US20200388754A1 - Phase transition based resistive random-access memory - Google Patents
Phase transition based resistive random-access memory Download PDFInfo
- Publication number
- US20200388754A1 US20200388754A1 US17/002,583 US202017002583A US2020388754A1 US 20200388754 A1 US20200388754 A1 US 20200388754A1 US 202017002583 A US202017002583 A US 202017002583A US 2020388754 A1 US2020388754 A1 US 2020388754A1
- Authority
- US
- United States
- Prior art keywords
- phase
- active material
- electrode
- lrs
- hrs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- The present patent application is a continuation application which is related to and claims the priority benefit of U.S. Non-Provisional Ser. No. 16/110,376 filed Aug. 23, 2018, now U.S. Pat. No. 10,756,263 to Appenzeller et al., which is a continuation-in-part application related to and which claims the priority benefit of U.S. Non-Provisional Ser. No. 15/987,867 filed May 23, 2018, now U.S. Pat. No. 10,505,109 to Appenzeller et al., the contents of each of which are hereby incorporated by reference in their entirety into the present disclosure.
- This invention was made with government support under HR0011-13-3-0002 awarded by the Department of Defense/Defense Advanced Research Projects Agency (DARPA). The government has certain rights in the invention.
- The present disclosure generally relates to memory devices, and in particular, to resistive random-access memory (RRAM) cells.
- This section introduces aspects that may help facilitate a better understanding of the disclosure. Accordingly, these statements are to be read in this light and are not to be understood as admissions about what is or is not prior art.
- Resistive random-access memory (RRAM)-based technology has gained attention of the semiconductor industry and researchers working at the forefront of emerging technologies due to its potential scalability, high operation speed, high endurance and ease of process flow. RRAM devices are typically two-terminal cells whose operation are based on changing the resistive state of an internal element to thereby store information in a nonvolatile fashion by applying a sufficiently high voltage or by driving a large enough current through the cell.
- Typically, two types of switching mechanisms are distinguished in RRAM devices. According to one type, valence change memory (VCM), oxide-based resistive random-access memory cells follow a resistive switching mechanism in which a cluster of localized valence changes lead to formation of a filament from a high resistive state to a low resistive state resulting in the electromigration of induced anions which modifies the valence states of the cations. According to another type, RRAM devices operating based on the electrochemical metallization rely on the anodic dissolution (oxidation) of an active metal electrode and electrodeposition (reduction) of the metal ions inside the active switching material.
- However, the observed RRAM behavior in both of the above described instances involves an uncontrollable movement of individual atoms. Accordingly, reliability aspects represent a substantial challenge.
- Therefore, there is an unmet need in the art for a new switching mechanism that can be used in RRAM cells and systems.
- A method of switching a phase-change device (Device) is disclosed. The method changing phase of the Device from a semiconducting 2H phase to a new 2Hd phase with a higher conductivity, the Device having an active material with a thickness including a phase transition material to thereby transition the Device from a high resistive state (HRS) to a low resistive state (LRS) by application of a set voltage and further to return the Device from the LRS back to the HRS by application of a reset voltage.
