US20180094145A1

US20180094145A1 - Coalescent and non-ionic surfactant blend

Info

Publication number: US20180094145A1
Application number: US15/285,770
Authority: US
Inventors: Jennifer Lynn Cogar; Damon Ray Billodeaux; Jerome Leonard Stavinoha, Jr.; Michelle Nicole Tuttle
Original assignee: Eastman Chemical Co
Current assignee: Eastman Chemical Co
Priority date: 2016-10-05
Filing date: 2016-10-05
Publication date: 2018-04-05
Also published as: US9932486B1; CN109790399A; EP3523374B1; CN109790399B; EP3523374A1; WO2018067344A1

Abstract

The invention is comprised of a coalescent and non-ionic surfactant blend additive for use in water-based architectural coating formulations. The dual-function blend is produced by reacting 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate with ethylene oxide in the presence of a basic catalyst and separating the desired ethoxylated coalescent and non-ionic surfactant blend from the reaction product.

Description

FIELD OF THE INVENTION

The invention generally relates to a coalescent and non-ionic surfactant blend. More particularly the invention relates to a coalescent and non-ionic surfactant blend that is a dual-function additive for architectural coatings.

BACKGROUND OF THE INVENTION

Architectural coatings formulators generally utilize discrete coalescing aid and surfactant additives to deliver good performance in common water-based latex paint formulations. Alkyl phenol ethoxylate (APE) has been a primary nonionic surfactant used for many years in latex paint formulation. However, there are environmental and health concerns relating to the use of APE in paint formulations. Various ethoxylated alcohols are possible replacements for traditional APE surfactant technology, however these discrete additives add to the cost of the formulation and increase the complexity and difficulty of adjusting paint formulations. Some of these discrete additives may partially provide both coalescing aid and surfactant functionality, but do not deliver adequate performance in common formulations to allow total replacement of two or more additives with a single additive. Thus there is a need for a single additive for architectural coatings formulation that provides both coalescing aid and surfactant performance.
The additive of the present invention addresses the needs of architectural coatings formulators who seek to simplify complex formulations and reduce manufacturing costs while maintaining paint performance. The present invention addresses this need as well as others, which will become apparent from the following description and the appended claims.

SUMMARY OF THE INVENTION

The invention is as set forth in the appended claims.
There is now provided a dual-function additive for water-based architectural coating formulations that functions as both a coalescent and non-ionic surfactant.
In particular, there is now provided a blend comprising:
a) structure (1);
b) structure (2);
c) structure (3); and
wherein n is 1 to 5.
In another aspect, there is now provided a coating composition comprising:
A. at least one latex compound;
B. at least one pigment;
C. a coalescent and non-ionic surfactant blend comprising:

- a) structure (1);

- b) structure (2); and

- c) structure (3);

wherein n equals 1 to 5.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-7 are graphs of the amount of ethoxylated blend added to latex paints versus the Minimum Film Formation Temperature (MFFT) measured in latex paints.

The FIGS. 8, 10, 12, 15, 16 and 17 are graphs of Delta E with multiple colorants.

The FIGS. 9, 11, 13, and 14 are graphs of paint film resistance to abrasion with 9, 11, 13 showing thickness loss measurements. FIG. 14 shows the relative number of cycles required to remove the paint film.

