US20170305066A1 - Lighting for additive manufacturing - Google Patents
Lighting for additive manufacturing Download PDFInfo
- Publication number
- US20170305066A1 US20170305066A1 US15/513,483 US201415513483A US2017305066A1 US 20170305066 A1 US20170305066 A1 US 20170305066A1 US 201415513483 A US201415513483 A US 201415513483A US 2017305066 A1 US2017305066 A1 US 2017305066A1
- Authority
- US
- United States
- Prior art keywords
- build material
- light
- monochromatic light
- band
- exposing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
- B29C64/20—Apparatus for additive manufacturing; Details thereof or accessories therefor
- B29C64/264—Arrangements for irradiation
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
- B29C64/10—Processes of additive manufacturing
- B29C64/165—Processes of additive manufacturing using a combination of solid and fluid materials, e.g. a powder selectively bound by a liquid binder, catalyst, inhibitor or energy absorber
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
- B29C64/30—Auxiliary operations or equipment
- B29C64/386—Data acquisition or data processing for additive manufacturing
- B29C64/393—Data acquisition or data processing for additive manufacturing for controlling or regulating additive manufacturing processes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B33—ADDITIVE MANUFACTURING TECHNOLOGY
- B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
- B33Y10/00—Processes of additive manufacturing
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B33—ADDITIVE MANUFACTURING TECHNOLOGY
- B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
- B33Y50/00—Data acquisition or data processing for additive manufacturing
- B33Y50/02—Data acquisition or data processing for additive manufacturing for controlling or regulating additive manufacturing processes
Definitions
- Additive manufacturing machines produce 3D (three-dimensional) objects by building up layers of material. Some additive manufacturing machines are commonly referred to as “3D printers” because they often use inkjet or other printing technology to apply some of the manufacturing materials. 3D printers and other additive manufacturing machines make it possible to convert a CAD (computer aided design) model or other digital representation of an object directly into the physical object.
- 3D printers Some additive manufacturing machines are commonly referred to as “3D printers” because they often use inkjet or other printing technology to apply some of the manufacturing materials. 3D printers and other additive manufacturing machines make it possible to convert a CAD (computer aided design) model or other digital representation of an object directly into the physical object.
- CAD computer aided design
- FIGS. 1-9 present a sequence of sections illustrating one example for additive manufacturing a two slice object.
- FIGS. 10-13 are flow diagrams illustrating example additive manufacturing processes.
- FIG. 14 is a graph showing one example of light absorption as a function of wavelength for black, yellow, magenta, cyan and colorless coalescing agents.
- FIG. 15 is a graph showing one example of spectral intensity as a function of wavelength for monochromatic light sources that emit light near the peak absorptions of some of the coalescing agents shown in FIG. 14 .
- FIG. 16 illustrates one example of a processor readable medium with lighting instructions for additive manufacturing.
- FIG. 17 is a block diagram illustrating one example of an additive manufacturing machine implementing a controller that includes a processor readable medium with lighting instructions, such as the medium shown in FIG. 16 .
- FIG. 18 is a block diagram illustrating one example of an additive manufacturing system implementing a CAD computer program product that includes a processor readable medium with lighting instructions, such as the medium shown in FIG. 16 .
- FIG. 19 illustrates one example of a carriage assembly with a coalescing agent dispenser and a monochromatic light source for an additive manufacturing machine, such as the machine shown in FIG. 17 or FIG. 18 .
- Additive manufacturing machines make a 3D object through the solidification of one or more layers of a build material.
- Additive manufacturing machines make objects based on data in a 3D model of an object generated, for example, with a CAD computer program product. The model data is processed into slices each defining that part of a layer or layers of build material to be solidified.
- Examples of additive manufacturing described below use a technique sometimes referred to as “light area processing” (LAP) in which an ink or other suitable coalescing agent is dispensed on to a layer of build material in the desired pattern and then exposed to light.
- Light absorbing components in the coalescing agent absorb light to generate heat that sinters, melts or otherwise coalesces the patterned build material, allowing the patterned build material to solidify.
- LAP light area processing
- LAP heating may occur in two steps. First, the build material is heated to and maintained at temperature just below its coalescing temperature, for example with a combination of resistive heaters and a lower intensity heater lamp. Second, a coalescing agent is “printed” or otherwise dispensed on to the build material in the desired pattern and exposed to a higher intensity coalescing lamp emitting light absorbed into the patterned build material, Presently, halogen lamps emitting light over a broad spectrum are usually used in both steps. Accordingly, carbon black ink is often used as the coalescing agent to absorb light over a broad spectrum to generate enough heat to effectively coalesce the patterned build material. The use of black ink, however, limits the color of the manufactured objects to black and grey.
