US20180096926A1 - Interconnection substrate and semiconductor package - Google Patents
Interconnection substrate and semiconductor package Download PDFInfo
- Publication number
- US20180096926A1 US20180096926A1 US15/718,414 US201715718414A US2018096926A1 US 20180096926 A1 US20180096926 A1 US 20180096926A1 US 201715718414 A US201715718414 A US 201715718414A US 2018096926 A1 US2018096926 A1 US 2018096926A1
- Authority
- US
- United States
- Prior art keywords
- metal layer
- layer
- interconnection
- metal
- protrusion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- The present application is based upon and claims the benefit of priority from the prior Japanese Patent Application No. 2016-197573 filed on Oct. 5, 2016, with the Japanese Patent Office, the entire contents of which are incorporated herein by reference.
- The disclosures herein relate to an interconnection substrate, a method of making the interconnection substrate, and a semiconductor package.
- Use of an interconnection structure having copper or the like for external connection terminals such as pads may involve performing a surface treatment that covers the surface of the interconnection structure with a metal layer. There are various types of surface treatment, among which electroless nickel plating is mainly used due to its excellent solderability and wire-bonding strength.
- In other cases than the use of an interconnection structure for external connection terminals (i.e., in the case of its use in an internal layer), surface treatment that covers a surface with a metal layer may also be used for the purpose of improving reliability through enhanced migration resistance. Electroless nickel plating may be used also in this case.
- Electroless nickel plating performed on the surface of an interconnection structure creates a nickel plating film spreading at the bottom, which gives rise to a problem of short-circuiting between interconnections in places where the interconnection pitch is narrow. This is because, while electroless nickel plating requires a pretreatment process of enhancing catalyst activity through adsorption of palladium, this palladium is readily adsorbed on the surface of insulating resin between interconnections, resulting in deposition of an electroless nickel plating film on the surface of insulating resin.
- To address this problem, technology has been developed that creates a nickel palladium alloy layer on the surface of insulating resin, followed by performing electroless nickel plating by using the nickel palladium alloy film as a catalyst layer. This technology allows the catalyst activity enhancement step to be omitted, thereby preventing the nickel plating film from having a spreading shape at the bottom (see
Patent Document 1, for example). - Use of the above-noted technology to cover the surface of an interconnection structure with a metal layer such as a nickel plating film, however, causes the metal layer to have a flat surface. As a result, provision of insulating resin (e.g., an interlayer insulating layer, underfill resin, or the like) on the metal layer results in the lack of sufficient adhesion between the insulating resin and the interconnection structure.
- According to an aspect of the embodiment, an interconnection substrate includes a first insulating layer and an interconnection structure formed on the first insulating layer, wherein the interconnection structure includes an interconnection pattern having a first metal layer, a second metal layer formed on the first metal layer, and a third metal layer formed on the second metal layer, and a fourth metal layer covering an upper surface and side surface of the interconnection pattern, wherein an outer perimeter of the second metal layer protrudes at the side surface of the interconnection pattern to form a first protrusion, and the fourth metal layer has a second protrusion that protrudes at a side surface of the interconnection structure at a position corresponding to the first protrusion.
- According to an aspect of the embodiment, a semiconductor package includes the interconnection substrate as described above, a semiconductor chip mounted on the interconnection substrate and electrically coupled to the interconnection structure, and insulating resin filling a gap between the interconnection substrate and the semiconductor chip and covering the interconnection structure.
- The object and advantages of the embodiment will be realized and attained by means of the elements and combinations particularly pointed out in the claims. It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are not restrictive of the invention, as claimed.
-
FIGS. 1A and 1B are cross-sectional views illustrating an example of an interconnection substrate according to an embodiment; -
FIG. 2 is a cross-sectional view illustrating an example of a semiconductor package according to the embodiment; -
FIGS. 3A through 3D are drawings (part 1) illustrating an example of the process steps of making the interconnection substrate according to the embodiment; -
FIGS. 4A through 4C are drawings (part 2) illustrating an example of the process steps of making the interconnection substrate according to the embodiment; -
FIGS. 5A through 5C are drawings (part 3) illustrating an example of the process steps of making the interconnection substrate according to the embodiment; -
FIGS. 6A through 6E are drawings illustrating an electroless nickel plating method that does not involve a catalyst activity enhancement step as a pretreatment step; -
FIGS. 7A and 7B are drawings (part 1) illustrating a comparative example; -
FIGS. 8A and 8B are drawings (part 2) illustrating a comparative example; and -
FIGS. 9A and 9B are drawings (part 3) illustrating a comparative example. - In the following, embodiments will be described by referring to the accompanying drawings. In these drawings, the same elements are referred to by the same references, and a duplicate description thereof may be omitted.
