatures, a layer with a much smaller thickness is sufficient than with conventional insulators. Thus, with a thickness of the order of 3 to 4 mm on metal pipes at a temperature of 150 ° C, the external temperature of the coating is 58 ° C. A 3.5 mm thick layer provides excellent sound insulation on the order of 20 decibels between the medium and the treble.
La composition conforme à l'invention adhère à n'importe quel type de support, par exemple à une surface métallique, même polie, à du verre ou à du plâtre sec ou humide, et elle peut éventuellement être appliquée en plusieurs couches superposées. Elle peut être utilisée avec avantage pour tout type d'isolation phonique ou thermique, aussi bien sur des machines que sur des façades de bâtiment .The composition according to the invention adheres to any type of support, for example to a metallic surface, even polished, to glass or to dry or wet plaster, and it can optionally be applied in several superposed layers. It can be used with advantage for any type of sound or thermal insulation, both on machines and on building facades.
Elle peut aussi servir à coller des plaques isolantes et à protéger ces plaques, qui peuvent être en matières cellulaires ou expansées, par exemple du verre cellulaire ou du polystyrène expansé.It can also be used to glue insulating plates and to protect these plates, which can be made of cellular or expanded materials, for example cellular glass or expanded polystyrene.
Une composition conforme à l'invention est par exemple la suivante (% en poids): Constituant liquideA composition in accordance with the invention is for example the following (% by weight): Liquid component
- Copolymère : 10%- Copolymer: 10%
- Plastifiant acrylique : 1 ,5% - Chlorure de stéaryl-diméthyl benzylammonium (composé antistatique ) : 1% - Chlorure d'un n-alcoyie en C 14 - Acrylic plasticizer: 1.5% - Stearyl dimethyl benzylammonium chloride (antistatic compound): 1% - Chloride from a C 14 n-alkyl
(composé germicide algicide ) : 1% - Paraffine chlorée émulsionnée avec un alkylphénol oxyéthyléné et un polyéther aliphatique (produit anti-feu ) : 1 % - Eau : q. s . p .(algicidal germicidal compound): 1% - Chlorinated paraffin emulsified with an oxyethylenated alkylphenol and an aliphatic polyether (anti-fire product): 1% - Water: q. s. p.
100%
Constituant solide100% Solid constituent
- Plâtre : 473.- Plaster: 473.
- Ciment : 29,3%- Cement: 29.3%
- Oxyde de titane : 5,6/o- Titanium oxide: 5.6 / o
- Vermiculite (produit anti-feu) : 7%- Vermiculite (anti-fire product): 7%
- Laurylsul fate en C12 (agent gonflant) : 0,07.- Laurylsul fate in C 12 (swelling agent): 0.07.
- Méthylhydroxypropylcellulose (retardateur de prise) : 1 -7%- Methylhydroxypropylcellulose (setting retarder): 1 -7%
- Sulfate d'aluminium : 6,3.o -Métasilicate de calcium naturel : 3%
- Aluminum sulphate: 6.3.o - Natural calcium metasilicate: 3%
Claims
1. Composition durcissable à deux constituants, l'un liquide, l'autre solide à l'état particulaire, que l'on mélange au moment de l'emploi, le constituant liquide comprenant une résine et un plastifiant en solution ou en suspension dans de l'eau, tandis que le constituant solide comprend un composé apte à provoquer l'expansion de ladite résine, et des charges, cette composition étant caractérisée en ce que ladite résine et ledit plastifiant sont respectivement un copolymère acrylique modifié et un plastifiant acrylique pour le composant liquide et en ce que le constituant solide contient, en % en poids, environ 30 à 60% de plâtre, environ 52 à 4% de ciment et, à titre d'agent de compatibilité, entre ces deux produits, environ 3 à 7% d'oxyde de titane ou d'oxyde d'aluminium.1. Curable composition with two components, one liquid, the other solid in the particulate state, which is mixed at the time of use, the liquid component comprising a resin and a plasticizer in solution or in suspension in water, while the solid component comprises a compound capable of causing the expansion of said resin, and fillers, this composition being characterized in that said resin and said plasticizer are respectively a modified acrylic copolymer and an acrylic plasticizer for the liquid component and in that the solid component contains, in% by weight, approximately 30 to 60% of plaster, approximately 52 to 4% of cement and, as a compatibility agent, between these two products, approximately 3 to 7% titanium oxide or aluminum oxide.
2. Composition selon la revendication 1, caractérisée en ce que le constituant liquide contient, en % en poids, environ 10 à 30 % de copolymère acrylique modifié et environ 1 à 6% de plastifiant acrylique.2. Composition according to claim 1, characterized in that the liquid constituent contains, in% by weight, approximately 10 to 30% of modified acrylic copolymer and approximately 1 to 6% of acrylic plasticizer.
3. Composition selon l'une des revendications 1 et 2, caractérisée en ce que le copolymère acrylique modifié est un sel de l'acide versatique.3. Composition according to one of claims 1 and 2, characterized in that the modified acrylic copolymer is a salt of versatic acid.
4. Composition selon l'une des revendications 1 à 3, caractérisée en ce que la granulométrie du constituant solide est d'environ 0,3 à 2,5 mm.4. Composition according to one of claims 1 to 3, characterized in that the particle size of the solid constituent is approximately 0.3 to 2.5 mm.
5. Composition selon l'une des revendications 1 à 4, caractérisée en ce que le constituant solide contient de la poudre d'aluminium ou de plomb.5. Composition according to one of claims 1 to 4, characterized in that the solid constituent contains aluminum or lead powder.
6. Utilisation d'une composition selon l'une des revendi¬cations 1 à 5, comme revêtement isophonique et isothermique . 6. Use of a composition according to one of claims 1 to 5, as an isophonic and isothermal coating.