US20200263283A1 - Ultrahigh strength multiphase steel and method for producing a steel strip from said multiphase steel - Google Patents

Ultrahigh strength multiphase steel and method for producing a steel strip from said multiphase steel Download PDF

Info

Publication number
US20200263283A1
US20200263283A1 US16/652,933 US201816652933A US2020263283A1 US 20200263283 A1 US20200263283 A1 US 20200263283A1 US 201816652933 A US201816652933 A US 201816652933A US 2020263283 A1 US2020263283 A1 US 2020263283A1
Authority
US
United States
Prior art keywords
strip
steel
hot
cold
steel strip
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/652,933
Other languages
English (en)
Inventor
Thomas Schulz
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Salzgitter Flachstahl GmbH
Original Assignee
Salzgitter Flachstahl GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Salzgitter Flachstahl GmbH filed Critical Salzgitter Flachstahl GmbH
Assigned to SALZGITTER FLACHSTAHL GMBH reassignment SALZGITTER FLACHSTAHL GMBH ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SCHULZ, THOMAS
Publication of US20200263283A1 publication Critical patent/US20200263283A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0242—Flattening; Dressing; Flexing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
    • C21D9/54—Furnaces for treating strips or wire
    • C21D9/56—Continuous furnaces for strip or wire
    • C21D9/561—Continuous furnaces for strip or wire with a controlled atmosphere or vacuum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/008—Ferrous alloys, e.g. steel alloys containing tin
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B1/00—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations
    • B21B1/22—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B1/00—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations
    • B21B1/22—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length
    • B21B2001/221—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length by cold-rolling
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B1/00—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations
    • B21B1/22—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length
    • B21B2001/225—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length by hot-rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/26—Methods of annealing
    • C21D1/32—Soft annealing, e.g. spheroidising
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Definitions

