US20210057645A1 - Memory device and method of forming the same - Google Patents
Memory device and method of forming the same Download PDFInfo
- Publication number
- US20210057645A1 US20210057645A1 US16/548,854 US201916548854A US2021057645A1 US 20210057645 A1 US20210057645 A1 US 20210057645A1 US 201916548854 A US201916548854 A US 201916548854A US 2021057645 A1 US2021057645 A1 US 2021057645A1
- Authority
- US
- United States
- Prior art keywords
- switching element
- planar electrode
- memory device
- limiting embodiments
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- The present disclosure relates generally to a memory device and a method of forming a memory device.
- Resistive random access memory (ReRAM) is a type of non-volatile memories (NVM), which has a simple structure, promising scalability, fast operation and low operation voltage.
- ReRAM typically has a metal-insulator-metal structure in which the insulator refers to a resistive-change material capable of providing variable resistances. The resistance change results from the formation or rupture of a conductive filament path between the two metal electrodes upon application of a voltage bias.
-
FIG. 1 shows a cross-sectional view of aconventional ReRAM 100. The ReRAM 100 includes abottom electrode 102, atop electrode 104, and aresistive layer 106 arranged between thebottom electrode 102 and thetop electrode 104. - When the
resistive layer 106 is insulating, the resistive layer has a high resistance and the ReRAM 100 is in a high resistance state. To set the ReRAM 100, a sufficiently high voltage bias (a set voltage Vset) is applied between the twoelectrodes filaments 108 may be formed between the top and bottom electrodes to make theresistive layer 106 conductive. As shown inFIG. 1 , multiple roots offilaments 108 are randomly generated over a large filament formation area provided by theresistive layer 106. When the resistive layer becomes conductive, theresistive layer 106 has a low resistance and the ReRAM 100 is switched to a low resistance state. To reset theReRAM 100, theresistive layer 106 is made insulating again by applying a sufficiently low voltage bias (a reset voltage Vreset) to the top andbottom electrodes filaments 108. The ReRAM 100 is then switched from the low resistance state to the high resistance state. Accordingly, the setting and resetting of the ReRAM 100 is done by applying predetermined voltage differences to the top andbottom electrodes filaments 108. - According to various non-limiting embodiments, there may be provided a memory device. The memory device may include a first planar electrode; a second planar electrode; and a switching element arranged between the first planar electrode and the second planar electrode to where a first side of the switching element is arranged over the first planar electrode and where a second side of the switching element is arranged under the second planar electrode. The switching element is thicker at the first side than the second side, and the switching element is configured to provide a conductive filament formation region.
- According to various non-limiting embodiments, there may be provided a method of forming a memory device. The method may include providing a first planar electrode; providing a switching element over the first planar electrode; and providing a second planar electrode over the switching element. The switching element is arranged to where a first side of the switching element is arranged over the first planar electrode and where a second side of the switching element is arranged under the second planar electrode. The switching element is thicker at the first side than the second side, and the switching element is configured to provide a conductive filament formation region.
- In the drawings, like reference characters generally refer to the same parts throughout the different views. Also, the drawings are not necessarily to scale, emphasis instead generally being placed upon illustrating the principles of the invention. Embodiments of the invention will now be illustrated for the sake of example only with reference to the following drawings, in which:
-
FIG. 1 shows a cross-sectional view of a conventional ReRAM. -
FIG. 2 shows a schematic diagram illustrating a cross-sectional view of a memory device according to various non-limiting embodiments. -
FIG. 3 shows a cross-sectional view of a memory device according to various non-limiting embodiments. -
FIG. 4 shows a cross-sectional view of a memory device according to various non-limiting embodiments. -
FIG. 5 shows a cross-sectional view of a memory device according to various non-limiting embodiments. -
FIG. 6 shows a perspective view of a memory device according to various non-limiting embodiments. -
FIG. 7 illustrates conductive filaments formed in a memory device according to various non-limiting embodiments. -
FIG. 8 shows a flowchart illustrating a method of forming a memory device according to various non-limiting embodiments. -
FIGS. 9A-9F illustrate a method of forming a memory device according to various non-limiting embodiments. -
FIGS. 10A-10F illustrate a method of forming a memory device according to various non-limiting embodiments. -
FIGS. 11A-11C illustrate a method of forming a memory device according to various non-limiting embodiments. -
FIGS. 12A-12G illustrate a method of forming a memory device according to various non-limiting embodiments. -
FIG. 13A shows a top view SEM image of agglomerated nanowires which may be formed according to the non-limiting embodiments ofFIGS. 12A to 12E . -
FIG. 13B shows a top view SEM image of non-agglomerated nanowires formed in a conventional method. - Aspects of the present invention and certain features, advantages, and details thereof, are explained more fully below with reference to the non-limiting examples illustrated in the accompanying drawings. Descriptions of well-known materials, fabrication tools, processing techniques, etc., are omitted so as not to unnecessarily obscure the invention in detail. It should be understood, however, that the detailed description and the specific examples, while indicating aspects of the invention, are given by way of illustration only, and are not by way of limitation. Various substitutions, modifications, additions, and/or arrangements, within the spirit and/or scope of the underlying inventive concepts will be apparent to those skilled in the art from this disclosure.
- Approximating language, as used herein throughout the specification and claims, may be applied to modify any quantitative representation that could permissibly vary without resulting in a change in the basic function to which it is related. Accordingly, a value modified by a term or terms, such as “about,” is not limited to the precise value specified. In some instances, the approximating language may correspond to the precision of an instrument for measuring the value.
- The terminology used herein is for the purpose of describing particular examples only and is not intended to be limiting of the invention. As used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprise” (and any form of comprise, such as “comprises” and “comprising”), “have” (and any form of have, such as “has” and “having”), “include (and any form of include, such as “includes” and “including”), and “contain” (and any form of contain, such as “contains” and “containing”) are open-ended linking verbs. As a result, a method or device that “comprises,” “has,” “includes” or “contains” one or more steps or elements possesses those one or more steps or elements, but is not limited to possessing only those one or more steps or elements. Likewise, a step of a method or an element of a device that “comprises,” “has,” “includes” or “contains” one or more features possesses those one or more features, but is not limited to possessing only those one or more features. Furthermore, a device or structure that is configured in a certain way is configured in at least that way, but may also be configured in ways that are not listed.
- It should be understood that the terms “on”, “over”, “top”, “bottom”, “down”, “side”, “back”, “left”, “right”, “front”, “lateral”, “side”, “up”, “down” etc., when used in the following description are used for convenience and to aid understanding of relative positions or directions, and not intended to limit the orientation of any device, or structure or any part of any device or structure. In addition, the singular terms “a”, “an”, and “the” include plural references unless context clearly indicates otherwise. Similarly, the word “or” is intended to include “and” unless the context clearly indicates otherwise.
- The non-limiting embodiments described below in context of the devices are analogously valid for the respective methods, and vice versa. Furthermore, it will be understood that the embodiments described below may be combined; for example, a part of one embodiment may be combined with a part of another embodiment.
- It will be understood that any property described herein for a specific device may also hold for any device described herein. It will be understood that any property described herein for a specific method may also hold for any method described herein. Furthermore, it will be understood that for any device or method described herein, not necessarily all the components or steps described must be enclosed in the device or method, but only some (but not all) components or steps may be enclosed.
- Various non-limiting embodiments relate to a memory device, for example, a non-volatile memory device, such as a resistive random access memory device (ReRAM).
-
FIG. 2 shows a schematic diagram illustrating a cross-sectional view of amemory device 200 according to various non-limiting embodiments. - As shown in
FIG. 2 , thememory device 200 may include a firstplanar electrode 202; a secondplanar electrode 204; and aswitching element 210 arranged between the firstplanar electrode 202 and the secondplanar electrode 204 to where afirst side 212 of theswitching element 210 is arranged over the firstplanar electrode 202 and where asecond side 214 of theswitching element 210 is arranged under the secondplanar electrode 204. The switchingelement 210 is thicker at thefirst side 212 than thesecond side 214, and theswitching element 210 is configured to provide a conductive filament formation region. - According to various non-limiting embodiments, the
memory device 200 provides the switchingelement 210 thicker at thefirst side 212 than thesecond side 214, and accordingly the conductive filament formation region provided therein is also thicker at thefirst side 212 than thesecond side 214. In this manner, the conductive filament formation region may be restricted or confined to a narrower/thinner area at thesecond side 214, which enables generation of more robust conductive filaments. Compared to conventional memory devices with set voltage (Vset) variation issues due to randomly generated filaments, thememory device 200 of various non-limiting embodiments generates more robust conductive filaments in a controlled manner and thus reduces the set voltage (Vset) variation of thememory device 200. Hence, improved switching performance can be achieved by thememory device 200 of various non-limiting embodiments. - In this context, the term “thicker” may refer to a larger dimension in width or diameter of the
switching element 210 at thefirst side 212. In other words, the switchingelement 210 may be wider at thefirst side 212 than thesecond side 214. In various non-limiting embodiments, the switchingelement 210 may be tapered from thefirst side 212 to thesecond side 214. In a non-limiting example, an angle between the side wall and the bottom surface of theswitching element 210 may be in a range from about 60° to about 80°. In various non-limiting embodiments, the switchingelement 210 may have a width or diameter in a range from about 70 nm to about 90 nm at thefirst side 212, a width or diameter in a range from about 20 nm to about 40 nm at thesecond side 214, and a height in a range from about 100 nm to about 120 nm. - According to various non-limiting embodiments, the switching
element 210 may have a triangular or trapezoidal cross-section.FIG. 2 shows a non-limiting exemplary embodiment of theswitching element 210 having a trapezoidal cross-section. It is understood that the switchingelement 210 may have a triangular cross-section in other non-limiting embodiments, such that thesecond side 214 of theswitching element 210 may be a sharp tip. - In various non-limiting embodiments, the switching
element 210 may have a shape selected from the group including a cone, a truncated cone, a pyramid, a truncated pyramid, or a wedge. In various non-limiting embodiments, the switchingelement 210 may have any other suitable shape which is thicker at thefirst side 212 than thesecond side 214. - In various non-limiting embodiments, the switching
element 210 may include a material configured to provide variable resistances upon application of a voltage bias. In various non-limiting embodiments, the switchingelement 210 may include a binary oxide material, examples of which may include but are not limited to silicon oxide, magnesium oxide, aluminium oxide, chromium oxide, manganese oxide, iron oxide, cobalt oxide, zinc oxide, germanium oxide, titanium oxide, nickel oxide, copper oxide, yttrium oxide, zirconium oxide, niobium oxide, molybdenum oxide, tin oxide, lanthanum oxide, hafnium oxide, tantalum oxide, tungsten oxide, cerium oxide, gadolinium oxide, ytterbium oxide, lutetium oxide, combinations thereof, or any other suitable materials. - According to various non-limiting embodiments, the first
planar electrode 202 and the secondplanar electrode 204 may have a substantially planar or flat shape, for example, in the form of a plate. In various non-limiting embodiments, the firstplanar electrode 202 and the secondplanar electrode 204 may include an electrically conductive material, such as a metallic material. Examples of the material in the firstplanar electrode 202 and the secondplanar electrode 204 may include but are not limited to aluminium, titanium, tungsten, ruthenium, nickel, copper, silver, iridium, platinum, gold, combinations thereof, or any other suitable materials. - According to various non-limiting embodiments, the
memory device 200 may further include a layer (not shown inFIG. 2 ) at least partially lining theswitching element 210. The layer may include a diffusion barrier layer, or an adhesion layer, or a combination of a diffusion barrier layer and an adhesion layer. Examples of the material of the layer may include but are not limited to titanium, titanium nitride, tantalum, tantalum nitride, combinations thereof, or any other suitable materials. In various non-limiting embodiments, the layer may have a thickness of less than 5 nm. - The
memory device 200 may further include a dielectric layer (not shown inFIG. 2 ) arranged between the firstplanar electrode 202 and the secondplanar electrode 204, wherein the dielectric layer is arranged around the switchingelement 210. The dielectric layer may include a dielectric material, examples of which may include but are not limited to silicon oxide, silicon nitride, combinations thereof, or any other suitable materials. - According to various non-limiting embodiments, the
memory device 200 may further include a component (not shown inFIG. 2 ) arranged between the switchingelement 210 and the secondplanar electrode 204, wherein the component is in electrical communication with the secondplanar electrode 204. - In various non-limiting embodiments, the component may include a nanopillar. The nanopillar may have a first end in contact with the switching
element 210, and a second end in contact with the secondplanar electrode 204. In various non-limiting embodiments, the second end of the nanopillar may include a sharp tip or a tapered tip in contact with the secondplanar electrode 204. - In various non-limiting embodiments, the component may include a film embedded with nanoparticles. In various non-limiting embodiments, the film may include an oxide film, and the nanoparticles may include metal nanoparticles. In various non-limiting embodiments, the metal nanoparticles may include nanocrystals. Examples of the material in the nanocrystals may include but are not limited to aluminium, titanium, tungsten, ruthenium, nickel, copper, silver, iridium, platinum, gold, combinations thereof, or any other suitable materials. In various non-limiting embodiments, the nanoparticles may have a diameter in a range from about 2 nm to about 10 nm.
- According to various non-limiting embodiments, the switching
element 210 may include a plurality of nanowires (not shown inFIG. 2 ) extending from the firstplanar electrode 202 toward the secondplanar electrode 204. - Each nanowire of the plurality of nanowires may include a first end and a second end, wherein the first ends of the plurality of nanowires are arranged near the first
planar electrode 202, and the second ends of the plurality of nanowires are arranged near the secondplanar electrode 204. In various non-limiting embodiments, an area enclosed by the first ends of the plurality of nanowires, e.g. at thefirst side 212 of theswitching element 210, is substantially thicker than an area enclosed by the second ends of the plurality of nanowires, e.g. at thesecond side 214 of theswitching element 210. In various non-limiting embodiments, the plurality of nanowires may be agglomerated at the second ends 214. In various non-limiting embodiments, each of the plurality of nanowires may have a length in a range from about 500 nm to about 1000 nm, and a diameter in a range from about 5 nm to about 20 nm. - According to various non-limiting embodiments, the
memory device 200 may be a non-volatile memory device, for example, a resistive random access memory device (ReRAM) wherein theswitching element 210 may include a binary oxide material as described in various non-limiting embodiments above. In various non-limiting embodiments, thememory device 200 may be any other resistive-based non-volatile memory, e.g. a phase-change random access memory device (PCRAM), where the resistances of theswitching element 210 may be switched between different states by applying appropriate voltage bias. In various non-limiting embodiments wherein thememory device 200 is a PCRAM, the switchingelement 210 may include a phase-change material which may be switched between a crystalline phase (in which the phase-change material may have a lower resistance) and an amorphous phase (in which the phase-change material may have a higher resistance) by joule heating. Examples of the phase-change material may include but are not limited to germanium-antimony-tellurium alloys, e.g. germanium telluride (GeTe), germanium antimony telluride (GeSbTe). -
FIG. 3 shows a cross-sectional view of amemory device 300 according to various non-limiting embodiments. Thememory device 300 is similar to thememory device 200 ofFIG. 2 , and thus the common features are labelled with the same reference numerals. Various embodiments described with reference toFIG. 2 are analogously valid for thememory device 300 ofFIG. 3 , and vice versa. - Similar to the
memory device 200, thememory device 300 includes the firstplanar electrode 202; the secondplanar electrode 204; and theswitching element 210 arranged between the firstplanar electrode 202 and the secondplanar electrode 204 to where thefirst side 212 of theswitching element 210 is arranged over the firstplanar electrode 202 and where thesecond side 214 of theswitching element 210 is arranged under the secondplanar electrode 204. The switchingelement 210 is thicker at thefirst side 212 than thesecond side 214, and theswitching element 210 is configured to provide a conductive filament formation region. - As shown in
FIG. 3 , thememory device 300 may further include alayer 306 at least partially lining theswitching element 210. In the non-limiting embodiments shown inFIG. 3 , thelayer 306 may be provided to fully line theswitching element 210, for example, along the top surface, the bottom surface and the sidewall surface of theswitching element 210. Thelayer 306 may also be arranged on the top surface of the firstplanar electrode 202. In various non-limiting embodiments, thelayer 306 may be provided to partially line theswitching element 210, for example, along one or more of the top surface, the bottom surface or the sidewall surface of theswitching element 210. - In various non-limiting embodiments, the
layer 306 may include a diffusion barrier layer, or an adhesion layer, or a combination of a diffusion barrier layer and an adhesion layer. Examples of the material of thelayer 306 may include but are not limited to titanium, titanium nitride, tantalum, tantalum nitride, combinations thereof, or any other suitable materials. In various non-limiting embodiments, the thickness of thelayer 306 may be less than 5 nm. - As shown in
FIG. 3 , thememory device 300 may further include adielectric layer 308 arranged between the firstplanar electrode 202 and the secondplanar electrode 204, wherein thedielectric layer 308 is arranged around the switchingelement 210. In the non-limiting embodiments where thelayer 306 is surrounding the sidewall surface of theswitching element 210, thedielectric layer 308 is arranged around the sidewall surface of theswitching element 210 with thelayer 306 sandwiched inbetween, as shown inFIG. 3 . In the non-limiting embodiments where thelayer 306 is arranged on the top surface of the firstplanar electrode 202, thedielectric layer 308 is arranged between thelayer 306 and the secondplanar electrode 204 as shown inFIG. 3 . Thedielectric layer 308 may include a dielectric material, such as silicon oxide, silicon nitride, combinations thereof, or any other suitable materials. -
FIG. 4 shows a cross-sectional view of amemory device 400 according to various non-limiting embodiments. Thememory device 400 is similar to thememory device 200 ofFIG. 2 and thememory device 300 ofFIG. 3 , and thus the common features are labelled with the same reference numerals. Various embodiments described with reference toFIG. 2 andFIG. 3 are analogously valid for thememory device 400 ofFIG. 4 , and vice versa. - Similar to the
memory device 300, thememory device 400 may also include thelayer 306 at least partially lining theswitching element 210. In the non-limiting embodiments shown inFIG. 4 , thelayer 306 may be provided to partially line theswitching element 210, for example, along the bottom surface of theswitching element 210. Thelayer 306 may also be arranged on the top surface of the firstplanar electrode 202. In other non-limiting embodiments, thelayer 306 may be provided along the side wall surface of theswitching element 210, for example. - As shown in
FIG. 4 , thememory device 400 may further include acomponent 420 arranged between the switchingelement 210 and the secondplanar electrode 204, wherein thecomponent 420 is in electrical communication with the secondplanar electrode 204. - In various non-limiting embodiments, the
component 420 may include ananopillar 420. Thenanopillar 420 may have a pillar shaped body at the bottom in contact with the switchingelement 210, and a tapered pointy end on top in contact with the secondplanar electrode 204. Thenanopillar 420 may have a width or diameter on the order of nanometers. In various non-limiting embodiments, thenanopillar 420 may have a height in a range from about 40 nm to about 50 nm, and a radius of curvature in a range from about 5 nm to about 20 nm. In a non-limiting embodiment, the radius of curvature of thenanopillar 420 may be about 20 nm at the bottom of the pillar shaped body in contact with the switchingelement 210, and the radius of curvature of thenanopillar 420 may be about 5 nm at the top of the pointy end in contact with the secondplanar electrode 204. When the pointy end of thenanopillar 420 is sufficiently sharp or thin, e.g. around 5 nm in the radius of curvature, the pointy end may be referred to as a sharp end or a sharp tip. In various non-limiting embodiments, thenanopillar 420 may be formed of metal, which may provide better conductivity for the conductive filaments formed therein. In various non-limiting embodiments, thenanopillar 420 may be formed of other suitable conductive materials. - According to various non-limiting embodiments, the
nanopillar 420 is provided to further concentrate the conductive filaments at thesecond side 214 of theswitching element 210, thereby generating more robust conductive filaments. - In the non-limiting embodiments shown in
FIG. 4 , thememory device 400 may include a plurality of switchingelements 210 arranged between the firstplanar electrode 202 and the secondplanar electrode 204, and a plurality of thecomponent 420 arranged between therespective switching element 210 and the secondplanar electrode 204. Such amemory device 400 may also be referred to as a memory array. The memory array includes a plurality of memory cells which may be arranged in one or more columns and rows, wherein each memory cell includes asingle switching element 210. The firstplanar electrode 202 and the secondplanar electrode 204 may be shared by the plurality of switchingelements 210 and the plurality ofcomponents 420 as shown in the non-limiting embodiments ofFIG. 4 , or may be separately provided for each of the plurality of switchingelements 210 andcomponents 420. Similar to thememory device 400 ofFIG. 4 , thememory devices elements 210 arranged between the firstplanar electrode 202 and the secondplanar electrode 204 in various non-limiting embodiments. -
FIG. 5 shows a cross-sectional view of amemory device 500 according to various non-limiting embodiments. Thememory device 500 is similar to thememory device FIGS. 2-4 , and thus the common features are labelled with the same reference numerals. Various embodiments described with reference toFIGS. 2-4 are analogously valid for thememory device 500 ofFIG. 5 , and vice versa. - Similar to the
memory device 400 ofFIG. 4 , thememory device 500 may also include acomponent 520 arranged between the switchingelement 210 and the secondplanar electrode 204, wherein thecomponent 520 is in electrical communication with the secondplanar electrode 204. - In the non-limiting embodiments shown in
FIG. 5 , thecomponent 520 may include afilm 522 embedded withnanoparticles 524. In various non-limiting embodiments, thefilm 522 may include an oxide film, and thenanoparticles 524 may include metal nanoparticles. In various non-limiting embodiments, thenanoparticles 524 may be nanocrystals 524 having a size of about 2 nm-10 nm, depending on a material selection for the nanocrystals. Examples of the material in thenanocrystals 524 may include but are not limited to aluminium, titanium, tungsten, ruthenium, nickel, copper, silver, iridium, platinum, gold, combinations thereof, or any other suitable materials. - According to various non-limiting embodiments, the
nanoparticles 524 are provided to further concentrate the conductive filaments at the second side 214 (e.g. the vertex region) of theswitching element 210, thereby generating more robust conductive filaments. - Similar to the
memory device 400 ofFIG. 4 , thememory device 500 may also include a plurality of switchingelements 210 arranged between the firstplanar electrode 202 and the secondplanar electrode 204. Such amemory device 500 may also be referred to as a memory array. The firstplanar electrode 202, the secondplanar electrode 204 and thecomponent 520 may be shared by the plurality of switchingelements 210, or may be separately provided for each of the plurality of switchingelements 210. -
FIG. 6 shows a perspective view of amemory device 600 according to various non-limiting embodiments. Thememory device 600 is similar to thememory devices FIGS. 2-5 , and thus the common features are labelled with the same reference numerals. Various embodiments described with reference toFIGS. 2-5 are analogously valid for thememory device 600 ofFIG. 6 , and vice versa. - In the non-limiting embodiments shown in
FIG. 6 , the switchingelement 210 may include a plurality ofnanowires 611 extending from the firstplanar electrode 202 toward the secondplanar electrode 204. - Each
nanowire 611 of the plurality ofnanowires 611 may include afirst end 612 and asecond end 614, wherein the first ends 612 of the plurality ofnanowires 611 are arranged near the firstplanar electrode 202 and the second ends 614 of the plurality ofnanowires 611 are arranged near the secondplanar electrode 204. In various non-limiting embodiments, an area enclosed by the first ends 612 of the plurality ofnanowires 611, e.g. at thefirst side 212 of theswitching element 210, is substantially thicker than an area enclosed by the second ends 612 of the plurality ofnanowires 611, e.g. at thesecond side 214 of theswitching element 210. - In various non-limiting embodiments, the plurality of
nanowires 611 may be formed of metal, such as but not limited to copper, silver, gold, alloys thereof, combinations thereof, or any other suitable material. Thenanowires 611 may have a length in a range from about 500 nm to about 1000 nm and a diameter in a range from about 5 nm to about 20 nm. - Similar to the
memory device 400 ofFIG. 4 , thememory device 600 may also include a plurality of switchingelements 210 arranged between the firstplanar electrode 202 and the secondplanar electrode 204. Such amemory device 600 may also be referred to as a memory array. The memory array includes a plurality of memory cells which may be arranged in one or more columns and rows, wherein each memory cell includes asingle switching element 210. The firstplanar electrode 202 and the secondplanar electrode 204 may be shared by the plurality of switchingelements 210, or may be separately provided for each of the plurality of switchingelements 210. Thelayer 306 may be arranged between the plurality of switchingelements 210 and the top surface of thefirst electrode 202, either as a common layer or as separated layers for the plurality of switchingelements 210. - Although the non-limiting embodiments of
FIG. 6 show fournanowires 611 included in each switchingelement 210, it is understood that any suitable number ofnanowires 611 may be included in theswitching element 210 in various non-limiting embodiments. For example, up to 100 nanowires may be included in aswitching element 210 depending on the thickness of the nanowire. - By providing the
switching element 210 including thenanowires 611, the conductive filament formation regions may be confined along thenanowires 611, such that the conductive filaments may be guided along thenanowires 611 and concentrated at the second ends 614 of thenanowires 611. Hence, thememory device 600 forms more robust filaments and provides improved switching performance. - According to various non-limiting embodiments described above, the
memory devices switching element 210. Therefore, thememory devices switching element 210. -
FIG. 7 illustrates conductive filaments formed in amemory device 300 according to various non-limiting embodiments. - As shown in
FIG. 7 , the switchingelement 210 is configured to provide a conductivefilament formation region 716, in whichconductive filaments 718 are formed between the firstplanar electrode 202 and the secondplanar electrode 204 when a predetermined voltage bias is applied. Theconductive filaments 718 may have multiple roots at thefirst side 212 of theswitching element 210 where the conductivefilament formation region 716 has a larger area. Theconductive filaments 718 may be restricted or concentrated at thesecond side 214 of theswitching element 210 where the conductivefilament formation region 716 has a smaller area. Compared to theconductive filaments 108 ofFIG. 1 having multiple roots spreading over a large region, theconductive filaments 718 ofFIG. 7 having less roots and concentrated at the second side of the switching element are more robust. By restricting the conductive path of theconductive filaments 718 through the switchingelement 210 of the various non-limiting embodiments, the Vset variation of thememory device 300 is reduced and the switching current at thetip area 214 of thememory device 300 is improved. Accordingly, better switching performance and better switching endurance can be achieved. In addition, due to a smaller area provided by the switchingelement 210, conductive filament diffusion may be reduced or eliminated, thereby achieving better retention of thememory device 300. - In the non-limiting embodiments shown in
FIG. 7 , conductive filaments are illustrated with reference to thememory device 300. It is understood that conductive filaments formed in thememory devices conductive filaments 718, and may also be restricted or concentrated at thesecond side 214 of theswitching element 210. In various non-limiting embodiments, thecomponents memory devices second side 214 of theswitching element 210. In various non-limiting embodiments, thenanowires 611 of thememory devices 600 may help to confine the conductive filaments in the small area of thenanowires 611, and may help to further concentrate the conductive filaments at thesecond side 214 of theswitching element 210 where the second ends 614 of thenanowires 611 are arranged in a smaller area than the first ends 612. - In the following, a method of forming the
memory devices -
FIG. 8 shows aflowchart 800 illustrating a method of forming a memory device according to various non-limiting embodiments. The method may be used to form thememory devices - At 802, a first planar electrode may be provided.
- At 804, a switching element may be provided over the first planar electrode.
- At 806, a second planar electrode may be provided over the switching element. The switching element may be arranged to where a first side of the switching element is arranged over the first planar electrode and where a second side of the switching element is arranged under the second planar electrode. The switching element is thicker at the first side than the second side, wherein the switching element is configured to provide a conductive filament formation region.
- According to various non-limiting embodiments, the first planar electrode and the second planar electrode may be provided with a substantially planar or flat shape, for example, in the form of a plate. In various non-limiting embodiments, the first planar electrode and the second planar electrode may include a metallic material, examples of which may include but are not limited to aluminium, titanium, tungsten, ruthenium, nickel, copper, silver, iridium, platinum, gold, combinations thereof, or any other suitable materials.
- According to various non-limiting embodiments, providing the switching element at 804 may include forming a switching layer over the first planar electrode, and etching or milling the switching layer to form the switching element. The switching element may have a triangular or trapezoidal cross-section.
- In various non-limiting embodiments, the switching layer may be formed using a sputtering deposition method, or other suitable processes. The switching layer may include a material configured to provide variable resistances upon application of a voltage bias. In various non-limiting embodiments, the switching layer may include a binary oxide material, examples of which may include but are not limited to silicon oxide, magnesium oxide, aluminium oxide, chromium oxide, manganese oxide, iron oxide, cobalt oxide, zinc oxide, germanium oxide, titanium oxide, nickel oxide, copper oxide, yttrium oxide, zirconium oxide, niobium oxide, molybdenum oxide, tin oxide, lanthanum oxide, hafnium oxide, tantalum oxide, tungsten oxide, cerium oxide, gadolinium oxide, ytterbium oxide, lutetium oxide, combinations thereof, or any other suitable materials. In various non-limiting embodiments, the switching layer may include a phase-change material, examples of which may include but are not limited to germanium-antimony-tellurium alloys, e.g. germanium telluride (GeTe), germanium antimony telluride (GeSbTe).
- In various non-limiting embodiments, the switching layer may be etched using atomic layer etching (ALE), or reactive ion etching (RIE), or any other suitable etching processes. In various non-limiting embodiments, the switching layer may be milled using focused ion beam (FIB) milling, or any other suitable milling processes.
- According to various non-limiting embodiments, the method may include forming a layer at least partially lining the switching element. In various embodiments, the layer may be formed using a sputtering deposition method, or any other suitable processes. The layer may include a diffusion barrier layer, or an adhesion layer, or a combination of a diffusion barrier layer and an adhesion layer. Examples of the material of the layer may include but are not limited to titanium, titanium nitride, tantalum, tantalum nitride, combinations thereof, or any other suitable materials.
- According to various non-limiting embodiments, the method may include forming a dielectric layer over the first planar electrode and the switching element, wherein the dielectric layer is arranged around the switching element. The dielectric layer may include a dielectric material, examples of which may include but are not limited to silicon oxide, silicon nitride, combinations thereof , or any other suitable materials. In various non-limiting embodiments, the dielectric layer may be formed using chemical vapor deposition or any other suitable deposition processes.
- According to various non-limiting embodiments, the method may further include forming a component on the switching element; and forming the second planar electrode on the component. The component is in electrical communication with the second planar electrode.
- In various non-limiting embodiments, forming the component may include forming a metal layer on the switching element, and milling the metal layer to form the component. The component may include a nanopillar. In various non-limiting embodiments, the nanopillar may have a first end in contact with the switching element, and a second end in contact with the second planar electrode. In various non-limiting embodiments, the second end of the nanopillar may include a sharp tip or a tapered tip in contact with the second planar electrode. In various non-limiting embodiments, the nanopillars may be formed using the FIB milling method, wherein the milling and polishing time may be controlled and optimized to form a sharp or tapered tip at the second end of the nanopillar.
- In various non-limiting embodiments, forming the component may include forming a film embedded with nanoparticles. In various non-limiting embodiments, the film may include an oxide film, and the nanoparticles may include metal nanoparticles. In various non-limiting embodiments, an oxide film with metal dopants may be deposited through radio frequency (RF) sputtering, and annealed at an elevated temperature for partial crystallization to form the nanoparticles, e.g., nanocrystals. The size of nanocrystals may be in a range from about 2 nm to about 10 nm, depending on the material selection for the nanocrystals. In various non-limiting embodiments, nanocrystals may be regularly or evenly arranged in the film, wherein the regular structural arrangement may be achieved by a self-assembly method through external forces (such as a magnetic or electric field).
- According to various non-limiting embodiments, providing the switching element may include forming a plurality of nanowires extending from the first planar electrode toward the second planar electrode. In various non-limiting embodiments, each nanowire of the plurality of nanowires may include a first end and a second end, wherein the first ends of the plurality of nanowires are arranged near the first planar electrode and the second ends of the plurality of nanowires are arranged near the second planar electrode. In various non-limiting embodiments, an area enclosed by the first ends of the plurality of nanowires, e.g. at the first side of the switching element, is substantially thicker than an area enclosed by the second ends of the plurality of nanowires, e.g. at the second side of the switching element. In various non-limiting embodiments, the plurality of nanowires may be agglomerated at the second ends. In various non-limiting embodiments, the plurality of nanowires may be formed using a porous anodized alumina oxide (AAO) template.
- Various non-limiting embodiments of the method of forming the memory device will be described in more detail below.
-
FIGS. 9A-9F illustrate a method of forming a memory device according to various non-limiting embodiments. - In the non-limiting embodiments of
FIGS. 9A-9F , the method of forming thememory device 300 is illustrated. Various non-limiting embodiments described in context of the method ofFIG. 8 are analogously valid for the method ofFIGS. 9A-9F , and vice versa. - In
FIG. 9A , the firstplanar electrode 202 is provided. In various non-limiting embodiments, thelayer 306 may be formed on the first planar electrode. Thelayer 306 may include the diffusion barrier layer, or the adhesion layer, or a combination of both. In a non-limiting embodiment, thelayer 306 with a thickness of less than 5 nm may be deposited on top of the firstplanar electrode 202 using the sputtering deposition method. In various non-limiting embodiments, ametallic film 922 with a thickness of about 100 nm may be deposited on thelayer 306 using the sputtering deposition method. - In
FIG. 9B , themetallic film 922 may be oxidized to form ametal oxide layer 924. Themetal oxide layer 924 may be formed by an oxidation process or annealing under an oxygen ambient. Themetal oxide layer 924 may be referred to as the switching layer described above. In the non-limiting embodiments ofFIG. 9B , themetal oxide layer 924 is formed as the switching layer. It is understood that other types of oxide layer, for example, silicon oxide layer, may be formed as the switching layer, depending on the material selected for the switching layer. - In
FIG. 9C , themetal oxide layer 924 may be etched to form theswitching element 210 which is thicker at thefirst side 212 than thesecond side 214. In a non-limiting embodiment, the width or diameter of theswitching element 210 may be about 70 nm at thefirst side 212 and may be about 20 nm at thesecond side 214. In the non-limiting example ofFIG. 9C , the switchingelement 210 may have a triangular or trapezoidal cross-section. - In various non-limiting embodiments, the switching
element 210 may be formed by atomic layer etching (ALE), which is able to remove targeted materials selectively at the atomic scale and does not cause damage to other parts of the structure. In a non-limiting example, the switchingelement 210 with a triangular shape and a minimum size of about 20 nm at thevertex area 214 may be formed by ALE. In alternative non-limiting embodiments, the switchingelement 210 may be formed by reactive ion etching (RIE), or any other suitable etching method. - In various non-limiting embodiments, the
layer 306 may also be etched such that only a portion of thelayer 306 under the bottom surface of theswitching element 210 is retained. - In
FIG. 9D , the layer 306 (e.g. diffusion barrier layer and/or adhesion layer) may be formed to cover the top surface of the firstplanar electrode 202, the sidewall surface of theswitching element 210, and the top surface of theswitching element 210. In a non-limiting embodiment, thelayer 306 may be formed with a thickness of less than 5 nm using the sputtering deposition method. - In
FIG. 9E , thedielectric layer 308 may be formed over the firstplanar electrode 202 and theswitching element 210, wherein thedielectric layer 308 is arranged around the switchingelement 210. In a non-limiting embodiment, thedielectric layer 308 may be formed by chemical vapor deposition (CVD). In various non-limiting embodiments, a chemical mechanical planarization (CMP) process may be carried out to planarize the top surface of thedielectric layer 308 and thelayer 306 on top of theswitching element 210. - In
FIG. 9F , the secondplanar electrode 204 may be provided over the switchingelement 210 to form thememory device 300 ofFIG. 3 . In various non-limiting embodiments, the secondplanar electrode 204 may also be provided over thedielectric layer 308 and thelayer 306 on top of theswitching element 210. The top surface of the structure shown inFIG. 9E may be capped with the secondplanar electrode 204 using the sputtering deposition method. - The non-limiting embodiments described with reference to
FIGS. 9A-9F may also be used to form thememory device 200 ofFIG. 2 , with the formation of thelayer 306 and thedielectric layer 308 be omitted. -
FIGS. 10A-10F illustrate a method of forming a memory device according to various non-limiting embodiments. - In the non-limiting embodiments of
FIGS. 10A-10F , the method of forming thememory device 400 is illustrated. Various non-limiting embodiments described in context of the methods ofFIG. 8 andFIGS. 9A-9F are analogously valid for the method ofFIGS. 10A-10F , and vice versa. - In
FIG. 10A , the firstplanar electrode 202 is provided. Similar to the process ofFIG. 9A , thelayer 306 may be formed on the firstplanar electrode 202 using the sputtering deposition method, and themetallic film 922 may be deposited on thelayer 306 using the sputtering deposition method. Thelayer 306 may include the diffusion barrier layer, or the adhesion layer, or a combination of both. In a non-limiting embodiment, thelayer 306 may have a thickness of less than 5 nm, and themetallic film 922 may have a thickness of about 100 nm. - In
FIG. 10B , themetallic film 922 may be oxidized to form themetal oxide layer 924, similar to the process ofFIG. 9B . Themetal oxide layer 924 may be formed by an oxidation process or annealing under an oxygen ambient. Themetal oxide layer 924 may be referred to as the switching layer described above. In the non-limiting embodiments ofFIG. 9B , themetal oxide layer 924 is formed as the switching layer. It is understood that other types of oxide layer, for example, silicon oxide layer, may be formed as the switching layer, depending on the material selected for the switching layer. - In
FIG. 10C , athin layer 1026 of metal may be deposited on themetal oxide layer 924, for example, to prevent severe damage of the metal oxide layer during the subsequent process (e.g. FIB milling). Themetal layer 1026 may also provide a better conductive path at the vertex area due to the sharp tip formation as illustrated inFIG. 10D below. In a non-limiting example, themetal layer 1026 may have a thickness in a range from about 50 nm to about 60 nm. - In
FIG. 10D , at least oneswitching element 210 and at least onecomponent 420 may be formed. In the non-limiting embodiments shown inFIG. 10D , four switchingelements 210 and fourcomponents 420 are formed, but it is understood that any number of switching elements and components may be formed in other non-limiting embodiments. - In various non-limiting embodiments, the
metal layer 1026 and themetal oxide layer 924 may be milled to form theswitching element 210 and thecomponent 420, for example, using FIB milling. The milling process may also be used to form theswitching element 210 of thememory devices - In various non-limiting embodiments, the
component 420 may include ananopillar 420. Thenanopillar 420 may have a pillar shaped body at the bottom in contact with the switchingelement 210, and a tapered pointy end on top. Thenanopillar 420 may have a width or diameter on the order of nanometers. In various non-limiting embodiments, thenanopillar 420 may have a height in a range from about 40 nm to about 50 nm, and a radius of curvature in a range from about 5 nm to about 20 nm. In a non-limiting embodiment, the radius of curvature of thenanopillar 420 may be about 20 nm at the bottom of the pillar shaped body in contact with the switchingelement 210, and the radius of curvature of thenanopillar 420 may be about 5 nm at the top of the pointy end in contact with the secondplanar electrode 204. When the pointy end of thenanopillar 420 is sufficiently sharp or thin compared to the bottom body, the pointy end may be referred to as a sharp end or a sharp tip. - In various non-limiting embodiments, milling and polishing time of the FIB milling process may be optimized, so as to form the
nanopillar 420 with a sharp tip at the vertex area. The radius of curvature at the tip of thenanopillar 420 may be substantially smaller than that at the pillar shaped bottom body of thenanopillar 420, such that the tip of thenanopillar 420 is a sharp tip. In a non-limiting example, the radius of curvature at the tip of thenanopillar 420 may be about 5 nm, and the radius of curvature at the bottom body of thenanopillar 420 may be about 20 nm. In various non-limiting embodiments, longer milling time and polishing time may produce nanopillars with sharper tips, and therefore with smaller radius of curvature at the tip compared to the body. In a non-limiting example, the milling time of about 140 s and the polishing time of about 80 s may be used as the optimized time, at which the nanopillar may be formed in a cone shape with a sharp tip at the vertex. - In
FIG. 10E , thedielectric layer 308 may be formed over the firstplanar electrode 202, the switchingelement 210 and thecomponent 420, wherein thedielectric layer 308 is arranged around the switchingelement 210 and thecomponent 420. In a non-limiting embodiment, thedielectric layer 308 may be formed by chemical vapor deposition (CVD). In various non-limiting embodiments, a chemical mechanical planarization (CMP) process may be carried out to planarize the top surface of thedielectric layer 308 and expose the tip of thecomponent 420. - In
FIG. 10F , the secondplanar electrode 204 may be provided over the switchingelement 210 to form thememory device 400 ofFIG. 4 . In various non-limiting embodiments, the secondplanar electrode 204 may also be provided over the dielectric layer and thecomponent 420. The top surface of the structure shown inFIG. 10E may be capped with the secondplanar electrode 204 using the sputtering deposition method. - According to various non-limiting embodiments, the
component 420 is in electrical communication with the secondplanar electrode 204, and is provided to further concentrate the conductive filaments at the tip area of theswitching element 210, thereby generating more robust conductive filaments. -
FIGS. 11A-11C illustrate a method of forming a memory device according to various non-limiting embodiments. - In the non-limiting embodiments of
FIGS. 11A-11C , the method of forming thememory device 500 is illustrated. Various non-limiting embodiments described in context of the methods ofFIG. 8 ,FIGS. 9A-9F andFIGS. 10A-10F are analogously valid for the method ofFIGS. 11A-11C , and vice versa. - In
FIG. 11A , the method may be carried out using similar processes ofFIGS. 9A-9E to form the structure obtained inFIG. 9E , with the difference that thelayer 306 is not formed on the top surface of theswitching element 210. Accordingly, the top surface of theswitching element 210 may be exposed. - In
FIG. 11B , thecomponent 520 may be formed on theswitching element 210, wherein thecomponent 520 may include thefilm 522 embedded with thenanoparticles 524. In various non-limiting embodiments, thefilm 522 may include an oxide film, and thenanoparticles 524 may include metal nanoparticles. In various non-limiting embodiments ofFIG. 11B , theoxide film 522 with metal dopants may be deposited through radio frequency (RF) sputtering, and may be annealed at an elevated temperature for partial crystallization to form thenanoparticles 524, e.g., nanocrystals 524. In other words, thenanocrystals 524 may be formed through oxide film sputtering by adding metal dopants. Thenanocrystals 524 are embedded within a matrix amorphous, and partially crystallized at the elevated temperature. - In various non-limiting embodiments, the size (e.g., the diameter or width) of the
nanocrystals 524 may be in a range from about 2 nm to about 10 nm, depending on the material selection for thenanocrystals 524. In various non-limiting embodiments, thenanocrystals 524 may have a substantially spherical shape. In various non-limiting embodiments, thenanocrystals 524 may be regularly arranged in thefilm 522, wherein the regular structural arrangement may be achieved by a self-assembly method through external forces (such as a magnetic or electric field). - In
FIG. 11C , the secondplanar electrode 204 may be provided over thecomponent 520 to form thememory device 500 ofFIG. 5 . In a non-limiting embodiment, the secondplanar electrode 204 may be formed on thecomponent 520 by the sputtering deposition process. - According to various non-limiting embodiments of
FIGS. 11A-11C , theconductive nanocrystals 524 may be provided to control and concentrate the conductive filaments at thesecond side 214 of theswitching element 210, by further reducing a contact area (e.g. to about 2-10 nm as provided by the nanocrystal) between the switchingelement 210 and the secondplanar electrode 204 at the vertex region of theswitching element 210. -
FIGS. 12A-12G illustrate a method of forming a memory device according to various non-limiting embodiments. - In the non-limiting embodiments of
FIGS. 12A-12G , the method of forming thememory device 600 is illustrated. Various non-limiting embodiments described in context of the methods ofFIG. 8 ,FIGS. 9A-9F ,FIGS. 10A-10F andFIGS. 11A-11C are analogously valid for the method ofFIGS. 12A-12G , and vice versa. - In
FIG. 12A , the firstplanar electrode 202 is provided. The firstplanar electrode 202 may include an electrically conductive material, such as metal. Examples of the material in the firstplanar electrode 202 may include but are not limited to aluminium, titanium, tungsten, ruthenium, nickel, copper, silver, iridium, platinum, gold, combinations thereof, or any other suitable materials. In a non-limiting example ofFIG. 12A , the firstplanar electrode 202 may include tungsten (W). - A
metal layer 1202 may be formed on the firstplanar electrode 202. In various non-limiting embodiments, themetal layer 1202 may be deposited by e-beam evaporation or physical vapor deposition. In a non-limiting example, themetal layer 1202 may include aluminium (Al). - In various non-limiting embodiments (not shown in
FIG. 12A ), a wafer, e.g. a silicon wafer may be provided and a layer of silicon oxide (SiO2) may be deposited on the wafer by chemical vapor deposition or thermal oxidation. The wafer and the SiO2 layer may be used as a substrate, on which the stack of the firstplanar electrode 202 and themetal layer 1202 may be arranged. - In
FIG. 12B , anodization of themetal layer 1202 is carried out to produce a layer of porous AAOs (Anodized Alumina Oxide) 1204 withpores 1206 inbetween. In various non-limiting embodiments, the anodization process may be carried out under various anodic conditions to produceporous AAOs 1204 with different pore size. In a non-limiting example, the anodization process may be carried out in a 0.3M oxalic acid solution at an anodization voltage (Van) of 25V-100V and a temperature of 3° C., to fabricate theAAOs 1204 with a pore diameter (Dp) of about 5 nm-20 nm, respectively. A platinum mesh may be used as the cathode in the anodization process. - In
FIG. 12C , the structure formed inFIG. 12B is submerged into a metal electrolyte bath, for example, a copper, silver or gold electrolyte bath, to formnanowires 1208 within thepores 1206. In a non-limiting embodiment, nanowires of about 500 nm-1000 nm in length and about 5 nm-20 nm in diameter may be grown in through-pore AAOs, by electrodeposition at room temperature. - In
FIG. 12D , theAAOs 1204 may be removed. In various non-limiting embodiments, the structure formed inFIG. 12C may be immersed in a 0.5-1M NaOH solution for about 4-5 hours to etch away theAAOs 1204 completely. The NaOH solution may then be diluted slowly with de-ionized (DI) water until pH7 was achieved. Subsequently, the DI water may be replaced with isopropanol (IPA) solution and sent for ultrasonic to clean away remaining residue, which may take about 5-10 min. The structure may then be dried with nitrogen. - Due to the gradual removal of AAOs 1204 and a high aspect ratio of the
nanowires 1208, the tip of thenanowires 1208 may tend to agglomerate and eventually form a conical bundle ofnanowires 611 as shown inFIG. 12E . The bundle ofnanowires 611 may be formed as the switchingelement 210 ofFIG. 6 , wherein the second ends 614 of thenanowires 611 may be agglomerated or joined. In various non-limiting embodiments, an area enclosed by the first ends 612 of the bundle ofnanowires 611 is substantially thicker than an area enclosed by the second ends 614 of the bundle ofnanowires 611 as shown inFIG. 12E . - In
FIG. 12F , thedielectric layer 308 may be formed over the firstplanar electrode 202 and the switchingelements 210 including the conical bundles ofnanowires 611 formed inFIG. 12E . Thedielectric layer 308 may be formed around the bundles ofnanowires 611. In a non-limiting embodiment, thedielectric layer 308 may be formed by chemical vapor deposition (CVD). In various non-limiting embodiments, a chemical mechanical planarization (CMP) process may be carried out to planarize the top surface of thedielectric layer 308. - In the non-limiting embodiments shown in
FIG. 12F , a plurality of switchingelements 210 are formed, for example, four switchingelements 210 including four bundles ofnanowires 611 are formed. It is understood that any number of switching elements may be formed in other non-limiting embodiments. - In
FIG. 12G , the secondplanar electrode 204 may be provided over the switchingelement 210 to form thememory device 600 ofFIG. 6 , with the difference that thelayer 306 may be omitted. In various non-limiting embodiments, the secondplanar electrode 204 may also be provided over thedielectric layer 308. In various non-limiting embodiments, the secondplanar electrode 204 may be deposited by physical vapour deposition (PVD). - According to various non-limiting embodiments of
FIGS. 12A-12G described above, the switchingelement 210 including a plurality ofnanowires 611 extending from the firstplanar electrode 202 toward the secondplanar electrode 204 may be formed. In various non-limiting embodiments, the first ends 612 of the plurality ofnanowires 611 are arranged near the firstplanar electrode 202, and the second ends 614 of the plurality ofnanowires 611 are arranged near the secondplanar electrode 204. In various non-limiting embodiments, an area enclosed by the first ends 612 of the plurality ofnanowires 611 is substantially thicker than an area enclosed by the second ends 614 of the plurality ofnanowires 611. -
FIG. 13A shows a top view SEM (scanning electron microscopy) image of agglomeratednanowires 1300 which may be formed according to the non-limiting embodiments ofFIGS. 12A to 12E . In various non-limiting embodiments, thenanowires 1310 may be agglomerated at their second ends, wherein their second ends may join around a hollow region. Accordingly, the switchingelement 210 including thenanowires 1310 may have a cross-section in a shape substantially close to a trapezoid. In various non-limiting embodiments, thenanowires 1320 may be agglomerated at their second ends, wherein their second ends may join toward a solid region. Accordingly, the switchingelement 210 including thenanowires 1320 may have a cross-section in a shape substantially close to a triangular. -
FIG. 13B shows a top view SEM image ofnon-agglomerated nanowires 1350 formed in a conventional method. As shown inFIG. 13B ,non-agglomerated nanowires 1350 may be arranged substantially parallel to and separated from each other. Compared to thenon-agglomerated nanowires 1350 ofFIG. 13B , the agglomeratednanowires 1300 of FIG. 13A formed according to various non-limiting embodiments ofFIGS. 12A to 12E may be included in theswitching element 210 to provide more concentrated conductive filaments. - According to various non-limiting embodiments described above, the
memory devices switching element 210. The simple fabrication according to various non-limiting embodiments ofFIGS. 8, 9A-9F, 10A-10F, 11A-11C, 12A-12G is able to prevent the defects of seams or voids occurred in conventional processes, since no gap fill is needed to form thememory devices - The following examples pertain to further embodiments.
- Example 1 may be a memory device including: a first planar electrode; a second planar electrode; and a switching element arranged between the first planar electrode and the second planar electrode to where a first side of the switching element is arranged over the first planar electrode and where a second side of the switching element is arranged under the second planar electrode. The switching element may be thicker at the first side than the second side, and the switching element may be configured to provide a conductive filament formation region.
- In Example 2, the subject matter of Example 1 may optionally include that the the switching element has a triangular or trapezoidal cross-section.
- In Example 3, the subject matter of Example 1 or Example 2 may optionally include that the memory device may further include a layer at least partially lining the switching element.
- In Example 4, the subject matter of any one of Examples 1 to 3 may optionally include that the memory device may further include a dielectric layer arranged between the first planar electrode and the second planar electrode, wherein the dielectric layer is arranged around the switching element.
- In Example 5, the subject matter of any one of Examples 1 to 4 may optionally include that the memory device may further include a component arranged between the switching element and the second planar electrode, wherein the component is in electrical communication with the second planar electrode.
- In Example 6, the subject matter of Example 5 may optionally include that the component may include a nanopillar.
- In Example 7, the subject matter of Example 5 may optionally include that the component may include a film embedded with nanoparticles.
- In Example 8, the subject matter of any one of Examples 1 to 4 may optionally include that the switching element may include a plurality of nanowires extending from the first planar electrode toward the second planar electrode.
- In Example 9, the subject matter of Example 8 may optionally include that each nanowire of the plurality of nanowires may include a first end and a second end, wherein the first ends of the plurality of nanowires are arranged near the first planar electrode and the second ends of the plurality of nanowires are arranged near the second planar electrode
- In Example 10, the subject matter of Example 9 may optionally include that an area enclosed by the first ends of the plurality of nanowires is substantially thicker than an area enclosed by the second ends of the plurality of nanowires.
- In Example 11, the subject matter of any one of Examples 1 to 10 may optionally include that the memory device is a resistive random access memory device or a phase-change random access memory device.
- Example 12 may be a method including: providing a first planar electrode; providing a switching element over the first planar electrode; and providing a second planar electrode over the switching element. The switching element is arranged to where a first side of the switching element is arranged over the first planar electrode and where a second side of the switching element is arranged under the second planar electrode. The switching element is thicker at the first side than the second side, and the switching element is configured to provide a conductive filament formation region.
- In Example 13, the subject matter of Example 12 may optionally include that: providing the switching element may include forming a switching layer over the first planar electrode; etching or milling the switching layer to form the switching element. The switching element may have a triangular or trapezoidal cross-section.
- In Example 14, the subject matter of Example 12 or Example 13 may optionally include that the method further includes forming a layer at least partially lining the switching element.
- In Example 15, the subject matter of any one of Examples 12 to 14 may optionally include that the method further includes forming a dielectric layer over the first planar electrode and the switching element, wherein the dielectric layer is arranged around the switching element.
- In Example 16, the subject matter of any one of Examples 12 to 15 may optionally include that the method further includes forming a component on the switching element; and forming the second planar electrode on the component. The component is in electrical communication with the second planar electrode.
- In Example 17, the subject matter of Example 16 may optionally include that forming the component may include forming a metal layer on the switching element; and milling the metal layer to form the component. The component may include a nanopillar.
- In Example 18, the subject matter of Example 16 may optionally include that forming the component may include forming a film embedded with nanoparticles.
- In Example 19, the subject matter of any one of Examples 12, 14 to 15 may optionally include that providing the switching element may include forming a plurality of nanowires extending from the first planar electrode toward the second planar electrode.
- In Example 20, the subject matter of Example 19 may optionally include that each nanowire of the plurality of nanowires includes a first end and a second end, wherein the first ends of the plurality of nanowires are arranged near the first planar electrode and the second ends of the plurality of nanowires are arranged near the second planar electrode.
- The invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The foregoing embodiments, therefore, are to be considered in all respects illustrative rather than limiting the invention described herein. Scope of the invention is thus indicated by the appended claims, rather than by the foregoing description, and all changes that come within the meaning and range of equivalency of the claims are intended to be embraced therein.
Claims (20)