US20200198000A1 - Method and apparatus for shaft diameter enlargement - Google Patents
Method and apparatus for shaft diameter enlargement Download PDFInfo
- Publication number
- US20200198000A1 US20200198000A1 US16/623,629 US201816623629A US2020198000A1 US 20200198000 A1 US20200198000 A1 US 20200198000A1 US 201816623629 A US201816623629 A US 201816623629A US 2020198000 A1 US2020198000 A1 US 2020198000A1
- Authority
- US
- United States
- Prior art keywords
- shaft
- intermediate portion
- holders
- temperature
- shaft diameter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- The present invention relates to a shaft diameter enlarging method and a shaft diameter enlarging apparatus.
- A shaft with a large-diameter portion at an intermediate portion of the shaft may be provided by cutting a thick shaft, by a combination of plastic working such as forging and finishing by a cutting or the like, or by joining an additional member on the shaft by welding. However, cutting takes a lot of efforts, and is uneconomical due to a lot of waste of material. Further, it is difficult to form a large-diameter portion at an intermediate portion when a workpiece is long-sized. With the method of joining the additional member on the workpiece by welding, there is effect of welding heat.
- A shaft diameter enlarging method is a solution to the above problems. With the shaft diameter enlarging method, an intermediate portion of a shaft is enlarged by applying a rotation, compression force, and bending to the shaft. In this way, a large-diameter portion is easily formed at the intermediate portion of the shaft, and there is no need for cutting or welding.
- The shaft diameter enlargement will be described in detail. A linear shaft is held by a pair of holders arranged with a gap provided between the holders. Then, with a rotation being applied about the axis of the shaft, at least one of the holders is moved in the direction toward the other holder, and one of the holders is biased gradually in a direction intersecting an axial line. Accordingly, the compression force and the bending force is applied to the shaft under a condition in which compression stress continuously acts at an outer side of the bending, whereby the shaft between the holders is plastically deformed in a radial direction. Subsequently, the bias of the holder is recovered gradually while maintaining the condition in which the compression stress continuously acts at the outer side the bending. In this way, the intermediate portion of the shaft is enlarged.
- When applying the bending and the rotation on the shaft, the rotation is performed while applying the compression force, and the bending is performed so as to obtain a desired shape. Thereafter, a bend restoration is performed, and the compression and the rotation are stopped. Thus, when the material of the shaft is a high strength steel or a large axial steel material, high compression force is required, and it is inevitable that an apparatus for performing the shaft diameter enlarging method on the shaft become large-sized. If the compression force is low, the number of rotations for shaft diameter enlargement for obtaining a desired shape increases, so that it takes much time. Further, the enlargement rate (the outer diameter of the enlarged intermediate portion of the shaft divided by the diameter of the original shaft) is limited to be about two times at the maximum, and therefore, applicable components are limited.
- According to a first related art shaft diameter enlarging method, deformation resistance of a shaft is reduced by heating the shaft before or during the shaft diameter enlargement (see, e.g., JP2005-088066A). With this related art, the intermediate portion of the shaft can be enlarged by smaller compression force, and the size of apparatus is prevented from becoming large. Further, since the plastic deformability of the shaft is improved, and the enlargement rate can be increased.
- In a second related art shaft diameter enlarging method, a shaft is heated to a temperature above the blue brittleness range, in view of the fact that, if the shaft is heated to be in the blue brittleness range, the shaft is hardened due to the blue brittleness effect so that the deformation resistance becomes high, in which case a desired enlarged portion may not be obtained, and there may be a defect such as a crack in the shaft (see, e.g., JP2007-167882A). As an example, in a case where the shaft is made of structural carbon steel JIS-S45C, when the temperature of the shaft is about 400° C. or below, due to the effect of the blue brittleness, the enlargement rate is not affected by the heating of the shaft. When the shaft is heated to 580° C. or above, more than double enlargement rate can be obtained, and a cracking damage can be suppressed.
- Similarly to the shaft diameter enlargement, forging involves a plastic deformation of a workpiece. The workpiece is typically heated to 700° C. to 850° C. in so-called warm forging, and the workpiece is typically heated to 950° C. or above in hot forging (including sub hot forging). Thus, like the forging, it may be conceivable also with regard to the shaft diameter enlargement in which the shaft is heated to 580° C. or above, to heat the shaft to a warm temperature range (700° C. to 850° C.) or a hot temperature range (950° C. or above). However, in the shaft diameter enlargement, the shaft is subject to the rotation, the compression force, and the bending, and so that load also acts on the holders holding the shaft. Further, the holders are typically made of tool steel such as die steel and high speed tool steel. The tempering temperature range of such tool steels is about 500° C. to 580° C. Furthermore, the time during which the shaft contacts with the holders is relatively longer than the time during which the workpiece contacts with a die in forging. Thus, in a case where the shaft is heated to the warm temperature range or the hot temperature range, the hardness of the holders may become lower due to tempering. When the hardness of the holders is lowered, the durability of the holders against repeated use is lowered so that the lifetime of the holders may be shortened.
- Illustrative aspects of the present invention provide a shaft diameter enlarging method and a shaft diameter enlarging apparatus which can increase an enlargement rate, prevent a crack caused by enlargement, and reduce running cost.
- According to an illustrative aspect of the present invention, a shaft diameter enlarging method for enlarging an intermediate portion of a shaft is provided. The shaft diameter enlarging method includes holding the shaft by a pair of holders with a gap between the pair of holders in an axial direction of the shaft, applying compression force in the axial direction to the intermediate portion arranged between the pair of holders, and applying alternating load in a direction intersecting the axial direction to the intermediate portion to enlarge the intermediate portion. When enlarging the intermediate portion, a temperature of the intermediate portion is set to be above a blue brittleness temperature range of the shaft, and a temperature of the holders is set to be below a tempering temperature range of the holders.
- According to another illustrative aspect of the present invention, a shaft diameter enlarging apparatus includes a pair of holders configured to hold a shaft with a gap between the pair of holders in an axial direction of the shaft, a presser configured to apply compression force in the axial direction to the intermediate portion arranged between the pair of holders, an alternating load generator configured to apply alternating load in a direction intersecting the axial direction to the intermediate portion to enlarge the intermediate portion, and a heating device configured to heat at least a portion of the shaft such that, during a period in which the compression force and the alternating load are applied to the intermediate portion of the shaft, a temperature of the intermediate portion is above a blue brittleness temperature range of the shaft, and a temperature of the pair of holders holding the shaft is below a tempering temperature range of the holders.
-
FIG. 1 is a schematic view illustrating an example of a shaft diameter enlarging apparatus according to an embodiment of the present invention. -
FIG. 2 is a graph showing a relation between a temperature and a tensile strength in various steel materials having different carbon content. -
FIG. 3A is a schematic view illustrating an example of a shaft diameter enlarging method using the shaft diameter enlarging apparatus ofFIG. 1 . -
FIG. 3B is another schematic view illustrating the example of the shaft diameter enlarging method. -
FIG. 3C is another schematic view illustrating the example of the shaft diameter enlarging method. -
FIG. 3D is another schematic view illustrating the example of the shaft diameter enlarging method. -
FIG. 3E is another schematic view illustrating the example of the shaft diameter enlarging method. -
FIG. 4 is a schematic view illustrating a shaft diameter enlarging method according to another embodiment of the present invention. -
FIG. 5 is a schematic view illustrating a shaft diameter enlarging method according to another embodiment of the present invention. -
FIG. 6 is a schematic view illustrating a shaft diameter enlarging method according to another embodiment of the present invention. -
FIG. 7 is a schematic view illustrating a shaft diameter enlarging method according to another embodiment of the present invention. -
FIG. 8 is a graph showing a counted number of rotations required to reach a predetermined enlargement rate and a result of checking of a presence of a crack for each test example. -
FIG. 9 is a graph showing a result of an evaluation of an elliptic amount for each test example. -
FIG. 10 is a schematic view illustrating an example of a heating device of the shaft diameter enlarging apparatus. -
FIG. 11 is a schematic view illustrating another example of the heating device of the shaft diameter enlarging apparatus. -
FIG. 12 is a schematic view illustrating another example of the heating device of the shaft diameter enlarging apparatus. -