  • the invention relates to an ultra high strength multi-phase steel with a dual-phase microstructure or complex-phase microstructure and with small proportions of residual austenite having improved production and excellent material properties for subsequent processing, in particular for lightweight vehicle construction according to the preamble of claim 1 .
  • Advantageous developments are described in dependent claims 2 to 24 .
  • the invention also relates to a method for producing steel strips from such a steel according to claim 25 and steel strips produced therewith according to claim 38 .
  • the invention relates to steels having a tensile strength in the region of at least 980 MPa, in the non-quenched state, for producing components which have improved deformability, such as e.g. with regard to hole expansion and improved joining suitability, such as e.g. welding properties.
  • the fiercely competitive car market means that producers are constantly forced to find solutions for reducing fleet fuel consumption and CO2 exhaust emissions whilst maintaining the highest possible level of comfort and passenger protection.
  • the weight saving of all of the vehicle components plays a decisive role as does, on the other hand, the most favorable possible behavior of the individual components in the event of high static and dynamic loading during operation and also in the event of a crash.
  • the steel suppliers take the aforementioned problem into account by providing ultra high strength steels. Furthermore, by providing ultra high strength steels having a smaller sheet thickness, the weight of the vehicle components can be reduced whilst the behavior of components remains the same or is possibly even improved.
  • This relates both to the processes performed by the car producer, e.g. stamping and deforming, optional thermal quenching with subsequent optional tempering, welding and/or surface post-treatment, such as phosphatizing and cathodic dip coating, and also the manufacturing processes performed by the suppliers of semi-finished products, such as e.g. surface finishing by means of metallic or organic coating.
  • Improved joining suitability e.g. in the form of better general welding capability, as well as a larger usable welding area for resistance spot welding and improved failure behavior of the weld seam (fracture pattern) under mechanical stress, and sufficient resistant to delayed hydrogen embrittlement (i.e. delayed fracture free) are also required to an increasing extent.
  • HFI high-frequency induction welding method
  • the hole expansion capability is a material property which describes the resistance of the material to crack initiation and crack propagation in deformation operations in regions close to the edge, such as e.g. during plunging.
  • the hole expansion test is regulated e.g. in the ISO 16630 standard. According to this, prefabricated holes which are stamped e.g. into a metal sheet are expanded by means of a mandrel.
  • the measurement variable is the change in hole diameter, related to the initial diameter, at which the first crack through the metal sheet occurs at the edge of the hole.
  • Improved edge crack insensitivity signifies an increased deformation capability of the sheet edges and can be described by an increased hole expansion capability. These circumstances are also known as the synonyms “Low Edge Crack” (LEC) or by “High Hole Expansion” (HHE) and Xpand®.
  • the bending angle describes a material property which allows conclusions to be drawn in respect of the material behavior in deformation operations with dominant bending proportions (e.g. during folding) or even in the event of crash loadings. Therefore, increased bending angles increase passenger compartment safety.
  • the determination of the bending angle (a) is regulated e.g. by means of the plate bending test in the standard VDA 238-100.
  • the aforementioned properties are important for components which have a very complex formation.
  • Improved welding capability is known to be achieved inter alia by means of a reduced carbon equivalent.
  • the failure behavior or the fracture pattern of the weld seam can be improved by significant addition by alloying with microalloy elements, in the case of low-carbon steels with a reduced carbon equivalent.
  • High-strength components must have sufficient resistance to material embrittlement with respect to hydrogen.
  • AHSS Advanced High Strength Steels
  • the characteristic processing properties of the dual-phase steels such as a very low yield strength ratio with very high tensile strength at the same time, strong cold solidification and good cold deformability are sufficiently known.
  • multi-phase steels such as complex-phase steels, ferritic-bainitic steels, bainitic steels and martensitic steels which have different structural compositions.
  • Complex-phase steels are, according to EN 10346, steels which contain small proportions of martensite, residual austenite and/or perlite in a ferritic/bainitic basic microstructure, wherein strong grain refinement is produced by means of delayed recrystallization or by precipitation of microalloy elements.
  • Ferritic-bainitic steels are, according to EN 10346, steels which contain bainite or solidified bainite in a matrix of ferrite and/or solidified ferrite.
  • the strength of the matrix is produced by means of a high dislocation density, by means of grain refinement and the precipitation of microalloy elements.
  • Dual-phase steels are, according to EN 10346, steels which have a ferritic basic microstructure, in which a martensitic second phase is incorporated in the shape of an island, occasionally with proportions of bainite as the second phase. In the case of high tensile strength, dual-phase steels demonstrate a low yield strength ratio and strong cold solidification.
  • TRIP steels are, according to EN 10346, steels which have a predominantly ferritic basic microstructure, in which bainite and residual austenite is incorporated, which can convert into martensite during deformation (TRIP effect). Owing to its intense cold solidification, the steel achieves high values for uniform elongation and tensile strength. High component strengths can be achieved in conjunction with the bake-hardening effect. These steels are suitable both for stretch-drawing and deep-drawing. However, during material deformation, higher sheet holder forces and press forces are required. A comparatively strong resilience is to be taken into account.
  • the high-strength steels comprising a single-phase microstructure include e.g. bainitic and martensitic steels.
  • Bainitic steels are, according to EN 10346, steels which are characterized by a very high yield strength and tensile strength with sufficiently high elongation for cold-forming processes. An effective welding capability is provided by reason of the chemical composition.
  • the microstructure consists typically of bainite.
  • the microstructure can contain in isolation small proportions of other phases, such as e.g. martensite and ferrite.
  • Martensitic steels are, according to EN 10346, steels which, by reason of thermomechanical rolling, contain small proportions of ferrite and/or bainite in a basic microstructure of martensite. This steel grade is characterized by a very high yield strength and tensile strength with sufficiently high elongation for cold-forming processes. Within the group of multi-phase steels, the martensitic steels have the highest tensile strength values. The suitability for deep-drawing is limited. The martensitic steels are suitable predominantly for bending deformation methods, such as roll-forming.
  • the strength/tensile strength ratio can be influenced in a targeted manner by tempering which is effected after hardening.
  • TRB® s with multi-phase microstructures is not possible without limitations, such as e.g. for the heat treatment prior to cold-rolling.
  • a homogeneous, multi-phase microstructure cannot be set in cold-rolled and hot-rolled steel strips by reason of a temperature gradient which occurs in the established process windows.
  • the cold-rolled steel strips are typically annealed in the continuous annealing method in a recrystallizing manner to produce a thin sheet which can be deformed in an effective manner.
  • the process parameters such as throughput speed, annealing temperatures and cooling rate, are set corresponding to the required mechanical-technological properties with the microstructure required for this purpose.
  • the aforementioned properties are significantly influenced e.g. by the steel compositions, the process parameters during hot rolling, the process parameters during acid-cleaning (e.g. stretch-bend-straightening) and the process parameters during cold-rolling even prior to continuous annealing.
  • the steel composition is fixed by analysis regulations which define MIN and MAX ranges.
  • the process parameters during hot-rolling such as e.g. the standard slab thickness, slab lying time, slab output temperature, pass plan during pre-strip rolling, standard pre-strip thickness, entry temperature into the hot strip line, pass plan during hot-rolling, end rolling temperature, hot strip cooling pattern, reeling temperature, are fixed depending upon the multi-phase steel to be produced.
  • stretch-bend-straightening influences the subsequent process step.
  • the hot strip thickness for producing a cold-rolling thickness is already fixed by a standard degree of thinning by rolling at the time of order conversion into the technical specifications (process parameters).
  • the thickness of the pre-strip during the hot-rolling process describes the starting thickness prior to entry into the multi-frame hot strip line, wherein the pre-strip has been manufactured in a reversing manner, in a plurality of passes (runs) from one slab having a defined standard thickness.
  • Typical slab thicknesses are between 250 mm and 300 mm (standard 250 mm, considered further here), the pre-strip thicknesses in the case of multi-phase steels typically range between 40 mm to 60 mm.
  • the pre-strip thicknesses for the subsequent hot-rolling are relatively constant, depending upon the material composition, e.g. at 45 mm (referred to here as standard).
  • the degree of thinning by cold-rolling describes the percentage difference in the hot strip starting thickness with respect to the cold strip end thickness based on the hot strip starting thickness.
  • the degrees of thinning by cold-rolling are relatively constant, they are up to approximately 40% in the case of thicker cold strips of more than 2 mm and are up to approximately 60% in the case of cold strips of up to 1 mm in thickness.
  • the cold strip is heated in the continuous annealing furnace to a temperature at which, during cooling, the required microstructure formation (e.g. dual-phase or complex-phase microstructure) is achieved.
  • the required microstructure formation e.g. dual-phase or complex-phase microstructure
  • the annealing treatment is typically performed in a continuous hot-galvanizing installation, in which the heat treatment or annealing and the downstream galvanizing take place in a continuous process.
  • This relates not only to flexibly rolled strips having different sheet thicknesses over the strip length but also primarily to strips having a different thickness and/or different width which have to be annealed in succession.
  • a homogeneous temperature distribution can be achieved only with difficulty specifically in the case of different thicknesses in the transition region from one strip to the other.
  • alloy compositions with excessively small process windows this can result in e.g. the thinner strip being moved too slowly through the furnace and as a result the productivity is reduced, or in the thicker strip being moved too quickly through the furnace and the required annealing temperature for the desired microstructure is not achieved. As a result, there is an increased amount of scrap.
  • the decisive process parameter for material having a relatively constant degree of thinning by cold-rolling is the setting of speed during continuous annealing because the phase conversion proceeds in dependence upon temperature and time. Therefore, the more insensitive the steel is in relation to the uniformity of the mechanical properties during changes in the temperature and time profiles during continuous annealing, the greater the process window.
  • a method for producing a steel strip having a different thickness over the strip length is described e.g. in DE 100 37 867 A1.
  • the narrow process window during the continuous annealing of strips of different thickness means that it is only possible with difficulty to achieve uniform mechanical properties over the entire length of the strip.
  • Complex-phase steels also have an even narrower process window than dual-phase steels.
  • the excessively small process window means that the regions having a smaller sheet thickness owing to the conversion processes during cooling have either excessively high levels of strength as a result of excessively large martensite proportions or the regions having a greater sheet thickness achieve excessively low levels of strength as a result of excessively small martensite proportions.
  • Homogeneous mechanical-technological properties over the strip length or width cannot be achieved in practical terms with the known alloy concepts during continuous annealing.
  • the known alloy concepts for multi-phase steels are characterized by an excessively narrow process window and therefore are unsuitable in particular for cold strip manufacture with variable pre-strip thicknesses and variable degrees of thinning by cold-rolling, and for flexibly rolled strips.
