US20230243100A1

US20230243100A1 - Meterable fiberous material

Info

Publication number: US20230243100A1
Application number: US17/902,042
Authority: US
Inventors: Christopher A. Mann; David G. Marsh; Robert T. Hamilton; Charles E. Miller; Harshadkumar Shah
Original assignee: International Paper Co
Current assignee: International Paper Co
Priority date: 2009-06-08
Filing date: 2022-09-02
Publication date: 2023-08-03
Also published as: TW201107558A; MX2010006286A; KR101222323B1; EP2302133A2; BRPI1002180B1; US20120199047A1; US8715463B2; CN101906733A; US20170191220A1; US20100307702A1; JP5331059B2; JP2011000883A; TWI454605B; EP2302133A3; US9617687B2; KR20100131926A; BRPI1002180A2; CN101906733B

Abstract

A particle or particles of cellulosic wood pulp fibers having a top and bottom face and a hexagonal perimeter, and methods of using it.

Description

SUMMARY

This relates to a cellulosic wood pulp in meterable form.
Cellulose wood pulp fibers can be used as a filler and/or reinforcement and/or property modifier in many materials. There is a need to be able to meter the amount of fiber being placed in the material so that there is a more even amount of fiber throughout the material.
As an example in the plastics industry, fillers and reinforcement materials are typically used to improve the properties of plastics. The addition of such materials can improve properties such as conductivity, strength, modulus values, notched impact resistance, density, absorbency, etc.
A partial list of plastic or polymeric materials which utilize fillers or reinforcing materials includes polyolefins, polyethylene, polypropylene, polyvinyl chloride, ABS, polyamides, mixtures of these, polyethylene terephthalate, polybutylene terephthalate, polytrimethylterephthalate, ethylene-carbon monoxide and styrene copolymer blends such as styrene/acrylonitrile and styrene/maleic anhydride thermoplastic polymers, polyacetals, cellulose butyrate, acrylonitrile-butadiene-styrene, certain methyl methacrylates, and poly chlorotrifluoroethylene polymers.
Fibrous materials are used as reinforcements in plastics. Glass fibers are used as a reinforcing component for plastics. Glass fibers are used as a reinforcement material for both thermoset plastics and thermoplastics. Glass fibers are used to impart mechanical strength, dimensional stability, and heat resistance to the product. Glass fibers, however, increase the density and weight of the product, are costly, and are abrasive, abrading the processing equipment.
Mineral fibers are another material used as a filler and for reinforcement. They also are dense and add to the weight of the product. They are also abrasive.
Cellulosic wood pulp fibers do not have these disadvantages. Cellulosic wood pulp fibers have relatively low densities as compared to glass fibers or mineral fillers. For example, cellulose wood pulp fibers have a density of approximately 1500 kg/m³in comparison to a density of 2500 kg/m³for E grade glass fibers. This provides a product that is less dense and weighs less. This is an important consideration in many applications including, for example, automotive applications. Cellulosic wood pulp fibers are not as abrasive as glass fibers and do not abrade the processing equipment to the same extent as glass fibers or mineral fillers.
Cellulose wood pulp fibers can be used as reinforcing and filler in thermoset or thermoplastic materials, as reinforcing in fiber-cement material, combined with more dense material as a densification modifier to make the combined product less dense and have less weight, and combined with other materials to make them more absorbent or to absorb at a faster rate.
In each of these uses it is necessary to have an understanding of the amount of fiber that is being added and for the fiber to be added in a uniform manner. It would be beneficial to have a cellulosic wood pulp fiber that is in a form that would allow it to be easily and uniformly meterable.

SUMMARY

This summary is provided to introduce a selection of concepts in a simplified form that are further described below in the Detailed Description. This summary is not intended to identify key features of the claimed subject matter, nor is it intended to be used as an aid in determining the scope of the claimed subject matter.