- color objects may be manufactured with LAP using colored and colorless inks that have high light absorption within a narrow band of wavelengths.
- Colorless inks that absorb only infrared light may be particularly desirable coalescing agents because they enable manufacturing objects that are the same color as the starting build material.
- 84030477 and 84030486 and titled 3-Dimensional Printing have been developed for use as ink based LAP coalescing agents
- Broad band halogen lamps may be inadequate for heating build material patterned with colored and colorless inks because only a small portion of the light emitted falls within the band of wavelengths where high light absorption occurs, and thus the amount of absorbed radiative energy may be inadequate to heat the patterned build material to a coalescing temperature.
- light emitted outside this band of wavelengths may have undesirable heating effects.
- New LAP lighting techniques have been developed to manufacture color objects (other than black and grey) using color and colorless coalescing agents, including the colorless dyes described in the 84030477 and 84030486 patent applications.
- Examples of the new techniques utilize monochromatic light covering the peak light absorption of the coalescing agent to develop the heat needed to reach coalescing temperatures.
- an additive manufacturing process includes dispensing a liquid coalescing agent on to build material in a pattern corresponding to an object slice and then exposing the patterned build material to monochromatic light within a band of wavelengths that includes a peak light absorption of the coalescing agent.
- the intensity of the monochromatic light needed for adequate heating may vary depending on the characteristics of the build material and coalescing agent, it is expected that monochromatic light with a spectral intensity at least 1 ⁇ 10 12 Wm ⁇ 3 sr ⁇ 1 (watts per cubic meter per steradian) will be sufficient for many implementations.
- a carriage assembly for an additive manufacturing machine carries an array of individually addressable monochromatic light sources along with an inkjet printhead to dispense the coalescing agent.
- Individual light sources may be energized selectively to illuminate only patterned build material to limit unwanted effects on surrounding build material and to reduce power consumption.
- the array may include a single set of monochromatic light sources (only one wavelength band) corresponding to a coalescing agent with an absorption peak within the band, or multiple sets of light sources (multiple wavelength bands) to accommodate a greater range of coalescing agents.
- the use of a monochromatic lighting array enables an integrated carriage assembly to carry both the printhead(s) and the light sources for immediate, targeted lighting.
- the electronic instructions to control monochromatic lighting in an additive manufacturing machine may reside on a processor readable medium implemented, for example, in a CAD computer program product, in an object model processor, or in the controller for the additive manufacturing machine.
- “coalesce” means to become a coherent mass by heating, for example by sintering or melting;
- a “coalescing agent” means a substance that causes or helps cause a build material to coalesce;
- a “coalescence modifier agent” means a substance that inhibits or prevents coalescence of a build material, for example by modifying the effect of a coalescing agent;
- monochromatic means within a band of wavelengths 30 nm or narrower; “polychromatic” means a band of wavelengths broader than 30 nm; and
- a “slice” means one or more slices of a multi-slice object or the object itself for a single slice object.
- FIGS. 10 and 11 are flow diagrams illustrating example additive manufacturing processes 100 and 130 , respectively, implemented in the example of FIGS. 1-9 .
- a supply 12 of powdered build material 14 is held on a delivery piston 16 in a supply bed 18 .
- a roller or other suitable layering device 20 moves build material 14 from supply bed 18 to a receiving piston 22 in a manufacturing bed 24 , as indicated by arrow 26 .
- Pistons 16 and 22 move up and down, respectively, as build material 14 is moved from supply bed 18 to manufacturing bed 24 .
- Any suitable build material 14 may be used to make the desired solid object, which may be hard or soft, rigid or flexible, elastic or inelastic. Also, while a powdered build material 14 is depicted by particles 28 in this example, suitable non-powdered build materials could be used.
- a first layer 30 of build material 14 is formed in manufacturing bed 24 as shown in FIG. 1 (block 102 in FIG. 11 ).
- Individual layers of build material 14 may be pre-heated in manufacturing bed 24 , as shown in FIG. 1 (block 104 in FIG. 10 ), or build material 14 may be pre-heated in supply bed 18 , or a combination of heating in both beds 18 and 24 .
- Pre-heating in this context refers to heating before light is applied to coalesce build material for coalescence, as described below with reference to FIG. 4 .
- the pre-heating temperature will vary depending on the characteristics of build material 14 , the pre-heating temperature usually will be 20° C. to 50° C. below the melting point or the sintering point for a nylon 12 powdered build material.