  • Laid-open document DE 10 2012 002 079 A1 discloses an ultra high strength multi-phase steel having minimum tensile strengths of 950 MPa which, even though it already has a very wide process window for the continuous annealing of hot or cold strips, it has been shown that even with this steel it is not possible to achieve either variable pre-strip thicknesses or variable degrees of thinning by cold-rolling with a single hot strip thickness (master hot strip thickness) whilst producing uniform material properties.
  • Laid-open document DE 10 2015 111 177 A1 discloses an ultra high strength multi-phase steel having minimum tensile strengths of 980 MPa which already has a very wide process window for the continuous annealing of hot or cold strips, and also e.g. with a single hot strip thickness (master hot strip thickness) thus achieving variable degrees of thinning by cold-rolling, continuously annealed cold strips having different thicknesses and with uniform material properties can be achieved.
  • Laid-open document DE 10 2014 017 274 A1 discloses an ultra high strength, air-hardenable multi-phase steel having minimum tensile strengths, in the non-air-hardened state, of 950 MPa which already has a very wide process window for the continuous annealing of hot or cold strips, and also e.g. with a single hot strip thickness (master hot strip thickness) thus achieving variable degrees of thinning by cold-rolling, continuously annealed cold strips having different thicknesses and with uniform material properties can be achieved and are suitable for the subsequent air-hardening process.
  • the aim of achieving the resulting mechanical-technological properties in a narrow region over the length and width of the strip by the controlled setting of the volume proportions of the microstructure components has the greatest priority and is only possible by means of an increased process window.
  • the known alloy concepts are characterized by a process window which is too narrow, and therefore is unsuitable for solving the present problem, in particular in the case of flexibly rolled strips. With the known alloy concepts it is currently possible to produce only steels of one strength class with defined cross-sectional regions (strip thickness and strip width) and so changed alloy concepts are required for different strength classes and/or cross-sectional regions.
  • PCM C+(Mn+Cu+Cr)/20+Ni/60+Mo/15+V/10+5 B
  • the characteristic standard elements such as carbon and manganese, as well as chromium or molybdenum and vanadium are taken into consideration (contents in wt. %).
  • the material processing properties deteriorate to an increasing extent, e.g. during welding, deforming and hot-dip finishing.
  • a low yield strength ratio (Re/Rm) is typical of a dual-phase steel and is used primarily for deformability in stretching and deep-drawing procedures.
  • a higher yield strength ratio (Re/Rm), as is typical of complex-phase steels, is also characterized by the resistance to edge cracks. This can be attributed to the smaller differences in the strengths of the individual microstructure components, which has a favorable effect upon homogeneous deformation in the region of the cut edge.
  • the analytical landscape for achieving multi-phase steels having minimum tensile strengths of 980 MPa is very diverse and comprises very large alloy ranges in the strength-increasing elements of carbon, manganese, phosphorous, aluminium and chromium and/or molybdenum, as well as in the addition of micro-alloys individually or in combinations, and in the material-characterizing properties, such as hole expansion and reduced carbon equivalent, etc.
  • the dimension spectrum is broad and is in the thickness range of 0.50 to 3.00 mm, wherein the range between 0.80 to 2.10 mm is relevant in terms of quantity.
  • Thickness ranges below 0.50 and above 3.00 mm are feasible.
  • the object of the invention is to provide a novel alloy concept for an ultra high strength multi-phase steel, a method for producing a steel strip from this ultra high strength multi-phase steel and to provide a steel strip which is produced according to this method and with which the process window for the continuous annealing of cold strips can be extended such that from different pre-strip thicknesses, a specified hot strip thickness (master hot strip thickness) it is possible to manufacture different cold strip thicknesses or from different hot strip thicknesses it is possible to manufacture a cold strip thickness (master cold strip thickness). Moreover, instead of constant pre-strip thicknesses variable pre-strip thicknesses can be used prior to the hot-rolling.
  • the most uniform possible cold strip material properties are to be achieved independently of the set pre-strip thickness and the set degree of cold-rolling.
  • the process window for the annealing, in particular continuous annealing, of steel strips which are cold-rolled to an end thickness is to be extended such that, in addition to strips having different cross-sections (cross-sectional jump), it is also possible to produce steel strips having a thickness (TRB®) which vanes over the strip length and optionally strip width, with the most homogeneous mechanical-technological properties possible.
  • TRB® thickness
  • this object is achieved by an ultra high strength multi-phase steel having a minimum tensile strength of 980 MPa with the following contents in wt. %:
  • Mn-Si+Cr is ⁇ 1.750 wt. % to ⁇ 2.250 wt. % with regard to a processing window which is as wide as possible during the annealing, in particular the continuous annealing, of cold strips of this steel.
  • the mechanical-technological properties are reliably achieved in a narrow range for cold strips having variable pre-strip thickness prior to hot-rolling, as well as variable degrees of thinning by cold-rolling during cold-rolling.
  • variable pre-strip thicknesses the cold-rolling process can be positively influenced by virtue of the fact that the steps of soft annealing of hot strip are performed prior to cold-rolling, double cold-rolling, soft annealing of the cold-rolled strip prior to the next cold-rolling step, without negative consequences on the production of the above-described master hot strip thickness or master cold strip thickness.
  • the previous production philosophy that the final cold strip thickness (end thickness) determines the necessary hot strip thickness and a standard pre-strip thickness is necessary can be disregarded to the extent that a selected pre-strip thickness and only one selected master hot strip thickness is required for different cold strip thicknesses.
  • a pre-strip can be produced from the multi-phase steel in the state of a slab, said pre-strip subsequently being hot-rolled with the hot strip thickness to be achieved.
  • the steel according to the invention offers the advantage of a considerably increased process window in comparison with the known steels. This results in an increased level of process reliability in the continuous annealing of a cold strip having a multi-phase microstructure. Therefore, for continuously annealed cold strips it is possible to ensure more homogeneous mechanical-technological properties in strips having variable degrees of thinning by cold-rolling, and in the strip or in the transition region of two strips even with different cross-sections and otherwise identical process parameters.
  • the inventive multi-phase steel to produce a steel strip, in which the multi-phase steel is used to produce a hot strip, from the hot strip the steel strip is cold-rolled with the end thickness to be achieved and subsequently the steel strip is annealed, in particular continuously annealed.
  • the properties of the multi-phase steel render it possible that, proceeding from a varying pre-strip thickness, a selected master hot strip having a specific thickness or selected hot strips having different thicknesses in a wide range of degrees of thinning by cold-rolling of 10% to 70%, steel strips are cold-rolled with the end thickness to be achieved.
  • the chemical composition of the multi-phase steel is selected in dependence upon the end thickness of the cold strip to be obtained. Therefore, within selectable thickness graduations of the cold strip to be obtained, it is possible to produce, from a master hot strip having a thickness, corresponding cold strips having one or more end thicknesses or else to produce from different hot strip thicknesses a master cold strip having a consistent thickness.
  • the steel strip is cold-rolled to an end thickness of 0.50 to 3.00 mm and the chemical composition of the multi-phase steel is selected as follows in dependence upon the end thickness to be achieved, even if variable pre-strip thicknesses are used.
  • the total content of Mn-Si+Cr is selected as follows in dependence upon the end thickness of the cold strip to be achieved:
  • the total content of Mn-Si+Cr+Mo is selected as follows in dependence upon the end thickness of the cold strip to be achieved:
  • the end thickness of the steel strip to be achieved is associated with the alloy composition of the pre-strip or hot strip produced from the multi-phase steel.
  • carbon equivalent CEV (IIW) is selected as follows in dependence upon the end thickness of the cold strip to be achieved:
  • end thickness 0.50 to 1.00 mm inclusive Mn content ⁇ 1.900 wt. % to ⁇ 2.200 wt. %, end thickness over 1.00 to 2.00 mm inclusive: Mn content ⁇ 2.050 wt. % to ⁇ 2.250 wt. %, end thickness over 2.00 mm to 3.00 mm inclusive: Mn content ⁇ 2.100 wt. % to ⁇ 2.350 wt. %.
  • the Cr content and the carbon equivalent CEV ( 1 W) are selected as follows in dependence upon the end thickness of the cold strip to be achieved:
  • end thickness 0.50 to 1.00 mm inclusive Cr content ⁇ 0.260 wt. % to ⁇ 0.330 wt. % and carbon equivalent CEV (IIW) ⁇ 0.62%
  • end thickness over 1.00 to 2.00 mm inclusive Cr content ⁇ 0.290 wt. % to ⁇ 0.360 wt. % and the carbon equivalent CEV (IIW) ⁇ 0.64%
  • end thickness over 2.00 to 3.00 mm inclusive Cr content ⁇ 0.320 wt. % to ⁇ 0.370 wt. % and the carbon equivalent CEV (IIW) ⁇ 0.66%.
  • ultra high strength cold strips which are produced in the continuous annealing method, are produced from multi-phase steel having varying sheet thicknesses, it is advantageously possible to produce loading-optimized components from this material by deformation technology.
  • the material produced can be produced as a cold strip via a hot-dip galvanizing line or a pure continuous annealing installation, in the temper-rolled and non-temper-rolled state and even in the heat-treated state (ageing) and in the stretch-formed and non-stretch-formed state (stretch-bend-straighten).
  • the alloy composition according to the invention can be used to produce steel strips by means of inter-critical annealing between Ac1 and Ac3 or with austenitising annealing over Ac3 with concluding controlled cooling, which results in a dual-phase or multi-phase microstructure.
  • Annealing temperatures of about 700 to 950° C. have proven to be advantageous. According to the invention, in dependence upon the entire process (only continuous annealing or with additional hot-dip finishing) there are different approaches for heat treatment.
  • the steel strip which is cold-rolled to an end thickness is cooled, starting from the annealing temperature, at a cooling rate of approximately 15 to 100° C./s to an intermediate temperature of approximately 160 to 250° C.
  • cooling can be performed in advance at a cooling rate of approximately 15 to 100° C./s to a previous intermediate temperature of 300 to 500° C. Cooling to room temperature is finally effected at a cooling rate of approximately 2 to 30° C./s (see method 1, FIG. 8 a ).
  • cooling can be performed at a cooling rate between approximately 15 and 100° C./s from the intermediate temperature of 300 to 500′C to room temperature.
  • Cooling is stopped as described above prior to entry into the melting bath and is continued only after exit from the bath until the intermediate temperature of approximately 200 to 250° C. is achieved. Depending upon the melting bath temperature, a holding temperature of approximately 400 to 470° C. is provided in the melting bath. Cooling to room temperature is then performed at a cooling rate of approximately 2 to 30° C./s (see method 2, FIG. 8 b ).
  • the carbon equivalent can be reduced, whereby the welding suitability is improved and excessive hard spots during welding are avoided. Furthermore, in the case of resistance spot welding the electrode service life can be considerably increased.
  • Associated elements are elements which are already present in the iron ore or get into the steel as a result of the production process. They are generally undesired by reason of their predominantly negative influences. The attempt is made to remove them to a tolerable content level or to convert them into less damaging forms.
  • Hydrogen (H) can diffuse as a single element through the iron lattice, without producing lattice tensions.
  • the hydrogen in the iron lattice is relatively mobile and can be relatively easily absorbed during the processing of the steel.
  • Hydrogen can be absorbed into the iron lattice only in atomic (ionic) form.
  • Hydrogen exerts a significant embrittling effect and diffuses preferably to locations which are favorable in terms of energy (flaws, grain boundaries etc.). Flaws thus function as hydrogen traps and can considerably increase the dwell time of the hydrogen in the material.
  • Cold cracks can be produced by means of a recombination to molecular hydrogen. This behavior occurs in the event of hydrogen embrittlement or in the event of hydrogen-induced tension crack corrosion. Even in the case of the delayed crack, the so-called delayed fracture, which occurs without external tensions, hydrogen is often stated to be the reason instigating this. Therefore, the hydrogen content in the steel should be kept as small as possible.
