WO1983000336A1 - Photo-crosslinkable telomers and production method thereof - Google Patents

Photo-crosslinkable telomers and production method thereof Download PDF

Info

Publication number
WO1983000336A1
WO1983000336A1 PCT/FR1982/000122 FR8200122W WO8300336A1 WO 1983000336 A1 WO1983000336 A1 WO 1983000336A1 FR 8200122 W FR8200122 W FR 8200122W WO 8300336 A1 WO8300336 A1 WO 8300336A1
Authority
WO
WIPO (PCT)
Prior art keywords
taxogen
group
telomeres
acid
type
Prior art date
Application number
PCT/FR1982/000122
Other languages
French (fr)
Inventor
De Vente De L'aluminium Pechiney Societe
Original Assignee
Boutevin, Bernard
Deiss, Willy-Jean
Maliszewicz, Marc
Pietrasanta, Yves
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Boutevin, Bernard, Deiss, Willy-Jean, Maliszewicz, Marc, Pietrasanta, Yves filed Critical Boutevin, Bernard
Priority to DE8282902181T priority Critical patent/DE3268119D1/en
Priority to AT82902181T priority patent/ATE17125T1/en
Publication of WO1983000336A1 publication Critical patent/WO1983000336A1/en
Priority to DK113383A priority patent/DK113383A/en
Priority to NO830813A priority patent/NO158348C/en
Priority to FI830825A priority patent/FI67712C/en

Abstract

Telomers and cotelomers having at least one photo-crosslinkable sequence and their production process. They have the general formula: <IMAGE> wherein the taxogen links -(Xi)- belong to the group comprised by hydroxy 2 ethyl acrylate and methacrylate, by acrylic or methacrylic acid, by vinylic or allylic alcohol, the links <IMAGE> are issued from the same taxogen Xi esterified by means of a group having in its molecule at least a double photo-crosslinkable bond and wherein 1 < x + y <= 1000, Z being selected in the group -H, -Cl, -Br and wherein R may be a simple or macromolecular radical, leading, in the latter case, to the formation of besequenced cotelomers. The production method comprises a telomerization by a redox or radicalar catalysis followed by a grafting of the photo-crosslinkable group, the first phase of telomerization being doubled in the case of a cotelomer. These products may be applied particularly to the coating of metals.

Description

TELOMERES PHOTORETICULABLES ET PROCEDE D ' OBTENTION PHOTORETICULABLE TELEOMERS AND PROCESS FOR OBTAINING SAME
La présente invention est relative à des télomères présentant une ou plusieurs séquences dont l 'une au moins po ssède, sur sa longueur , des groupements latéraux insaturés répartis statistiquement et ayant des propriétés de photoréticulation.The present invention relates to telomeres having one or more sequences of which at least one has, along its length, unsaturated lateral groups distributed statistically and having photocrosslinking properties.
Cette invention concerne également un procédé d ' obtention de ces télomères .The invention also relates to a method for obtaining these telomeres.
Les télomères sont des produits organiques de synthèse résultant d ' une réaction dite de télomérisation dans laquelle un composé organique non saturé Xi appelé "taxogène" réagit en présence de catalyseurs ou d ' initiateurs avec un autre composé AZ appelé "télogène" pour donner par condensation de Xi la formation d 'une séquence de n maillons bivalents —(Xi) - , et la division du télogène AZ en deux parties qui viennent s ' accrocher aux extrémités de la séquence pour donner un produit de formule générale : A-(Xi) -Z appelé télo n mère. Celui-ci peut , à son tour , servir d ' agent télogène pour un autre taxogène Yi et conduire à l ' obtention de cotélomères bisêquencés de formule générale :Telomeres are synthetic organic products resulting from a so-called telomerization reaction in which an unsaturated organic compound X i called "taxogen" reacts in the presence of catalysts or initiators with another AZ compound called "telogen" to give by condensation of X i the formation of a sequence of n divalent links - (X i ) -, and the division of the telogen AZ into two parts which come to hang at the ends of the sequence to give a product of general formula: A- (X i ) -Z called tele mother. This can, in turn, serve as a telogen agent for another taxogen Y i and lead to the production of bis-sequenced cotelomers of general formula:
A' -(Y in) -'A"-(Xi)n-ZA '- (Y in ) - ' A "- (X i ) n -Z
ou A' et A" résultent de la division de A.where A 'and A "result from the division of A.
La demanderesse s ' est intéressée particulièrement à ces produits et à leurs dérivés résultant du greffage sur l 'une au moins des séquences de greffons latéraux insaturés.The Applicant is particularly interested in these products and their derivatives resulting from the grafting on at least one of the sequences of unsaturated lateral grafts.
Les molécules de bas poids moléculaire possédant des insaturations sont déj à connues ou commercialisées . Par exemple, dans le cas de greffons allyliques, la commercialisation de la tétraallyloxy-1, 1, 2, 2 éthane est un fait et, dans le cas des greffons acryliques, on connaît les acrylates de diols, de triols ou de tétraols. Mais, ces compo sés ne comportent pas plus de quatre groupements photopolymërisables.Low molecular weight molecules with unsaturations are already known or marketed. For example, in the case of allylic grafts, the marketing of tetraallyloxy-1, 1, 2, 2 ethane is a fact and, in the case of acrylic grafts, the acrylates of diols, triols or tetraols are known. However, these compounds do not contain more than four photopolymerizable groups.
Des molécules de poids moléculaire compris entre 1000 et 3000 (oligomères télêchëliques) possédant deux groupements acryliques en extrémités de chaîne sont largement utilisées industriellement . Ces macromolécules sont obtenues, par exemple, à partir de polyesters ou de polyuréthanes dihydroxyïés . Enfin, des polymères de haut po ids moléculaire possédant des groupements acryliques et/ou allyliques subst itués sont connus depuis longtemps et leurs applications font encore l ' obj et de nombreux brevets et publications . On peut citer , par exemple, les alcools polyvinyliques et les poly(meth) acrylates de glycol substitués par des groupements acryliques du type cinnamique, β- (2-furyl)acrylique, β -(pyridyl) acrylique. Pour ce type de macromolécules, très peu de composés à greffons acryliques ou allyliques non substitués ont été décrits dans la littérature. Notons, néamoins, le brevet français no 2 412 572 où ces greffons sont réalisés à 1 aide de ponts carbonates.Molecular weight molecules between 1000 and 3000 (telechelic oligomers) having two acrylic groups at the chain ends are widely used industrially. These macromolecules are obtained, for example, from polyesters or dihydroxy polyurethanes. Finally, high molecular weight polymers having substituted acrylic and / or allylic groups have been known for a long time and their applications are still the subject of numerous patents and publications. Mention may be made, for example, of polyvinyl alcohols and poly (meth) acrylates of glycol substituted by acrylic groups of the cinnamic type, β- (2-furyl) acrylic, β - (pyridyl) acrylic. For this type of macromolecule, very few compounds with unsubstituted acrylic or allylic grafts have been described in the literature. Note, néamoins, French Patent No. 2,412,572 which these grafts are made using 1 carbonates bridges.
L' originalité de l ' invention provient du fait que l' on a synthétisé des télomères monosëquencés et des télomères biséquencës ou cotélomères ayant des séquences de longueur déterminée et réalisé sur ceux-ci le greffage en nombre contrôlé de groupements particuliers . Ce qui a conduit à des produits nouveaux présentant une combinaison de propriétés intéressantes susceptibles d ' application dans différents domaines techniques .The originality of the invention comes from the fact that monosequenced telomeres and bisequenced or cotelomeric telomeres having sequences of determined length have been synthesized and grafting onto these, grafting in a controlled number of particular groups. This has led to new products with a combination of interesting properties which can be applied in different technical fields.
C' est ainsi que la demanderesse a pu faire des produits ayant des séquences de longueur courte, c ' est-à-dire de masse moléculaire relativement petite ayant en conséquence, une viscosité faible et par suite pouvant être utilisés sans solvant .This is how the applicant has been able to make products having sequences of short length, that is to say of relatively small molecular mass, consequently having a low viscosity and consequently being able to be used without solvent.
Elle a également mis au point des télomères monosëquencés ayant des maillons de structure telle qu ' il a été possible d ' y accrocher un certain nombre de groupements à haute réactivitë comme les dérivés acryliques et allyliques leur conférant ainsi des propriétés de photorëticulation remarquables mais tout en laissant des maillons de la séquence non greffés et leur permettant ainsi d ' exercer leurs propres propriétés, à savoir , par exemple dans le cas de maillons à fonction acide ou alcool une solubilité plus ou moins grande dans l ' eau ou une aptitude à l' adhérence sur les métaux.It has also developed single sequence telomeres having links of structure such that it has been possible to hang there a certain number of groups with high reactivity such as acrylic and allylic derivatives thus conferring on them remarkable photoreticulation properties but while leaving links in the sequence ungrafted and thus allowing them to exercise their own properties, namely, in the case of links with an acid or alcohol function, a greater or lesser solubility in water or an aptitude for adhesion to metals.
En étendant son invention à des télomères biséquencës , la demanderesse a pu , suivant la constitution de cette deuxième séquence, faire apparaître ou développer d ' autres propriétés telles que, par exemple, des propriétés de surface améliorées lorsqu ' il y a présence de radicaux fluorés, ou de souplesse quand il s 'agit de radicaux diëniques ou encore de résistance aux hydrocarbures quand on fait appel à des radicaux acryliques tels que l ' acry lonitrile, par exemple.By extending its invention to bisequence telomeres, the applicant has been able, according to the constitution of this second sequence, to reveal or develop other properties such as, for example, improved surface properties when fluorinated radicals are present. , or flexibility when it is diene radicals or resistance to hydrocarbons when using acrylic radicals such as acry lonitrile, for example.
Les télomères selon l ' invention répondent à la formule générale :
Figure imgf000005_0001
dans laquelle la séquence des maillons -(Xi)- et -- - est issue d'un
Figure imgf000005_0003
même taxogène X. possédant une fonction libre appartenant au groupe constitué par les fonctions alcool primaire, acide, alcool secondaire et où les maillons - correspondent à la forme estërifiêe de Xi, R' étant le ra
Figure imgf000005_0002
dical du groupement servant à l ' estërif ication, RCC12 - et -Z étant les parties du télogène RCC12Z où -Z appartient au groupe constitué par les radicaux -H, -Cl, -Br et R appartient au groupe constitué par des radicaux simples et des radicaux macromoléculaires caractérisés en ce que Xi appartient au groupe constitué par les sous-groupes X1 , X2, X3, X4 dans lesquels X1 est représenté par l'acrylate d 'hydroxy 2 êthyle et le methacrylate d 'hydroxy 2 ëthyle, X2 est représenté par l'acide acrylique et l ' acide méthacry lique, X3 est représenté par l ' alcool vinylique, X, est représenté par l ' al cool allylique, que 0 <x ≤ 500, 1 < y ≤ 500, 1 < x + y ≤ 1000, que le groupement servant à l' ester if ication possède au moins une double liaison photoréticulable et appartient au groupe constitué par des acides et des chlorures d 'acides pour X 1 , X 3 et X4 et par des alcools pour X2.The telomeres according to the invention correspond to the general formula:
Figure imgf000005_0001
in which the sequence of links - (X i ) - and - - comes from a
Figure imgf000005_0003
same taxogen X. having a free function belonging to the group constituted by the functions primary alcohol, acid, secondary alcohol and where the links - correspond to the esterified form of X i , R 'being the ra
Figure imgf000005_0002
dical of the group used for esterification, RCC1 2 - and -Z being the parts of the telogen RCC1 2 Z where -Z belongs to the group constituted by the radicals -H, -Cl, -Br and R belongs to the group constituted by simple radicals and macromolecular radicals characterized in that X i belongs to the group consisting of the subgroups X 1 , X 2 , X 3 , X 4 in which X 1 is represented by 2-hydroxyethyl acrylate and methacrylate of 2 hydroxy ethyl, X 2 is represented by acrylic acid and methacrylic acid, X 3 is represented by vinyl alcohol, X, is represented by allyl al cool, that 0 <x ≤ 500, 1 <y ≤ 500, 1 <x + y ≤ 1000, that the group used for the ester if ication has at least one photocrosslinkable double bond and belongs to the group consisting of acids and acid chlorides for X 1 , X 3 and X 4 and with alcohols for X 2 .
Ainsi les télomères revendiqués sont caractérisés notamment par la présence d 'une séquence où le taxogène présente une fonction libre telle que la fonction alcool primaire dans l' acrylate, le methacrylate d ' hydroxy 2 ëthyle et l ' alcool allylique, la fonction acide dans l' acide acrylique et méthacrylique et la fonction alcool secondaire dans l'alcool vinylique. Le nombre de mailIons de cette séquence est compris entre 1 et 1000 et parmi ceux-ci tous ou au moins la moitié sont estérif iés par des groupements acides ou alcools présentant au moins une liaison ëthylénique photoréticulable. Ces groupements sont répartis statistiquement le long de la séquence et permettent au télomère obtenu, de développer simultanément les propriétés liées à la présence des différentes fonctions non estërif iëes .Thus, the claimed telomeres are characterized in particular by the presence of a sequence in which the taxogen has a free function such as the primary alcohol function in the acrylate, hydroxyethyl methacrylate and allyl alcohol, the acid function in the. acrylic and methacrylic acid and the secondary alcohol function in vinyl alcohol. The number of mails of this sequence is between 1 and 1000 and among these all or at least half are esterified by acid or alcohol groups having at least one ethylene photocrosslinkable bond. These groups are statistically distributed along the sequence and allow the telomer obtained, to simultaneously develop the properties linked to the presence of the various non-esterified functions.
Suivant la structure du taxogène formant les maillons de la séquence, on peut utiliser différents groupements pour assurer l ' esterification. C ' est ainsi que dans le cas où le taxogène est X ou X, ou X, et possède donc une fonction alcool , on choisit l' acide acrylique, ou l' acide mëthacrylique ou l' acide cinnamique ou l 'acide furyl acrylique ou l' acide cinnamylidène ou encore l' acide allylique. Dans le cas où le taxogène possède une fonction acide repérée par X , on choisit un alcool tel que l ' acrylate ou le methacrylate d 'hydroxy 2 éthyle, ou l ' alcool allylique ou encore l' alcool cinnamique.Depending on the structure of the taxogen forming the links of the sequence, we may use different groupings to ensure esterification. It is thus that in the case where the taxogen is X or X, or X, and therefore has an alcohol function, acrylic acid is chosen, or methacrylic acid or cinnamic acid or furyl acrylic acid or cinnamylidene acid or allylic acid. In the case where the taxogen has an acid function identified by X, an alcohol such as acrylate or 2-hydroxyethyl methacrylate, or allyl alcohol or cinnamic alcohol is chosen.
Z qui peut être un radical -H, -Cl ou -Br est de préférence limité au radi- cal -Cl quand le taxogène est du type X1 et X2.Z which may be a radical -H, -Cl or -Br is preferably limited to the radical -Cl when the taxogen is of the X 1 and X 2 type .
En ce qui concerne R, il appartient au groupe constitué par des radicaux simples et des radicaux macromoléculaires. Ces radicaux macromoléculaires sont issus d ' autres télomères dans lesquels Y1 est le taxogène et conduisent alors à la formation de cotélomères biséquencës bénéficiant des avantages apportés par les propriétés des deux séquences.Regarding R, it belongs to the group consisting of simple radicals and macromolecular radicals. These macromolecular radicals come from other telomeres in which Y 1 is the taxogen and then lead to the formation of bisequence cotelomers benefiting from the advantages brought by the properties of the two sequences.
En fonction du taxogène Xi, le radical R peut prendre différentes formes.Depending on the taxogen X i , the radical R can take different forms.
C ' est ainsi qu' avec X 1 , R peut être un radical simple appartenant au groupe constitué par -Cl, CH -O-CO-, CF3- correspondant respectivement aux télogènes tétrachlorure de carbone, trichloroacétate de méthyle et trifluorotrichloroêthane.It is thus that with X 1 , R can be a simple radical belonging to the group consisting of -Cl, CH -O-CO-, CF 3 - corresponding respectively to the telogenes carbon tetrachloride, methyl trichloroacetate and trifluorotrichloroethane.
R peut aussi être un radical macromolëculaire appartenant au groupe constitué par :R can also be a macromolecular radical belonging to the group consisting of:
Figure imgf000006_0001
c ' est-à-dire que ces radicaux sont issus respectivement des télomères :chlorotrifluoroêthylène-tétrachlorure de carbone, acétate de vinyle-chloroforme, acétate de vinyle-tëtrachlorure de carbone, acide méthacrylique-têtrac hlorure de carbone, methacrylate de méthyle-tétrachlorure de carbone, isoprène-tétra chlorure de carbone.
Figure imgf000006_0001
that is to say that these radicals are respectively from the telomeres: chlorotrifluoroethylene-carbon tetrachloride, vinyl acetate-chloroform, vinyl acetate-carbon tetrachloride, methacrylic acid-tettrac chloride carbon, methyl methacrylate-carbon tetrachloride, isoprene-carbon tetra chloride.
Avec X2, R peut être un radical simple appartenant au groupe constitué par -C1 et -CF3 correspondant respectivement aux télogènes tétrachlorure de carbone et trifluorotrichloroéthane, et aussi le radical macromoléculaire -(CF-2-CFCl)-nC1l où l≤ n1 ≤ 10, c ' est-à-dire qu' il est issu du télomère chloro trifluoroêthylène-tétrachlorure de carbone.With X 2 , R can be a simple radical belonging to the group consisting of -C1 and -CF 3 corresponding respectively to the carbon tetrachloride and trifluorotrichloroethane telogen, and also the macromolecular radical - (CF- 2 -CFCl) - n C 1 l where l≤ n 1 ≤ 10, that is to say that it comes from the telomer chloro trifluoroethylene carbon tetrachloride.
Avec X3 , R peut être le radical simple appartenant au groupe constitué par -Cl, (C2 H50) -P0- ou un radical macromolëculaire appartenant au groupe constitué est-à-dire
Figure imgf000007_0001
que ces radicaux sont issus respectivement des télomères tétrachlorure de carbone, chloroforme, hydrogënophosphonate de diêthyle, bromotrichlorométha ne et des télomères acétate de vinyle et isoprène avec les télogènes tétrachlorure de carbone ou chloroforme.With X 3 , R can be the simple radical belonging to the group consisting of -Cl, (C 2 H 5 0) -P0- or a macromolecular radical belonging to the group constituted, that is to say
Figure imgf000007_0001
that these radicals are respectively from the telomeres carbon tetrachloride, chloroform, diethyl hydrogenphosphonate, bromotrichloromethane and the telomeres vinyl acetate and isoprene with the telogen carbon tetrachloride or chloroform.
Avec X, , R peut être un radical .simple appartenant au groupe, constitué parWith X,, R can be a simple radical belonging to the group, constituted by
-CCI2 -C0 H, -CCI2 -CO 2 CH 3 -CCI 3, (C 2 H 50) -PO-, c -est-à-dire qu' ils sont issus respectivement des télogènes : acide trichloroacétique, trichloro acétate de mêthyle, chloroforme, hydroxygënophosphonate de diêthyle.-CCI 2 -C0 H, -CCI 2 -CO 2 CH 3 -CCI 3 , (C 2 H 5 0) -PO-, ie they come from telogenes respectively: trichloroacetic acid, trichloro methyl acetate, chloroform, diethyl hydroxygenophosphonate.
La présente invention concerne également un procédé de fabrication des télomères et cotélomères décrits ci— dessus.The present invention also relates to a process for manufacturing the telomeres and cotelomers described above.
De manière générale, on procède en deux étapes principales : -la première consiste en une tëlomërisation du taxogène qui peut être dédou- blée en réutilisant le télomère obtenu comme nouvel agent télogène pour l' obtention de cotélomères biséquencës; il s 'agit alors d 'une bistéloméri- sation. -la deuxième consiste en une ester if ication au cours de laquelle on greffe sur les maillons de la séquence du télomère ou de l'une au moins des sé- quences du cotëlomère. un groupement non saturé destiné à rendre le produit obtenu photoréticulable. Toutefois, il est aussi possible dans certains cas de procéder à l' estérif ication avant de tëlomëriser .In general, there are two main stages: the first consists of telomerization of the taxogen which can be resolved by reusing the telomer obtained as a new telogen agent for obtaining bisequence cotelomers; it is then a bistelomerization. the second consists of an ester if ication during which one grafts on the links of the sequence of the telomer or of at least one of the sequences of the cotelomer. an unsaturated group intended to make the product obtained photocrosslinkable. However, it is also possible in certain cases to carry out the ester ification before tëlomëriser.
Mais, suivant le taxogène mis en oeuvre dans une télomérisation ou le taxogène présent dans le radical macromolëculaire R intervenant dans une bistëlo mérisation, des particularités apparaissent dans la synthèse de chacun de ces produits.However, depending on the taxogen used in a telomerization or the taxogen present in the macromolecular radical R involved in a bistel merization, particularities appear in the synthesis of each of these products.
Ainsi, dans le cas d'une réaction de télomérisation, si le taxogène utilisé est du type vinylique, diénique conjugué, allylique, l'agent télogène choisi est le chloroforme et la catalyse est alors përoxydique (le peroxyde de ben- zoyle ou l'azobisisobutyronitrile sont alors utilises comme initiateurs de télomérisation) . La coupure qui s' effectue est la coupure C-H et dans ce cas, une des extrémités téléchéliques est le groupe trichlorométhyle : CCl3.Thus, in the case of a telomerization reaction, if the taxogen used is of the vinylic, conjugated diene, allylic type, the telogenic agent chosen is chloroform and the catalysis is then hydroxide (benzoyl peroxide or azobisisobutyronitrile are then used as telomerization initiators). The cut which takes place is the CH cut and in this case, one of the telechelic ends is the trichloromethyl group: CCl 3 .
Si le taxogène est du type acrylique, diénique conjugué ou le chlorotrifluo- ro et hylènç, l'agent télogène est alors le tétrachlorure de carbone et la catalyse est du type redox (le couple FeCl3/benzoïne est le plus utilisé mais d'autres métaux et/ou sels de métaux de transition : Mg, Cu, etc. . peuvent eux aussi être employés) . Dans ces cas, la coupure de l'agent télogène est du type C-Cl mais comme dans le cas cité ci-dessus, il reste toujours à l' extrémité du télomère un groupement trichlorométhyle.If the taxogen is of the acrylic, conjugated diene or chlorotrifluoro and hylen type, the telogenic agent is then carbon tetrachloride and the catalysis is of the redox type (the FeCl 3 / benzoin couple is the most used but others transition metals and / or salts of metals: Mg, Cu, etc. can also be used). In these cases, the cleavage of the telogen agent is of the C-Cl type, but as in the case cited above, there always remains at the end of the telomer a trichloromethyl group.
Dans le cas d'une réaction de bistélomérisation où les télomères obtenus ci-dessus, et qui sont du type RCC1 , servent alors d'agents télogènes, si le nouveau taxogène est vinylique, cette réaction se fait par catalyse përoxydique (voir ci-dessus) . Pour tous les autres taxogènes : acrylique, diénique conjugué, chlorotrifluoroéthylène, la catalyse est de type redox.In the case of a bistelomerization reaction where the telomeres obtained above, and which are of the RCC1 type, then serve as telogen agents, if the new taxogen is vinyl, this reaction is carried out by hydroxide catalysis (see above) ). For all other taxogens: acrylic, conjugated diene, chlorotrifluoroethylene, the catalysis is of the redox type.
De plus, lorsque les taxogènes sont du type vinylique et allylique, on utilise respectivement l'acétate de vinyle et l'acétate d'allyle comme matériau de base pour la télomérisation et on procède ensuite à une hydrolyse en présence de mëthanolate de sodium de façon à faire apparaître les fonctions alcool sur lesquelles seront greffés par la suite les groupements photorëticulablés.In addition, when the taxogens are of the vinyl and allyl type, vinyl acetate and allyl acetate are used respectively as the base material for the telomerization and then hydrolysis is carried out in the presence of sodium methanolate so to reveal the alcohol functions on which the photo-crosslinked groups will be grafted thereafter.
En ce qui concerne le nombre de maillons : x + y, figurant dans les différen tes séquences des taxogènes, il est indiqué par le degré de polymérisation moyen en nombre DPn , et l ' indice de polydispersité DP de la réaction de télomérisation qui sont fonction de paramètres déjà connus dans la littérature.Regarding the number of links: x + y, appearing in the different Your sequences of taxogens, it is indicated by the average degree of polymerization in number DP n , and the polydispersity index DP of the telomerization reaction which are a function of parameters already known in the literature.
MAYO a défini une loi générale pour la télomérisation përoxydique : + C r et BOUTEVIN et coll pour les télomérisations
Figure imgf000009_0001
par caMAYO defined a general law for the peroxidic telomerization: + C r and BOUTEVIN et al for the telomerizations
Figure imgf000009_0001
by that
avec c t _ étant les constantes de
Figure imgf000009_0002
Figure imgf000009_0003
sfert au télogène et au catalyseurwith ct _ being the constants of
Figure imgf000009_0002
Figure imgf000009_0003
use of telogen and catalyst
Ces lois ont ëtë appliquées dans le cadre de l' invention et ont permis de déterminer au préalable les DP des différentes séquences souhaitées. Les résultats obtenus en tubes scellés ont été ensuite extrapolés sur réacteur semi- industriel pour des manipulations pilotes. Dans celui-ci, les étapes 1 et 2, étapes permettant d'arriver aux cotélomères biséquencës, ont pu être effectuées d'une seule traite après addition du second monomère dans la réaction lorsque la première étape a ëtë menée à son terme (voir exemple n° 4) .These laws were applied within the framework of the invention and made it possible to determine beforehand the DPs of the various desired sequences. The results obtained in sealed tubes were then extrapolated on a semi-industrial reactor for pilot manipulations. In this one, steps 1 and 2, steps making it possible to arrive at the bisequence cotelomers, could be carried out in one go after addition of the second monomer in the reaction when the first step has been completed (see example n ° 4).
Pour ce qui est de l'ester if ication, différentes méthodes existantes dans le cas des molécules simples ou des polymères ont ëtë adaptées -aux cotélomères biséquencës. Les méthodes utilisées sont fonction des groupements à greffer et des structures des taxogènes.With regard to the ester if ication, different existing methods in the case of simple molecules or polymers have been adapted -to bisequence cotelomers. The methods used depend on the groups to be grafted and the structures of the taxogens.
Ainsi, dans le cas de taxogènes du type X 1 , X 3, et X4 qui forment donc des séquences polyols, on a vu plus haut que les groupements servant à l' estérification étaient soit des acides, soit des chlorures d'acide.Thus, in the case of taxogens of the X 1 , X 3 , and X 4 type which therefore form polyol sequences, it was seen above that the groups used for the esterification were either acids or acid chlorides.
Lorsqu' il s'agit de chlorures d 'acide acryliques tels que le chlorure d' acide cinnamique par exemple, le mode opératoire utilisé est celui de l' activation par les complexes de pyrid±αium ou la méthode de Schotten Baumann.When it comes to acrylic acid chlorides such as cinnamic acid chloride for example, the procedure used is that of activation by pyrid ± αium complexes or the Schotten Baumann method.
Par contre, lorsqu'il s'agit d'acide acrylique, on recourt à l ' ester if ication azëotropique directe en utilisant l'acide paratoluène sulfonique ou l ' acide sulfurique comme catalyseur . Cette ester if ication s' effectue à l'aide de sol vant aromatique ou de solvant du type chloré : CH2 Cl2 ou CHCl3 par exemple lorsque celle-ci doit s ' effectuer à faible température du fait du risque de polymérisation thermique.On the other hand, when it is acrylic acid, recourse is had to direct azeotropic esterification using paratoluene sulfonic acid or sulfuric acid as catalyst. This if ication ester is carried out using soil aromatic or chlorine-type solvent: CH 2 Cl 2 or CHCl 3 for example when it has to be carried out at low temperature due to the risk of thermal polymerization.
Dans le cas de taxogènes du type X qui forment donc des séquences poly- acides, on procède avant greffage à l'activation des fonctions acides par passage au chlorure d 'acide en utilisant le chlorure de thionyle pur à reflux. Le greffage s' effectue alors dans le tétrahydrofuranne ou dans tout autre solvant aprotique et exempt d ' eau sous courant d 'azote.In the case of type X taxogens which therefore form polyacid sequences, the activation of the acid functions is carried out before grafting by passage through acid chloride using pure thionyl chloride at reflux. The grafting is then carried out in tetrahydrofuran or in any other aprotic solvent and free of water under a stream of nitrogen.
L' invention sera mieux comprise à l 'aide des exemples d 'application donnés ci-après à titre non limitatif .The invention will be better understood with the aid of the application examples given below without implied limitation.
Les réactions de télomérisation ou/et de cotélomêrisation ont été effectuées en tubes scellés ou en réacteur sous pression, et , dans le cas où les points d' êbullition des taxogènes et des télogènes sont suffisamment élevés, elles ont été réalisées en réacteur pyrex à pression atmosphérique. L' ensemble des structures décrites dans ces exemples ont été déterminées à l ' aide des méthodes d'analyses suivantes : analyse centésimale, résonance magnétique du proton, chromatographie par permeation de gel, mesure de viscosité, spectrophoto mëtrie infra rouge.The telomerization and / or cotelomerization reactions were carried out in sealed tubes or in a pressure reactor, and, in the case where the boiling points of taxogens and telogens are sufficiently high, they were carried out in a pyrex pressure reactor. atmospheric. All of the structures described in these examples were determined using the following analysis methods: centesimal analysis, proton magnetic resonance, gel permeation chromatography, viscosity measurement, infrared spectrophoto metric.
Exemple 1 : Télomérisation du taxogène X : 1 ' acrylate d ' hydroxy 2 éthyle avec le télogène 1 , 1, 1 trifluorotrichloroéthane.Example 1: Telomerization of taxogen X: 1 hydroxy 2 ethyl acrylate with telogen 1, 1, 1 trifluorotrichloroethane.
Figure imgf000010_0001
Figure imgf000010_0001
Dans un réacteur, on met 174 g d ' acrylate d ' hydroxy 2 éthyle; 281 .25 g de CF-CC1, ; 2, 43 g de chlorure ferrique; 3, 15 g de benzoxne et 200 ce d 'acétonitrile. On chauffe sous agitation pendant 12 heures à une température de 115° C et sous une pression de 4 , 4 bars. A la fin de la réaction, on évapore le solvant et on obtient 272 g d'un produit visqueux.174 g of 2-hydroxyethyl acrylate are placed in a reactor; 281 .25 g of CF-CC1,; 2.43 g of ferric chloride; 3.15 g of benzoxne and 200 cc of acetonitrile. The mixture is heated with stirring for 12 hours at a temperature of 115 ° C. and under a pressure of 4.4 bars. At the end of the reaction, the solvent is evaporated off and 272 g of a viscous product are obtained.
Par ailleurs, sous 20 Torr, on élimine le taxogène n'ayant pas réagi. Le taux de transformation en télomère est égal à 90 % . Le compose de mono addition est sépare par distillation (température d ' êbullition : 92° C sous 0, 5.10-2 Torr) . Après précipitation fractionnée du brut de réaction, on détermine par analyse centésimale le degré de polymérisation moyen de chaque fraction. On obtient ainsi :Furthermore, under 20 Torr, the unreacted taxogen is eliminated. The conversion rate to telomer is 90%. The mono addition compound is separated by distillation (boiling temperature: 92 ° C. at 0, 5.10 -2 Torr). After fractional precipitation of the reaction crude, the average degree of polymerization of each fraction is determined by centesimal analysis. We thus obtain:
- produits solubles dans l'éther : DP -£ 5 (3 % en poids du total) - produits solubles dans le ghloroforme : DP ≈ 9 (53 % en poids du" total)- products soluble in ether: DP - £ 5 (3% by weight of the total) - products soluble in the ghloroform : DP ≈ 9 (53% by weight in the " total)
- produits solubles dans l'acétone : DP = 11 (26 % en poids du total) ... n- products soluble in acetone: DP = 11 (26% by weight of the total) ... n
- produits solubles dans le mëthanol : DP = 18 (18 7- en poids du total)- products soluble in methanol: DP = 18 (18 7- by weight of the total)
Exemple 2 : Estërif ication du télomère de l'exemple 1 par l'acide acrylique. On prend le produit DP = 9. On effectue à 39,5° C l' estërif ication azêotro- pique directe de ce polyol, dans le chlorure de méthylène (CH„C1 ) et en utilisant l'acide paratoluène sulfonique comme catalyseur, par l'acide acrylique en excès. On obtient après purification le produit suivant :Example 2 Esterification of the telomer of Example 1 with acrylic acid. The product DP = 9 is taken. The azeotropic esterification of this polyol is carried out at 39.5 ° C. in methylene chloride (CH 2 C1) and using paratoluene sulfonic acid as catalyst, by excess acrylic acid. The following product is obtained after purification:
CF3CCl2- [(CH2-CH)4,5-(CH2 - CH)4,5]-Cl C=0 C=0CF 3 CCl 2 - [(CH 2 -CH) 4.5 - (CH 2 - CH) 4.5 ] -Cl C = 0 C = 0
I II I
0-CH2 -CH 2 -OH 0-CH2 -CH 2 -0-C-CH=CH2 0-CH 2 -CH 2 -OH 0-CH 2 -CH 2 -0-C-CH = CH 2
00
Exemple 3 : Estërif ication du télomère de l'exemple 1 par le chlorure de cinnamoyle.Example 3 Esterification of the telomer of Example 1 with cinnamoyl chloride.
Les différentes fractions obtenues à l'exemple 1 sont greffées avec le chlorure de cinnamoyle selon le mode opératoire suivant : dans un ballon à deux tubulures et fond plat, muni d'un réfrigérant et d'une ampoule à brome, et d'un système d'agitation magnétique, on introduit de la pyridine fraîchement distillée. Par l'ampoule à brome, on fait tomber goutte à goutte le chlorure de cinnamoyle en solution dans du tétrachlorure de carbone ou dans du toluène. Après la fin de l'addition et l'apparition d'un précipité laiteux, on introduit le télomère en solution dans la pyridine. Après une demi-heure de réaction à température ambiante, le premier précipité disparaît alors qu'un second précipité granuleux apparaît. On évapore la pyridine et on obtient un produit soluble dans le chloroforme.The different fractions obtained in Example 1 are grafted with cinnamoyl chloride according to the following procedure: in a flask with two tubes and flat bottom, provided with a condenser and a dropping funnel, and a system with magnetic stirring, freshly distilled pyridine is introduced. Cinnamoyl chloride dissolved in carbon tetrachloride or in toluene is dropped by the dropping funnel. After the end of the addition and the appearance of a milky precipitate, the telomer is introduced in solution in pyridine. After half an hour of reaction at room temperature, the first precipitate disappears while a second granular precipitate appears. The pyridine is evaporated and a product soluble in chloroform is obtained.
Pour toutes les fractions de l'exemple 1, on obtient toujours un greffage de l'ordre de 75 %. Dans le cas de la fraction soluble dans le chloroforme (DP = 9) , nous obtenons le produit de formule suivante CF3CCl2 - [(CH2- CH)2 - (CH2-CH)7] -ClFor all the fractions of Example 1, grafting of the order of 75% is always obtained. In the case of the fraction soluble in chloroform (DP = 9), we obtain the product of the following formula CF 3 CCl 2 - [(CH 2 - CH) 2 - (CH 2 -CH) 7 ] -Cl
II
C=0 C=O O- CH -CH--OH OC = 0 C = O O- CH -CH - OH O
CH2-CH2-O-C-CH=CH-f 0 φ représentant un noyau benzénique.CH 2 -CH 2 -OC-CH = CH-f 0 φ representing a benzene nucleus.
Exemple 4 : Bistêlomérisation de l' acrylate d' hydroxy 2 ëthyle avec le télomère CCl,-isoprène puis greffage de l'acide acrylique. Dans un réacteur pilo-te de 4,51, on met 773 g d'acrylate d'hydroxy 2 éthyle; 103 g de tétrachlorure de carbone; 683 g d'acêtonitrile; 10,8 g de chlorure ferrique; 14 g de benzoïne. On effectue la réaction à 110° C sous 4,4 bars pendant 4 heures, moment où la pression diminue (3,5 bars) ; on ajoute alors directement 907 g d'isoprène. On prolonge la réaction pendant 6 heures. Après évaporât ion et traitement, on obtient 1095 g de cotëlomère bisêquencé. On effectue alors le greffage de l'acide acrylique comme décrit à l'exemple 2 et on obtient le produit final :Example 4: Bistelomerization of 2-hydroxyethyl acrylate with the telomer CCl, -isoprene then grafting of acrylic acid. In a 4.51 pilo-te reactor, 773 g of 2-hydroxyethyl acrylate are placed; 103 g of carbon tetrachloride; 683 g of acetonitrile; 10.8 g of ferric chloride; 14 g of benzoin. The reaction is carried out at 110 ° C. under 4.4 bars for 4 hours, when the pressure decreases (3.5 bars); 907 g of isoprene are then added directly. The reaction is continued for 6 hours. After evaporation and treatment, 1095 g of bis-sequenced cotelomer are obtained. The acrylic acid is then grafted as described in Example 2 and the final product is obtained:
Cl-(CH2-CH=CCH3-CH2)21-CC12- [(CH2-CH)7- (CH2-CH)6] -Cl l CO2 CO2 Cl- (CH 2 -CH = CCH 3 -CH 2 ) 21 -CC1 2 - [(CH 2 -CH) 7 - (CH 2 -CH) 6 ] -Cl l CO 2 CO 2
CH2 CH -CH -0-C-CH=CH2 1 IICH 2 CH -CH -0-C-CH = CH 2 1 II
CH2 O I OH soit un cotëlomère biséquencë acrylate d'hydroxy 2 éthyle-isoprëne avec un taux de greffons acrylique de l'ordre de 45 %.CH 2 OI OH is a bis-sequential ethyl 2-isoprene hydroxy acrylate cotelomer with an acrylic graft rate of around 45%.
Exemple 5 : Bistêlomérisation du taxogène X2 : l'acide acrylique avec le tëlomère du tétrachlorure de carbone et du chlorotrifluoroëthylène Cl(CFCl-CF2)3,5-CCl3 + (CH2=CH) →Example 5: Bistelomerization of Taxogen X 2 : Acrylic Acid with the Telomer of Carbon Tetrachloride and Chlorotrifluoroethylene Cl (CFCl-CF 2 ) 3.5 -CCl 3 + (CH 2 = CH) →
C02H Cl-(CFCl-CF2)3, 5-CCl2-(CH2-CH)11,5-Cl |C0 2 H Cl- (CFCl-CF 2 ) 3, 5 -CCl 2 - (CH 2 -CH) 11 , 5 -Cl |
C02HC0 2 H
Dans un réacteur pyrex d'une capacité égale, à 1 litre, on met 2,5 moles d'acide acrylique (180 g); 0,49 mole de Cl-(CFCl-CF2)3 5-CCl3 (77,5 g); 2,034.10-2 mole de chlorure ferrique (3,17 g); 1,95.10-2 mole de benzoxne (4,14 g) et 200 g de butyronitrile. La réaction s'effectue au reflux du solvant pendant une durée de 24 heures. Après êvaporation du butyronitrile, on récupère le télogène n'ayant pas réagi (14,5 g) et on obtient 140 g de produit. Le taux de transformation en télomère est égal à 50 !.. Après précipitation fraction- née, on obtient 100 g de produits blancs solides, solubles à l,acëtonitrile (DP = 44) et 40 g de produits jaunes solides, solubles à l'êther (DP =11,5)2.5 moles of acrylic acid (180 g) are placed in a pyrex reactor with a capacity equal to 1 liter; 0.49 moles of Cl- (CFCl-CF 2 ) 3 5 -CCl 3 (77.5 g); 2,034.10 -2 mole of ferric chloride (3.17 g); 1.95.10 -2 moles of benzoxne (4.14 g) and 200 g of butyronitrile. The reaction is carried out at reflux of the solvent for a period of 24 hours. After evaporation of the butyronitrile, the unreacted telogen is recovered (14.5 g) and 140 g of product are obtained. The degree of conversion of telomere is 50! .. After precipitation fractionation born, one obtains 100 g of solid white product, soluble in, acetonitrile (DP = 44) and 40 g of yellow solid product, soluble in the ether (DP = 11.5)
Exemple 6 : Activation des fonctions acides du cotëlomère de l'exemple 5.Example 6: Activation of the acid functions of the cotelomer of Example 5.
La fraction de DP = 11,5 obtenue à l'exemple 5 est traitée coiπme suit. Dans n un réacteur en pyrex muni d'un réfrigérant, on introduit 27 g de ce télomère. On ajoute du chlorure de thionyle (SGCl_) pur. On chauffe à reflux pendant 114 heures en agitant fortement la solution (agitation magnétique) . Après êva poration des produits volatils, on obtient 30,3 g du produit suivant : C1-(CFC1-CF2)3 _-CCl2-(CH2-CH)11 5-Cl C0C1 soit une transformation totale des fonctions acides en fonctions chlorures d'acide.The fraction of DP = 11.5 obtained in Example 5 is treated as follows. 27 g of this telomer are introduced into a pyrex reactor fitted with a condenser. Pure thionyl chloride (SGCl 2) is added. The mixture is heated to reflux for 114 hours with vigorous stirring of the solution (magnetic stirring). After evaporation of the volatile products, 30.3 g of the following product are obtained: C1- (CFC1-CF 2 ) 3 _-CCl 2 - (CH 2 -CH) 11 5 -Cl C0C1 or a total transformation of the acid functions into acid chloride functions.
Exemple 7 : Estërif ication par l'alcool cinnamique du cotëlomère de l'exemple précédent.Example 7: Esterification by cinnamic alcohol of the cotelomer of the previous example.
Un tiers en poids du produit obtenu à l'exemple 6 (10,1 g) est mis en solution dans du têtrahydrofuranne anhydre. Dans un ballon muni d'un réfrigérant, d'une ampoule à brome, et d'un système permettant de faire barbotter un courant d'azote dans la solution, on met le cotëlomère, ainsi que 19,4 g d'al- cool cinnamique. On porte la réaction à une température de 40° C et on la suit par le dégagement d'acide chlorhydrique qui se produit. A la fin de ce dégagement, on évapore le solvant et on obtient, après purification, le produit de formule : C1-(CFCl-CF2)3, 5-CCl2- [(CH2-CH) 1,5 -(CH2-CH) 10] -Cl l lOne third by weight of the product obtained in Example 6 (10.1 g) is dissolved in anhydrous tetrahydrofuran. In a flask fitted with a condenser, a dropping funnel, and a system allowing a stream of nitrogen to be bubbled into the solution, the cotelomer is placed, as well as 19.4 g of alcohol. cinnamic. The reaction is brought to a temperature of 40 ° C and is followed by the evolution of hydrochloric acid which occurs. At the end of this evolution, the solvent is evaporated and, after purification, the product of formula: C1- (CFCl-CF 2 ) 3, 5 -CCl 2 - [(CH 2 -CH) 1.5 - ( CH 2 -CH) 10 ] -Cl ll
C02H C=0 l O-CH2-CH=CH_ Ψ soit un greffage de 87 %.C0 2 HC = 0 l O-CH 2 -CH = CH_ Ψ or a grafting of 87%.
Exemple 8 : Estërification par l'alcool allylique du cotëlomère de l'exemple 6 On effectue le greffage de l'alcool allylique (15 g) sur un second tiers du produit, de l'exemple 6 (10,1 g) selon le mode opératoire décrit à l'exemple 7. On obtient, après purification, le produit suivant :Example 8 Esterification with Allyl Alcohol of the Cotelomer of Example 6 The grafting of the allyl alcohol (15 g) is carried out on a second third of the product of Example 6 (10.1 g) according to the mode procedure described in Example 7. After purification, the following product is obtained:
C1-(CFC1-CF2)3 5-CCl-- £(CH2-CH)2 .-(CH.-CH).'] -ClC1- (CFC1-CF 2 ) 3 5 -CCl-- £ (CH 2 -CH) 2 .- (CH.-CH). ' ] -Cl
CO-H C=0CO-H C = 0
O-CH -CH=CH2 soit un greffage de 71 %.O-CH -CH = CH 2, ie a grafting of 71%.
Exemple 9 : Greffage par 1 '.acrylate d'hydroxy 2 ëthyle du cotëlomère de l'exemple 6 On effectue le greffage de 1* acrylate d'hydroxy 2 ëthyle (33,5 g) sur le dernier tiers du produit de l'exemple 6 (10,1 g) selon le mode opératoire décrit à l'exemple 7, mais cette fois à température ambiante. Après purification, on obtient le produit suivant : Cl-(CFCl-CF2)3,5-CCl2-[(CH2-CH)6,6-(CH2-CH)4,9] -ClEXAMPLE 9 Grafting with 1 hydroxy 2 ethyl acrylate of the cotelomer of Example 6 The graft of 1 hydroxy 2 ethyl acrylate (33.5 g) is carried out on the last third of the product of example 6 (10.1 g) according to the procedure described in Example 7, but this time at room temperature. After purification, the following product is obtained: Cl- (CFCl-CF 2 ) 3.5 -CCl 2 - [(CH 2 -CH) 6.6 - (CH 2 -CH) 4.9 ] -Cl
CO2 H C=0 l O ICO 2 HC = 0 l OI
CH2 -CH2 -0-C-CH=CH2 llCH 2 -CH 2 -0-C-CH = CH 2 ll
O soit un greffage de 43 %..O or a grafting of 43% ..
Exemple 10 : Bistêlomérisation du taxogène Y. : l'isoprène avec le télomère acétate de vinyle-chloroforme.Example 10: Bistelomerization of taxogen Y.: isoprene with the telomer vinyl acetate-chloroform.
H-(CH-CH2)30-CC13 + (CH2-CCH3=CH-CH2) →-H- (CH-CH 2 ) 30 -CC1 3 + (CH 2 -CCH 3 = CH-CH 2 ) → -
OCCH3 ll 0OCCH 3 ll 0
H-(CH-CH2)30-CCl2-(CH2-CCH3=CH2-CH2)n-ClH- (CH-CH 2 ) 30 -CCl 2 - (CH 2 -CCH 3 = CH 2 -CH 2 ) n -Cl
0-CCH0-CCH
O Dans un tube scellé, on met 6,75 g (2,5. x10-3 mole) de télomère acétate de vinyle-chloroforme (DPn = 30); 6,8 g de méthyl 2 butaάiène 1,3 (0,1 mole); 0,13 g de chlorure ferrique; 0,17 g de benzoïne et 30 ce d'acêtonitrile. Après un temps de réaction de 12 heures à une température de 90° C, on obtient 13,8 g d'un produit visqueux. Soit un taux de transformation en cotëlomère de 100 %. Exemple 11 : Hydrolyse et estërification du cotëlomère de l'exemple 10.O 6.75 g (2.5 x 10 -3 mole) of vinyl acetate-chloroform telomer (DP n = 30) are placed in a sealed tube; 6.8 g of methyl 2 butaάiene 1.3 (0.1 mole); 0.13 g of ferric chloride; 0.17 g of benzoin and 30 cc of acetonitrile. After a reaction time of 12 hours at a temperature of 90 ° C., 13.8 g of a viscous product are obtained. Or a 100% cotelomer conversion rate. Example 11: Hydrolysis and esterification of the cotelomer of Example 10.
H-(CH-CH2)30-CCl2-(CH3-CCH2=CH-CH2)n-Cl + 30 Cl-C-CH=CH-Ψ I "H- (CH-CH 2 ) 30 -CCl 2 - (CH 3 -CCH 2 = CH-CH 2 ) n -Cl + 30 Cl-C-CH = CH-Ψ I "
OH OOH O
Le produit obtenu à l'exemple 10 est traité au mëthanolate de sodium. On obtient deux produits : un insoluble au méthanol (70 % en poids), et un second, soluble au méthanol et au chloroforme (30 % en poids). Pour ces deu produits, on effectue le greffage du chlorure de cinnamoyle selon la méthode exposée à l'exemple 3. On obtient un greffage de 100 % et les produits de formules suivantes : 70 % de H-(CH-CH2)30-CCl2-(CH2-CCH3=CH-CH2)65-Cl l OC-CH=CH- φ lThe product obtained in Example 10 is treated with sodium methanolate. Two products are obtained: an insoluble in methanol (70% by weight), and a second, soluble in methanol and in chloroform (30% by weight). For these two products, the grafting of cinnamoyl chloride is carried out according to the method described in Example 3. A grafting of 100% is obtained and the products of the following formulas: 70% of H- (CH-CH 2 ) 30 - CCl 2 - (CH 2 -CCH 3 = CH-CH 2 ) 65 -Cl l OC-CH = CH- φ l
30 % de H-(CH-CH2)30-CC1--(CH2-CCH3=CH-CH2)42-C1 l30% H- (CH-CH 2 ) 30 -CC1 - (CH 2 -CCH 3 = CH-CH 2 ) 42 -C1 l
0C-CH=CH-φ l 00C-CH = CH-φ l 0
Exemple 12 : Bistêlomérisation du télomère acide acrylique-tétrachlorure de carbone avec l' isoprène. C1-(CH-CH2)4 0-CC13 + (CH2-CCH3=CH-CH2) CO2 H On met dans un tube en verre 12 , 2 g de Cl(CH-CH2 ) 40 -CCl3 (4 x 10-3 mole) lExample 12: Bistelomerization of the acrylic acid-carbon tetrachloride telomer with isoprene. C1- (CH-CH 2 ) 4 0 -CC1 3 + (CH 2 -CCH 3 = CH-CH 2 ) CO 2 H We put in a glass tube 12.2 g of Cl (CH-CH 2 ) 40 - CCl 3 (4 x 10 -3 mole) l
C02H synthétisés comme à l' exemple 5 , mais en utilisant le tétrachlorure de carbone comme agent télogène et 1 ' acétonitrile comme solvant ; 10, 88 g d' iso prène (0, 16 mole) ; 0, 195 g de chlorure ferrique (1 , 25.10-3 mole) et 0, 262 g de benzoïne (1, 25.10-3 mole) et 100 cc d 'acétonitrile. On obtient 18, 2 g de produit, soit un taux de transformation en télomère de 55 % . 6 g de ce produit sont solubles dans l' éther et 12 g y sont insolubles. On a donc les produits de formules suivantes : 6 g de Cl-(CH-CH2)40-CCl2-(CH2-CCH3=CH-CH2) 50-C1 l C02HC0 2 H synthesized as in Example 5, but using carbon tetrachloride as the telogen agent and acetonitrile as solvent; 10.88 g of iso prene (0.16 mole); 0.195 g of ferric chloride (1.25.10 -3 mole) and 0.262 g of benzoin (1.25.10 -3 mole) and 100 cc of acetonitrile. 18.2 g of product are obtained, ie a conversion rate into the telomer of 55%. 6 g of this product are soluble in ether and 12 gy are insoluble. We therefore have the products of the following formulas: 6 g of Cl- (CH-CH 2 ) 40 -CCl 2 - (CH 2 -CCH 3 = CH-CH 2 ) 50 -C1 l C0 2 H
12 g de Cl-(CH-CH2)40-CCl2-(CH2-CCH3=CH-CH2) 18-Cl l C02H12 g of Cl- (CH-CH 2 ) 40 -CCl 2 - (CH 2 -CCH 3 = CH-CH 2 ) 18 -Cl l C0 2 H
Exemple 13 : Estërif ication suivie d'une télomérisationExample 13: Esterification followed by telomerization
On effectue le greffage du chlorure, de cinnamoyle sur 1 ' acrylate d ' hydroxy 2 éthyle comme décrit à l' exemple 3. On obtient le monomère suivant : CH2=CH-C-0-CH2-CH2-0-C-CH=CH-ψ ll ll 0 0 avec un rendement de 90 % . Ce produit (24,2 g) est alors mis en réaction dan un réacteur en pyrex avec 15,4 g de tétrachlorure de carbone; 1,62 g de chlorure ferrique; 2,12 g de benzoxne et 50 ce d'acétonitrile.The grafting of the cinnamoyl chloride is carried out on the hydroxy 2 ethyl acrylate as described in Example 3. The following monomer is obtained: CH 2 = CH-C-0-CH 2 -CH 2 -0-C-CH = CH-ψ ll ll 0 0 with a yield of 90%. This product (24.2 g) is then reacted in a pyrex reactor with 15.4 g of carbon tetrachloride; 1.62 g of ferric chloride; 2.12 g of benzoxne and 50 cc of acetonitrile.
La réaction dure 24 heures à reflux de l'acétonitrile. On obtient 27 g de produit correspondant à la formule :The reaction lasts 24 hours at reflux of acetonitrile. 27 g of product are obtained corresponding to the formula:
CC13-(CH2-CH)10-C1CC1 3 - (CH 2 -CH) 10 -C1
C=0C = 0
0-CH2-CH2-0-C-CH=CH-Ψ l O0-CH 2 -CH 2 -0-C-CH = CH-Ψ l O
Exemple 14 : Télomérisation de l'aαêtate d 'allyle.Example 14: Telomerization of allyl ααetate.
Dans un réacteur d'une capacité égale à 1 litre, on met 2 % en mole de pe- roxyde de benzoyle, une mole d'acétate d'allyle et r moles de télogène en solution dans 300 ml de benzène. Après élimination du monomère (évaporation et lavage à l' éther de pétrole) , on obtient un produit visqueux (rendement de 80 %) , dont le DPn , en fonction de r et des télogènes utilisés, sont réunis dans le tableau suivant :2% by mole of benzoyl peroxide, one mole of allyl acetate and r moles of telogen dissolved in 300 ml of benzene are placed in a reactor with a capacity equal to 1 liter. After elimination of the monomer (evaporation and washing with petroleum ether), a viscous product is obtained (80% yield), the DP n of which , as a function of r and of the telogens used, are combined in the following table:
Figure imgf000016_0001
Figure imgf000016_0001
Exemple 15 : Estërif ication des télomères de l'acétate d 'allyle. Les produits obtenus à l' exemple 14 sont traités de la même façon qu' à l' exemple 11. On obtient avec un taux de greffage de 100 % les télomères photoréticulables correspondants.Example 15 Esterification of the telomeres of allyl acetate. The products obtained in Example 14 are treated in the same way as in Example 11. The corresponding photocurable telomeres are obtained with a grafting rate of 100%.
Les télomères et cotélomères photoréticulables selon l' invention, en raison de leurs propriétés d 'hydro solubilité, d'encrophilie, de souplesse, d'adhérence aux métaux, de résistance aux huiles, trouvent leurs applications aussi bien: dans l' imprimerie : fabrication de plaques offset, photogravure, flexographie, que dans la réalisation de certains éléments d 'ordinateurs ou de microprocesseurs (circuits imprimés) et comme agent de revêtement de certains produits métallurgiques. The photocrosslinkable telomeres and cotelomers according to the invention, because of their properties of water solubility, incrophilia, flexibility, of adhesion to metals, of resistance to oils, find their applications as well: in printing: manufacture of offset plates, photogravure, flexography, as in the realization of certain elements of computers or microprocessors (printed circuits) and as coating agent for certain metallurgical products.

Claims

REVENDICATIONS
1/ Télomères de formule générale R-CC1 -Z dans laquelle la
Figure imgf000018_0001
séquence des maillons -- est Issue d'un même taxogène X. possé
Figure imgf000018_0002
dant une fonction libre appartenant au groupe constitué par les fonctions alcool primaire, acide, alcool secondaire et où les maillons - - corres
Figure imgf000018_0003
pondent à la forme estërif iêe de Xi, R' étant le radical du groupement servant à l' estërif ication, RCCl2 - et -Z étant les parties du télogène RCCl2Z où -Z appartient au groupe constitué par les radicaux -H, -Cl, -Br et R appartient au groupe constitué par des radicaux simples et des radicaux macromo- lëculaires, caractérisés en ce que Xi appartient au groupe constitué par les sous-groupes X 1, X 2, X 3, X4 dans lesquels X1 est représente par l'acrylate d' hydroxy 2 éthyle et le methacrylate d'hydroxy 2 ëthyle, X2 est représenté par l'acide acrylique et l'acide méthacrylique, X3 est représenté par l'alcool vinylique, X4 est représenté par l'alcool allylique, que 0< x ≤ 500, 1 <y≤ 500, l < x + y ≤ 1000, que le groupement servant à l'ester if ication possède au moins une double liaison photoréticulable et appartient au groupe constitué par des acides et des chlorures d 'acides pour X 1 , X3, et X4 et par des alcools pour X2.1 / Telomeres of general formula R-CC1 -Z in which the
Figure imgf000018_0001
sequence of links - Is from the same taxogen X. possé
Figure imgf000018_0002
dant a free function belonging to the group constituted by the functions primary alcohol, acid, secondary alcohol and where the links - - corres
Figure imgf000018_0003
lie in the esterified form of X i , R 'being the radical of the group used for esterification, RCCl 2 - and -Z being the parts of the telogen RCCl 2 Z where -Z belongs to the group consisting of the radicals -H , -Cl, -Br and R belongs to the group consisting of simple radicals and macromolecular radicals, characterized in that X i belongs to the group constituted by the subgroups X 1 , X 2 , X 3 , X 4 in which X 1 is represented by 2-hydroxyethyl acrylate and 2-hydroxyethyl methacrylate, X 2 is represented by acrylic acid and methacrylic acid, X 3 is represented by vinyl alcohol, X 4 is represented by allyl alcohol, that 0 <x ≤ 500, 1 <y≤ 500, l <x + y ≤ 1000, that the group used for the ester if ication has at least one photocrosslinkable double bond and belongs to the group consisting of acids and acid chlorides for X 1 , X 3 , and X 4 and by alcohols for X 2 .
2/ Télomères suivant la revendication 1, caractérisés en ce que le groupe- ment servant à l' ester if ication de X 1, X3 et X4 appartient au groupe constitué par l'acide acrylique, l'acide méthacrylique, l'acide cinnamique, l' acide furyl acrylique, l 'acide cinnamylidène et l'acide allylique.2 / Telomeres according to claim 1, characterized in that the group used for the esterification of X 1 , X 3 and X 4 belongs to the group consisting of acrylic acid, methacrylic acid, acid cinnamic, furyl acrylic acid, cinnamylidene acid and allylic acid.
3/ Télomères suivant la revendication 1 , caractérisés en ce que le groupe ment servant à l' ester if ication de X2 appartient au groupe constitué par l'acrylate et le methacrylate d'hydroxy 2 éthyle, l'alcool allylique et l'alcool cinnamique.3 / Telomeres according to claim 1, characterized in that the group used for the ester if ication of X 2 belongs to the group consisting of acrylate and methacrylate of hydroxy 2 ethyl, allyl alcohol and alcohol cinnamic.
4/ Télomères suivant la revendication 1 , caractérisés en ce que quand le taxogène est du type X 1 et X 2 le radical -Z est de préférence limité à -Cl.4 / Telomeres according to claim 1, characterized in that when the taxogen is of type X 1 and X 2 the radical -Z is preferably limited to -Cl.
5/ Télomères suivant la revendication 1, caractérisés en ce que lorsque le taxogène est du type X1 , R est un radical simple appartenant au groupe constitué par -Cl, CH3-0-CO-, CF3~.5 / Telomeres according to claim 1, characterized in that when the taxogen is of type X 1 , R is a simple radical belonging to the group consisting of -Cl, CH 3 -0-CO-, CF 3 ~.
6/ Télomères suivant la revendication 1, caractérisés en ce que lorsque le taxogène est du groupe constitu6 / Telomeres according to claim 1, characterized in that when the taxogen is of the group constit
Figure imgf000019_0001
Figure imgf000019_0002
où l ≤ n2 ≤ 500. 7/ Télomères suivant la revendication 1, caractérisés en ce que lorsque le taxogène est du type X2, R est un radical simple appartenant au groupe constitué par -Cl, -CF3.
Figure imgf000019_0001
Figure imgf000019_0002
where l ≤ n 2 ≤ 500. 7 / Telomeres according to claim 1, characterized in that when the taxogen is of the X 2 type, R is a simple radical belonging to the group consisting of -Cl, -CF 3 .
8/ Télomères suivant la revendication 1, caractérisés en ce que lorsque le taxogène est du type X_, R est le radical ntacror-olêculaire -(CF2-CFCl)n1 où l≤n1 ≤10.8 / Telomeres according to claim 1, characterized in that when the taxogen is of the X_ type, R is the ntacror-oleic radical - (CF 2 -CFCl) n1 where l≤n 1 ≤10.
9/ Télomères suivant la revendication 1J caractérisés en ce que lorsque le taxogène est du type X_, R est un radical simple appartenant au groupe cons- titué par -Cl et (C2H50)2-P0-.9 / Telomeres according to claim 1J, characterized in that when the taxogen is of the X_ type, R is a simple radical belonging to the group consisting of -Cl and (C 2 H 5 0) 2 -P0-.
10/ Télomères suivant la revendication 1, caractérisés en ce que lorsque le taxogène est du type X , R est un radical macronolëculaire appartenant au groupe constitué par -(CH2-CH)n -Cl, -(CH2-C=CH-CH2)n -Cl où 1≤ n2 ≤ 500. 2 l 2 O CH3 10 / Telomeres according to claim 1, characterized in that when the taxogen is of type X, R is a macronolecular radical belonging to the group consisting of - (CH 2 -CH) n -Cl, - (CH 2 -C = CH- CH 2 ) n -Cl where 1≤ n 2 ≤ 500. 2 l 2 O CH 3
CO-CH3 CO-CH 3
11/ Télomères suivant la revendication 1 , caractérises en ce que lorsque le taxogène est du type X, , R est un radical sinple appartenant au groupe constitué par -CCl2-C02H, -CCl2-C02CH3, -CCI3, (C2H5 O) 2-P0-.11 / Telomeres according to claim 1, characterized in that when the taxogen is of type X,, R is a simple radical belonging to the group consisting of -CCl 2 -C0 2 H, -CCl 2 -C0 2 CH 3 , -CCI 3 , (C 2 H 5 O) 2 -P0-.
12/ Procédé de fabrication de télomères du type X. suivant la revendication 1 , caractérisé en ce que l ' on télomérise le taxogène en présence d 'un catalyseur puis on estérifié de manière à greffer sur - les maillons de la sêquence du télomère obtenu un groupement non saturé. 13/ Procédé de fabrication de télomères suivant la revendication 12, caractérisé en ce que l'on bistëlomërise le télomère obtenu avant de l'estéri- fier.12 / A method for manufacturing telomeres of type X. according to claim 1, characterized in that the taxogen is telomerized in the presence of a catalyst and then esterified so as to graft on - the links of the sequence of the telomer obtained unsaturated grouping. 13 / A method of manufacturing telomeres according to claim 12, characterized in that the telomer obtained is bistelomized before being esterified.
14/ Procédé de fabrication de télomères suivant la revendication 12, caractérisé en ce que lorsque le taxogène est du type vinylique, allylique, on tëlomërise en présence d'un catalyseur péroxydique et utilise le chloroforme comme télogène.14 / A process for manufacturing telomeres according to claim 12, characterized in that when the taxogen is of the vinyl, allylic type, it is telomomerized in the presence of a peroxide catalyst and uses chloroform as telogen.
15/ Procédé de fabrication de télomères suivant la revendication 12, caractérisé en ce que lorsque le taxogène est du type acrylique, diénique conjugué chlorotrifluoroëthylène, on tëlomérise en présence d'un catalyseur redox et utilise le tétrachlorure de carbone comme télogène.15 / A process for manufacturing telomeres according to claim 12, characterized in that when the taxogen is of the acrylic, diene conjugated chlorotrifluoroethylene type, it is telomerized in the presence of a redox catalyst and uses carbon tetrachloride as telogen.
16/ Procédé de fabrication de télomères suivant les revendications 12 et 13, caractérisé en ce que si le nouveau taxogène est du type vinylique et allylique, la bistêlomérisation se fait en présence d'un catalyseur péroxydique.16 / A process for manufacturing telomeres according to claims 12 and 13, characterized in that if the new taxogen is of the vinyl and allylic type, the bistelomerization takes place in the presence of a peroxide catalyst.
17/ Procédé de fabrication de télomères suivant les revendications 12 et 13, caractérisé en ce que si le nouveau taxogène est du type acrylique diénique conjugué, chlorotrifluoroëthylène, la bistêlomérisation se fait en présence d'un catalyseur redox.17 / A process for manufacturing telomeres according to claims 12 and 13, characterized in that if the new taxogen is of the conjugated diene acrylic, chlorotrifluoroethylene type, the bistelomerization takes place in the presence of a redox catalyst.
18/ Procédé de fabrication de télomères suivant les revendications 14 et 16, caractérisé en ce que le taxogène mis en oeuvre est un acétate que l'on hydrolyse ensuite par le méthanolate de sodium de façon à faire apparaître les fonctions alcool, sur lesquelles seront greffés par la suite les groupement photoréticulables.18 / A method of manufacturing telomeres according to claims 14 and 16, characterized in that the taxogen used is an acetate which is then hydrolyzed by sodium methanolate so as to reveal the alcohol functions, on which will be grafted thereafter the photocrosslinkable groupings.
19/ Procédé de fabrication de télomères suivant la revendication 12, caractérisé en ce que lorsque l'esterification est faite au moyen de chlorure d'acide acrylique, on procède à une activation par les complexes de pyridinium.19 / A method of manufacturing telomeres according to claim 12, characterized in that when the esterification is done by means of acrylic acid chloride, one proceeds to an activation by the pyridinium complexes.
20/ Procédé de fabrication de télomères suivant la revendication 12, caractérisé en ce que lorsque l'esterification est faite au moyen de l'acide acrylique, on recourt à l'esterification aZ.êotropique directe en présence d'acide paeatoluène sulfonique et d'un solvant.20 / A process for manufacturing telomeres according to claim 12, characterized in that when the esterification is carried out by means of acrylic acid, recourse is had to direct ester aZ.eotropic esterification paeatoluene sulfonic acid and a solvent.
21/ Procédé de fabrication de télomères suivant la revendication 12, caractérisé en ce que lorsque l'estërif ication est faite sur un taxogène du type X2, on procède avant greffage à l'activation des fonctions acides par passage au chlorure d'acide en utilisant le chlorure de thionyle. 21 / A method of manufacturing telomeres according to claim 12, characterized in that when the esterification is made on a taxogen of type X 2 , one proceeds before grafting to the activation of the acid functions by passage to acid chloride in using thionyl chloride.
PCT/FR1982/000122 1981-07-22 1982-07-20 Photo-crosslinkable telomers and production method thereof WO1983000336A1 (en)