- In the following, an interconnection structure will be described by using an example in which an interconnection structure is used as pads disposed on the surface layer of an interconnection substrate.
-
FIGS. 1A and 1B are cross-sectional views illustrating an example of an interconnection substrate according to the present embodiment.FIG. 1A illustrates the whole view, andFIG. 1B illustrates an enlarged view of an area A illustrated inFIG. 1A . - An
interconnection substrate 1 illustrated inFIG. 1A is a coreless interconnection substrate which includes aninterconnection layer 10, aninsulating layer 20, at least oneinterconnection structure 30, and asolder resist layer 40. The interconnection structure disclosed herein may also be used in an interconnection substrate having a core. - In the present embodiment, for the sake of convenience, the side of the
interconnection substrate 1 on which thesolder resist layer 40 is situated is referred to as an upper side or a first side, and the side on which theinsulating layer 20 is situated is referred to as a lower side or a second side. Further, the surface of a member situated toward thesolder resist layer 40 side is referred to as an upper surface or a first surface, and the other surface of the member situated toward the insulatinglayer 20 side is referred to as a lower surface or a second surface. It may be noted, however, that theinterconnection substrate 1 may be used in an upside-down position, or may be placed at any angle. Further, a plan view refers to a view taken in the direction perpendicular to anupper surface 20 a of theinsulating layer 20, and a plan view shape refers to the shape of an object as viewed in the direction perpendicular to theupper surface 20 a of theinsulating layer 20. - In the
interconnection substrate 1, theinterconnection layer 10 is embedded in the lower surface side of theinsulating layer 20. The lower surface of theinterconnection layer 10 is exposed through the lower surface of theinsulating layer 20. The upper surface and side faces of theinterconnection layer 10 are covered with theinsulating layer 20. The lower surface of theinterconnection layer 10 may be flush with the lower surface of theinsulating layer 20, for example. - The lower surface of each distinct part of the
interconnection layer 10 exposed through the lower surface of theinsulating layer 20 may have a circular plan-view shape, for example, which may be used as a pad for connection with another interconnection substrate or the like. Theinterconnection layer 10 may have an interconnection line pattern in addition to the one or more pads. Copper (Cu) may be used as the material of theinterconnection layer 10. Theinterconnection layer 10 may alternatively have a multilayer structure comprised of a plurality of metal layers. The thickness of theinterconnection layer 10 may be about 10 to 20 micrometers, for example. - The insulating
layer 20 covers the upper surface and side faces of theinterconnection layer 10. Non-photosensitive (thermosetting) epoxy insulating resin or polyimide insulating resin may be used as the material of the insulatinglayer 20. Alternatively, photosensitive epoxy insulating resin or acrylic insulating resin may be used as the material of the insulatinglayer 20. The insulatinglayer 20 may include filler such as silica (SiO2). The thickness of the insulatinglayer 20 may be about 10 to 50 micrometers, for example. The insulatinglayer 20 may have via holes formed therethrough, through which theinterconnection layer 10 and theinterconnection structure 30 may be connected to each other. - The
interconnection structure 30 is formed on theupper surface 20 a of the insulatinglayer 20 that is a surface layer (i.e., a layer exposed on the surface). Theinterconnection structure 30 includes ametal layer 31, ametal layer 32, ametal layer 33, ametal layer 34, and ametal layer 35. - The
metal layer 31 is directly disposed on theupper surface 20 a of the insulatinglayer 20. The material of themetal layer 31 may be copper (Cu), titanium (Ti), chrome (Cr), an alloy of two or more of these metals, or a multilayered film comprised of two or more layers of these metals. The thickness of themetal layer 31 may approximately be 0.01 to 1 micrometer, for example. The plan view shape of themetal layer 31 may be circular, for example. - The
metal layer 32 is formed on themetal layer 31. The plan view shape of themetal layer 32 is substantially the same as the plan view shape of themetal layer 31. Themetal layer 32 is formed to align with themetal layer 31 in a plan view. The material of themetal layer 32 may be a metal whose standard electrode potential is positive relative to themetal layer 35 and that is inactive against a reducing agent for electroless plating used to make themetal layer 35. The thickness of themetal layer 32 may be about 4 to 6 micrometers, for example. - The standard electrode potential, which is an electrode potential in an oxidation reduction reaction when the standard hydrogen electrode (NHE) is used as a reference, is −0.257 V for Ni and +0.342 V for Cu, for example.
- The
metal layer 33 is formed on themetal layer 32. Themetal layer 34 is formed on themetal layer 33. Themetal layer 34 is formed to align with the metal layers 31 and 32 in a plan view. The outer perimeter of themetal layer 33 protrudes outwardly relative to the side surface of themetal layer 32 and the side surface of themetal layer 34 to form afirst protrusion 33 x. In the case of the plan view shape of the metal layers 32 and 34 being circular, thefirst protrusion 33 x protrudes outwardly in an annular shape outside the metal layers 32 and 34 in a plan view. The width W1 of thefirst protrusion 33 x may be 0.5 to 3 micrometers, for example. - The material of the
metal layer 33 may be a metal that exhibits catalytic activity toward an electroless plating reducing agent used to make themetal layer 35. The thickness of themetal layer 33 may be about 1 to 3 micrometers, for example. The material of themetal layer 34 may be a metal whose standard electrode potential is positive relative to themetal layer 35 and that is inactive against a reducing agent for electroless plating used to make themetal layer 35. The thickness of themetal layer 34 may be about 4 to 6 micrometers, for example. Themetal layer 34 and themetal layer 32 may be made of the same material, or may be made of respective, different materials. - The
metal layer 35 is formed to cover the side surface of themetal layer 31, the side surface of themetal layer 32, thefirst protrusion 33 x of themetal layer 33, and the upper surface and side surface of themetal layer 34. Themetal layer 35 has asecond protrusion 35 x that protrudes on the side surface thereof at the position corresponding to thefirst protrusion 33 x of themetal layer 33. In the case in which the plan view shape of themetal layer 35 except for thesecond protrusion 35 x is circular, thesecond protrusion 35 x protrudes outwardly in an annular shape outside such a circular shape in a plan view. The width W2 of thesecond protrusion 35 x may be 0.5 to 3 micrometers, for example. The thickness of the metal layer 35 (except for the portion where thesecond protrusion 35 x is formed) may approximately be 1 to 10 micrometers, for example. - The material of the
metal layer 35 may be an alloy having nickel (Ni) as a main component, for example. In such a case, cupper (Cu) may be used as the material of the metal layers 31, 32, and 34, for example. Further, the material of themetal layer 33 may be palladium (Pd) or nickel (Ni), for example. - The solder resist
layer 40 is selectively formed on theupper surface 20 a of the insulatinglayer 20. The material of the solder resistlayer 40 may be insulating photosensitive resin containing phenolic resin, polyimide resin, or like as a main component, for example. The solder resistlayer 40, which has photosensitive resin as a main component, may also include a filler material such as silica, alumina, or the like according to need. The thickness of the solder resistlayer 40 may be about 5 to 30 micrometers, for example. - The solder resist
layer 40 has at least oneopening 40 x. Theinterconnection structure 30 is exposed through theopening 40 x (non-solder mask defined: NSMD). A surface treatment layer (not shown) may be formed on only the upper surface or the upper surface and side surface of theinterconnection structure 30 exposed through theopening 40 x. Examples of the surface treatment layer may include an Au layer, a Pd/Au layer (which is a metal layer having a Pd layer and an Au layer laminated in this order), and the like. In place of forming of a metal layer, anti-oxidizing treatment such as OSP (i.e., organic solderability preservative) treatment or the like may be applied. The OSP treatment serves to form an organic film comprised of an azole compound, an imidazole compound, or the like as a surface treatment layer. - As illustrated in
FIG. 2 , theinterconnection substrate 1 may have asemiconductor chip 60 mounted (flip-chip mounted) thereon to form asemiconductor package 2, for example. Thesemiconductor chip 60 has at least one electrode pad electrically coupled to theinterconnection structure 30 of theinterconnection substrate 1 through a bump 70 (e.g., solder bump).Underfill resin 80 fills a gap between theinterconnection substrate 1 and thesemiconductor chip 60 to serve as insulating resin covering theinterconnection structure 30 and thebump 70. - As described above, the
interconnection structure 30 exposed through theopening 40 x in theinterconnection substrate 1 serves to function as a pad that is electrically coupled to a semiconductor chip or the like. In thesemiconductor package 2, thesecond protrusion 35 x of themetal layer 35 provides an anchoring effect for theunderfill resin 80, thereby improving the adhesion between theinterconnection structure 30 and theunderfill resin 80. - Improvement of the adhesion between the
interconnection structure 30 and insulating resin as provided by thesecond protrusion 35 x of theinterconnection structure 30 is not limited to the semiconductor package structure as illustrated inFIG. 2 , but may also be observed in the configuration in which the interconnection substrate is a standalone element. - In the
interconnection substrate 1, the solder resistlayer 40 may cover the upper surface perimeter and side surface of theinterconnection structure 30 so as to expose the upper surface center of theinterconnection structure 30 through theopening 40 x (solder mask defined: SMD). In this case, thesecond protrusion 35 x of themetal layer 35 provides an anchoring effect for the solder resistlayer 40, thereby improving the adhesion between theinterconnection structure 30 and the solder resistlayer 40 serving as insulating resin. - Alternatively, the
interconnection structure 30 may be formed as an inner layer rather than on the surface layer. For example, theinterconnection layer 10 that is an inner layer in theinterconnection substrate 1 may have the same structure as theinterconnection structure 30. In this case, the insulatinglayer 20 covers theinterconnection layer 10, and thesecond protrusion 35 x of themetal layer 35 provides an anchoring effect for the insulatinglayer 20. Adhesion between theinterconnection layer 10 and the insulatinglayer 20 serving as insulting resin is thus improved. It may be noted that use of the same structure as theinterconnection structure 30 for the inner-layer interconnection layer 10 also provides an effect of increasing migration resistance so as to improve reliability. - In the following, a description will be given of a method of making an interconnection substrate according to the present embodiment.
FIGS. 3A to 3D throughFIGS. 5A to 5C are drawings illustrating an example of the process of making an interconnection substrate according to the present embodiment. This embodiment is directed to the process steps of making asingle interconnection substrate 1. Alternatively, however, a plurality of structures to serve as respective interconnection substrates may be made as a single piece, followed by being divided into respect interconnection substrates. - In the process step illustrated in
FIG. 3A , asupport body 500 is put in place, and, then, theinterconnection layer 10 is formed on thesupport body 500. Thesupport body 500 may be a silicon plate, a glass plate, a metal foil plate, or the like. In this embodiment, thesupport body 500 is a copper foil. The thickness of thesupport body 500 may be about 35 to 100 μm, for example. Theinterconnection layer 10 may be formed by use of electrolytic plating that utilizes thesupport body 500 as a power feed layer, for example. Specifically, a resist layer having openings corresponding to theinterconnection layer 10 is formed on the upper surface of thesupport body 500. Electrolytic plating utilizing thesupport body 500 as a plating power feed layer then forms theinterconnection layer 10 made of copper or the like in the openings on the upper surface of thesupport body 500. Subsequently, the resist layer is removed. - In the process step illustrated in
FIG. 3B , the insulatinglayer 20 is formed on the upper surface of thesupport body 500 such as to cover theinterconnection layer 10. Specifically, insulating epoxy resin or the like having a film shape is laminated onto the upper surface of thesupport body 500 such as to cover theinterconnection layer 10, for example. Subsequently, the laminated insulating epoxy resin or the like is heated above the curing temperature to be cured under mechanical pressure. Instead of laminating the insulating epoxy resin or the like having a film shape, insulating epoxy resin or the like in a liquid form or paste form may be applied by use of a spin coating method or the like and then cured. - In the process steps illustrated in
FIG. 3C throughFIG. 4C , a semi-additive method is used to form part of the interconnection structure 30 (i.e., except for the metal layer 35). As illustrated inFIG. 3C , electroless plating or sputtering is used to form ametal layer 310 that covers the entirety of theupper surface 20 a of the insulatinglayer 20. The thickness of themetal layer 310 may approximately be 0.01 to 1 micrometer, for example. Themetal layer 310 is a copper layer, for example. - As illustrated in