DETAILED DESCRIPTION OF THE INVENTION

Unless otherwise indicated, all numbers expressing quantities of ingredients, properties such as molecular weight, reaction conditions, and so forth used in the specification and claims are to be understood as being modified in all instances by the term “about.” Unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that may vary depending upon the desired properties sought to be obtained by the present invention. At the very least, each numerical parameter should be construed in light of the number of reported significant digits and by applying ordinary rounding techniques. Further, the ranges stated in this disclosure and the claims are intended to include the entire range specifically and not only the endpoint(s). For example, a range stated to be 0 to 10 is intended to disclose all whole numbers between 0 and 10 such as, for example 1, 2, 3, 4, etc., all fractional numbers between 0 and 10, for example 1.5, 2.3, 4.57, 6.1113, etc., and the endpoints 0 and 10. Also, a range associated with chemical substituent groups such as, for example, “C₁to C₅alkyl groups” is intended to specifically include and disclose C₁and C₅alkyl groups as well as C₂, C₃, and C₄alkyl groups.
Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in its respective testing measurements.
As used in the specification and the appended claims, the term “blend” means two or more uniformly dispersed liquid substances.
As used in the specification and the appended claims, the singular forms “a,” “an” and “the” include their plural referents unless the context clearly dictates otherwise. In addition, references to a composition containing or including “an” alcohol or “a” surfactant is intended to include other ingredients, in addition to the one named. The terms “containing” or “including” are intended to be synonymous with the term “comprising”, meaning that at least the named compound, element, particle, or method step, etc., is present in the composition or article or method, but does not exclude the presence of other compounds, catalysts, materials, particles, method steps, etc., even if the other such compounds, material, particles, method steps, etc., have the same function as what is named, unless expressly excluded in the claims.
Also, it is to be understood that the mention of one or more process steps does not preclude the presence of additional process steps before or after the combined recited steps or intervening process steps between those steps expressly identified. Moreover, the lettering of process steps or ingredients is a convenient means for identifying discrete activities or ingredients and the recited lettering can be arranged in any sequence, unless otherwise indicated.
In one aspect of the invention, ethoxylated derivatives of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, are a dual-function additive for water-based architectural coatings formulations. The additive delivers coalescing aid and nonionic surfactant performance in a single material without supplemental additions of other discrete coalescing aids and nonionic surfactants.
The present invention provides a blend comprising:
a) structure (1);
b) structure (2);
c) structure (3); and
wherein n is 1 to 5.
In one embodiment of the invention, the multifunctional blend of the present invention is produced by reacting 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate (also known as Eastman Texanol™ Ester Alcohol, and TXOL) with ethylene oxide (also known as 1,2-epoxyethane, oxirane, and EO) in the presence of a base catalyst. Although not bound to any particular reaction theory, it is theorized that under reaction conditions TXOL converts to a mixture of TXOL, 2,2,4-trimethyl-1,3-pentanediol (TMPD), and 2,2,4-trimethyl-1,3-pentanediol diisobutyrate (TXIB). The ethoxylation reaction adds a hydrophilic portion to the hydroxyl groups in TXOL and TMPD. In the case of TXIB, since there are no hydroxyl groups for the EO to react with, it is theorized that a transesterification reaction takes place between TXIB and an ethoxylated TXOL molecule generating the ethoxylated TXIB and a TXOL. Additionally, the ethoxylated products can also isomerize. Thus, the ethoxylation reaction product is a mixture of ethoxylate materials represented by structures (1), (2), and (3) where n can equal one to five, along with unreacted starting materials.
In various embodiments of the invention, the ethoxylation process can be carried out in a reactor, such as a batch stirred autoclave, a continuous stirred tank, a plug flow reactor, a trickle bed, or a loop reactor.
In other embodiments of the invention, a catalyst can be used in the ethoxylation process. Suitable catalysts possess alkaline characteristics. The catalyst can be heterogeneous such as a hydrotalcite, calcium oxide, or magnesium oxide. The catalyst can be homogeneous such as hydroxides of sodium, potassium, cesium, or lithium. The catalyst can be an alkaline or alkaline earth metal salt of an alcohol such as ethanol, propanol, butanol, isobutanol or 2-ethylhexanol. Such salts are commonly referred to as “alkoxides”. The homogeneous catalyst can also be an alkaline or alkaline earth metal salt of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate or 2,2,4-trimethyl-1,3-pentanediol.
In some embodiments of this invention sufficient ethylene oxide may be used to achieve one to five moles EO per mole of ethoxylate. Higher levels of ethoxylation may be achieved, however as the amount of ethoxylation increases the reaction product becomes more difficult to recover by separation methods such as distillation and form highly colored materials due to excessive heating.
In another embodiment of the invention, the reaction is conducted at temperatures of 100° C. to 200° C. In other embodiments the reaction is conducted at temperatures of 125° C. to 170° C. The reaction is conducted at pressures such that the ethylene oxide is kept in the liquid phase. In some embodiments of the invention the reaction is conducted under pressures of 345 kPa to 1800 kPa. In other embodiments of the invention, the reaction is conducted under pressures of 861 kPa to 1241 kPa.
The crude reactor product can contain disproportionation and transesterification products such as isobutanol, 2,4-dimethyl-3-pentanone, and isobutyl butyrate. The raw reactor product can also contain unreacted starting materials. These unreacted starting materials can be separated from the desired multifunctional blend. Any method of separation can be used to separate the desired mixture of ethoxylates from the raw reaction product. Flash distillation, column distillation, cross current extraction, or other methods known to those versed in the art may be used.
In a paint formulation, coalescing aid functionality helps in the formation of the paint film, especially at lower temperatures. The coalescing aid acts as a plasticizer in latex emulsions. The coalescing aid lowers the glass transition temperature (Tg) of the latex polymer. As the paint dries the polymers that have been softened by the coalescing aid are allowed to flow together and form a film after the water has left the system. Nonionic surfactant functionality improves pigment wetting during paint processing and the overall stability of finished water-based latex paints. The nonionic surfactant lowers the interfacial tension between the liquid paint and the substrate as well as between the water in the paint and the dispersed pigment particles. A non-ionic surfactant enhances the mechanical stability and shelf-life of latex paints. Non-ionic surfactant also helps with the stability of the paint during the post-addition of pre-dispersed pigments, during point-of-sale tinting.
The multifunctional blend of the present invention is effective in a variety of latex paint formulations including acrylic, vinyl acrylic, vinyl versatate vinyl acrylics, ethylene vinyl acetate, and styrene acrylic latexes. It also performs with a variety of pigment types such as single pigments or mixtures of pigment types including TiO₂, calcium carbonate, talc, silica, nepheline syenite, and clays and with a ratio of pigments to total paint solids of 10% to 85%.

EXAMPLES

Synthesis of

Ethoxylated

2,2,4-trimethyl-1,3-pentanediol monoisobutyrate

Example 1

150 g (700 mmol) of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate (TXOL) containing, 0.25% Na by weight, was placed in a 300 mL stainless steel autoclave. The autoclave was sealed and purged with nitrogen. 20 mL (17.5 g, 400 mmol) of ethylene oxide (EO) was condensed from a sample bomb and pressured into the autoclave with nitrogen. The molar ratio of TXOL to EO was 1.2 mmol of TXOL per mmol of EO. The autoclave was placed into a computer controlled heating and stirring apparatus. The reactor was brought to 125° C. and charged with nitrogen to a pressure of 861.8 kPa. The mixture was stirred at 700 rpm. The apparatus was held at pressure and temperature for 2 hours. The apparatus was cooled in an ice bath to below 10° C., vented, and the contents sampled.
Reactor effluent was subjected to vacuum distillation to produce material for testing. The effluent was charged to a 500 mL round bottom flask with a Vigreux fractionating column, chilled condenser, and fraction collecting vessel. The entire apparatus was placed under 11 torr of vacuum and heated with an electric heating mantle. A base temperature of 230° C. was reached and light materials were removed overhead at 182° C. Heating was discontinued when the base pot temperature began to rise above 230° C. The base material was filtered and used for testing in subsequent examples. The reaction product was analyzed by gas chromatography. A typical product contains 0-5% molecules with n=1, 75-90% molecules with 2≦n≦5, and 5-10% molecules with n≧16. Results are presented in Table 1.

Example 2

Example 2 was carried out similarly to Example 1, except with 0.9 mmol of TXOL per mmol of EO.

Examples 3 & 4

Examples carried out in a manner similar to Example 1 with indicated ratio of reactants (Table 1). The 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate used in these examples contained 0.4% Na by weight.

TABLE 1

	TXOL:EO	EO
Example	(mol:mol)	Conversion	% EO1^a	% EO2^a	% EO3^a	% EO4^a	% EO5^a

1	1.8	88%	77.7	22.2	0	0	0
2	0.87	70%	47.3	33.1	13.4	6.2	0
3	2	91%	37.6	29.3	19.7	4.2	9.1
4	1.3	100%	29.9	30.7	18.5	11.6	9.2

^amole % of ethoxylates containing 1, 2, 3, 4, or 5 moles of EO.

Example 5

The batch autoclave was modified to allow for constant feed of ethylene oxide into the reactor. The EO sample bomb was connected to an IPSCO model syringe pump. The pump was charged with EO from the bomb. The autoclave was loaded with 100 g of TXOL containing 0.13% Na by weight. The autoclave was brought to 170° C. and 965 kPa with N₂. When temperature and pressure were reached, EO was continuously fed into the autoclave at 0.8 mL/min. During EO addition, the autoclave reached a pressure of 1723 kPa. At this point, the feed pump was discontinued and temperature maintained. After 3 hours of total reaction time, the autoclave was cooled, and the contents analyzed by gas chromatography. Approximately 57 g of EO were fed into the unit to give a TXOL:EO ratio of 0.36. Results are presented in Table 2.