FIG. 13 is a schematic view illustrating another example of the heating device of the shaft diameter enlarging apparatus. -
FIG. 1 illustrates an example of a shaft diameter enlarging apparatus according to an embodiment of the present invention. - A shaft
diameter enlarging apparatus 1 illustrated inFIG. 1 is configured such that, when a pair ofholders 2, 3 holding a shaft W with a gap in an axial direction of the shaft W are moved toward to each other in the axial direction of the shaft W, compression force in the axial direction is applied to the intermediate portion of the shaft W arranged between the pair ofholders 2, 3, and an alternating load in a direction intersecting with the axial direction is applied to the intermediate portion of the shaft W arranged between the pair ofholders 2, 3, so that the intermediate portion of the shaft W is enlarged while being compressed in the axial direction. - The
holder 2 is supported by a support base 4 to be movable along a reference line A in which the shaft W is arranged, and is moved by a translational drive unit 5 (an example of a presser). When theholder 2 is moved toward the holder 3 along the reference line A, the compression force in the axial direction is loaded to the intermediate portion of the shaft W held by theholders 2, 3, so as to compress the intermediate portion of the shaft W. - In the shaft
diameter enlarging apparatus 1, when the shaft W is rotated by bending the intermediate portion of the shaft W by the bending angle, the alternating load in the direction intersecting with the axial direction acts on the intermediate portion of the shaft W. The holder 3 is tilted with respect to the reference line A by a tilt drive unit 6 (an example of an alternating load generator), so as to bend the intermediate portion of the shaft W by the bending angle. Further, in a state in which the intermediate portion of the shaft W is bent by the bending angle, the holder 3 is rotated by a rotary drive unit 7 (an example of the alternating load generator). The shaft W held by the holder 3 is rotated according to the rotation of the holder 3, and theholder 2 holding the shaft W is also rotated in response to the holder 3 and the shaft W. - A
controller 8 controls the translational drive unit 5, the tilt drive unit 6, and therotary drive unit 7 based on set conditions. - The intermediate portion of the shaft W is heated before the shaft diameter enlargement and/or during the shaft diameter enlargement. Only the intermediate portion may be heated, or the entire shaft W including the intermediate portion may be heated.
- The shaft W can be heated by using a furnace such as a combustion furnace and an electric furnace. Alternatively, resistance heating or induction heating may be used to heat the shaft W. The resistance heating is performed by attaching an electrode to a workpiece in a contacting manner to directly pass electric current through the workpiece, so that the workpiece is heated by Joule heat. The induction heating is performed by arranging a heating coil connected to an AC power supply close to a workpiece, so that alternating flux generated by the heating coil is cross-linked with the workpiece to generate eddy current on the surface of the workpiece and to heat the surface of the workpiece by Joule heat.
- In the resistance heating, the electrode is brought into contact with the intermediate portion of the shaft W held by the pair of
holders 2, 3, so as to partially heat the intermediate portion. In the induction heating, the heating coil is arranged to be close to the intermediate portion of the shaft W held by the pair ofholders 2, 3, so as to partially heat the intermediate portion. Both heating methods can be suitably used for heating during the shaft diameter enlargement. Particularly, it is preferable to use the induction heating by which the shaft W can be heating in a non-contacting manner. - When enlarging the intermediate portion of the shaft W, the temperature of the intermediate portion of the shaft W is set to be above the blue brittleness range of the shaft W and below the tempering temperature range of the
holders 2, 3. -
FIG. 2 shows a relation between a temperature and a tensile strength (stress) of various steel materials in which the carbon content is different. - A graph shown in
FIG. 2 is from “the Japan Institute of Metals and Materials, the Iron and Steel Institute of Japan, ‘Handbook of Steel Materials’, first edition, Maruzen Inc., June 1967, p. 552”. Basically, the tensile strength of the steel material reduces in accordance with an increase of the temperature of the steel material. This indicates that in the shaft diameter enlargement, the deformation resistance at the time of enlarging the intermediate portion of the shaft W can be reduced by increasing the temperature of the shaft W. However, in the blue brittleness range (in the illustrated example, the temperature range of about 200° C. to 400° C.), the tensile strength increases in accordance with the increase of the temperature. In the temperature range above the blue brittleness range, the tensile strength reduces again in accordance with the increase of the temperature. - Accordingly, the temperature of the intermediate portion of the shaft W is set to be above the blue brittleness range of the shaft W. This makes it possible to reduce the deformation resistance at the time of enlarging the intermediate portion of the shaft W and to increase the enlargement rate. In addition, it is possible to prevent a crack resulting from the enlargement.
- A solid round rod or a hollow round rod which is made of a steel material such as carbon steel for mechanical structure (e.g., JIS-S45C) or alloy steel for mechanical structure (e.g., JIS-SCr420H) and has a cross-sectional circular shape is used as the shaft W. The upper limit temperature of the blue brittleness range of JIS-S45C is less than 400° C., and the upper limit temperature of the blue brittleness range of JIS-SCr420H is also less than 400° C. Therefore, the temperature of the intermediate portion of the shaft W is preferably 400° C. or more.
- In the temperature range above the blue brittleness range, the tensile strength monotonously reduces in accordance with an increase of the temperature of the intermediate portion of the shaft W. Therefore, from a viewpoint of increasing the enlargement rate and preventing a crack resulting from the enlargement, there is no upper limit for the temperature of the intermediate portion of the shaft W. However, the hardness of the
holders 2, 3 is lowered by tempering when the temperature of theholders 2, 3 is increased by the thermal conduction from the shaft W to theholders 2, 3 such that the temperature of theholders 2, 3 reaches the tempering temperature range. In view of this, the temperature of theholders 2, 3 is set to be below the tempering temperature range of theholders 2, 3. Accordingly, it is possible to prevent the hardness of theholders 2, 3 from being lowered by tempering and to extend the lifetime of theholders 2, 3. - Generally, the
holders 2, 3 are made of tool steel such as the die steel (e.g., JIS-SKD61) or the high speed tool steel (e.g., JIS-SKH51). The tempering temperature range of JIS-SKD61 is 500° C. to 560° C., and the tempering temperature range of JIS-SKH51 is 560° C. to 580° C. Therefore, the temperature of theholders 2, 3 is preferably below 580° C. more preferably below 500° C. - Considering the temperature increase of the
holders 2, 3 due to the thermal conduction from the shaft W and also the thermal conduction loss, the upper limit temperature of the intermediate portion of the shaft W can be set to be slightly above the tempering temperature range of theholders 2, 3. For example, the upper limit temperature of the intermediate portion of the shaft W may be set to 700° C. with respect a typical tempering temperature range (500° C. to 580° C.) of theholders 2, 3. Preferably, the upper limit temperature of the intermediate portion of the shaft W is below the tempering temperature range of theholders 2, 3, so that it is possible to ensure that the temperature of theholders 2, 3 does not reach the tempering temperature range. - An example of a shaft diameter enlarging method using the shaft
diameter enlarging apparatus 1 will be described with reference toFIGS. 3A to 3E . - In this example, as illustrated in
FIG. 3A , the intermediate portion Wa of the shaft W is heated by a heating device 9 before the shaft diameter enlargement. The entire shaft W may be heated. Only the intermediate portion Wa of the shaft W or the entire shaft W is heated such that the temperature of the intermediate portion Wa exceeds the blue brittleness range of the shaft W at least at the time of starting the shaft diameter enlargement, in consideration of heat dissipation after the heating, preferably such that the temperature of the intermediate portion Wa is maintained above the blue brittleness range of the shaft W until the entire process of the shaft diameter enlargement is completed, and also in consideration of thermal conduction from the shaft W to theholders 2, 3 such that theholders 2, 3 holding the shaft W are maintained below the tempering temperature range. - Next, as illustrated in
FIG. 3B , the shaft W is held by theholders 2, 3. Anaxial length 14 of the intermediate portion Wa of the unprocessed shaft W is appropriately set according to the axial length L and the outer diameter D of the enlarged intermediate portion Wa in the relation with D0 in which the outer diameter of the intermediate portion Wa is set as D0. - Next, as illustrated in
FIG. 3C , in a state in which the shaft W is held by theholders 2, 3, theholder 2 is moved in a translational manner by the translational drive unit 5 (seeFIG. 1 ) along the reference line A, and the compression force in the axial direction is applied to the intermediate portion Wa of the shaft W. In addition, the holder 3 is inclined by the tilt drive unit 6 (seeFIG. 1 ) with respect to the reference line A, and is rotated by the rotary drive unit 7 (seeFIG. 1 ). - The shaft W held by the
holders 2, 3 is bent about a bending center O of the intermediate portion Wa on the reference line A, and is rotated about a central axis. The alternating load is applied to the bent intermediate portion Wa in the direction intersecting with the axial direction of the shaft W according to the bending and the rotation of the shaft W. A bending angle θ of the intermediate portion Wa, that is, the inclination angle with respect to the reference line A of the holder 3 is set to an angle in which the bending of the shaft W is within the deformation of the elastic limit. The bending angle is varied according to the elastic limit of the material of the shaft W, but typically is about 2° to 4°. - Next, as illustrated in
FIG. 3D , in the intermediate portion Wa of the shaft W, the inside of the bent portion is swelled by the plastic flow. Further, in accordance with the compression and the rotation of the shaft W, the swelling caused by the plastic flow grows over the entire circumference, and the intermediate portion Wa is enlarged gradually. Further, the compression of the shaft W by the translational movement of theholder 2 is stopped when the gap of theholders 2, 3 becomes a predetermined gap. Here, a process of enlarging the intermediate portion Wa of the shaft W is ended. - Next, as illustrated in
FIG. 3E , with the compression force being continuously applied to the shaft W by the translational drive unit 5 and through theholders 2, 3, the holder 3 which is inclined with respect to the reference line A is arranged back along the reference line A, and the bending of the shaft W is restored. By the bend restoration of the shaft W, the thickness of the enlarged intermediate portion Wa (hereinafter, the enlarged portion) is made uniform over the entire circumference. The shaft diameter enlarging with respect to the shaft W is completed through the above steps, and the rotation of the shaft W is stopped. Thereafter, the cutting or the like is performed on the enlarged portion Wa as necessary, and the enlarged portion Wa is molded in a desired shape (e.g., a columnar shape). - Since the temperature of the intermediate portion Wa of the shaft W is set to be above the blue brittleness range of the shaft W, the deformation resistance of the shaft W is reduced, so that it is possible to increase the enlargement rate. For example, it is possible to obtain two times or more of the enlargement rate. Further, it is possible to prevent a crack resulting from the enlargement. In addition, since the
holders 2, 3 are maintained to be below the tempering temperature range, it is possible to prevent the hardness of theholders 2, 3 from being lowered by tempering, thereby extending the lifetime of theholders 2, 3 and saving the running cost. Further, for the purpose of maintaining theholders 2, 3 to be below the tempering temperature range, the upper limit temperature of the intermediate portion Wa of the shaft W is set to be slightly above the tempering temperature range of theholders 2, 3 but below the warm temperature range. Thus, it is possible to suppress decarburization of the intermediate portion Wa, and to save the material by reducing the amount of cutting required for removing a scale generated on the surface of the intermediate portion Wa due to the decarburization or for removing the decarburization layer in which the strength is reduced due to the decarburization. It is also advantageous in that the running cost is further reduced by saving the energy required to heat the shaft W. - In the example illustrated in
FIGS. 3A to 3E , the intermediate portion Wa of the shaft W is heated only before the shaft diameter enlargement. However, the intermediate portion Wa may be heated during the shaft diameter enlargement or may be heated before the shaft diameter enlargement and during the shaft diameter enlargement. By heating the intermediate portion Wa during of the shaft diameter enlargement, the temperature drop due to heat dissipation is prevented, so that it is possible to ensure that the temperature of the intermediate portion Wa is maintained above the blue brittleness range. Accordingly, it is possible to further increase the enlargement rate and to further prevent a crack from being generated by the enlargement. - In the example described above, the holder 3 is tilted with respect to the reference line A to bend the shaft W, and the shaft W is rotated about the central axis so that the alternating load is applied to the intermediate portion Wa of the shaft W. However, the method for applying alternating load to the intermediate portion Wa is not limited thereto.