-
FIG. 1 is a schematic view of a cross section of a resistive random-access memory (RRAM) cell according to the present disclosure. -
FIG. 2 is a schematic view of a cross section of another RRAM cell according to the present disclosure. -
FIG. 3 is a schematic of a system, according to the present disclosure, where a cell according to the present disclosure is coupled to a selectable source via a switch. -
FIG. 4 is a flowchart depicting a method that represents an exemplary process for making the cells, according to the present disclosure. -
FIG. 5 is an exemplary IV graph illustrating characteristics of the RRAM device ofFIG. 1 for a vertical MoTe2 device. -
FIG. 6 is an exemplary IV graph illustrating characteristics of the RRAM device ofFIG. 2 . -
FIG. 7 is a perspective schematic of a vertical transition metal dichalcogenide (TMD) RRAM device ofFIG. 1 . -
FIG. 8A is an optical image of the cell shown inFIG. 7 . -
FIG. 8B is a scanning electron microscopy (SEM) image of the cell shown inFIG. 7 . -
FIG. 9 is a graph of current (I) in A/cm2 vs. voltage (V) in volts representing normalized IV curves of an exemplary pristine vertical MoTe2 device lacking tunneling barriers. -
FIG. 10A is a graph of an exemplary IV graph illustrating current compliance characteristics of a MoTe2-based RRAM device. -
FIG. 10B is a graph of an exemplary current vs. time graph showing read disturb measurements on a representative MoTe2 device. -
FIG. 11A shows representative IV curves for various MoTe2 thicknesses corresponding to moderate fields. -
FIG. 11B shows representative IV curve for various Mo0.96W0.04Te2 thicknesses corresponding to moderate fields. -
FIG. 11C is a graph of forming/set voltage in volts vs. flake thickness in nm for MoTe2. -
FIG. 12A is a current mapping schematic of a MoTe2 flake after the set process and the formation of the low resistance state (LRS) has occurred using conductive AFM (C-AFM). -
FIG. 12B is a set of C-AFM images of a pristine MoTe2 flake (left: topography and right: current map). -
FIG. 13A is a cross-sectional atomic-resolution high-angle annular dark field (HAADF)-STEM image of a Mo0.96W0.04Te2 device. -
FIGS. 13B and 13C are atomic-resolution HAADF images of the marked box inFIG. 13A taken along the [120]2H zone-axis, showing the intact 2H and distorted 2Hd structures, respectively of the Mo0.96W0.04Te2 device. -
FIG. 13D shows corresponding nano-beam diffraction (NBD) pattern taken from the distorted 2Hd area of the Mo0.96W0.04Te2 device. -
FIG. 14 is a graph of resistance vs. pulse number showing pulse-measurements, where devices were continuously switched between a high resistive and a low resistive state by applying a set and reset voltage of 1.2 V and −1V, respectively. - For the purposes of promoting an understanding of the principles of the present disclosure, reference will now be made to the embodiments illustrated in the drawings, and specific language will be used to describe the same. It will nevertheless be understood that no limitation of the scope of this disclosure is thereby intended.
- In the present disclosure, the term “about” can allow for a degree of variability in a value or range, for example, within 10%, within 5%, or within 1% of a stated value or of a stated limit of a range.
- In the present disclosure, the term “substantially” can allow for a degree of variability in a value or range, for example, within 90%, within 95%, or within 99% of a stated value or of a stated limit of a range.
- A novel switching mechanism that can be used in resistive random-access memory (RRAM) cells and systems is disclosed. A method for fabricating this novel switching mechanism is also provided.
- The present disclosure relates to a new switching mechanism in RRAM devices and fabrication thereof. The active material is made from phase transition materials, e.g. MoTe2, Mo1-xWxTe2, GaTe, ReSe2, ReS2, or other such materials known to a person having ordinary skill in the art. These classes of materials may be used in fabrication of neuromorphic computing, in-memory computing or memristor-based nonvolatile logic circuits and devices.
- The RRAM topology described in the present disclosure is based on a class of electric field induced phase transition materials (also referred to as the active material, herein). By applying an electrical field to this active material, the cell is transformed from a high resistive state (HRS) to a low resistive state (LRS). This transformation can be viewed as setting the cell to a value of “1”. By reversing the electrical field, the cell can be transformed from the LRS back to the HRS, i.e., resetting the cell back to “0”.