FIG. 3D , a photosensitive resist layer 510 (e.g., dry-film resist or the like) is formed on themetal layer 310. The resistlayer 510 is then patterned through exposure and development, which forms theopenings 510 x selectively exposing the upper surface of themetal layer 310. - As illustrated in
FIG. 4A , electrolytic plating utilizing themetal layer 310 as a power feed layer forms the metal layers 32, 33, and 34 successively on the portions of themetal layer 310 exposed through theopenings 510 x of the resistlayer 510, thereby selectively forming multilayer structures comprised of the metal layers 32, 33, and 34. The thickness of themetal layer 32 may be about 4 to 6 micrometers, for example. The thickness of themetal layer 33 may be about 1 to 3 micrometers, for example. The thickness of themetal layer 34 may be about 4 to 6 micrometers, for example. - As was previously described, the material of the metal layers 32 and 34 may be a metal whose standard electrode potential is positive relative to the
metal layer 35 and that is inactive against a reducing agent for electroless plating used to make themetal layer 35. Further, the material of themetal layer 33 may be a metal that exhibits catalytic activity toward an electroless plating reducing agent used to make themetal layer 35. In the example used herein, themetal layer 35 is an alloy layer having nickel as a main component, and the metal layers 32 and 34 are copper layers, with themetal layer 33 being a palladium layer. - As illustrated in
FIG. 4B , the resistlayers 510 illustrated inFIG. 4A is removed. The resist layers 510 may be removed by use of a stripping solution containing sodium hydroxide or the like, for example. - As illustrated in
FIG. 4C , the multilayer structures comprised of the metal layers 32, 33, and 34 are used as masks to remove, by etching, the portions of themetal layer 310 that are not covered with the multilayer structures. As a result, the remaining portions of themetal layer 310 become themetal layer 31, with the metal layers 32, 33, and 34 laminated in this order on themetal layer 31. In the example described here, an etching solution that removes thecopper metal layer 310 while being inactive against palladium is used. Examples of such etching solution include a hydrogen peroxide/sulfuric acid solution, a sodium persulfate solution, an ammonium persulfate solution, and the like. - In this process, the metal layers 32 and 34 are selectively etched while the
metal layer 33 is not etched, which causes the outer perimeter of themetal layer 33 to protrude relative to the side surface of themetal layer 32 and the side surface of themetal layer 34 to form thefirst protrusion 33 x. Namely, because the metal layers 32 and 34 are copper layers, these layers are etched together with the etching of thecopper metal layer 310, but themetal layer 33 which is a palladium layer is not etched together. As a result, the outer perimeter of themetal layer 33 protrudes outwardly relative to the side surface of themetal layer 32 and the side surface of themetal layer 34 to form thefirst protrusion 33 x. Themetal layer 34 is formed such as to align with the metal layers 31 and 32 in a plan view. In the case of the plan view shape of the metal layers 32 and 34 being circular, thefirst protrusion 33 x protrudes in an annular shape outside the circular shape of the metal layers 32 and 34 in a plan view. The width of thefirst protrusion 33 x may be 0.5 to 3 micrometers, for example. - The
metal layer 310 need not be limited to the same material as that of the metal layers 32 and 34, and may be copper (Cu), titanium (Ti), chrome (Cr), an alloy of two or more of these metals, or a multilayered film comprised of two or more layers of these metals, for example. In the case of themetal layer 310 being not a copper layer, the process step of etching and removing the portions of themetal layer 310 that are not covered by the multilayer structures of the metal layers 32, 33, and 34 may be performed separately from the process step of etching the metal layers 32 and 34 to form thefirst protrusion 33 x at the outer perimeter of themetal layer 33. - As illustrated in
FIG. 5A , the solder resistlayer 40 is formed on theupper surface 20 a of the insulatinglayer 20. The solder resistlayer 40 may be initially formed by applying insulating resin in a liquid form or paste form all over the multilayer structures of the metal layers 31 through 34 by use of a screen printing method, a roll coating method, a spin coating method, or the like. Alternatively, an insulating resin film may be laminated all over the multilayer structures of the metal layers 31 through 34. The insulating resin used here may be a photosensitive insulating epoxy resin, a photosensitive insulating acrylic resin, or the like. The applied or laminated insulating resin is then subjected to exposure and development (i.e., photolithography) to form theopenings 40 x of the solder resistlayer 40 which expose the upper surface and side surface of the multilayer structures each comprised of the metal layers 31 through 34 stacked one on another. - As illustrated in
FIG. 5B , themetal layer 35 is formed to cover the side surface of themetal layer 31, the side surface of themetal layer 32, thefirst protrusion 33 x of themetal layer 33, and the upper surface and side surface of themetal layer 34. Themetal layer 35 is formed such as to have thesecond protrusion 35 x protruding on the side surface thereof at the position corresponding to thefirst protrusion 33 x. In this example, an alloy layer having nickel as a main component is formed as themetal layer 35 by electroless plating that does not involve a catalyst activity enhancement step as a pretreatment step. The plating solution may be of a nickel phosphorus type for which hypophosphite is used as a reducing agent, for example. - As illustrated in
FIG. 5C , thesupport body 500 illustrated inFIG. 5B is removed to complete the final form of theinterconnection substrate 1 illustrated inFIG. 1 . Thesupport body 500 made of a copper foil may be removed by wet etching using a ferric chloride solution, a copper chloride solution, an ammonium persulfate solution, or the like, for example. A metal layer that is not removable by the solution for etching copper may preferably be formed as the bottom layer of theinterconnection layer 10 in the process step illustrated inFIG. 3A . With this arrangement, such a metal serves as an etch stop layer, thereby preventing the etching solution for removing thesupport body 500 from etching theinterconnection layer 10. - It may be noted that the process step of forming the solder resist
layer 40 illustrated inFIG. 5A may be performed afterFIG. 5B orFIG. 5C , i.e., after the formation of theinterconnection structure 30. In so doing, the solder resistlayer 40 may be formed such as to cover the upper surface perimeter and side surface of theinterconnection structure 30 while exposing the center of the upper surface of theinterconnection structure 30 through theopening 40 x. - In the process step illustrated in
FIG. 5B , electroless plating (which uses a plating solution of a nickel phosphorus type for which hypophosphite is used as a reducing agent) that does not involve a catalyst activity enhancement step as a pretreatment step forms an alloy layer as themetal layer 35 having nickel as a main component. In the following, this mechanism will be described by referring toFIGS. 6A through 6E . - As illustrated in
FIG. 6A , hypophosphorous acid (H3PO2) starts to undergo a decomposition reaction (oxidative decomposition: H3PO2->H3PO3) on the surface of thefirst protrusion 33 x of themetal layer 33 made of Pd because Pd exhibits a catalyst activity with respect to hypophosphite serving as a reducing agent. In contrast, a decomposition reaction of hypophosphorous acid does not occur on the surface of the metal layers 31, 32, and 34 made of Cu because such a surface exhibits almost no activity with respect to hypophosphite serving as a reducing agent. - Subsequently, as illustrated in
FIG. 6B , the decomposition reaction of hypophosphorous acid continues on the surface of thefirst protrusion 33 x of themetal layer 33 made of Pd, resulting in the deposition of Ni. In contrast, no decomposition reaction of hypophosphorous acid occurs on the surface of the metal layers 31, 32, and 34 made of Cu, resulting in no deposition of Ni. - As illustrated in
FIG. 6C , Ni also exhibits a catalyst activity with respect to hypophosphorous acid as does Pd, so that a decomposition process of hypophosphorous acid occurs on the surface of Ni. Since a local cell reaction is formed between Ni and Cu, electrons e− generated by the decomposition reaction move to the surface of Cu. As Ni ions (Ni2+) receive the electrons e-generated by the decomposition reaction, the reduction and deposition of Ni also occur on the surface of the metal layers 31, 32, and 34 made of Cu. - As illustrated in
FIG. 6D , the reaction illustrated inFIG. 6C continues so as to produce Ni that covers all the surface of the metal layers 31, 32, and 34 made of Cu, which results in the disappearance of the local cell reaction. - As illustrated in
FIG. 6E , a decomposition reaction of hypophosphorous acid continues on the surface of Ni, resulting in further deposition of Ni to thicken themetal layer 35. Themetal layer 35 has thesecond protrusion 35 x formed thereon that protrudes on the side surface thereof at the position corresponding to thefirst protrusion 33 x of themetal layer 33. - The above description has been provided with respect to the case in which the
metal layer 33 is Pd. Alternatively, themetal layer 33 may be Ni, Zn, Fe, or the like. In such a case also, the same or similar structure as illustrated inFIG. 6E may be obtained through the same or similar mechanism as described above. - In the following, the advantages of the disclosed technology will be described by referring to a comparative example (
FIGS. 7A and 7B throughFIGS. 9A and 9B ).FIGS. 7A and 7B are directed to an example in which a multilayer structure having acopper layer 320, a nickel-palladium alloy layer 330, and acopper layer 340 successively formed on an insulatinglayer 200 is subjected to the subtractive method to form amultilayer structure 100 as a first comparative example. - As illustrated in
FIG. 7A , the multilayer structure having thecopper layer 320, the nickel-palladium alloy layer 330, and thecopper layer 340 formed one on another is etched by the subtractive method using a resistlayer 950 as a mask. In this case, thecopper layer 340 situated at the top of the multilayer structure is immersed in etching solution for a longer time period than is thecopper layer 320 situated at the bottom, which means a greater etch amount on the side surface of thecopper layer 340 than on the other surfaces. As a result, the horizontal width of thecopper layer 340 becomes thinner than the other layers as illustrated inFIG. 7B . AfterFIG. 7B , the resistlayer 950 is removed, and, then, electroless nickel plating is performed by using the nickel-palladium alloy layer 330 as a catalyst layer. This method is not suitable for miniaturization of interconnection structures because the width of thecopper layer 340 turns out thinner than the other layers. - In the case of palladium being dominant at the time of etching illustrated in
FIG. 7B , thecopper layer 340 functions as a local anode to cause electrons to flow as shown by arrows inFIG. 8A , resulting in over-etching of thecopper layer 340. In the case of nickel being dominant at the time of etching illustrated inFIG. 7B , nickel functions as a local anode to cause electrons to flow as shown by arrows inFIG. 8B , resulting in over-etching of the nickel-palladium alloy layer 330. A normal interconnection shape may not be retained in either case. - Even if some measures are taken to overcome the problems illustrated in
FIGS. 7A and 7B andFIGS. 8A and 8B , the subtractive method has the function to etch the nickel-palladium alloy layer 330 in addition to the copper layers 320 and 340. As a result, the side surface of themultilayer structure 100 ends up being flat without a protrusion. Namely, the outer perimeter of the nickel-palladium alloy layer 330 does not protrude relative to the side surface of thecopper layer 320 and the side surface of thecopper layer 340. In this case, only the side surface of the nickel-palladium alloy layer 330 is exposed on the surface of themultilayer structure 100. The small area size of such an exposed surface does not provide a sufficient catalyst activity, resulting in a reduced reactivity that is unlikely to segregate a nickel plating film. - Even if a
nickel plating layer 350 is segregated on the upper surface and side surface of themultilayer structure 100 as illustrated inFIG. 9B , the side surface of thenickel plating layer 350 would end up being flat, without having a portion corresponding to thesecond protrusion 35 x illustrated inFIG. 1B . As a result, an anchoring effect does not come into being when insulating resin covers themultilayer structure 100 having the nickel plating layer. 3.50 on the surface thereof, thereby failing to secure sufficient adhesion between themultilayer structure 100 and the insulating resin. - The structure and production method of the
interconnection substrate 1, on the other hand, can obviate the problems described in connection withFIGS. 7A and 7B throughFIGS. 9A and 9B . - Namely, electroless nickel plating is performed while the
metal layer 34 has substantially the same horizontal width as that of themetal layer 32 in a plan view without becoming thinner. Further, the provision of thefirst protrusion 33 x of themetal layer 33 serves to improve the reactivity of electroless nickel plating because of an increase in the area size of the catalyst layer exposed on the surface. Despite the absence of a catalyst placing process, thus, an electroless nickel plating film is deposited on all the surfaces (i.e., upper surface and side surface) of the multilayer structure comprised of the metal layers 31 through 34. - Moreover, the
metal layer 35 has thesecond protrusion 35 x formed thereon that protrudes on the side surface thereof at the position corresponding to thefirst protrusion 33 x of themetal layer 33. As a result, when theinterconnection structure 30 is covered with insulating resin, thesecond protrusion 35 x of themetal layer 35 creates an anchoring effect with respect to the insulating resin, thereby improving adhesion between theinterconnection structure 30 and the insulating resin. - Omitting a catalyst activity process serves to prevent the nickel plating film constituting the
metal layer 35 from having a spreading shape at the bottom, which enables the narrowing of pitches of theinterconnection structures 30. - According to at least one embodiment, adhesion between a metal layer and insulating resin is improved in an interconnection substrate having an interconnection structure in which the metal layer covers the surface of an interconnection.
- All examples and conditional language recited herein are intended for pedagogical purposes to aid the reader in understanding the invention and the concepts contributed by the inventor to furthering the art, and are to be construed as being without limitation to such specifically recited examples and conditions, nor does the organization of such examples in the specification relate to a showing of the superiority and inferiority of the invention. Although the embodiment(s) of the present inventions have been described in detail, it should be understood that the various changes, substitutions, and alterations could be made hereto without departing from the spirit and scope of the invention.
- The present disclosures non-exhaustively include the subject matter set out in the following clauses:
-
-
Clause 1. A method of making an interconnection substrate, comprising: - forming on an insulating layer an interconnection pattern having a first metal layer, a second metal layer, and a third metal layer disposed one on another;
-
- selectively etching the first metal layer and the third metal layer relative to the second metal layer to form a first protrusion that is an outer perimeter of the second metal layer protruding at a side surface of the interconnection pattern; and
- forming a fourth metal layer covering a side surface of the first metal layer, the first protrusion, and an upper surface and a side surface of the third metal layer,
- wherein the forming of the fourth metal layer results in a second protrusion being formed to protrude at a side surface of the fourth metal layer at a position corresponding to the first protrusion.
-
-
Clause 2. The method as recited inclause 1, wherein the first metal layer and the third metal layer are made of a metal whose standard electrode potential is positive relative to nickel and that is inactive against a reducing agent for electroless nickel plating,
-
- wherein the second metal layer is made of a metal that exhibits a catalytic activity toward the reducing agent for electroless nickel plating, and
- wherein the forming of the fourth metal layer utilizes electroless nickel plating to deposit an alloy containing nickel as a main component on the side surface of the first metal layer and the upper surface and side surface of the third metal layer after plating an alloy containing nickel as a main component on the first protrusion, thereby forming the fourth metal layer.
-
- Clause 3. The method as recited in
clause 2, wherein a plating solution used in the electroless nickel plating is of a nickel phosphorus type for which hypophosphite is used as a reducing agent. - Clause 4. The method as recited in
clause 1, further comprising forming a fifth metal layer on the insulating layer before the forming of the interconnection pattern,
- Clause 3. The method as recited in
- wherein the forming of the interconnection pattern forms the interconnection pattern on the fifth metal layer,
- wherein the forming of the first protrusion removes that portion of the fifth metal layer which is not covered with the interconnection layer, in addition to selectively etching the first metal layer and the third metal layer, and
- wherein the forming of the fourth metal layer forms the fourth metal layer covering a side surface of the fifth metal layer, the side surface of the first metal layer, the first protrusion, and the upper surface and side surface of the third metal layer.
Claims (6)