Example 6

This example was carried out using the apparatus described in Example 5. The autoclave was loaded with 100 g of TXOL and brought to an operating temperature of 170° C. and pressure of 689 kPa. EO was fed into the reactor at a rate of 0.6 mL/min until a pressure of 1723 kPa was reached. The reaction was allowed to progress for 3 hours. Results are presented in Table 2.

TABLE 2

	EO Feed	TXOL:EO	EO
Example	(mL/min)	(mol:mol)	Conversion	% EO1 ^a	% EO2 ^a	% EO3 ^a	% EO4 ^a	% EO5 ^a

5	0.8	0.36	69%	21.5	32.7	22.2	14.2	9.4
6	0.6	0.36	66%	21.4	32.2	22.2	14.7	9.5

^amole % of ethoxylates containing 1, 2, 3, 4, or 5 moles of EO.

Examples 7-9

These examples were carried out as described in Example 6, except the reactor was brought to an operating pressure of 345 kPa before EO was fed at a rate of 6.4 mL/min. The reactions in these examples were carried out at various temperatures as indicated in Table 3.

TABLE 3

	Temperature	EO
Example	(° C.)	Conversion	% EO1 ^a	% EO2 ^a	% EO3 ^a	% EO4 ^a	% EO5 ^a

7	170	70%	21.2	32.1	22.4	14.7	9.5
8	180	77%	18.3	29.6	22.8	15.6	13.6
9	160	67%	19.5	31.3	22.7	15.6	10.9

^amole % of ethoxylates containing 1, 2, 3, 4, or 5 moles of EO.

Example 10

The apparatus in Example 5 was utilized. The autoclave was charged with 100 g of TXOL containing 0.24% Na by weight and brought to an operating temperature of 170° C. The reactor was brought to 689 kPa with N₂and EO feed was commenced at 0.5 mL/min. After 3 hours of feed time, the reactor pressure reached 1585 kPa and EO feed was terminated. The reactor was maintained at 170° C. until 5.5 hours had elapsed and the internal pressure had fallen to 1150 kPa. The reactor was cooled and samples were taken from the reaction mixture. Results are shown in Table 4.

TABLE 4

	TXOL	EO
Example	Conversion	Conversion	% EO1 ^a	% EO2 ^a	% EO3 ^a	% EO4 ^a	% EO5 ^a

10	95%	38%	10.1%	23.6%	25.7%	21.5%	19.2%

^amole % of ethoxylates containing 1, 2, 3, 4, or 5 moles of EO.

The functionality of these ethoxylate blends was tested in a variety of latex types and in several typical paint formulations. Coalescing efficiency was compared to common commercial controls in a variety of latexes. Performance dependent on film formation enhanced by the coalescent and stability and wetting properties generally provided by non-ionic surfactant were compared to control formulations containing common coalescents and non-ionic surfactants. Paints were prepared by replacing both the coalescent and the non-ionic surfactant with the invention ethoxylate blends. The level of ethoxylate blend was based on coalescent required to obtain a targeted Minimum Film Formation Temperature (MFFT) in the latex. The function of a coalescent is to lower the temperature where a latex can form a film thereby reducing the MFFT.
The ethoxylate blends were split to replace the surfactant in the high-shear pigment dispersion phase for pigment wetting and the coalescent in the lower shear letdown phase of the formulation.