- Now referring to
FIG. 1 , an exemplary embodiment of acell 100 according to the present disclosure is provided. Thecell 100 includes asubstrate 102, afirst electrode 104 formed atop thesubstrate 102 and anactive material 108 formed atop thefirst electrode 104. On the active material (also referred to as the active material layer) 108 is anisolation layer 110 atop and within which is asecond electrode 112 formed. Thefirst electrode 104 and thesecond electrode 112 provide electrical connectivity to thecell 100. A perspective view of thecell 100 is shown inFIG. 7 representing one exemplary embodiment of the second 112 electrode and its disposition with respect to theactive material layer 108 and theisolation layer 110. - The
substrate 102 inFIG. 1 can be made from a variety of suitable materials known to a person having ordinary skill in the semiconductor art. For example, thesubstrate 102 can be made from silicon, silicon dioxide, glass, sapphire, germanium, gallium arsenide, indium phosphate, alloys of silicon and germanium, titanium oxide, single polymer, such as polyethylene (PE), biaxially oriented polypropylene (BOPP), polyethylene terephthalate (PET), polyvinyl chloride (PVC) and the like including flexible substrates. Theelectrodes electrodes electrodes electrodes - The
active material 108 is formed on thefirst electrode 104. Theactive material 108 is made from electric field induced phase transition materials, e.g. MoTe2, Mo1-xWxTe2, GaTe, ReSe2, ReS2, or other such materials known to a person having ordinary skill in the art. The phase transition materials discussed herein can change phase based on inducement of electric field, by joules heating, or a combination thereof. Suitable methods for forming theactive material 108 include CVD growth or exfoliated from bulk materials. The thickness of theactive material layer 108 depends on what set/reset voltage RRAM devices require as will be discussed below. However, suffice it to say that according to one embodiment of the present disclosure the thickness is between about 0.6 nm and 40 nm. - The
isolation layer 110 is used to ensure that only vertical transport occurs from thefirst electrode 104 to thesecond electrode 112 without any lateral transport contributions. The thickness of theisolation layer 110 depends on the applied voltage (described inFIG. 3 ) to ensure that no leakage current exists in the chosen layout. Anopen window 114 can be formed in theisolation layer 110 which size depends on the need of device area. Theisolation layer 110 may be formed from silicon dioxide (SiO2), boron nitride (BN) or metal oxide materials, such as aluminum oxide (Al2O3), hafnium dioxide (HfO2), other two-dimensional (2D) insulators that do not undergo a phase transition, or polymers and other isolation material used in the semiconductor industry known to a person having ordinary skill in the art. Theopen window 114 can be formed by first applying a selective protective (resist) layer and then applying a buffered hydrofluoric acid (HF) to dissolve unprotected regions of the isolation material in case of SiO2. The photoresist is removed by a chemical solution or by oxidizing in an oxygen plasma or a UV ozone system, as known to a person having ordinary skill in the art. An alternative way is reactive-ion etching (RIE), known to a person having ordinary skill in the art. - The
window 114 allows electrical contact between thesecond electrode 112 and theactive material layer 108. While a window is shown, it should be appreciated that a network of vias can also be used, as known to a person having ordinary skill in the art. In one embodiment, thewindow 114 can be sized as small as the minimum feature size of the technology utilized, however, according to one embodiment between about 20 nm to about 2 μm in width and about 20 nm to about 2 μm in length. Alternatively, a network of vias providing substantially the same amount of surface area can also be used. - Referring to
FIG. 2 , another exemplary embodiment of acell 200 according to the present disclosure is provided. Thecell 200 includes asubstrate 202, afirst electrode 204 formed atop thesubstrate 202 and atunneling barrier layer 206 formed atop thefirst electrode 204. Thetunneling barrier 206 works to reduce the set/reset current level in thedevice 200, as will be discussed in greater detail below. Thetunneling barrier 206 may be formed from silicon dioxide (SiO2) or metal oxide materials, such as aluminum oxide (Al2O3), hafnium dioxide (HfO2), boron nitride (BN), other two-dimensional (2D) materials such as MoS2, WSe2, MoSe2 and the like including 2D insulators that do not undergo a phase transition. The thickness of thetunneling barrier 206 depends on the requirement of set/reset current levels. Atop thetunneling barrier layer 206 is a layer ofactive material 208. Atop the active material (also referred to as the active material layer) 208 is anisolation layer 210 atop which is asecond electrode 212 formed. Thefirst electrode 204 and thesecond electrode 212 provide electrical connectivity to thecell 200. Thetunneling barrier layer 206 and theactive material layer 208 can swap positions. Additionally, thetunneling barrier layer 206 can be provided on both sides of theactive material layer 208 referring to a construction including the first electrode 204-the tunneling layer 206-the active material layer 208-thetunneling layer 206. - The
substrate 202 can be made from a variety of suitable materials known to a person having ordinary skill in the semiconductor art. For example, thesubstrate 202 can be made from silicon, silicon dioxide, glass, sapphire, germanium, gallium arsenide, indium phosphate, alloys of silicon and germanium, titanium oxide, single polymer, such as polyethylene (PE), biaxially oriented polypropylene (BOPP), polyethylene terephthalate (PET), polyvinyl chloride (PVC) and the like including flexible substrates. Theelectrodes electrodes electrodes electrodes - The
active material 208 is formed on thefirst electrode 204. Theactive material 208 is made from electric field induced phase transition materials, e.g. MoTe2, Mo1-xWxTe2, GaTe, ReSe2, ReS2, or other such materials known to a person having ordinary skill in the art. Suitable methods for forming theactive material 208 include CVD growth or exfoliated from bulk materials. The thickness of theactive material layer 208 depends on what set/reset voltage RRAM devices require as will be discussed below. However, suffice it to say that according to one embodiment of the present disclosure the thickness is between about 0.6 nm and 40 nm. - The
isolation layer 210 is used to ensure that only vertical transport occurs from thefirst electrode 204 to thesecond electrode 212 without any lateral transport contributions. The thickness of theisolation layer 210 depends on the applied voltage (described inFIG. 3 ) to ensure that no leakage current exists in the chosen layout. Anopen window 214 can be formed in theisolation layer 210 which size depends on the need of device area. Theisolation layer 210 may be formed from silicon dioxide (SiO2), boron nitride (BN) or metal oxide material, such as aluminum oxide (Al2O3), hafnium dioxide (HfO2), or polymers, and other isolation material used in the semiconductor industry known to a person having ordinary skill in the art. Theopen window 214 can be formed by first applying a selective protective (resist) layer and then applying a buffered hydrofluoric acid (HF) to dissolve unprotected regions of the isolation material in case of SiO2. The photoresist is removed by a chemical solution or by oxidizing in an oxygen plasma or a UV ozone system, as known to a person having ordinary skill in the art. - The
window 214 allows electrical contact between thesecond electrode 212 and theactive material layer 208. While a window is shown, it should be appreciated that a network of vias can also be used, as known to a person having ordinary skill in the art. In one embodiment, thewindow 214 can be sized between about 20 nm to about 2 μm in width and about 20 nm to about 2 μm in length in length. Alternatively, a network of vias providing substantially the same amount of surface area can also be used. - Referring to
FIG. 3 , asystem 300 is shown where acell 302 is coupled to aselectable source 304 via aswitch 306. Thesource 304 is configured to provide a positive and a negative voltage in order to set and reset thecell 302. Thecell 302 as described above can be any of theexemplary embodiments switch 306 isolates thedevice 302 from thesource 304, allowing thedevice 302 to remain in its non-volatile state. In operation, thesource 304 applies controlled positive potentials or alternatively negative potentials) to the second electrode (112 or 212 inFIG. 1 or 2 ). Note that thecell 302 shown may be part of a larger cross bar geometry or other high-density memory array. - Referring to
FIG. 4 , amethod 400 is shown that represents an exemplary process for making thecells method 400 is based on a flow diagram for one embodiment of the present disclosure of fabricating phase transition-based RRAMs. Themethod 400 includes process steps that are performed upon a substrate (102, 202 inFIGS. 1 and 2 ). In one illustrative embodiment, such processing steps are sequentially performed in the depicted order. In alternate embodiments, at least two processing steps may be performed contemporaneously or in a different order. For the device without tunneling barriers (e.g., thedevice 100 ofFIG. 1 ), thestep 404 ofFIG. 4 is eliminated. Conventional sub-processes, such as application and removal of lithographic masks or sacrificial and protective layers, cleaning processes, and the like, are well known in the art and are not shown in themethod 400. Atstep 402 ofFIG. 4 , a first electrode (104 or 204 inFIG. 1 or 2 ) is formed on the substrate (102 or 202 inFIG. 1 or 2 ). - At
step 406 ofFIG. 4 , the active material layer (108 or 208 inFIG. 1 or 2 ) is formed on the first electrode (104 or 204 inFIG. 1 or 2 ). Methods suitable for forming such active material layer, e.g. MoTe2, Mo1-xWxTe2, GaTe, ReSe2, ReS2, are CVD growth or exfoliated from bulk materials. The thickness of the active layer (108 or 208 inFIG. 1 or 2 ) depends on set/reset voltage which RRAM devices require, as described in fuller detail below. Atstep 408 ofFIG. 4 , an isolation layer (110 or 210 inFIG. 1 or 2 ) is formed upon the active material layer (108 or 208 inFIG. 1 or 2 ). The isolation layer (110 or 210 inFIG. 1 or 2 ) is used to ensure that only vertical transport occurs from the first electrode (104 or 204 inFIG. 1 or 2 ) to the second electrode (112 or 212 inFIG. 1 or 2 ) without any lateral transport contributions. The thickness of the isolation layer (110 or 210 inFIG. 1 or 2 ) depends on the voltage of the voltage source 304 (shown inFIG. 3 ) to ensure that no leakage current exists in the chosen layout. Atstep 410 ofFIG. 4 , a contact window (114 or 214 inFIG. 1 or 2 ) is formed in isolation layer (110 or 210 inFIG. 1 or 2 ) upon the active material layer (108 or 208 inFIG. 1 or 2 ). The window allows electrical contact between the second electrode (112 or 212 inFIG. 1 or 2 ) and the active material layer (108 or 208 inFIG. 1 or 2 ). - At
step 412 ofFIG. 4 , the second electrode (112 or 212 inFIG. 1 or 2 ) is formed upon the isolation layer (110 or 210 inFIG. 1 or 2 ), coupling to the active material layer (108 or 208 inFIG. 1 or 2 ). The first electrode (104 or 204 inFIG. 1 or 2 ) and the second electrode (112 or 212 inFIG. 1 or 2 ) may be formed from at least one conductive material (e.g., a metal, an alloy of the metal, or a conductive compound) that is compatible with respective underlying and overlying material layers, as discussed above. Instep 404 ofFIG. 4 , the tunneling barrier layer (206 inFIG. 2 ) is formed upon the first electrode (204 inFIG. 2 ) to reduce the set/reset current level indevice 200. The tunneling barrier layer (206 inFIG. 2 ) may be formed from silicon dioxide (SiO2) or metal oxide materials, such as aluminum oxide (Al2O3), hafnium dioxide (HfO2), boron nitride (BN), other two-dimensional (2D) materials such as MoS2, WSe2, MoSe2, and the like including 2D insulators that do not undergo a phase transition or polymers and other isolation material used in the semiconductor industry known to a person having ordinary skill in the art. The thickness of the tunneling barrier (206 inFIG. 2 ) depends on the requirement of set/reset current levels. In one exemplary embodiment, the tunneling barrier (206 inFIG. 2 ) comprises 4.5 nm thick aluminum oxide (Al2O3). A 3 nm thick aluminum (Al) layer was deposited onto the first electrode (204 inFIG. 2 ) prior to oxidation of the Al in an oxygen rich environment at around 250° C. for 6 h. The set/reset current for this embodiment is 10−7 A for the LRS at 3V. It should be appreciated that the structures discussed herein are symmetrical with respect to the first electrode (104 or 204 inFIG. 1 or 2 ) and the second electrode (112 or 212 inFIG. 1 or 2 ). Therefore, the same procedures and structures discussed can be repeated with the tunneling barrier layer (206 inFIG. 2 ) being formed against the second electrode (212 inFIG. 2 ). - Referring to
FIG. 5 , an exemplary IV graph illustrating characteristics of the RRAM device ofFIG. 1 is provided for a vertical MoTe2 device from a flake with a thickness of about 10 nm. More specifically, the graphs inFIG. 5 show the dependence of current I on the applied voltage V initially in anunformed state 603 as shown by a curve of hollow circles and then the device transitioning to a formed state 604 including a high resistance state (HRS) 604-1 and a low resistive state (LRS) 604-2 as shown by a curve of solid circles. The characteristic 603 ofFIG. 1 is reproducible and substantially does not change after multiple scans between −1 V and 1 V as shown by hollow circles. The situation however changes when the voltage range is extended to a forming voltage. While not fully shown inFIG. 5 , the forming voltage VForming is described in fuller detail below. Thecell 100 ofFIG. 1 can transition into a formed state 604 and remain in that state indefinitely as illustrated. The formed state includes a set voltage represented by 604-3 at which point thecell 100 transitions from the HRS 604-1 to LRS 604-2 and a reset voltage 604-4 at which point thecell 100 transitions from the LRS 604-2 back to the HRS 604-1. Once thecell 100 is transitioned into the formed state 604, it remains in that state indefinitely and by sweeping the voltage it can be set and reset (i.e., transition from the HRS 604-1 to LRS 604-2 and back to HRS 604-1). The set voltage depends on theactive material layer 108 thickness. In the depicted embodiment, thecell 100 has a set voltage VSET of between about 1 V to about 1.2 V. After the forming event, device characteristics can be cycled to exhibit typical bipolar RRAM type of behavior in terms of: a) remaining in their LRS 604-2 when no voltage is applied, b) preserving the low resistive state over an appreciable voltage range until a sufficient reset voltage (here VRESET is between about −0.9 V and −1.1 V) of polarity opposite to the set voltage is reached, and c) remaining in their respective HRS 604-1 until the set voltage is reached. Note, the device can be formed by negative voltage, then the set voltage polarity would be negative and reset voltage polarity would be positive. It should be appreciated that the entirety of the cycle described herein could have started with negative voltages instead of positive voltages resulting in negative set and reset negative voltages. - Referring to
FIG. 6 , an exemplary IV graph illustrating characteristics of the cell 200 (shown inFIG. 2 ) is provided. More specifically, the graph inFIG. 6 shows dependence of current I from the applied voltage V. With the tunneling barrier 206 (seeFIG. 2 ) in place, the current I through thecell 200 is reduced to 0.1 μA (shown inFIG. 6 ) in the depicted embodiment for the LRS at 3V. Thecell 200 is set into LRS without the transitioning from an unformed state into a formed state described above with respect toFIG. 5 (called forming-free) and the LRS does not require introducing any current compliance through an external circuitry (not shown, however, can be accomplished by a semiconductor parameter analyzer or even by a simple circuit including a biased transistor or a switching field effect transistor, as known to a person having ordinary skill in the art), another desirable feature in RRAM cells. The set/reset voltage depends on the thicknesses of theactive layer material 208 and thetunneling barrier 206. It should be appreciated that wherever in the present disclosure samples are discussed with respect to the forming process, that such samples refer toFIGS. 1 and 7 , in which no tunneling barrier layer 206 (seeFIG. 2 ) exists. However, where samples are discussed withsuch tunneling barrier 206, those portions refer to samples whereby no forming is needed. - Referring to
FIG. 7 , a perspective schematic of a vertical transition metal dichalcogenide (TMD) RRAM device also shown inFIG. 1 is shown, according to the present disclosure. Correspondingly, referring toFIGS. 8A and 8B optical and scanning electron microscopy (SEM) images of the cell shown inFIG. 7 are shown, respectively. The second electrode 112 (FIG. 7 ) contact area is between about 0.01 μm2 to about 0.5 μm2 according to one exemplary embodiment. The cell shown inFIG. 7 ensures that only vertical transport occurs from thefirst electrode 104 to thesecond electrode 112 without any lateral transport contributions. Because of the large aspect ratio between thesecond electrode 112 area and the flake thickness of theactive material 108, spreading resistance contributions can be ignored and the active device area is substantially identical to the top contact area. Referring toFIG. 9 area normalized IV curves of exemplary vertical MoTe2 device before forming are shown for devices lacking a tunneling barrier (example cell 100 inFIG. 1 ). The first electrode (104 inFIG. 1 ) is grounded. The results shown confirm the expected trend of current densities with thickness, i.e., the thinner the flakes the higher current densities. The device characteristics shown are reproducible and they remain substantially the same after several scans between −1 V and 1 V. However, when the voltage range is extended beyond −1 V to 1 V, the results change. In particular, vertical MoTe2 TMD devices transition into LRS as discussed inFIG. 5 . - The details on the forming process are discussed below. As long as a critical forming voltage which depends on TMD thickness is not reached, the pristine metal-MoTe2-metal devices exhibit reproducible IV curves shown as hollow circles in
FIG. 5 . Progressing beyond this forming voltage results in the RRAM behavior as described above, resulting in the resistive switching behavior. Two factors contribute to the forming: external electric fields and Joule heating are both factors during the formation of conductive filaments. However, once a filament is formed, a voltage lower than the forming voltage (i.e., a set voltage) is used to switch between the HRS and LRS of the cell. A transition back to the HRS occurs when a reverse polarity electric field is applied, due to a rupture of filaments. It should be appreciated that the set voltage discussed here depends monotonically on the flake thickness for flakes with thicknesses below about 15 nm (seeFIG. 11C ) necessitating in that a critical electric field is needed to trigger the memristive behavior. Set voltages vary for the same flake thickness experimentally by about 0.2 V, which is a result of the prototype fabrication approach used, but is expected to be reduced by proper sample processing in a large fab. It should also be appreciated that after the aforementioned forming process has occurred, the state defined by the HRS remains more conductive than the original state of the device (i.e., solid circles in HRS 604-1 state are higher on the current curve than hollow circles representing pre-formation inFIG. 5 ) which is indicative that a permanent electronic change has occurred in the device. Along the same line, with reference toFIG. 5 , the current ratio between the HRS and the LRS is about 50 but can be between about 10 and about 100 when the compliance is set to about 400 PA. - To further understand the switching mechanism in TMDs, exfoliated MoTe2 based RRAM cells with thicknesses between about 6 nm and about 36 nm were fabricated. All cells were nonvolatile and stable. When considering a metal oxide-based RRAM cell, a set current compliance can be used to control the LRS resistance which then determines the diameter and/or the number of conductive filaments formed in the LRS. Conversely, the reset voltage through the modulation of the ruptured filament length can be used to change the HRS resistance. Referring to
FIG. 10A , IV curves for different current compliance values (1 mA, 600 μA, and 400 μA) are provided for MoTe2-based RRAM cells. As discussed above, the current compliance is inversely related to the LRS resistance, which means that a higher current compliance results in a lower LRS resistance. InFIG. 10A the flake thickness for the device is about 15 nm.FIG. 10B is a graph of current vs. time (s) which shows the performance of the same device under a 0.5 V read disturb with the current compliance set to 1 mA. As shown, both states show a stable resistance over a period of time (e.g., 1000 s) at room temperature. For flake thicknesses from about 6 nm to about 36 nm, the set voltages can be tuned from 0.9 V to 2.3 V. Referring toFIG. 11A the set voltages in the representative IV curves are shown corresponding to moderate fields in the range of about 106 V/cm. It should be appreciated that the RRAM behavior is independent of the choice of contact metal. As an example, using Ni instead of Ti/Ni as top electrode resulted in the same RRAM performance. Also, as shown inFIG. 11B , IV curves for Mo0.96W0.04Te2 are provided for different flake thicknesses. While only W0.04 constituent is shown inFIG. 11B , other percentages have also been studied, and those percentages can range from about 0 to about 0.09. - The relationship below provides a relationship between forming/set voltage vs. flake thickness which is shown
FIG. 11C . The curve fit is based on the following formula: -
V Forming =E CR ·T MoTe2 −qn 1/2k sε0 T MoTe2 2, -
V Set =E CR ·T MoTe2 −qn 2/2k sε0(T MoTe2 −d gap)2, - where VForming is the forming voltage and Vset is the set voltage,
ECR is electric field and according to one embodiment is about 0.16 V/nm,
dGap represents the distance of ruptured filament during the reset process and according to one
embodiment is about 2.1 nm,
Ks is relative permittivity and according to one embodiment is about 8 for MoTe2,
q is electric charge and is about 1.6·10−19 C,
n1 is charge concentration in the MoTe2 material and according to one embodiment is about 1.8·1024 m−3,
n2 is charge concentration in the formed filament and according to one embodiment is about 2.5·1024 m−3,
ε0 is permittivity in vacuum which is about 8.85·10−14 F/cm, and
TMoTe2 is the flake thickness which according to one embodiment is between about 0.6 nm and 40 nm. The relationship provided in the above equation can be used to determine VForming and VSet voltages for differing characteristics. - The impact of the material preparation and composition on RRAM characteristics by extending experiments to 2H—MoTe2 obtained using different approaches and further to 2H—Mo1-xWxTe2 alloys were also investigated. One can deduce the observed RRAM effect is not related to the processing conditions by making the observation that MoTe2 devices can be fabricated using either commercial material or crystals synthesized according to this work which utilize different temperatures and transport agents. As such, Mo1-xWxTe2 devices exhibit very similar switching behavior and their set voltage characteristics also depend monotonically on the flake thickness as shown in
FIG. 11B . Furthermore, observing the set voltages for the Mo1-xWxTe2 alloys show a tendency of being smaller than for the MoTe2 devices. This observation implies that the critical electric field needed to trigger the RRAM behavior may have been reduced in alloys. - As discussed above, application of an electric bias, results in an electric field and Joule heating inside the sample as part of the electroforming process in RRAM devices. Formation of conductive filaments can result for the LRS from both the field and the heating. However, the HRS is characterized by the absence of these filaments. To confirm formation of these filaments, conductive atomic force microscopy (C-AFM) measurements were carried out for MoTe2 RRAM cells, results of which are shown in
FIGS. 12A and 12B . Referring toFIG. 12A , a C-AFM image for current mapping of a MoTe2 flake after the set process and the formation of the LRS has occurred is shown. The dashed square represents the active device area before removal of the top electrode. It should be noted that the bright spot marked with an arrow is the filament. Referring toFIG. 12B , C-AFM images of a pristine MoTe2 flake are provided. In the left panel a topography is shown and in the right panel a current map is shown. These images provide evidence that the aforementioned highly conductive area does not exist in pristine flakes but only in devices that underwent a forming process. - To analyze the formation, first, a fully functional MoTe2 device was biased to form the LRS. Next using a wet chemical etching process as described below the top electrode is removed. This wet etching allows local analysis of the surface resistivity after the filament formation. The inset of
FIG. 12A shows a bright spot of about 80 nm in diameter, which is indicative of a current path through the TMD. In contrast, the associated MoTe2 flakes that did not undergo a forming process show a uniform, highly resistive surface as shown inFIG. 12B . The chemical etching process referred to above is described: 1) The etching includes polymethyl methacrylate (PMMA) as etch mask to define the etching area. 2) The etching further includes nickel etchant TFB to etch away the top Ni contact. 3) The etching also includes buffered oxide etch (BOE) to remove the Ti layer to gain access the TMD. The etching process discussed herein did not aversely affect the TMD or result in any other unrelated features to the forming process during the C-AFM measurements that would be unrelated. - Next the inventors of the present disclosure went about to identify the exact nature of the observed phase change. To this end, scanning transmission electron microscopy (STEM) of cross-section of samples were utilized for both MoTe2 and Mo1-xWxTe2 devices. The same forming process described herein as related to RRAM devices to create filaments in the flakes was undertaken prior to the STEM analysis.
FIG. 13A shows a cross-sectional atomic-resolution high-angle annular dark field (HAADF)-STEM image of a Mo0.96W0.04Te2 device. It should be noted that the HAADF-STEM image shown inFIG. 13A displays the TMD flake both in the active Ni/Ti/Mo0.96W0.04Te2/Au/Ti/SiO2 (right side) and non-active region (left side) where an SiO2 isolation layer on top of the TMD prevented RRAM operation. In all cases, the non-active area only exhibited the original 2H phase of Mo0.96W0.04Te2, while, in the active region, two structurally distinct domains are observed—the domains are marked as 2H and 2Hd inFIGS. 13B and 13C , which is a zoom-in HAADF image of the marked box inFIG. 13A .FIG. 13B is an atomic-resolution HAADF image of the 2H region taken along the [120]2H zone-axis with well-resolved atomic columns of Mo/W and Te.FIG. 13C is a structural HAADF image from the 2Hd domain taken along the [120]2H zone-axis. Instead of the well-aligned atomic columns as observed for the 2H structure, the atomic columns of the 2Hd structure shows a distinct ‘splitting’ for both Te and Mo/W atomic columns, which suggests that the atoms in each atomic column experienced a substantial relative displacement, primarily along the c-direction, upon electric field application.FIG. 13D shows corresponding nano-beam diffraction (NBD) pattern taken from the distorted 2Hd area, which is still indexed as the 2H structure. There are no additional reflections beyond the 2H superlattice reflections observed, suggesting that the 2Hd phase is a distorted metallic modification of the 2H structure, i.e., some transient state with atoms displaced toward one of the lower symmetry structures, but still within the crystal symmetry of the 2H structure. - It can be observed that the phase is reversible and does not involve a change from an amorphous to a crystalline state as typically observed in conventional phase change materials (PCMs). Instead, MoTe2 and Mo1-xWxTe2 remain crystalline when undergoing the local phase transition from a semiconducting 2H to a metallic 2Hd phase. In comparison to, e.g., VO2 that can also undergo an insulator-to-metal phase transition under an electric field but requires a hold current and exhibits a unipolar switching behavior, the MoTe2 phase transition reported here is bipolar, nonvolatile and it occurs at room-temperature.
- Next, to further show stability in the electric field induced phases of MoTe2, pulse-measurements were carried out, where devices were continuously switched between a HRS and a LRS as shown in
FIG. 14 by applying a set and reset voltage of about 1.2 V and about −1V, respectively. A reproducible set and reset of the device between a low resistance state and high resistance state is achievable when short voltage pulses are used to manipulate the RRAM state. In addition, another pair of stable resistance values can be programmed into the device when higher reset voltages (about −1.5 V) are applied. - Those having ordinary skill in the art will recognize that numerous modifications can be made to the specific implementations described above. The implementations should not be limited to the particular limitations described. Other implementations may be possible.
Claims (10)