- In the example illustrated in
FIG. 4 , it is similar to the shaft diameter enlarging method illustrated inFIGS. 3A to 3E in that alternating load is applied to the intermediate portion Wa by the bending and the rotation of the shaft W, but the shaft W is bent by sliding the holder 3 in a direction intersecting the reference line A rather than by tilting the holder 3. - In the example illustrated in
FIG. 5 , theholder 2 holds the shaft W in a non-rotatable and restrained manner, whereas the holder 3 holds the shaft W in a rotatable and unrestrained manner. In this state, the holder 3 is turned about the reference line A, whereby the intermediate portion Wa of the shaft W is bent, and the alternating load is applied to the bent intermediate portion Wa of the shaft W. - In the example illustrated in
FIG. 6 , the end portion of the shaft W is held by theholders 2, 3 in a non-rotatable and restrained manner, and the holder 3 is rotated about the reference line A in a reciprocating manner, so that the alternating load is applied to the intermediate portion Wa of the shaft W. - In the example illustrated in
FIG. 7 , bending or torsional vibration is applied to the shaft W by a vibration generator OSC, so that the alternating load is applied to the intermediate portion Wa of the shaft W. - Hereinafter, the description will be given about test examples.
- In a first test example, in the shaft made of JlS-SCr420H, the entire shaft is heated in the electric furnace before the shaft diameter enlargement, and the shaft diameter enlargement is performed under the condition of the compression force of 2,000 kN and the bending angle of 4.0° by using the above-described shaft
diameter enlarging apparatus 1. The upper limit temperature of the blue brittleness range of JIS-SCr420H is less than 400° C. While the temperature (the temperature at the time of starting the shaft diameter enlargement) of the shaft is changed diversely, the number of the rotations required until the enlargement rate becomes 3.0 is measured, and the presence/absence of the crack in the obtained enlarged portion is checked. The presence/absence of the crack is checked by the color check using a color dye contrast penetrant. A result is shown inFIG. 8 . InFIG. 8 , a sample in which the crack is observed is indicated by “x”, and a sample in which the crack is not observed is indicated by “∘”. - As shown in
FIG. 8 , it is found that when the temperature of the shaft is higher, the number of the rotations required until the enlargement rate becomes 3.0 tends to be smaller, and the deformation resistance is small. Further, in the samples in which the temperature of the shaft is 400° C. or less, the crack is checked in the enlarged portion in all the samples. On the other hand, in the samples in which the temperature of the shaft is 400° C. or more, the crack is not checked in the enlarged portion in all the samples. From the above, it is found that when the shaft diameter enlargement is performed in a state in which the intermediate portion of the shaft is made have the temperature above the blue brittleness range, it is possible to increase the enlargement rate and to prevent the occurrence of the crack caused by the enlargement. - Next, in a second test example, with respect to the shaft which is made of JIS-SCr420H and in which the solidification pattern observed in the sectional surface of a rolled steel bar is elliptic and the shaft which is made of JIS-SCr420H and in which the solidification pattern observed in the sectional surface of the rolled steel bar is rectangular, under the same processing conditions as that of the first test example, while the temperature (the temperature at the time of starting the shaft diameter enlargement) of the shaft is changed diversely, the shaft diameter enlargement is performed until the enlargement rate becomes 3.0, and the elliptic amount is evaluated which is a difference between the long diameter and the short diameter of the obtained enlarged portion. The solidification pattern of the shaft is a cross sectional shape of the shaft during forging of a continuous forging and rolling for producing the shaft. The solidification pattern generally relates to isotropy and anisotropy of a plastic deformation of the shaft. A result is shown in
FIG. 9 . - As shown in
FIG. 9 , in a case where the solidification pattern is elliptic and in a case where the solidification pattern is rectangular, the elliptic amount tends to be smaller when the temperature of the shaft is higher. That is, it is found that the enlargement progresses in an isotropic manner, and thus the deformation resistance is smaller when the temperature of the shaft is higher, and the deformation in a circumferential direction progresses uniformly such that the effect of the solidification pattern is hardly received. For example, in a case where the enlarged portion is processed in a columnar shape by the cutting after the shaft diameter enlargement, when the elliptic amount is smaller, the cutting allowance can be made smaller, and the waste of the material can be reduced further, which is economical. - Next, some examples of the heating device 9 will be described.
- In the example illustrated in
FIG. 10 , the heating device 9 is configured to heat the intermediate portion of the shaft W or the entire shaft W including the intermediate portion before the shaft diameter enlargement. The shaft W is heated by, for example, furnace heating, resistance heating, or induction heating. The heating device 9 is provided next to the pair ofholders 2, 3. The shaft W heated by the heating device 9 is transferred from the heating device 9 to the pair ofholders 2, 3 by arobot 10. The shaft W is then held by the pair ofholders 2, 3 and is subjected to the shaft diameter enlargement. - In the example illustrated in
FIG. 11 , the heating device 9 is configured to heat the intermediate portion of the shaft W held by one of theholders 2, 3 before the shaft diameter enlargement by induction heating. The heating device 9 has a heating coil 11 of a spiral shape. The heating coil 11 is moved along the reference line A such that the shaft W held by theholder 2 is inserted into the heating coil 11. High frequency alternating current is applied to the heating coil 11 to heat the intermediate portion of the shaft W inside the heating coil 11 by induction heating. If the intermediate portion of the shaft W is longer than the entire length of the heating coil 11, theheating coil 1 may be moved along the reference line A. After the heating of the intermediate portion of the shaft W, the heating coil 11 is moved along the reference line A to remove the shaft W out of the heating coil 11. The heating coil 11 is then moved away from the reference line A. The shaft W is subsequently held by the pair ofholders 2, 3 and is subjected to the shaft diameter enlargement. - In the example illustrated in
FIG. 12 , the heating device 9 is configured to heat the intermediate portion of the shaft W held by the pair ofholders 2, 3, before the shaft diameter enlargement and/or during the shaft diameter enlargement, by induction heating. The heating device 9 has aheating coil 12 of an arc shape. Theheating coil 12 is placed close to the intermediate portion of the shaft W held by the pair ofholders 2, 3, such that an inner peripheral surface of theheating coil 12 and an outer peripheral surface of the intermediate portion of the shaft W face each other. High frequency alternating current is applied to theheating coil 12 so that the intermediate portion of the shaft W facing the inner peripheral surface of theheating coil 12 heated by induction heating. The intermediate portion of the shaft W can be heated over its entire circumference by rotating the shaft W by the rotary drive unit 7 (seeFIG. 1 ). If the intermediate portion of the shaft W is longer than the entire length of theheating coil 12, theheating coil 12 may be moved along the reference line A. When heating the intermediate portion of the shaft W during the shaft diameter enlargement, theheating coil 12 is moved radially outward in accordance with the enlargement of the intermediate portion of the shaft W. The shaft diameter enlargement may be performed on the shaft W being heated in this way. - In the example illustrated in
FIG. 13 , the heating device 9 is configured to heat the intermediate portion of the shaft W held by the pair ofholders 2, 3, before the shaft diameter enlargement and/or during the shaft diameter enlargement, by resistance heating. The heating device 9 has a pair ofelectrodes holders 2, 3. Direct current or alternating current is applied between the pair ofelectrodes holders 2, 3 and the intermediate portion of the shaft W held by theholders 2, 3, whereby the intermediate portion of the shaft W is heated by resistance heating. The shaft diameter enlargement may be performed also on the shaft W being heated in this way. - This application claims priority to Japanese Patent Application No. 2017-173281 filed on Sep. 8, 2017 and Japanese Patent Application No. 2018-138035 filed on Jul. 23, 2018, the entire contents of which are incorporated herein by reference.
Claims (7)