Example 11

The ethoxylate blends assist with coalescence in a variety of latex types as evidenced by reduction of latex MFFT with addition of material. The results are shown in FIGS. 1-7. Example 11 demonstrates that the ethoxylate blends act as coalescents (reducing the minimum film formation temperature). FIGS. 1-7 represent results obtained in seven different types of architectural latexes. These include pure acrylics, styrene acrylics, and vinyl acrylics. The data is expressed as the amount of ethoxylated blend of this invention used as a percent of the latex solids (or the phr—parts per hundred resin). MFFT is tested by ASTM D2354. Two versions of the invention ethoxylate blends (MFA B and MFA E) were compared to conventional coalescents, Texanol™ ester alcohol (Texanol), Optifilm™ enhancer 300 (OE300) and, Optifilm™ enhancer 400 (OE 400). The coalescents Texanol™ ester alcohol, Optifilm™ enhancer 300 and, Optifilm™ enhancer 400 are products of Eastman Chemical Company. The results show that the invention ethoxylate blends decrease the MFFT of each of the latexes in a similar way as conventional coalescents.
Examples 12-17 show performance of the invention ethoxylate blends in a variety of paint formulations. Table 5-10 show the different formulations. For Tables 5-7, each table shows the relative quantity of materials used (in grams) and the order the materials were added. The portion labeled “grind” indicates that it was prepared with a high shear disperser with a saw tooth blade. The portion labeled “letdown” was prepared with a low shear mixer and a paddle blade. Tables 8-10 are written in US form which is pounds (lb.) per 100 gallons (gal).
For each formulation, the Figs. show two properties. FIGS. 8, 10, and 12 shows Delta E with multiple colorants. Delta E is the difference in overall color between the control paint and the paints containing the invention ethoxylate blend materials. Delta E is calculated from LAB measurements on a spectrophotometer as described in ASTM D2244. One primary function of a non-ionic surfactant is to enable pre-dispersed colorants to be added to the base paint and develop the appropriate level of color. In this case, Delta E is compared to the control paint that contains both a common coalescent and a common non-ionic surfactant. Delta E of less than 1 indicates that the paint containing the ethoxylate blend of this invention is very similar to the control paint. There is also data representing the control paint (Texanol) with the surfactant removed. In some cases, this shows significantly higher Delta E, again confirming that the ethoxylate blends of this invention are providing surfactant functionality.
The FIGS. 9, 11 and 13 represents scrub resistance. These tests were done by using ISO Method 11998. Scrub resistance is a key paint property that is impacted by coalescent performance because it improves film formation. Lower film thickness loss indicates good durable films. FIG. 14 shows also scrub resistance results, but tested by a different method, ASTM D2486. This is presented as the percent of the control scrub resistance that is maintained by the experimental paints. It shows the scrub data for three different formulations (Table 8, 9 and 10). Examples 12-17 show that the latex paints containing the invention ethoxylate blends perform similarly to the control latex paints containing conventional separate surfactants and coalescent aids materials.

Example 12: Vinyl Silk Paint

TABLE 5

Grams of Raw Material in Vinyl Silk Paint Formulation

		Texanol	Texanol
		EA	No	Sample	Sample
	Raw Material	Control	Surfactant	#1-	#2-
Grind	Description	Sample	Sample	MFA B	MFA E

	Water	44.3	48.1	47.4	48.3
	Cellulosic Thickener	1.4	1.4	1.4	1.4
	Neutralizing Agent	0.4	0.4	0.4	0.4
	Defoamer	0.4	0.4	0.4	0.4
	Dispersant	3.5	3.5	3.5	3.5
	Non-ionic Surfactant	3.8	0.0	0.0	0.0
	Multi-Functional
	Additive (MFA B)	0.0	0.0	1.9	0.0
	Multi-Functional	0.0	0.0	0.0	1.4
	Additive (MFA E)
	Biocide	0.2	0.2	0.2	0.2
	Fine Kaolin extender	9.0	9.0	9.0	9.0
	Pigment	34.5	34.5	34.5	34.5
Letdown
	vinyl	77.0	77.0	77.0	77.0
	acetate/VeoVa10/
	acrylate
	Opaque Polymer	9.0	9.0	9.0	9.0
	Coalescent	3.2	3.2	0.0	0.0
	Multi-Functional	0.0	0.0	1.9	0.0
	Additive (MFA B)
	Multi-Functional
	Additive (MFA E)	0.0	0.0	0.0	1.4
	Neutralizing Agent	1.2	1.2	1.2	1.2
	Defoamer	0.4	0.4	0.4	0.4
	Water	18.3	18.1	18.3	18.3
Total		206.6	206.4	206.9	206.4
Grams

The Delta E results of the paint formulations in Table 5 are shown in FIG. 8 and the scrub resistance results of the paint formulations in Table 5 are shown in FIG. 9.

Example 13: Vinyl Matt Paint

TABLE 6

Grams of Raw Material in a Vinyl Matt Paint Formulation

		Texanol EA	Texanol (no
	Raw Material	Control	surfactant)	Sample #1-	Sample #2-
Grind	Description	Sample	Sample	MFA B	MFA E

	Water	52.4	52.4	52.5	52.5
	Cellulosic Thickener	1.6	1.6	1.6	1.6
	Neutralizing Agent	1.4	1.4	1.4	1.4
	Defoamer	0.6	0.6	0.6	0.6
	Nonionic surfactant	1.4	0.0	0.0	0.0
	Multi-Functional
	Additive B	0.0	0.0	0.7	0.0
	Multi-Functional	0.0	0.0	0.0	0.6
	Additive E
	Dispersant	1.0	1.0	1.0	1.0
	Biocide	0.5	0.5	0.5	0.5
	Calcium/Magnesium	16.8	16.8	16.8	16.8
	Carbonate
	Talc	9.8	9.8	9.8	9.8
	Flash Calcined Clay	19.6	19.6	19.6	19.6
	Titanium Dioxide	22.4	22.4	22.4	22.4
Letdown
	Styrene Acrylic	25.8	25.8	25.8	25.8
	Coalescent	0.9	0.9	0.0	0.0
	Multi-Functional
	Additive B	0.0	0.0	0.7	0.0
	Multi-Functional
	Additive E	0.0	0.0	0.0	0.6
	HASE Thickener	1.2	1.2	1.2	1.2
	Defoamer	0.6	0.6	0.6	0.6
	Neutralizing Agent	0.4	0.4	0.4	0.4
	Water	37.0	37.0	34.2	34.2
Total Grams		193	192	190	190

The Delta E results of the paint formulations in Table 6 are shown in FIG. 10 and the scrub resistance results of the paint formulations in Table 6 are shown in FIG. 11.

Example 14: High Performance Matt Paint

TABLE 7

Grams of Raw Material in a High Performance Matt Paint
Formulation

		Texanol EA	Texanol No
	Raw Material	Control	Surfactant	Sample #1-	Sample #2-
Grind	Description	Sample	Sample	MFA B	MFA E

	Water	43.8	43.8	43.8	43.8
	Cellulosic Thickener	1.3	1.3	1.3	1.3
	Neutralizing Agent	0.8	0.8	0.8	0.8
	Defoamer	8.0	8.0	8.0	8.0
	Dispersant	0.9	0.9	0.9	0.9
	Non-ionic Surfactant	1.6	0.0	0.0	0.0
	Multi-Functional
	Additive (MFA B)	0.0	0.0	1.5	0.0
	Multi-Functional
	Additive (MFA E)	0.0	0.0	0.0	1.5
	Biocide	0.6	0.6	0.6	0.6
	Calcium/Magnesium	19.1	19.1	19.1	19.1
	Carbonate
	Talc	9.5	9.5	9.5	9.5
	Flash Calcine Clay	23.9	23.9	23.9	23.9
	Titanium Dioxide	1 23.0	1 23.0	1 23.0	23.0
Letdown
	Pure Acrylic Latex	55.0	55.0	55.0	55.0
	Coalescent	2.0	2.0	0.0	0.0
	Multi-Functional
	Additive	0.0	0.0	1.5	0.0
	Multi-Functional	0.0	0.0	0.0	1.5
	Additive
	Neutralizing Agent	0.6	0.6	0.6	0.6
	Associative	1.2	1.2	1.2	1.2
	Thickener
	Water	14.0	15.5	14.6	14.6
Total Grams		205.1	205.1	205.1	205.1

The Delta E results of the paint formulations in Table 7 are shown in FIG. 12 and the scrub resistance results of the paint formulations in Table 7 are shown in FIG. 13.

Example 15: Interior/Exterior Flat Formulation

TABLE 8

Material	Grams	Liters	Calculated:

Grind			PVC, %	45.6
Water	222.9	0.223	Volume Solids. %	38.2
Hydroxyethylcellulose	3.6	0.006	Weight Solids, %	63.1
Viscosity Controller
Copolymer Pigment	24.0	0.023	Deco Directive VOC,	12
Dispersant			g/L
Non-ionic surfactant/	2.6	0.003	Dispersant, % on	1.0
Experimental*			pigment
Defoamer	1.2	0.001	Coalescent, % on	4.3
			binder solids
Biocide	2.2	0.002

Titanium Dioxide	269.6	0.068	* Amounts shown for Texanol
			control; levels varied
Micronized Nepheline	239.7	0.092
Syenite filler/extender
Diatomaceous Earth	18.0	0.008
Let Down
Prepared grind	783.7	0.426
Water	68.3	0.068
Acrylic Emulsion	419.4	0.400
Defoamer	1.8	0.002
Texanol/Optifilm 400/	9.0	0.009
Experimental*
Propylene Glycol	12.0	0.012
Hydrophobically	27.0	0.026
Modified
Ethylene Oxide
Urethane (HEUR)
Rheology Modifier
Water	59.9	0.060
Totals	1381.0	1.00

The Delta E results of the paint formulations in Table 8 are shown in FIG. 15.

Example 16: Interior Flat Formulation

TABLE 9

Ingredients	Lbs.	Gals.

Grind:
Water	445.0	53.45
Hydroxyethylcellulose	6.0	0.54
Thickener
Biocide	1.0	0.11
Pigment Disperscent	12.0	1.31
Non-ionic Detergent/	2.2	0.25
experimental
2-amino-2-methyl-1-	2.0	0.25
propanol, Co-dispersant
Defoamer	2.0	0.26
Titanium Dioxide	100.0	3.13
Calcined Kaolin	150.0	6.80
Calcium Carbonate	150.0	6.61
Diatomaceous Earth	25.0	1.30
Attapulgite Thickening	10.0	0.51
Agent
Subtotal	905.2	74.52
Letdown:
Water	46.4	5.57
High Molecular Weight	173.0	19.12
Vinyl-Acrylic Latex
Texanol/experimental	4.2	0.53
Defoamer	2.0	0.26
Total	1130.8	100.00
Properties:
Pigment Volume	65.0%
Concentration
Volume Solids	29.1%
Weight Solids	47.7%

The Delta E results of the paint formulations in Table 9 are shown in FIG. 16.

Example 17: Interior Semi-Gloss Paint

TABLE 10

Material Name	Pounds	Gallons

Grind
Water	206.4	24.79
Hydrophilic Copolymer	5.5	0.55
Dispersant
2-amino-2-methyl-1-propano,l	2.0	0.25
Co-dispersant
CARBOWET 106*	2.0	0.25
Defoamer	2.0	0.24
Titanium Dioxide	250.0	7.50
Calcium Carbonate	27.4	1.15
Biocide	1.5	0.18
Grind Sub-total	496.8	34.91
Let Down
Acrylic Emulsion	415.0	46.89
Texanol	14.9	1.89
Defoamer	2.0	0.12
Hydrophobically Modified	21.0	2.41
Ethylene Oxide Urethane
(HEUR) Rheology Modifier
Non-ionic Urethane Rheology	4.5	0.52
Modifier
Water	110.4	13.26
Totals	1064.5	100.0
Pigment Volume	28.1%
Concentration, %
Volume solids, %	31.6%
Weight solids, %	46.3%

* CARBOWET 106 is the tradename for an ethoxylated nonionic surfactant sold by Air Products and Chemicals, Inc.
The Delta E results of the paint formulations in Table 10 are shown in FIG. 17.

The scrub resistance of the paints described in Tables 8, 9 and 10 are shown in FIG. 14.
The ethoxylate blends of this invention provide improved efficiency of TiO₂compared to conventional coalescent and surfactant additives. Changes in the surfactant/wetting aid can also offer the chance for improved TiO2 efficiency. The ethoxylated blends offer the same hiding and tint strength performance with a 10% or more reduction in TiO2 levels by volume. These properties are shown in Examples 18-20 and Tables 11-13. Table 14 shows the formulations for the information provided in Tables 11, 12 and 13.

Example 18: Spreading Rate as Specific Contrast Ratio

TABLE 11

Conventional Coalescent
Plus Surfactant	MFA SAMPLE B	MFA SAMPLE E

	−10%	−20%		−10%	−20%		−10%	−20%
Control	TiO2	TiO2	Control	TiO2	TiO2	Control	TiO2	TiO2

SR@99.5 CR	5.5	4.0	3.6	5.0	5.0	5.5	5.6	5.9	4.7
SR@98 CR	7.1	5.9	5.3	6.7	6.7	6.9	7.4	7.4	6.4
SR@95 CR	10.3	9.6	8.6	10.0	10.1	9.7	11.1	10.4	10.0

Example 19: Whiteness Index

TABLE 12

Conventional Coalescent
Plus Surfactant	MFA SAMPLE B	MFA SAMPLE E

Whiteness Index	80.77	80.47	78.82	81.06	80.59	80.17	80.59	80.95	80.26

Example 20: Tint Strength Results (ASTM D4838-88)

TABLE 13

Conventional Coalescent
Plus Surfactant	MFA SAMPLE B	MFA SAMPLE E

% TSAV

	100	99.25	97.05	100.62	100.91	98.94	101.81	101.43	99.11

TABLE 14

Vinyl Matt (PVC 77%)

	Conventional Coalescent
	plus Surfactant	MFA SAMPLE B	MFA SAMPLE E

		−10%	−20%		−10%	−20%		−10%	−20%
Grind	Control	TiO2	TiO2	Control	TiO2	TiO2	Control	TiO2	TiO2

Water	81.3	81.3	82.6	83.0	83.6	84.1	83.1	83.7	84.2
Non-ionic, Low	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5	2.5
Viscosity, Water
Soluble
Cellulose Ether
Coalescent	2.2	2.2	2.2	2.2	2.2	2.2	2.2	2.2	2.2
Neutralization
Amine
Defoamer	0.9	0.9	0.9	0.9	0.9	0.9	0.9	0.9	0.9
Phenol-free	2.2	2.2	2.2	0.0	0.0	0.0	0.0	0.0	0.0
Nonionic
Wetting agent
and Emulsifier
MFA Sample B	0.0	0.0	0.0	1.1	1.1	1.1	0.0	0.0	0.0
MFA Sample E	0.0	0.0	0.0	0.0	0.0	0.0	1.0	1.0	1.0
Hydrophilic	1.5	1.5	1.5	1.5	1.5	1.5	1.5	1.5	1.5
Copolymer
Dispersant
Biocide	0.8	0.8	0.8	0.8	0.8	0.8	0.8	0.8	0.8
Dolomite	26.1	26.9	27.8	26.6	27.6	28.6	26.6	27.6	28.6
Powder
Talc	15.2	15.3	15.6	15.5	15.6	16.0	15.5	15.7	16.0
Calcined Kaolin	30.4	31.0	31.7	31.0	31.8	32.6	31.0	31.8	32.7
Chloride-	34.8	31.3	27.9	35.4	32.1	28.7	35.5	32.2	28.4
Process Rutile
Titanium
Dioxide Pigment

Letdown

APEO-Free	40.0	40.0	40.7	40.7	41.0	41.3	40.8	41.1	41.3
Anionic Styrene
Acrylic Binder
Texanol	1.4	1.4	1.4	0.0	0.0	0.0	0.0	0.0	0.0
MFA Sample B	0.0	0.0	0.0	1.1	1.1	1.1	0.0	0.0	0.0
MFA Sample E	0.0	0.0	0.0	0.0	0.0	0.0	0.9	1.0	1.0
Hydrophobically	1.9	1.9	1.9	1.9	1.9	1.9	1.9	1.9	1.9
Modified Anionic
Thickener
Defoamer	0.9	0.9	0.9	0.9	0.9	0.9	0.9	0.9	0.9
Coalescent	0.6	0.6	0.6	0.6	0.6	0.6	0.6	0.6	0.6
Neutralization
Amine
Water	57.4	57.4	58.4	54.0	54.4	54.8	54.1	54.5	54.8
Total	300	300	300	300	300	300	300	300	300

The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.

Claims

We claim:

1. A coalescent and non-ionic surfactant blend comprising:

a) structure (1);

b) structure (2); and

c) structure (3);

wherein n is 1 to 5.

2. The coalescent and non-ionic surfactant blend of claim 1 further comprising a mixture of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, di-isopropyl ketone, isobutyl isobutyrate, isobutanol, and 2-isobutoxy-ethanol.

3. A composition derived by reacting 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate (TXOL) with ethylene oxide in the presence of a catalyst, at temperatures of from about 100° to 200° C., and under pressures of from about 345 kPa to 1800 kPa and separating ethoxylatedstructures (1), (2) and (3) from the reaction mixture:

wherein n is 1 to 5.

4. A coating composition comprising:

A. at least one latex compound;

B. at least one pigment;

C. a coalescent and non-ionic surfactant blend comprising:

a) 10 to 60 weight percent structure (1);

b) 5 to 50 weight percent structure (2);

c) 0 to 30 weight percent structure (3); and

based on the total weight of said coalescent and non-ionic surfactant mixture and wherein n is 1 to 5.

5. The coating composition of claim 4 wherein said latex compound is selected from the group comprising acrylic latex, vinyl acrylic latex, vinyl versatate vinyl acrylics latex, ethylene vinyl acetate latex, and styrene acrylic latex.

6. The coating composition of claim 4 wherein said pigment is TiO2, calcium carbonate, talc, silica, nepheline syenite, or clay.

7. A coalescent and non-ionic surfactant blend for use in aqueous architectural coatings comprising:

a) 10 to 60 weight percent structure (1);

b) 5 to 50 weight percent structure (2);

c) 0 to 30 weight percent structure (3); and

d) the balance to 100 weight percent a mixture of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, di-isopropyl ketone, isobutyl isobutyrate, isobutanol, and 2-isobutoxy-ethanol and wherein n is 1 to 5.