DESCRIPTION OF THE DRAWINGS

The foregoing aspects and many of the attendant advantages of this invention will become more readily appreciated as the same become better understood by reference to the following detailed description, when taken in conjunction with the accompanying drawings, wherein:

FIG. 1 is a top plan view of an embodiment of the invention.

FIG. 2 is a side plan view of the embodiment of FIG. 1 .

FIG. 3 is an isometric view of the embodiment of FIGS. 1 and 2 .

FIG. 4 is a top plan view of another embodiment of the invention.

FIG. 5 is a side plan view of the embodiment of FIG. 4 .

DETAILED DESCRIPTION

The present invention can utilize a number of tree species as the source of the pulp, paperboard and paper fibers. Coniferous and broadleaf species and mixture of these can be used. These are also known as softwoods and hardwoods. Typical softwood species are various spruces (e.g., Sitka Spruce), fir (Douglas fir), various hemlocks (Western hemlock), tamarack, larch, various pines (Southern pine, White pine, and Caribbean pine), cypress and redwood or mixtures of same. Typical hardwood species are ash, aspen, cottonwood, basswood, birch, beech, chestnut, gum, elm, eucalyptus, maple oak, poplar, and sycamore or mixtures thereof. Recycled cellulosic material can be used as starting material for the fibers. The present invention can use chemical, mechanical, thermomechanical and chemithermomechanical pulp. Kraft, sulfite and soda chemical pulps can be used. The fibers can be bleached or unbleached. The present invention can be used with unbleached Douglas fir chemical pulp fibers.
The use of softwood or hardwood species may depend in part on the fiber length desired. Hardwood or broadleaf species have a fiber length of 1-2 mm. Softwood or coniferous species have a fiber length of 3.5 to 7 mm. Douglas fir, grand fir, western hemlock, western larch, and southern pine have fiber lengths in the 4 to 6 mm range. Pulping and bleaching may reduce the average length slightly because of fiber breakage.
In the manufacture of pulp woody material is disintegrated into fibers either in a chemical or mechanical type process. The fibers can then optionally be bleached. The fibers are then combined with water in a stock chest to form a slurry. The slurry then passes to a headbox and is then placed on a wire, dewatered and dried to form a pulp sheet. Additives may be combined with the fibers in the stock chest, the headbox or both. Materials may also be sprayed on the pulp sheet before, during or after dewatering and drying.
Traditionally, pulp has been added to other materials either in sheet, bale or fibrous form after the pulp sheet or bale has been comminuted or slurried. It would be advantageous to have pulp in alternative form, such as particles, that could be metered in metering devices well known in the art. In the present invention it has been found that cellulosic wood pulp fibers can be made into particulate form and the shape of these particles will determine the speed and uniformity by which the fiber can be metered and processed. A particle having a hexagonal shape can be fed faster and more uniformly than a particle having a square shape.
In one embodiment the particles are placed in a metering system. The particles are placed in a volumetric or weight loss system and metered and conveyed to the next process step. In one embodiment a single or twin screw feeder is used to meter and convey the particles into the next process step. The next process step will depend on the material with which the particles are being mixed. The material can be a thermoset or thermoplastic material, an aqueous solution for cement such as portland cement or a dry material such as clay or loam. In some embodiments the particles will be formed into fibers, fiber bundles or a mixture of fibers and fiber bundles before or during the mixing. In other embodiments the particles may substantially remain as particles during the mixing.
A partial list of plastic or polymeric materials which can utilize the cellulose wood pulp fibers can include polyolefins, polyethylene, polypropylene, polyvinyl chloride, ABS, polyamides, mixtures of these, polyethylene terephthalate, polybutylene terephthalate, polytrimethylterephthalate, ethylene-carbon monoxide and styrene copolymer blends such as styrene/acrylonitrile and styrene/maleic anhydride thermoplastic polymers, polyacetals, cellulose butyrate, acrylonitrile-butadiene-styrene, certain methyl methacrylates, and polychlorotrifluoroethylene polymers. A complete list of thermoset or thermoplastic material which can utilize cellulose wood pulp fiber is known to those skilled in the art.
Cellulosic wood pulp fibers can be in the form of commercial cellulosic wood pulps, bleached board and paper. These materials are typically delivered in roll or baled form. The thickness of the pulp sheet, paper or board (the fiber sheet) is one factor that can determine the thickness of the particle. The fiber sheet has two opposed substantially parallel faces and the distance between these faces will be the thickness of the particle. A typical fiber sheet can be from 0.1 mm to 4 mm thick. In some embodiments the thickness may be from 0.5 mm to 4 mm. One of the other factors affecting the particle thickness is the presence of any pretreatment to the fiber sheet. Thus the particle can be thicker or thinner than the fiber sheet.
The fiber sheet, and the particles, can have a basis weight of from 12 g/m²(gsm) to 2000 g/m². In one embodiment the particles could have a basis weight of 600 g/m²to 1900 g/m². In another embodiment the particles could have a basis weight of 500 g/m²to 900 g/m². For a paper sheet one embodiment could have a basis weight of 70 gsm to 120 gsm. In another embodiment a paperboard could have a basis weight of 100 gsm to 350 gsm. In another embodiment a fiber sheet for specialty use could have a basis weight of 350 gsm to 500 gsm.
Pulp additives or pretreatment may also change the character of the particle. A pulp that is treated with debonders will provide a looser particle than a pulp that does not have debonders. A looser particle may disperse more readily in the material with which it is being combined.
The particle has a hexagonal shape, one embodiment of which is shown in FIG. 1 . The hexagon can be of any type from fully equilateral to fully asymmetric. If it is not equilateral, the major axis may be from 4 to 8 millimeters (mm) and the minor axis may be from 2 to 5 mm. Some of the sides of the hexagon may be of the same length and some or all of the sides may be of different lengths. The circumference or perimeter of the hexagon may be from 12 mm to 30 mm and the area of the upper or lower face 24 or 26 of the particle may be from 12 to 32 mm². In one embodiment the particles could have a thickness of 0.1 to 1.5 mm, a length of 4.5 to 6.5 mm, a width of 3 to 4 mm and an area on one face of 15 to 20 mm². In another embodiment the particles could have a thickness of 1 to 4 mm, a length of 5 to 8 mm, a width of 2.5 to 5 mm and an area on one face of 12 to 20 mm².
Two examples of a hexagonally shaped particle are shown.
In FIGS. 1-3 , particle 10 is hexagon shaped and has two opposed sides 12 and 18 which are equal in length and are longer than the other four sides 14, 16, 20 and 22. The other four sides 14, 16, 20 and 22 may be the same length, as shown, or the four sides may be different lengths. Two of the sides, one at each end such as 14 and 20 or 14 and 22 may be the same length, and the other two at each end, 16 and 22 or 16 and 20, may be the same length or have different lengths. In each of these variations, the sides 10 and 18 may the same length or of different lengths. The edges of the particles may be sharp or rounded.
The distance between the top 24 and bottom 26 of particle 10 may be from 0.1 mm to 4 mm.
FIGS. 4 and 5 illustrate an embodiment in which each of the six sides the hexagon is of a different length. The embodiment shown is illustrative and the order of the lengths of the sides and size of the lengths of the sides can vary.
Particles of the shape, size and basis weight described above can readily be metered in weight loss and volumetric feeder systems well known in the art.
The alignment of the fibers within the particle can be parallel to the major axis of the hexagon or perpendicular to the major axis of the hexagon or any orientation in between.
The hexagonal particles can be formed on a Henion dicer, but other means could be used to produce a hexagonal particle.
The hexagonal particles have a number of advantages over square or rectangular particles. A particle with a hexagonal circumference can be produced faster than a particle with a rectangular or square circumference and can be metered faster than a particle with a rectangular or square circumference. In one embodiment, hexagonal particles are produced at 1.6 times the rate of square particles.
As an example of the benefits provided by hexagonal particles, a CF 405 pulp from the Weyerhaeuser NR Company, Columbus, Miss. mill was formed into a hexagonal particle 6.14 mm (˜¼ inch) on the long axis and 3.36 mm (˜⅛ inch) on the short axis, a 3/32 inch (2.38 mm) square particle and a ⅛ inch (3.18 mm) square particle. The particles were metered through both a twin screw and single screw feeder. Standard vibration agitation as routinely practiced in the art was used to prevent bridging. The rotational speed range was the same for the three particles for each test. The amounts fed through the twin screw feeder in pounds/hour/rpm were 1.61 for the hexagonal particles, 1.16 for the 3/32″ square particles and 0.905 for the ⅛″ square particles. The amounts fed through the single screw feeder in pounds/hour/rpm were 1.73 for the hexagonal particles, 0.45 for the 3/32″ square particles and 0.65 for the ⅛″ square particles.
While illustrative embodiments have been illustrated and described, it will be appreciated that various changes can be made therein without departing from the spirit and scope of the invention.

Claims

1. A cellulosic wood pulp fiber particle having two opposed faces and a hexagonal perimeter, a major axis length of 4 to 8 mm, a width of 2 to 5 mm and a thickness of 0.1 mm to 4 mm.

2. The particle of claim 1, wherein the wood pulp fiber is in the form of a wood pulp sheet, a paperboard sheet or a paper sheet.

3. The particle of claim 1, wherein the hexagonal perimeter forms an equilateral hexagon.

4. The particle of claim 1, wherein the sides of the hexagon formed by the hexagonal perimeter have different lengths.

5. The particle of claim 1, wherein two opposed sides of the hexagon formed by the hexagonal perimeter have the same length, and said two opposed sides are longer than the other sides of the hexagon.

6. The particle of claim 1, wherein the particle has a basis weight of 12 to 2000 g/mm².

7. The particle of claim 1, wherein each of the two opposed faces have an area of 12 to 30 mm².

8. The particle of claim 1, wherein the length of the hexagonal perimeter is 12 mm to 32 mm.

9. A method of combining wood pulp fibers with a material, the method comprising:

providing wood pulp fiber particles having two opposed faces and a hexagonal perimeter, a major axis length of 4 to 8 mm, a width of 2 to 5 mm and a thickness of 0.1 mm to 4 mm;

metering the particles through a feeder to a mixer;

forming fibers, fiber bundles, or a mixture thereof from the particles before or during the mixing; and

mixing the fibers, fiber bundles, or mixture thereof with a material to form a blend of the fibers, fiber bundles or mixture thereof and the material.

10. The method of claim 9, wherein the material is a thermoplastic resin.

11. The method of claim 9, wherein the material is cement.

12. The method of claim 9, wherein the material is a thermoset resin.

13. A method of combining wood pulp fibers with a material, the method comprising:

providing wood pulp fiber particles having two opposed faces and a hexagonal perimeter, a major axis length of 4 to 8 mm, a width of 2 to 5 mm and a thickness of 0.1 mm to 4 mm; and

metering the particles through a feeder to a mixer.

14. The method of claim 13, wherein the material is a dry constituent having a higher bulk density than the fiber, to produce a blend with a bulk density lower than the bulk density of the dry constituent.

15. The method of claim 13, wherein the material is a dry constituent having a lower bulk density than the fiber, to produce a blend with a bulk density higher than the bulk density of the dry constituent.

16. The method of claim 13, wherein the material is a dry constituent having a lower absorbent capacity than the fiber, to produce a blend with a higher absorbent capacity than the dry constituent.

17. The method of claim 13, wherein the material is a dry constituent having a higher absorbent capacity than the fiber, to produce a blend with a lower absorbent capacity than the dry constituent.

18. The method of claim 13, wherein the material is a dry constituent having a lower absorbency rate than the fiber, to produce a blend with a higher absorbent rate than the dry constituent.