  • the hydrogen content in the steel according to the invention is limited to ⁇ 0.0010 wt. % (10 ppm) or advantageously to ⁇ 0.0008 wt. %, optimally to ⁇ 0.0005 wt. %.
  • a more uniform microstructure which, in the case of the steel according to the invention, is achieved inter alia by its widened process window, also reduces the susceptibility to hydrogen embrittlement.
  • Oxygen (O) in the molten state, the steel has a relatively large absorbency for gases. However, at room temperature oxygen is soluble only in very small quantities. In a similar manner to hydrogen, oxygen can diffuse only in atomic form into the material. Owing to the highly embrittling effect and the negative effects upon the ageing resistance, every attempt is made during production to reduce the oxygen content.
  • Phosphorous (P) is a trace element from the iron ore and is dissolved in the iron lattice as a substitution atom. Phosphorus increases the hardness by means of mixed crystal hardening and improves the hardenability. However, attempts are generally made to lower the phosphorous content as much as possible because inter alia its low solubility in the solidifying medium means that it exhibits a strong tendency towards segregation and greatly reduces the level of toughness. The attachment of phosphorous to the grain boundaries causes grain boundary fractures. Moreover, phosphorous increases the transition temperature from tough to brittle behavior up to 300° C. During hot-rolling, near-surface phosphorous oxides at the grain boundaries can result in the formation of fractures.
  • phosphorous is used in small quantities ( ⁇ 0.1 wt. %) as a microalloy element, e.g. in higher-strength IF-steels (interstitial free), bake-hardening steels or even in some alloy concepts for dual-phase steels.
  • the steel according to the invention differs from known analysis concepts, which use phosphorous as a mixed crystal forming agent, inter alia in that phosphorous is not alloyed thereto but instead is set as low as possible.
  • the phosphorous content in the steel according to the invention is limited to quantities which are unavoidable in the production of steel.
  • P should be ⁇ 0.020 wt. %.
  • S Sulphur
  • Sulphur is bound as a trace element in the iron ore. Sulphur is not desirable in steel (the exception being machining steels) because it exhibits a strong tendency towards segregation and has a greatly embrittling effect. Therefore, attempts are made to achieve, where possible, a very low content of sulphur in the melt, e.g. by means of vacuum treatment. Furthermore, the sulphur present is converted by the addition of manganese into the relatively innocuous compound manganese sulphide (MnS). The manganese sulphides are often rolled out in lines during the rolling process and function as nucleation sites for the conversion.
  • the sulphur content in the steel according to the Invention is limited to ⁇ 0.0020 wt. % or advantageously to ⁇ 0.0015 wt. %, optimally to ⁇ 0.0010 wt. %.
  • Alloy elements are generally added to the steel in order to Influence specific properties in a targeted manner.
  • An alloy element can thereby influence different properties in different steels. The effect generally depends greatly upon the quantity and solution state in the material. Accordingly, the relationships can be very varied and complex.
  • Carbon (C) is considered to be the most important alloy element in steel. Its targeted introduction at an amount of up to 2.06 wt. % turns iron first into steel. The carbon proportion is often drastically reduced during the production of steel. In the case of dual-phase steels for continuous hot-dip finishing, its proportion according to EN 10346 or VDA 239-100 is at most 0.230 wt. %, a minimum value is not specified.
  • Carbon is interstitially dissolved in the iron lattice owing to its comparatively small atomic radius.
  • the solubility is at most 0.02% in the ⁇ -iron and is at most 2.06% in the ⁇ -iron.
  • Carbon, in dissolved form increases the hardenability of steel considerably and is therefore essential for forming a sufficient quantity of martensite.
  • excessively high carbon contents increase the hardness difference between ferrite and martensite and restrict weldability.
  • the steel according to the invention contains carbon contents of ⁇ 0.115 wt. %.
  • Carbon also forms carbides.
  • a microstructure phase which occurs almost in every steel is cementite (Fe 3 C).
  • substantially harder special carbides can be formed with other metals such as e.g. chromium, titanium, niobium but also vanadium. Therefore, it is not only the type but also the distribution and extent of the precipitation which is of crucial significance for the resulting increase in strength. Therefore, in order to ensure, on the one hand, sufficient strength and, on the other hand, effective weldability, improved hole expansion, an improved bending angle and a sufficient resistance to hydrogen-induced crack formation (delayed fracture free), the minimum C content is fixed to 0.075 wt. % and the maximum C content is fixed to 0.115 wt. %, contents having a cross-section-dependent differentiation are advantageous, such as:
  • end thickness 0.50 mm to 1.00 mm Inclusive (C ⁇ 0.100 wt. %) end thickness over 1.00 to 2.00 mm inclusive (C ⁇ 0.105 wt. %) end thickness over 2.00 to 3.00 mm inclusive (C ⁇ 0.115 wt. %)
  • silicon (Si) binds oxygen and is therefore used for killing purposes in the course of deoxidation of the steel. It is important for the subsequent steel properties that the segregation coefficient is considerably less than e.g. that of manganese (0.16 in comparison with 0.87). Segregations generally lead to a lined arrangement of the microstructure components which impair the deforming properties, such as e.g. hole expansion and bending capability.
  • the addition of silicon produces a strong mixed crystal hardening.
  • an addition of 0.1% silicon produces an Increase in tensile strength by approximately 10 MPa, wherein in the case of an addition of up to 2.2% silicon the elongation is only slightly impaired. This has been examined for different sheet thicknesses and annealing temperatures. The increase from 0.2% to 0.5% silicon produced an increase in strength of approximately 20 MPa in yield strength and approximately 70 MPa in tensile strength. The elongation at fracture decreases by about 2%.
  • a further important effect is that silicon shifts the formation of ferrite towards shorter times and temperatures and therefore permits the production of sufficient ferrite prior to quench hardening.
  • this provides a basis for improved cold-rollability.
  • the accelerated formation of ferrite causes the austenite to be enriched with carbon and thus stabilized. Since silicon hinders the formation of carbide, the austenite is additionally stabilized. Therefore, during the accelerated cooling the formation of bainite can be suppressed in favor of martensite.
  • silicon in the span according to the invention has resulted in further surprising effects which are described hereinafter.
  • the above-described delay in the formation of carbide could also be brought about e.g. by aluminium.
  • aluminium forms stable nitrides and so sufficient nitrogen is not available for the formation of carbonitrides with microalloy elements.
  • Alloying with silicon obviates this problem because silicon does not form either carbides or nitrides. Therefore, silicon indirectly has a positive effect upon the precipitate formation by microalloys which, in turn, have a positive effect upon the strength of the material. Since the increase in the conversion temperatures caused by silicon tends to promote grain coarsening, a microalloy with niobium, titanium and boron is particularly expedient, as is the targeted setting of the nitrogen content in the steel according to the invention.
  • the atmospheric conditions during the annealing treatment in a continuous hot-dip coating installation produces a reduction of iron oxide which can form on the surface e.g. during cold-rolling or as a result of storage at room temperature.
  • oxygen-affine alloy components such as e.g. silicon, manganese, chromium, boron
  • the gas atmosphere is oxidizing, as a result of which a segregation and selective oxidation of these elements can take place.
  • the selective oxidation can take place both externally, i.e. on the substrate surface, and Internally within the metallic matrix.
  • silicon in particular, diffuses to the surface during annealing and forms, on its own or together with manganese, oxides on the steel surface. These oxides can inhibit the contact between the substrate and the melt and can prevent or significantly impair the wetting reaction. As a result, non-galvanized locations, so-called “bare spots” or even large-surface regions without any coating can occur. Furthermore, the adhesion of the zinc or zinc alloy layer on the steel substrate can be reduced by reason of an impaired wetting reaction, resulting in insufficient inhibitor layer formation.
  • the internal oxidation of the alloy elements can be influenced in a targeted manner by setting the oxygen partial pressure of the furnace atmosphere (N 2 —H 2 -protective gas atmosphere).
  • the set oxygen partial pressure must satisfy the following equation, wherein the furnace temperature is between 700 and 950° C.
  • Si, Mn, Cr, B define the corresponding alloy proportions in the steel in wt. % and pO2 defines the oxygen partial pressure in mbar.
  • the furnace region consists of a combination of a direct fired furnace (DFF) or non-oxidizing furnace (NOF) and a downstream radiant tube furnace (see method 2 in FIG. 8 b )
  • DFF direct fired furnace
  • NOF non-oxidizing furnace
  • the selective oxidation of the alloy elements can likewise be influenced by the gas atmospheres of the furnace regions.
  • the oxygen partial pressure and therefore the oxidation potential for iron and the alloy elements can be set by the combustion reaction in the NOF. This is to be set in such a way that the oxidation of the alloy elements takes place internally below the steel surface and possibly a thin iron oxide layer forms on the steel surface after passage through the NOF region. This is achieved e.g. by reducing the CO value below 4 vol. %.
  • the possibly formed iron oxide layer is reduced and similarly the alloy elements are further oxidized internally.
  • the set oxygen partial pressure in this furnace region must satisfy the following equation, wherein the furnace temperature is between 700 and 950° C.
  • Si, Mn, Cr, B define the corresponding alloy proportions in the steel in wt. % and pO 2 defines the oxygen partial pressure in mbar.
  • the dew point of the gas atmosphere N 2 —H 2 -protective gas atmosphere
  • the oxygen partial pressure are to be set in such a way as to avoid oxidation of the strip prior to dipping in the melting bath.
  • Dew points in the range of ⁇ 30 to ⁇ 40° C. have proven to be advantageous.
  • the method route selected is that involving continuous annealing with subsequent electrolytic galvanizing (see method 1 in FIG. 8 a ), it is not necessary to implement any particular measures in order to ensure the galvanizing capability. It is known that the galvanization of more highly alloyed steels can be achieved substantially more easily by means of electro-deposition than by means of continuous hot-dipping methods. In the case of electrolytic galvanizing, pure zinc is deposited directly onto the strip surface. In order not to hinder the electron flow between the steel strip and the zinc ions and therefore galvanization, it is necessary to ensure that no surface-covering oxide layer is present on the strip surface. This condition is generally ensured by a standard reducing atmosphere during annealing and by pre-cleaning prior to electrolysis.
  • the minimum silicon content is fixed to 0.400 wt. % and the maximum silicon content is fixed to 0.500 wt. %.
  • Manganese (Mn) is added to almost all steels for the purpose of desulphurisation in order to convert the noxious sulphur into manganese sulphides. Moreover, by means of mixed crystal hardening, manganese increases the strength of the ferrite and shifts the ⁇ -/ ⁇ -conversion towards lower temperatures.
  • a main reason for adding manganese by alloying in multi-phase steels, such as e.g. in the case of dual-phase steels, is the considerable improvement in the potential hardness increase.
  • the perlite and bainite conversion is shifted towards longer times and the martensite starting temperature is decreased.
  • Manganese like silicon, tends to form oxides on the steel surface during the annealing treatment.
  • manganese oxides e.g. MnO
  • Mn mixed oxides e.g. Mn 2 SiO 4
  • manganese is to be considered to be less critical in a small Si/Mn or Al/Mn ratio because globular oxides are more likely to form instead of oxide films.
  • high manganese contents can negatively influence the appearance of the zinc layer and the zinc adhesion.
  • the above-stated measures for setting the furnace regions during continuous hot-dip coating serve to reduce the formation of Mn oxides or Mn mixed oxides on the steel surface after annealing.
  • the manganese content is fixed to 1.900 wt. % to 2.350 wt. %.
  • the manganese content is preferably in a range between ⁇ 1.900 wt. % to ⁇ 2.200 wt. %, in the case of end thicknesses of 1.00 to 2.00 mm inclusive, said manganese content is in a range between ⁇ 2.050 wt. % to ⁇ 2.250 wt. % and in the case of end thicknesses of 2.00 to 3.00 mm inclusive, it is in a range between ⁇ 2.100 wt. % to ⁇ 2.350 wt. %.