- Any suitable heater 32 may be used. In the example shown in FIG. 1 , heater 32 includes a heating lamp positioned over bed 24 . In other examples, heater 32 may include a resistive heater in the powder bed used alone or with a heating lamp.
- a coalescing agent 34 is dispensed on to build material 14 in layer 30 in a pattern corresponding to the first object slice (block 106 in FIG. 10 ), for example with an inkjet type dispenser 36 .
- This pattern for coalescing agent 34 is depicted by an area 38 of dense stippling in the figures.
- a coalescence modifier agent 40 may be dispensed on to build material 14 in layer 30 for example with an inkjet type dispenser 44 , as shown in FIG. 3 (block 108 in FIG. 10 ).
- Modifier agent 40 blocks or neutralizes the effects of the coalescing agent and may be applied before or after coalescing agent (or both before and after) to help control the degree of coalescence of targeted areas of build material for improved dimensional accuracy and overall quality of the manufactured object.
- modifier agent 40 is dispensed on to an area 42 covering the area where a second object slice will overhang the first slice. Overhang area 42 covered by coalescence modifier agent 40 is depicted by light stippling in the figures.
- Coalescence modifier agent 40 may also be dispensed on to other areas of build material layer 30 to help define other aspects of the object slice, including interspersed with the pattern of the coalescing agent to change the material characteristics of the slice.
- two dispensers 36 , 44 are shown, agents 34 and 40 could be dispensed from the same dispensers integrated into a single device, for example using different printheads (or groups of printheads) in a single inkjet printhead assembly.
- Coalescing agent 34 includes a light absorbing component to absorb light to generate heat that sinters, melts or otherwise coalesces patterned build material 38 .
- the rate of light absorption for different types of coalescing agents 34 will vary over different parts of the electromagnetic spectrum depending on the characteristics of the light absorbing component. For example, a yellow colorant may have a peak light absorption at about 450 nm wavelength light. A cyan colorant, by contrast, may have a peak light absorption at about 700 nm wavelength light. Black ink may have high absorption across a broad band of wavelengths compared to high absorption for yellow and cyan across narrow bands of wavelengths.
- the area of layer 30 patterned with coalescing agent 34 is exposed to monochromatic light 46 from a light source 48 to coalesce build material patterned with coalescing agent 34 , allowing the patterned build material to solidify and form first object slice 50 (block 110 in FIG. 10 ).
- light source 48 is configured to emit monochromatic light 46 within a band of wavelengths that includes the peak light absorption of coalescing agent 34 with sufficient intensity to coalesce patterned build material.
- Any suitable light source 48 may be used to emit monochromatic light including, for example, LEDs, laser diodes and other sources that emit monochromatic light directly as well as light sources that emit monochromatic light by filtering, splitting, dispersing, refracting or otherwise producing monochromatic light from polychromatic light.
- the process may be repeated for second and subsequent layers to form a multi-slice object.
- a second layer 52 of build material 14 is formed in manufacturing bed 24 over first layer 30 (block 112 in FIG. 10 ) and pre-heated (block 114 in FIG. 10 ).
- a coalescing agent 34 is dispensed on to build material 14 in layer 52 in a pattern 54 corresponding to the second object slice (block 116 in FIG. 10 ), including along the edge of an area 56 overhanging first slice 50 .
- FIG. 5 a second layer 52 of build material 14 is formed in manufacturing bed 24 over first layer 30 (block 112 in FIG. 10 ) and pre-heated (block 114 in FIG. 10 ).
- a coalescing agent 34 is dispensed on to build material 14 in layer 52 in a pattern 54 corresponding to the second object slice (block 116 in FIG. 10 ), including along the edge of an area 56 overhanging first slice 50 .
- a coalescence modifier agent 40 is dispensed on to build material 14 in layer 52 in area 58 to help prevent the unwanted coalescence and solidification of build material along the edge of the overhang (block 118 in FIG. 10 ).
- the area 54 of layer 52 patterned with coalescing agent 34 is exposed to monochromatic light 46 to coalesce build material and form second object slice 60 overhanging first slice 46 (block 120 in FIG. 10 ).
- Agent dispensers 36 and 44 may be carried back and forth across manufacturing bed 24 together with light source 48 , as indicated by arrows 62 in FIGS. 1-8 , on a single carriage or on two or more separate carriages. Also, it may be possible in some implementations to use stationary agent dispensers 36 , 44 and/or light sources 48 .
- Coalescing agent 34 dispensed on to build material 14 in second layer 52 may be the same as or different from the coalescing agent dispensed on to first layer 30 . Accordingly, monochromatic light 46 to coalesce patterned build material in second layer 52 may be the same or different wavelength from the light to coalesce patterned build material in first layer 30 . Also, while distinct first and second slices 50 and 60 are shown in FIG.
- the two slices actually fuse together into a single part upon coalescing and solidification of the second slice.
- the now fused slices 50 , 60 may be removed from manufacturing bed 24 as a finished object 10 shown in FIG. 9 .
- a simple two-slice object 10 is shown, the same process steps may be used to form more complex, multi-slice objects.
- FIG. 11 illustrates another example of an additive manufacturing process 130 .
- a liquid coalescing agent is dispensed on to build material in a pattern corresponding to a slice (block 132 ) and patterned build material is exposed to monochromatic light within a band of wavelengths that includes a peak light absorption of the coalescing agent (block 134 ).
- the wavelength of the monochromatic light will vary depending on the peak absorption of the light absorbing component in the coalescing agent. Several examples are described below with reference to the graphs shown in FIGS. 14 and 15 .
- the intensity of the monochromatic light should be great enough to allow the patterned build material to reach a coalescing temperature within a practical period of time. Thus, as shown in FIG.
- exposing patterned build material to monochromatic light in block 134 of FIG. 11 may be performed, for example, by exposing patterned build material to monochromatic light with a spectral intensity at least 1 ⁇ 10 12 Wm ⁇ 3 sr ⁇ 1 .
- exposing patterned build material to monochromatic light in block 134 of FIG. 11 may be performed by exposing patterned build material to monochromatic light with a spectral intensity at least 1 ⁇ 10 12 Wm ⁇ 3 sr ⁇ 1 to raise the temperature of the patterned build material 20° C. to 50° C. in a quite practical time of 1 second or less.
- FIG. 14 shows light absorption as a function of wavelength for black, yellow, magenta, cyan and colorless ink coalescing agents.
- a colorant acts as the light absorbing component in each ink which, for the color inks represented in FIG. 14 , is a color pigment.
- the pigment based inkjet inks represented in FIG. 14 are commercially available from Hewlett-Packard Company as C8750 (black), C4905 (yellow), C4904 (magenta), and C4903 (cyan).
- a colorless dye acts as the light absorbing component in the colorless dye based ink represented in FIG. 14 . Two such dyes are described in the 84030477 and 84030486 patent applications noted above.
- FIG. 15 shows spectral intensity as a function of wavelength for several examples of commercially available light sources that emit monochromatic light near the peak absorptions for the color coalescing agents shown in FIG. 14 . (Suitable light sources that emit monochromatic light near the peak absorption for the colorless coalescing agent shown in FIG. 14 are not yet readily available commercially.)
- FIG. 15 also shows the spectral intensity of a 2500K halogen lamp relative to the monochromatic light sources.
- a colorless ink such as that represented in FIG. 14 will absorb 60% or more light in the band of 800 nm to 1350 nm, including 808 nm light emitted by the infrared laser diode in FIG. 15 .
- a yellow ink such as that represented in FIG. 14 will absorb 60% or more light in the band of 380 nm to 500 nm, including the 450 nm light emitted by the blue laser diode and the 470 nm light emitted by the blue LED in FIG. 15 .
- a magenta ink such as that represented in FIG. 14 will absorb 60% or more light in the band of 420 nm to 600 nm, including the 590 nm light emitted by the yellow LED in FIG. 15 .
- a cyan ink such as that represented in FIG. 14 will absorb 60% or more light in the band of 520 nm to 700 nm, including the 590 nm light emitted by the yellow LED and the 640 nm red LED in FIG. 15 .
- a black ink such as that represented in FIG. 14 will absorb 60% or more light across the full spectrum of visible light (380 nm to 700 nm), including light emitted by any of the color LEDs and laser diodes in FIG. 15 .
- the spectral intensity of the monochromatic light is significantly higher at or near peak absorption than the spectral intensity of the polychromatic light emitted by a 2500K halogen lamp. It has been demonstrated that monochromatic light sources such as the LEDs and laser diodes represented in FIG. 15 produce enough energy to generate the heat needed to coalesce polymer build materials when matched to the proper light absorbing component in the coalescing agent.
- a nylon 12 build material powder that coalesces at about 185° C. is pre-heated to about 150° C., patterned with a yellow ink from FIG. 14 , and exposed to a blue LED emitting 470 nm light from a distance less than 2 cm.
- the yellow ink absorbing nearly 100% of the incident light should generate sufficient heat to reach the coalescing temperature of about 185° C. at least 10 times faster than with a 2500K halogen lamp. If the patterned build material is exposed to a blue laser diode emitting 450 nm light, the coalescing temperature may be reached even faster. While the threshold absorption for adequate heating will vary depending on the build material and the monochromatic light source, it is expected that sufficient heat may be generated in an exposure time less than 1 second if the coalescing agent absorbs incident light at a rate of 60% or more for matching light with a spectral intensity at least 1 ⁇ 10 12 Wm ⁇ 3 sr ⁇ 1 .
- FIG. 16 is a block diagram illustrating a processor readable medium 64 with instructions 66 to control lighting during the manufacture of a 3D object.
- a processor readable medium 64 is any non-transitory tangible medium that can embody, contain, store, or maintain instructions for use by a processor.
- Processor readable media include, for example, electronic, magnetic, optical, electromagnetic, or semiconductor media. More specific examples of suitable processor readable media include a hard drive, a random access memory (RAM), a read-only memory (ROM), memory cards and sticks and other portable storage devices.
- Lighting instructions 66 include instructions to control monochromatic lighting during the manufacture of a 3D object, for example by exposing patterned build material to monochromatic light at block 134 in FIGS. 11-13 .
- Instructions 66 may include other lighting instructions, for example instructions to pre-heat build material at block 104 in FIG. 10 with a heating lamp 32 in FIGS. 1-8 .
- Processor readable medium 64 with instructions 66 may be implemented, for example, in a CAD computer program product, in an object model processor, or in a controller for an additive manufacturing machine.
- Control data to inhibit solidification can be generated, for example, by processor readable instructions on the source application, usually a CAD computer program product, in an object model processor, or by processor readable instructions on the additive manufacturing machine.
- FIG. 17 is a block diagram illustrating one example of an additive manufacturing machine 68 implementing a controller 70 with lighting instructions 66 .
- machine 68 includes controller 70 , a manufacturing bed or other suitable support 24 , a roller or other suitable build material layering device 20 , a coalescing agent dispenser 36 , a coalescence modifier agent dispenser 44 , a heater 32 and a light source 48 .
- the in-process object structure is supported on support 24 during manufacturing.
- support 24 is movable at the urging of controller 70 to compensate for the changing thickness of the in-process structure, for example as layers of build material are added during manufacturing.
- Build material layering device 20 layers build material on support 24 and on the in-process structures and may include, for example, a device to dispense the build material and a blade or roller to distribute the build material uniformly to the desired thickness for each layer.
- Coalescing agent dispenser 36 dispenses coalescing agent selectively at the direction of controller 70 on to build material, for example as described above with reference to FIGS. 2 and 6 .
- Coalescence modifier agent dispenser 44 dispenses modifier agent selectively at the direction of controller 70 on to build material, for example as described above with reference to FIGS. 3 and 7 .
- Manufacturing machine 68 may include a heater 32 if it is desired to pre-heat the build material.
- Manufacturing machine 36 includes a light source 48 to apply light energy to coalesce build material treated with coalescing agent, for example as described above with reference to FIGS. 5 and 8 .
- Controller 70 represents the processor (or multiple processors), the associated memory (or multiple memories) and instructions, and the electronic circuitry and components needed to control the operative elements of machine 68 .
- controller 70 includes a memory 72 having a processor readable medium 64 with lighting instructions 66 and a processor 74 to read and execute instructions 66 .
- controller 70 would receive control data and other instructions from a CAD program to make an object and execute local lighting instructions 66 as part of the process of making the object.
- lighting instructions 66 may be embodied in a processor readable medium 64 separate from controller 70 , for example as part of a CAD computer program product shown in FIG. 18 .
- an additive manufacturing system 76 includes an additive manufacturing machine 68 operatively connected to a CAD computer program product 78 with lighting instructions 66 residing on a processor readable medium 64 .
- Any suitable connection between machine 68 and CAD program product 78 may be used to communicate instructions and control data to machine 68 including, for example, a wired link, a wireless link, and a portable connection such as a flash drive or compact disk.
- FIG. 19 illustrates one example of a carriage assembly 79 for an additive manufacturing machine such as machine 68 shown in FIGS. 17 and 18 .
- carriage assembly 79 includes a carriage 80 carrying agent dispensers 36 , 44 and a light source 48 .
- Carriage 80 is movable back and forth over manufacturing bed 24 to dispense coalescing and modifier agents 34 , 40 , for example as shown in FIGS. 2-3 and 6-7 , and to expose patterned build material to monochromatic light 46 , for example as shown in FIGS. 4 and 8 .
- FIG. 19 illustrates one example of a carriage assembly 79 for an additive manufacturing machine such as machine 68 shown in FIGS. 17 and 18 .
- carriage assembly 79 includes a carriage 80 carrying agent dispensers 36 , 44 and a light source 48 .
- Carriage 80 is movable back and forth over manufacturing bed 24 to dispense coalescing and modifier agents 34 , 40 , for example as shown in FIGS. 2-3 and 6-7 , and to expose patterned build material to
- agent dispensers 36 and 44 are configured as elongated inkjet printheads that span the width of bed 24 with an array of nozzles 82 through which the agents are dispensed on to build material supported on bed 24 , or that span so much of the width of bed 24 corresponding to a build zone 88 for layering and coalescing the build material. While two printheads 36 , 44 with only a single line of dispensing nozzles are shown, other configurations are possible. For example, more or fewer printheads could be used each with a different array of dispensing nozzles, including printheads and nozzles to dispense multiple different color (or colorless coalescing agents.
- light source 48 is configured as a pair of light bars 84 that span the width of bed 24 with an array of individually addressable LEDs, laser diodes or other monochromatic light sources 86 , or that span so much of the width of bed 24 corresponding to a build zone 88 for layering and coalescing the build material.
- Each of the light sources 86 or each of multiple groups of the light sources 86 is individually addressable in the array to emit light selectively independent of any other light source in the array or of any other group of light sources in the array.
- Each light bar 84 is positioned outboard of agent dispensers 36 , 44 to enable illuminating patterned build material on bed 24 immediately after dispensing an agent 34 , 40 , if desired, when carriage 80 is moving in either direction across bed 24 .
- Individual light sources 86 may be energized selectively at the direction of the controller 70 to illuminate only patterned build material to limit unwanted effects on surrounding build material and to reduce power consumption.
- each light bar 84 may include a single set of monochromatic lights (only one wavelength band) corresponding to coalescing agents with absorption peaks within that band, or multiple sets of lights (multiple wavelength bands) to accommodate a greater range of coalescing agents. Other suitable lighting configurations are possible.
- light source 48 may he supported on a carriage distinct from the carriage supporting the agent dispenser(s).
- light source 48 may be configured as a stationary array of monochromatic light sources 86 covering build zone 88 .
- each light bar 84 includes a line of monochromatic red light sources, a line of monochromatic green light sources and a line of monochromatic blue light sources to cover corresponding absorption peaks for cyan, magenta, and yellow coalescing agents, respectively.
- Lines or other arrays of multiple monochromatic light sources enable manufacturing an object with different color parts using a single light source 48 .
- a first color (or colorless) coalescing agent 34 may be dispensed at block 106 in FIG.
- dispensing a coalescing agent at one or both blocks 106 and 116 may include patterning build material with multiple, different coalescing agents 34 and exposing the different patterns to corresponding multiple, different monochromatic light 46 to obtain different colors within the same layer of build material.
- Suitable coalescing agents include water or solvent based dispersions with a light absorbing component.
- the coalescing agent may be an ink that includes colored or colorless pigments or dyes as the light absorbing component.
- Suitable coalescence modifier agents may separate individual particles of the build material to prevent the particles from joining together and solidifying as part of the slice.
- this type of coalescence modifier agent include colloidal, dye-based, and polymer-based inks, as well as solid particles that have an average size less than the average size of particles of the build material.
- the molecular mass of the coalescence modifier agent and its surface tension should be such that it enables the agent to penetrate sufficiently into the build material to achieve the desired mechanical separation.
- a salt solution may be used as a coalescence modifier agent.
- inks commercially known as CM996A and CN673A available from Hewlett-Packard Company may be used as a coalescence modifier agent.
- Suitable coalescence modifier agents may act to modify the effects of a coalescing agent by preventing build material from reaching its coalescing temperature during heating.
- a fluid that exhibits a suitable cooling effect may be used as this type of coalescence modifier agent.
- heat in the build material may be absorbed evaporating the fluid to help prevent build material from reaching its coalescing temperature.
- a fluid with a high water content may be a suitable coalescence modifier agent.
- Other types of coalescence modifier agent may be used.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Physics & Mathematics (AREA)
- Mechanical Engineering (AREA)
- Optics & Photonics (AREA)
- Health & Medical Sciences (AREA)
- Toxicology (AREA)
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/US2014/057715 WO2016048357A1 (en) | 2014-09-26 | 2014-09-26 | Lighting for additive manufacturing |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2014/057715 A-371-Of-International WO2016048357A1 (en) | 2014-09-26 | 2014-09-26 | Lighting for additive manufacturing |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/735,211 Continuation US20200139627A1 (en) | 2014-09-26 | 2020-01-06 | Lighting for additive manufacturing |
Publications (1)
Publication Number | Publication Date |
---|---|
US20170305066A1 true US20170305066A1 (en) | 2017-10-26 |
Family
ID=55581673
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US15/513,483 Abandoned US20170305066A1 (en) | 2014-09-26 | 2014-09-26 | Lighting for additive manufacturing |
US16/735,211 Pending US20200139627A1 (en) | 2014-09-26 | 2020-01-06 | Lighting for additive manufacturing |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/735,211 Pending US20200139627A1 (en) | 2014-09-26 | 2020-01-06 | Lighting for additive manufacturing |
Country Status (5)
Country | Link |
---|---|
US (2) | US20170305066A1 (zh) |
EP (1) | EP3197667B1 (zh) |
CN (1) | CN107073827B (zh) |
TW (2) | TWI664070B (zh) |
WO (1) | WO2016048357A1 (zh) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2019190461A1 (en) * | 2018-03-26 | 2019-10-03 | Hewlett-Packard Development Company, L.P. | Lighting assembly |
EP3711962A1 (en) * | 2019-03-22 | 2020-09-23 | HP Scitex Ltd | Radiation sources for colorants |
US20220250319A1 (en) * | 2019-08-05 | 2022-08-11 | Hewlett-Packard Development Company, L.P. | Additive manufacturing with laser arrays |
Families Citing this family (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP3445565B1 (en) * | 2016-04-20 | 2022-08-17 | Hewlett-Packard Development Company, L.P. | Three-dimensional (3d) printing with epoxy mold compound |
CN108602265B (zh) * | 2016-05-17 | 2020-09-08 | 惠普发展公司,有限责任合伙企业 | 具有调整的冷却剂液滴的3d打印机 |
US11072112B2 (en) | 2016-07-19 | 2021-07-27 | Hewlett-Packard Development Company, L.P. | Additive manufacturing including selective heating |
CN109153178A (zh) | 2016-07-22 | 2019-01-04 | 惠普发展公司,有限责任合伙企业 | 3d打印中的移位 |
WO2018046582A1 (de) | 2016-09-08 | 2018-03-15 | Ineos Styrolution Group Gmbh | Thermoplastische polymerpulver für das selektive lasersintern (sls) |
WO2020058312A1 (de) | 2018-09-21 | 2020-03-26 | Ineos Styrolution Group Gmbh | Thermoplastische polymerpulver und deren anwendung für das selektive lasersintern |
WO2020058313A1 (de) | 2018-09-21 | 2020-03-26 | Ineos Styrolution Group Gmbh | Verfahren des selektiven lasersinterns unter verwendung von thermoplastischen polymerpulvern |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060093958A1 (en) * | 2004-10-28 | 2006-05-04 | Vladek Kasperchik | Color forming compositions and associated methods |
US20060134419A1 (en) * | 2004-12-21 | 2006-06-22 | Degussa Ag | Use of polyarylene ether ketone powder in a three-dimensional powder-based moldless production process, and moldings produced therefrom |
US20070183918A1 (en) * | 2004-03-16 | 2007-08-09 | Degussa Ag | Method and device for producing three-dimensional objects using laser technology and for applying an absorber using an ink jet method |
Family Cites Families (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
SE509088C2 (sv) * | 1997-04-30 | 1998-12-07 | Ralf Larsson | Sätt och anordning för framställning av volymkroppar |
US6658314B1 (en) * | 1999-10-06 | 2003-12-02 | Objet Geometries Ltd. | System and method for three dimensional model printing |
JP2001145956A (ja) * | 1999-11-19 | 2001-05-29 | Meiko:Kk | 光硬化性樹脂三次元造形物の積層造形装置及びその積層造形方法 |
US20020093115A1 (en) * | 2001-01-12 | 2002-07-18 | Jang B. Z. | Layer manufacturing method and apparatus using a programmable planar light source |
JP2002316363A (ja) * | 2001-02-16 | 2002-10-29 | Fuji Photo Film Co Ltd | 光造形装置及び露光ユニット |
CN1188464C (zh) * | 2002-04-26 | 2005-02-09 | 北京北方恒利科技发展有限公司 | 用于激光烧结快速成型制品的尼龙粉末材料 |
GB0317387D0 (en) * | 2003-07-25 | 2003-08-27 | Univ Loughborough | Method and apparatus for combining particulate material |
DE102004020452A1 (de) * | 2004-04-27 | 2005-12-01 | Degussa Ag | Verfahren zur Herstellung von dreidimensionalen Objekten mittels elektromagnetischer Strahlung und Auftragen eines Absorbers per Inkjet-Verfahren |
CN101180174B (zh) * | 2005-05-20 | 2012-08-08 | 亨斯迈先进材料(瑞士)有限公司 | 快速原型开发设备和快速原型开发方法 |
KR101238340B1 (ko) * | 2011-07-28 | 2013-03-04 | 박인백 | 가시광선 스캔형 저비용 쾌속조형장치 |
US8686062B1 (en) * | 2012-11-02 | 2014-04-01 | Xerox Corporation | Radiation curable red gel ink formulations |
CN103921444B (zh) * | 2014-05-04 | 2016-09-14 | 中山市东方博达电子科技有限公司 | 光固化3d打印机、光固化3d打印方法及装置 |
-
2014
- 2014-09-26 EP EP14902469.7A patent/EP3197667B1/en active Active
- 2014-09-26 US US15/513,483 patent/US20170305066A1/en not_active Abandoned
- 2014-09-26 WO PCT/US2014/057715 patent/WO2016048357A1/en active Application Filing
- 2014-09-26 CN CN201480082184.9A patent/CN107073827B/zh active Active
-
2015
- 2015-09-10 TW TW104129938A patent/TWI664070B/zh active
- 2015-09-10 TW TW107136776A patent/TWI680860B/zh active
-
2020
- 2020-01-06 US US16/735,211 patent/US20200139627A1/en active Pending
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070183918A1 (en) * | 2004-03-16 | 2007-08-09 | Degussa Ag | Method and device for producing three-dimensional objects using laser technology and for applying an absorber using an ink jet method |
US20060093958A1 (en) * | 2004-10-28 | 2006-05-04 | Vladek Kasperchik | Color forming compositions and associated methods |
US20060134419A1 (en) * | 2004-12-21 | 2006-06-22 | Degussa Ag | Use of polyarylene ether ketone powder in a three-dimensional powder-based moldless production process, and moldings produced therefrom |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2019190461A1 (en) * | 2018-03-26 | 2019-10-03 | Hewlett-Packard Development Company, L.P. | Lighting assembly |
US11181244B2 (en) | 2018-03-26 | 2021-11-23 | Hewlett-Packard Development Company, L.P. | Lighting assembly |
EP3711962A1 (en) * | 2019-03-22 | 2020-09-23 | HP Scitex Ltd | Radiation sources for colorants |
US10838182B2 (en) | 2019-03-22 | 2020-11-17 | Hp Scitex Ltd. | Radiation sources for colorants |
US11390094B2 (en) | 2019-03-22 | 2022-07-19 | Hp Scitex Ltd. | Radiation sources for colorants |
US20220250319A1 (en) * | 2019-08-05 | 2022-08-11 | Hewlett-Packard Development Company, L.P. | Additive manufacturing with laser arrays |
Also Published As
Publication number | Publication date |
---|---|
TWI664070B (zh) | 2019-07-01 |
TWI680860B (zh) | 2020-01-01 |
TW201622955A (zh) | 2016-07-01 |
WO2016048357A1 (en) | 2016-03-31 |
US20200139627A1 (en) | 2020-05-07 |
EP3197667B1 (en) | 2021-06-02 |
TW201906714A (zh) | 2019-02-16 |
EP3197667A1 (en) | 2017-08-02 |
EP3197667A4 (en) | 2018-05-16 |
CN107073827A (zh) | 2017-08-18 |
CN107073827B (zh) | 2022-06-10 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20220362992A1 (en) | Lighting for additive manufacturing | |
US20200139627A1 (en) | Lighting for additive manufacturing | |
US10688716B2 (en) | Consolidating a build material for additive manufacturing | |
US20210197461A1 (en) | Additive manufacturing | |
EP3271146B1 (en) | Coalescing agent concentrations and contone densities for three-dimensional objects | |
TWI642534B (zh) | 積層製造方法和裝置 | |
US20230191695A1 (en) | Three-dimensional object production | |
US11220046B2 (en) | Additive manufacturing | |
US20210016350A1 (en) | Preheat dyed build materials with preheating sources | |
US20230286054A1 (en) | Increasing energy absorption during additive manufacturing | |
WO2017127114A1 (en) | Layering powdered build material for additive manufacturing | |
US11780166B2 (en) | Preheat build materials with preheating sources | |
WO2017127113A1 (en) | Layering powdered build material for additive manufacturing |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P., TEXAS Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NAUKA, KRZYSZTOF;GANAPATHIAPPAN, SIVAPACKIA;ZHAO, LIHUA;AND OTHERS;SIGNING DATES FROM 20140925 TO 20140926;REEL/FRAME:042060/0409 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |