USRE47975E1 - Perpendicular magnetic tunnel junction (pMTJ) with in-plane magneto-static switching-enhancing layer - Google Patents
Perpendicular magnetic tunnel junction (pMTJ) with in-plane magneto-static switching-enhancing layer Download PDFInfo
- Publication number
- USRE47975E1 USRE47975E1 US16/100,649 US201816100649A USRE47975E US RE47975 E1 USRE47975 E1 US RE47975E1 US 201816100649 A US201816100649 A US 201816100649A US RE47975 E USRE47975 E US RE47975E
- Authority
- US
- United States
- Prior art keywords
- layer
- magnetic
- sel
- sttmram
- free layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (29)