  • a further special feature of the invention is that the variation in the manganese content can be compensated for by simultaneously changing the silicon content.
  • the increase in strength (in this case the yield strength, YS) by manganese and silicon is generally described in an effective manner by the Pickering equation:
  • the coefficients of manganese and silicon are approximately equal for the yield strength and for the tensile strength, thus providing the option of substituting manganese by silicon.
  • chromium (Cr) in dissolved form and even in small quantities can considerably increase the hardenability of steel.
  • Cr chromium in the form of chromium carbides effects particle solidification.
  • the associated increase in the number of nucleation sites with a simultaneously lowered content of carbon leads to a reduction in hardenability.
  • chromium In dual-phase steels, the addition of chromium mainly improves the potential hardness increase. Chromium in the dissolved state shifts the perlite and bainite conversion towards longer times and at the same time lowers the martensite starting temperature.
  • a further important effect is that chromium considerably increases the tempering resistance and so in the hot-dip bath there is almost no loss of strength.
  • chromium is a carbide forming agent. Should chromium-iron-mixed carbides be present, the austenitising temperature must be selected, prior to hardening, to be high enough in order to dissolve chromium carbides. Otherwise, the increased number of nuclei can cause a deterioration in the potential hardness increase.
  • Chromium likewise tends to form oxides on the steel surface during the annealing treatment, as a result of which the hot-dip quality can be impaired.
  • the above-stated measures for setting the furnace regions during continuous hot-dip coating serve to reduce the formation of Cr oxides or Cr mixed oxides on the steel surface after annealing.
  • the chromium content is fixed to contents of 0.250 wt. % to 0.400 wt. %.
  • the chromium content is preferably in a range between ⁇ 0.260 wt. % to ⁇ 0.330 wt. %, in the case of end thicknesses of 1.00 to 2.00 mm inclusive, said chromium content is in a range between a 0.290 wt. % to ⁇ 0.360 wt. % and in the case of end thicknesses of 2.00 to 3.00 mm inclusive, it is in a range between a 0.320 wt. % to ⁇ 0.370 wt. %.
  • the chromium content is preferably in a range between ⁇ 0.260 wt. % to ⁇ 0.330 wt. %, in the case of a carbon equivalent CEV(IIW) of ⁇ 0.62%, in the case of end thicknesses of 1.00 to 2.00 mm inclusive, said chromium content is in a range between ⁇ 0.290 wt. % to ⁇ 0.360 wt. % in the case of a carbon equivalent CEV(IIW) of ⁇ 0.66% and in the case of end thicknesses of 2.00 to 3.00 mm inclusive, it is in a range between ⁇ 0.320 wt. % to ⁇ 0.370 wt. % in the case of a carbon equivalent CEV(IIW) of ⁇ 0.66%.
  • Chromium contents between ⁇ 0.250 wt. % to ⁇ 0.370 wt. % can be used in the case of end thicknesses of less than 0.50 mm and chromium contents between >0.370 wt. % to ⁇ 0.400 wt. % can be used in the case of end thicknesses of greater than 3.00 mm.
  • Molybdenum (Mo) the addition of molybdenum results, in a similar manner to the addition of chromium and manganese, in the Improvement of hardenability. The perlite and bainite conversion is shifted towards longer times and the martensite starting temperature is decreased. At the same time, molybdenum is a strong carbide forming agent which allows the production of finely distributed mixed carbides, inter alia also with titanium. Moreover, molybdenum considerably increases the tempering resistance and so no losses in strength are to be expected in the hot-dip bath. Molybdenum also acts by mixed crystal hardening but is less effective than manganese and silicon.
  • the content of molybdenum is set between more than 0.200 wt. % to 0.300 wt. %.
  • the Mo content is advantageously set to a range between more than 0.200 wt. % to 0.250 wt. %.
  • the alloy concept according to the invention has proven to be advantageous for the alloy concept according to the invention to have a total content of Mo+Cr of ⁇ 0.650 wt. %.
  • Copper the addition of copper can increase the tensile strength and the potential hardness increase. In conjunction with nickel, chromium and phosphorous, copper can form a protective oxide layer on the surface which can considerably reduce the corrosion rate.
  • copper can form, at the grain boundaries, noxious oxides which can produce negative effects particularly for hot-deformation processes. Therefore, the content of copper is fixed to ⁇ 0.050 wt. % and is thus limited to quantities which are unavoidable in steel production.
  • Vanadium (V) in the case of the present alloy concept, the content of vanadium of ⁇ 0.005 wt. % to ⁇ 0.020 wt. % is fixed, optimally limited to ⁇ 0.005 wt. % to ⁇ 0.015 wt. %.
  • Tin (Sn) since, in the case of the present alloy concept, an addition of tin is not necessary, the content of tin is fixed to ⁇ 0.040 wt. % and therefore limited to unavoidable quantities associated with steel.
  • Aluminium is generally added to the steel by alloying in order to bind the oxygen and nitrogen dissolved in the iron. Oxygen and nitrogen are thus converted into aluminium oxides and aluminium nitrides. These precipitations can effect grain refinement by increasing the nucleation sites and can thus increase the toughness properties and strength values.
  • Titanium nitrides have a lower enthalpy of formation and are formed at higher temperatures.
  • aluminium like silicon shifts the formation of ferrite towards shorter times and thus permits the formation of sufficient ferrite in the dual-phase steel. It also suppresses the formation of carbide and thus results in a delayed conversion of the austenite. For this reason, aluminium is also used as an alloy element in residual austenite steels (TRIP steels) in order to substitute a part of the silicon.
  • TRIP steels residual austenite steels
  • the aluminium content is limited to 0.010 wt. % to a maximum of 0.060 wt. % and is added for the purpose of killing the steel.
  • Niobium acts differently in steel. During hot-rolling on the production line, it delays the recrystallization by virtue of the formation of very finely distributed precipitations, whereby the nucleation site density is increased and a finer grain is produced after the conversion. The proportion of dissolved niobium also acts to inhibit recrystallization.
  • the precipitations act to increase strength in the final product. They can be carbides or carbonitrides. They are often mixed carbides, into which titanium is also incorporated. This effect begins from 0.005 wt. % and is most pronounced from 0.010 wt. % niobium. Moreover, the precipitations prevent the grain growth during the (partial) austenitisation in the hot-dip galvanizing. Above 0.060 wt. % niobium, no additional effect is to be expected. Contents of 0.025 wt. % to 0.045 wt. % have proven to be advantageous.
  • Boron (B) is an extremely effective alloying agent for achieving variable degrees of thinning by cold-rolling. Tests have surprisingly shown that the range for the addition of boron, which is very narrow according to the invention, has a pronounced effect with regard to the uniformity of the mechanical properties of the produced cold strips with a variable degree of thinning by cold-rolling in the subsequent processing. This pronounced effect initially results in the possibility of setting, instead of with a relatively constant degree of thinning by cold-rolling, defined characteristic value ranges after the process steps ( FIG. 8 a , 8 b or 8 c ) also with the material with variable degrees of thinning by cold-rolling on the basis of a master hot strip thickness or on the basis of a master cold strip thickness.
  • boron is an effective element for increasing hardenability which becomes effective even in very small quantities.
  • the martensite starting temperature remains unaffected thereby.
  • boron In order to become effective, boron must be present in a solid solution. Since it has a high affinity to nitrogen, the nitrogen must initially be removed, preferably by the stoichiometrically required quantity of titanium. By reason of its low solubility in iron, the dissolved boron preferably becomes attached to the austenite grain boundaries. At this location, it partially forms Fe—B carbides which are coherent and decrease the grain boundary energy. Both effects act in such a way as to delay the formation of ferrite and perlite and thus increase the hardenability of the steel.
  • the boron content for the alloy concept according to the invention is fixed to values of more than 0.0005 wt. % to 0.0010 wt. %, advantageously to values ⁇ 0.0009 wt. % or optimally to >0.0006 wt. % to ⁇ 0.0009 wt. %.
  • Nitrogen (N) can be both an alloy element and an associated element from steel production. Excessively high contents of nitrogen produce an increase in strength associated with a rapid loss of toughness as well as ageing effects.
  • N Nitrogen
  • titanium and niobium fine grain hardening can be achieved via titanium nitrides and niobium (carbo)nitrides. Moreover, coarse grain formation is suppressed during reheating prior to hot-rolling.
  • the N content is therefore fixed to values of a 0.0020 wt. % to ⁇ 0.0120 wt. %.
  • niobium and titanium For the total contents of niobium and titanium, contents of ⁇ 0.100 wt. % have proven to be advantageous and owing to the basic interchangeability of niobium and titanium up to a minimum niobium content of 0.005 wt. % and for cost reasons contents of ⁇ 0.090 wt. % have proven to be particularly advantageous.
  • total contents of ⁇ 0.102 wt. % have proven to be advantageous and total contents of ⁇ 0.092 wt. % have proven to be particularly advantageous. Higher contents no longer have the effect of providing improvement in terms of the invention.
  • Calcium (Ca) an addition of calcium in the form of calcium-silicon mixed compounds causes deoxidation and desulphurisation of the molten phase in steel production. For instance, reaction products are converted into slag and the steel is cleaned. According to the invention, the increased level of purity results in improved properties in the end product.
  • a Ca content of ⁇ 0.0010 wt. % to ⁇ 0.0060 wt. % is set. Contents of ⁇ 0.0030 wt. % have proven to be advantageous.
  • the annealing temperatures for the dual-phase microstructure to be achieved are between approximately 700 and 950° C. for the steel according to the invention so that, depending upon the temperature range, a partially austenitic (two-phase region) or a fully austenitic microstructure (austenite region) is achieved.
  • the continuously annealed and occasionally hot-dip-finished material can be manufactured in the temper-rolled (cold-post-rolled) or non-temper-rolled state and/or in the stretch-bend-straightened or non-stretch-bend-straightened state and also in the heat-treated state (ageing).
  • the steel strips consisting of the alloy composition according to the Invention are characterized during further processing by high edge crack insensitivity and a high bending angle.
  • the steel strips according to the invention have a delayed fracture free-state for at least 6 months whilst meet the requirements according to SEP 1970 for hole pull and hoop test pieces after provision by the steel producer,
  • the very small characteristic value differences of the steel strip longitudinally and transversely with respect to its rolling direction are advantageous for the subsequent material use.
  • the cutting of blanks from a strip can be performed independently of the rolling direction (e.g. transversely, longitudinally and diagonally or at an angle with respect to the rolling direction) and therefore the waste is minimized.
  • the hot strip is produced according to the invention with end rolling temperatures in the austenitic region above Ar3 and at reeling temperatures above the bainite starting temperature.
  • a blank is cut from a steel strip according to the invention which is then heated to a temperature above Ac3.
  • the heated blank is deformed into a component and is then hardened in a deforming tool or in air with optional subsequent tempering.
  • the steel according to the invention has the property that the hardening occurs even during cooling in stationary air so that separate cooling of the deforming tool can be omitted.
  • the microstructure of the steel is converted to the austenitic range by heating, preferably to temperatures over 950° C. under a protective gas atmosphere. During subsequent cooling in air or protective gas, a martensitic microstructure is formed for a high-strength component.
  • Subsequent tempering facilitates the reduction of intrinsic tensions in the hardened component.
  • the hardness of the component is reduced such that the required toughness values are achieved.
  • FIG. 1 shows (schematically) the process chain for the production of a strip consisting of the steel according to the invention
  • FIG. 2 shows (schematically) the time-temperature curve of the process steps of hot-rolling and cold-rolling and continuous annealing (with optional hot-dip finishing), as well as component manufacturing, optional quenching (air-hardening) and optional tempering by way of example for the steel according to the invention
  • FIG. 3 shows the chemical composition (examples 1 to 4) of the steel according to the invention
  • FIG. 4 a shows mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the hot-rolled state (HR),
  • FIG. 4 b shows mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the cold-rolled state (CR),
  • FIG. 5 a shows solidification behavior during cold-rolling of the steel according to the invention, characteristic values transversely to the rolling direction
  • FIG. 5 b shows solidification behavior during cold-rolling of the steel according to the invention, cold flow curve
  • FIG. 6 a shows mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the fine sheet state (HDG),
  • FIG. 6 b shows results of the hole expansion tests according to ISO 16630 and of the plate bending test according to VDA 238-100 on the steel according to the invention, in the fine sheet state (HDG),
  • FIG. 7 a shows mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the state HR, CR and HDG; example 1 (pre-strip thickness 40 mm),
  • FIG. 7 b shows mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the state HR, CR and HDG; example 2 (pre-strip thickness 45 mm),
  • FIG. 7 c shows mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the state HR, CR and HDG; example 3 (pre-strip thickness 50 mm),
  • FIG. 7 d shows mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the state HR, CR and HDG; example 4 (pre-strip thickness 55 mm),
  • FIG. 7 e shows mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the state HR, CR and HDG as an overview
  • FIG. 8 a shows method 1, temperature-time curves (annealing variants shown schematically),
  • FIG. 8 b shows method 2, temperature-time curves (annealing variants shown schematically),
  • FIG. 8 c shows method 3, temperature-time curves (annealing variants shown schematically).
  • FIG. 1 schematically illustrates the process chain for the production of a strip from the steel according to the invention.
  • the process routes possible in the invention are shown. Up until acid-cleaning, the process route is the same for all steels according to the invention, thereafter, deviating process routes are followed depending on the desired results.
  • the acid-cleaned hot strip can be cold-rolled and hot-dip finished with different degrees of thinning by rolling.
  • a soft annealed hot strip or soft annealed cold strip can also be cold-rolled and hot-dip finished.
  • Material can also optionally be processed without a hot-dip finishing procedure, i.e. only within the scope of continuous annealing with and without subsequent electrolytic galvanizing. From the optionally coated material a complex component can now be produced. Subsequently, a quenching process can optionally take place, such as e.g. air-hardening where the heat-treated component is cooled in the air. Optionally, a tempering step can conclude the thermal treatment of the component.
  • a quenching process can optionally take place, such as e.g. air-hardening where the heat-treated component is cooled in the air.
  • a tempering step can conclude the thermal treatment of the component.
  • FIG. 2 schematically illustrates the time-temperature curve of the process steps of hot rolling and continuous annealing of strips made from the alloy composition according to the invention.
  • the time- and temperature-dependent conversion for the hot rolling process and also for a heat treatment after cold-rolling, component manufacture, as well as optional quenching with optional tempering are shown.
  • FIG. 3 shows in examples 1 to 4 which come from a melt in order to exclude the analytical influence in this case, the alloy compositions of the steel according to the invention, depending upon the produced pre-strip thickness.
  • Cold strips having a cold strip desired thickness of 1.50 mm were produced from a hot strip desired thickness of 2.30 mm.
  • example 1 shows the alloy composition for a pre-strip thickness of 40 mm, example 2 for a pre-strip thickness of 45 mm, example 3 for a pre-strip thickness of 50, example 4 for a pre-strip having a thickness of 55 mm.
  • FIG. 4 shows the mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the hot-rolled state (HR, Hot Rolled) in FIG. 4 a and in the cold-rolled state (CR, Cold Rolled) in FIG. 4 b.
  • FIG. 5 shows the solidification behavior, via the mechanical characteristic values transversely to the rolling direction, during cold-rolling of the steel according to the invention, in a table in FIG. 5 a and in a graph as a cold flow curve in FIG. 5 b.
  • FIG. 6 shows the mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the fine sheet state (HDG, Hot Dipped Galvanized) in FIG. 6 a and the results of the hole expansion tests according to ISO 16630 and of the plate bending test according to VDA 238-100 in the fine sheet state (HDG) longitudinally and transversely to the rolling direction, as well as the corresponding products with the tensile strength, in FIG. 6 b.
  • FIG. 7 shows the mechanical characteristic values (transversely to the rolling direction) of the steel according to the invention in the state HR, CR and HDG using a pre-strip thickness of 40 mm in FIG. 7 a, 45 mm in FIG. 7 b, 50 mm in FIG. 7 c, 55 mm in FIG. 7 d and in FIG. 7 e as a summarizing graphical overview.
  • FIG. 8 schematically illustrates three variations of the temperature-time curves according to the invention in the case of annealing treatment and cooling and of austenitisation conditions which differ in each case.
  • Method 1 presents the annealing and cooling of the produced steel strip cold-rolled to the end thickness in a continuous annealing installation.
  • the strip is heated to a temperature in the range of about 700 to 950° C. (Ac1 to Ac3).
  • the annealed steel strip is then cooled from the annealing temperature at a cooling rate between approximately 15 and 100° C./s to an intermediate temperature (ZT) of approximately 200 to 250° C.
  • ZT intermediate temperature
  • This schematic illustration does not show a second Intermediate temperature (approximately 300 to 500° C.).
  • the steel strip is then cooled in air at a cooling rate between approximately 2 and 30° C./s until room temperature (RT) is reached or cooling at a cooling rate between approximately 15 and 100° C./s is maintained until room temperature is reached.
  • RT room temperature
  • Method 2 ( FIG. 8 b ) shows the process according to method 1 but the cooling of the steel strip is briefly interrupted during passage through the hot-dipping vessel for the purposes of a hot-dip finishing procedure, in order then to continue the cooling at a cooling rate between approximately 15 and 100° C./s to an intermediate temperature of approximately 200 to 250° C.
  • the steel strip is then cooled in air at a cooling rate between approximately 2 and 30° C./s until reaching room temperature.
  • Method 2 corresponds to annealing, e.g. hot-dip galvanizing with combined direct fired furnace and radiant tube furnace, as depicted in FIG. 8 b.
  • Method 3 ( FIG. 8 c ) likewise shows the process according to method 1 in a hot-dip finishing procedure but cooling of the steel strip is Interrupted by a short pause (approximately 1 to 20 s) at an intermediate temperature in the range of approximately 200 to 400° C. and heating is effected to the temperature (ST) required for the hot-dip finishing procedure (approximately 400 to 470° C.).
  • ST temperature required for the hot-dip finishing procedure
  • the steel strip is then cooled to an intermediate temperature of approximately 200 to 250° C.
  • the subsequent cooling in air of the steel strip takes place at a cooling rate of approximately 2 and 30° C./s until room temperature is reached.
  • Method 3 corresponds e.g. to a process being carried out in a continuous annealing installation, as depicted in FIG. 8 c .
  • reheating of the steel is optionally achieved directly prior to the zinc bath.
  • the decreases from the slab with respect to the pre-strip vary in the subsequent examples from 78% to 84% for subsequent hot-rolling to a hot strip thickness of 2.30 mm with corresponding decreases of 94% to 96%.
  • the cold strip desired thickness of 1.50 mm is achieved with a degree of thinning by cold-rolling of 35%. It is impressively shown that both for very low pre-strip thicknesses and also for greater pre-strip thicknesses, and the range therebetween, relatively uniform values provided with a conventional fluctuation range are achieved for the tensile strength and yield strength, transversely to the rolling direction.
  • the steel according to the invention similarly permits the use of a master hot strip thickness with varying degrees of thinning by cold-rolling, as well as the use of master cold strip thicknesses without influencing the previous fact.
  • variable pre-strip thicknesses can significantly influence the cold-rollability, such as the necessary rolling forces, without the higher hot strip strength (HR), and higher cold strip strength (CR), with a decreasing pre-strip thickness, leading to considerable fluctuations in the fine sheet (HDG):
  • a steel according to the invention comprising 0.104% C; 0.443% Si; 2.178% Mn; 0.012% P; 0.0004% S; 0.0045% N; 0.038 Al; 0.330% Cr; 0.208% Mo; 0.0372% Ti; 0.0332% Nb; 0.007% V; 0.0006% B; 0.0020% Ca; 0.027% Cu; 0.047% Ni; 0.008% Sn; 0.00038% H according to method 3 corresponding to FIG.
  • the slab material of 250 mm was rolled prior to the hot-rolling in the pre-line into a pre-strip of 40 mm in a reversing manner with a percentage decrease of 84% and subsequently hot-rolled in the hot wide strip line at a desired end rolling temperature of 910° C. with a decrease of 94% and reeled at a desired reeling temperature of 650° C. with a master hot strip thickness of 2.30 mm and cold rolled after acid-cleaning without additional heat treatment (such as e.g. batch-type annealing) to 1.50 mm in one pass (degree of thinning by cold-rolling 35%).
  • additional heat treatment such as e.g. batch-type annealing
  • the yield strength ratio Re/Rm in the transverse direction was 66%.
  • the yield strength ratio Re/Rm in the transverse direction was 77%.
  • Alloy composition in wt. % A steel according to the invention comprising 0.104% C; 0.443% Si; 2.178% Mn; 0.012% P; 0.0004% S; 0.0045% N; 0.038 Al; 0.330% Cr; 0.208% Mo; 0.0344% Ti; 0.0372% Nb; 0.007% V; 0.0006% B; 0.0020% Ca; 0.027% Cu; 0.047% Ni; 0.008% Sn; 0.00038% H according to method 3 corresponding to FIG.
  • the slab material of 250 mm was rolled prior to the hot-rolling in the pre-line into a pre-strip of 45 mm in a reversing manner with a percentage decrease of 82% and subsequently hot-rolled in the hot wide strip line at a desired end rolling temperature of 910° C. with a decrease of 95% and reeled at a desired reeling temperature of 650° C. with a master hot strip thickness of 2.30 mm and cold rolled after acid-cleaning without additional heat treatment (such as e.g. batch-type annealing) to 1.50 mm in one pass (degree of thinning by cold-rolling 35%).
  • additional heat treatment such as e.g. batch-type annealing
  • the yield strength ratio Re/Rm in the transverse direction was 67%.
  • the yield strength ratio Re/Rm in the transverse direction was 70%.
  • Alloy composition in wt. % A steel according to the invention comprising 0.104% C; 0.443% Si; 2.178% Mn; 0.012% P; 0.0004% S; 0.0045% N; 0.038 Al; 0.330% Cr; 0.208% Mo; 0.0344% Ti; 0.0372% Nb; 0.007% V; 0.0006% B; 0.0020% Ca; 0.027% Cu; 0.047% Ni; 0.008% Sn; 0.00038% H according to method 3 corresponding to FIG.
  • the slab material of 250 mm was rolled prior to the hot-rolling in the pre-line into a pre-strip of 50 mm in a reversing manner with a percentage decrease of 80% and subsequently hot-rolled in the hot wide strip line at a desired end rolling temperature of 910° C. with a decrease of 96% and reeled at a desired reeling temperature of 650° C. with a master hot strip thickness of 2.30 mm and cold rolled after acid-cleaning without additional heat treatment (such as e.g. batch-type annealing) to 1.50 mm in one pass (degree of thinning by cold-rolling 35%).
  • additional heat treatment such as e.g. batch-type annealing
  • the yield strength ratio Re/Rm in the transverse direction was 65%.
  • the yield strength ratio Re/Rm in the transverse direction was 69%.
  • Alloy composition in wt. % A steel according to the invention comprising 0.104% C; 0.443% Si; 2.178% Mn; 0.012% P; 0.0004% S; 0.0045% N; 0.038 Al; 0.330% Cr; 0.208% Mo; 0.0344% TI; 0.0372% Nb; 0.007% V; 0.0006% B; 0.0020% Ca; 0.027% Cu; 0.047% Ni; 0.008% Sn; 0.00038% H according to method 3 corresponding to FIG.
  • the slab material of 250 mm was rolled prior to the hot-rolling in the pre-line into a pre-strip of 55 mm in a reversing manner with a percentage decrease of 78% and subsequently hot-rolled in the hot wide strip line at a desired end rolling temperature of 910° C. with a decrease of 96% and reeled at a desired reeling temperature of 650° C. with a master hot strip thickness of 2.30 mm and cold rolled after acid-cleaning without additional heat treatment (such as e.g. batch-type annealing) to 1.50 mm in one pass (degree of thinning by cold-rolling 35%).
  • additional heat treatment such as e.g. batch-type annealing
  • the yield strength ratio Re/Rm in the transverse direction was 66%.
  • the yield strength ratio Re/Rm in the transverse direction was 70%.
  • the invention has been described above with the aid of fine sheet steel sheets with an end thickness to be achieved of 1.50 mm in the thickness range of 0.50 to 3.00 mm. It is also possible, if required, to produce end thicknesses in the range of 0.10 to 4.00 mm.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
US16/652,933 2017-10-06 2018-09-27 Ultrahigh strength multiphase steel and method for producing a steel strip from said multiphase steel Abandoned US20200263283A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
DE102017123236.2 2017-10-06
DE102017123236.2A DE102017123236A1 (de) 2017-10-06 2017-10-06 Höchstfester Mehrphasenstahl und Verfahren zur Herstellung eines Stahlbandes aus diesem Mehrphasenstahl
PCT/EP2018/076307 WO2019068560A1 (de) 2017-10-06 2018-09-27 Höchstfester mehrphasenstahl und verfahren zur herstellung eines stahlbandes aus diesem mehrphasenstahl

Publications (1)

Publication Number Publication Date
US20200263283A1 true US20200263283A1 (en) 2020-08-20

Family

ID=63713874

Family Applications (1)

Application Number Title Priority Date Filing Date
US16/652,933 Abandoned US20200263283A1 (en) 2017-10-06 2018-09-27 Ultrahigh strength multiphase steel and method for producing a steel strip from said multiphase steel

Country Status (7)

Country Link
US (1) US20200263283A1 (de)
EP (1) EP3692178B1 (de)
KR (1) KR20200063167A (de)
CN (1) CN111247258B (de)
DE (1) DE102017123236A1 (de)
RU (1) RU2742998C1 (de)
WO (1) WO2019068560A1 (de)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20220281393A1 (en) * 2019-12-03 2022-09-08 Bfc Fahrzeugteile Gmbh Metal band
WO2023148294A1 (de) * 2022-02-03 2023-08-10 STG Stanztechnik GmbH & Co. KG Verstärkungsband für einen formkörper aus einer spritzfähigen formmasse sowie formkörper mit einem derartigen verstärkungsband
WO2024105429A1 (en) * 2022-11-14 2024-05-23 Arcelormittal High toughness press-hardened steel part and method of manufacturing the same
WO2024105428A1 (en) * 2022-11-14 2024-05-23 Arcelormittal High toughness press-hardened steel part and method of manufacturing the same

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102020110319A1 (de) * 2020-04-15 2021-10-21 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung eines Stahlbandes mit einem Mehrphasengefüge und Stahlband hinzu

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19610675C1 (de) 1996-03-19 1997-02-13 Thyssen Stahl Ag Mehrphasenstahl und Verfahren zu seiner Herstellung
DE10037867A1 (de) 1999-08-06 2001-06-07 Muhr & Bender Kg Verfahren zum flexiblen Walzen eines Metallbandes
TWI248977B (en) * 2003-06-26 2006-02-11 Nippon Steel Corp High-strength hot-rolled steel sheet excellent in shape fixability and method of producing the same
US7442268B2 (en) * 2004-11-24 2008-10-28 Nucor Corporation Method of manufacturing cold rolled dual-phase steel sheet
US7608155B2 (en) * 2006-09-27 2009-10-27 Nucor Corporation High strength, hot dip coated, dual phase, steel sheet and method of manufacturing same
DE102006054300A1 (de) * 2006-11-14 2008-05-15 Salzgitter Flachstahl Gmbh Höherfester Dualphasenstahl mit ausgezeichneten Umformeigenschaften
MX2008016192A (es) * 2007-03-30 2009-03-09 Sumitomo Metal Ind Acero de baja aleacion para accesorios tubulares para campos petroleros y tuberia de acero sin costuras.
PL2028282T3 (pl) 2007-08-15 2012-11-30 Thyssenkrupp Steel Europe Ag Stal dwufazowa, płaski wyrób wytworzony ze stali dwufazowej i sposób wytwarzania płaskiego wyrobu
EP2031081B1 (de) 2007-08-15 2011-07-13 ThyssenKrupp Steel Europe AG Dualphasenstahl, Flachprodukt aus einem solchen Dualphasenstahl und Verfahren zur Herstellung eines Flachprodukts
JP5438302B2 (ja) * 2008-10-30 2014-03-12 株式会社神戸製鋼所 加工性に優れた高降伏比高強度の溶融亜鉛めっき鋼板または合金化溶融亜鉛めっき鋼板とその製造方法
JP4924730B2 (ja) * 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
EP2439291B1 (de) * 2010-10-05 2013-11-27 ThyssenKrupp Steel Europe AG Mehrphasenstahl, aus einem solchen Mehrphasenstahl hergestelltes kaltgewalztes Flachprodukt und Verfahren zu dessen Herstellung
DE102012002079B4 (de) * 2012-01-30 2015-05-13 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung eines kalt- oder warmgewalzten Stahlbandes aus einem höchstfesten Mehrphasenstahl
DE102012002642B4 (de) * 2012-02-08 2013-08-14 Salzgitter Flachstahl Gmbh Warmband zur Herstellung eines Elektroblechs und Verfahren hierzu
CN104245971B (zh) * 2012-03-30 2017-09-12 奥钢联钢铁有限责任公司 高强度冷轧钢板和生产该钢板的方法
DE102013013067A1 (de) * 2013-07-30 2015-02-05 Salzgitter Flachstahl Gmbh Siliziumhaltiger, mikrolegierter hochfester Mehrphasenstahl mit einer Mindestzugfestigkeit von 750 MPa und verbesserten Eigenschaften und Verfahren zur Herstellung eines Bandes aus diesem Stahl
MX2016016129A (es) * 2014-06-06 2017-03-28 Arcelormittal Hoja de acero galvanizada multifasica de alta resistencia, metodo de produccion y uso.
DE102014017273A1 (de) * 2014-11-18 2016-05-19 Salzgitter Flachstahl Gmbh Hochfester lufthärtender Mehrphasenstahl mit hervorragenden Verarbeitungseigenschaften und Verfahren zur Herstellung eines Bandes aus diesem Stahl
DE102014017275A1 (de) * 2014-11-18 2016-05-19 Salzgitter Flachstahl Gmbh Hochfester lufthärtender Mehrphasenstahl mit hervorragenden Verarbeitungseigenschaften und Verfahren zur Herstellung eines Bandes aus diesem Stahl
DE102014017274A1 (de) 2014-11-18 2016-05-19 Salzgitter Flachstahl Gmbh Höchstfester lufthärtender Mehrphasenstahl mit hervorragenden Verarbeitungseigenschaften und Verfahren zur Herstellung eines Bandes aus diesem Stahl
DE102015111177A1 (de) * 2015-07-10 2017-01-12 Salzgitter Flachstahl Gmbh Höchstfester Mehrphasenstahl und Verfahren zur Herstellung eines kaltgewalzten Stahlbandes hieraus

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20220281393A1 (en) * 2019-12-03 2022-09-08 Bfc Fahrzeugteile Gmbh Metal band
WO2023148294A1 (de) * 2022-02-03 2023-08-10 STG Stanztechnik GmbH & Co. KG Verstärkungsband für einen formkörper aus einer spritzfähigen formmasse sowie formkörper mit einem derartigen verstärkungsband
WO2024105429A1 (en) * 2022-11-14 2024-05-23 Arcelormittal High toughness press-hardened steel part and method of manufacturing the same
WO2024105428A1 (en) * 2022-11-14 2024-05-23 Arcelormittal High toughness press-hardened steel part and method of manufacturing the same
WO2024105531A3 (en) * 2022-11-14 2024-07-11 Arcelormittal High toughness press-hardened steel part and method of manufacturing the same
WO2024105535A3 (en) * 2022-11-14 2024-07-11 Arcelormittal High toughness press-hardened steel part and method of manufacturing the same

Also Published As

Publication number Publication date
WO2019068560A1 (de) 2019-04-11
EP3692178B1 (de) 2022-06-08
EP3692178A1 (de) 2020-08-12
KR20200063167A (ko) 2020-06-04
CN111247258A (zh) 2020-06-05
CN111247258B (zh) 2022-04-26
RU2742998C1 (ru) 2021-02-12
DE102017123236A1 (de) 2019-04-11

Similar Documents

Publication Publication Date Title
RU2684655C1 (ru) Сверхпрочная многофазная сталь и способ производства холоднокатаной стальной полосы из нее
US10612113B2 (en) Micro-alloyed high-strength multi-phase steel containing silicon and having a minimum tensile strength of 750 MPA and improved properties and method for producing a strip from said steel
CN110291217B (zh) 高强度钢板及其制造方法
US20150337408A1 (en) High strength multi-phase steel, and method for producing a strip from said steel
EP2703512A1 (de) Hochfeste stahlplatte mit hervorragender formbarkeit und materialstabilität sowie herstellungsverfahren dafür
US10640855B2 (en) High-strength air-hardening multiphase steel having excellent processing properties, and method for manufacturing a strip of said steel
RU2615957C2 (ru) Высокопрочная многофазная сталь и способ изготовления полосы из этой стали
CN111433380A (zh) 高强度镀锌钢板及其制造方法
US10626478B2 (en) Ultra high-strength air-hardening multiphase steel having excellent processing properties, and method for manufacturing a strip of said steel
US20200263283A1 (en) Ultrahigh strength multiphase steel and method for producing a steel strip from said multiphase steel
CN114645219A (zh) 高强度镀锌钢板及其制造方法
RU2682913C2 (ru) Сверхвысокопрочная, закаливающаяся на воздухе, многофазная сталь, обладающая отличными технологическими характеристиками, и способ получения полос указанной стали
CA2786381C (en) High-strength galvanized steel sheet having excellent formability and spot weldability and method for manufacturing the same
KR102708307B1 (ko) 고강도 열간 압연 또는 냉간 압연 및 어닐링된 강 및 그 제조 방법
US10570476B2 (en) High-strength steel sheet and production method therefor
EP3276021B1 (de) Hochfestes stahlblech und herstellungsverfahren dafür
KR101889181B1 (ko) 굽힘성 및 신장플랜지성이 우수한 고장력강 및 이의 제조방법
JP2003193189A (ja) 深絞り性に優れた複合組織型高張力溶融亜鉛めっき鋼板およびその製造方法
US12098441B2 (en) Flat steel product having improved processing properties
JP2005220417A (ja) 伸びフランジ成形性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
KR20230129177A (ko) 코일링 온도에 영향을 받는 냉간 압연 스트립 또는강
KR20230129244A (ko) 개선된 아연 접착력을 갖는 아연 또는 아연-합금 코팅된스트립 또는 강

Legal Events

Date Code Title Description
AS Assignment

Owner name: SALZGITTER FLACHSTAHL GMBH, GERMANY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:SCHULZ, THOMAS;REEL/FRAME:052288/0804

Effective date: 20200316

STPP Information on status: patent application and granting procedure in general

Free format text: APPLICATION DISPATCHED FROM PREEXAM, NOT YET DOCKETED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION