US20170279130A1 - Separator layer for flow battery - Google Patents

Separator layer for flow battery Download PDF

Info

Publication number
US20170279130A1
US20170279130A1 US15/079,239 US201615079239A US2017279130A1 US 20170279130 A1 US20170279130 A1 US 20170279130A1 US 201615079239 A US201615079239 A US 201615079239A US 2017279130 A1 US2017279130 A1 US 2017279130A1
Authority
US
United States
Prior art keywords
electrode
flow battery
separator layer
polymer
recited
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/079,239
Inventor
Scott Alan Eastman
Wei Xie
Michael L. Perry
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
RTX Corp
Original Assignee
United Technologies Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by United Technologies Corp filed Critical United Technologies Corp
Priority to US15/079,239 priority Critical patent/US20170279130A1/en
Assigned to UNITED TECHNOLOGIES CORPORATION reassignment UNITED TECHNOLOGIES CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: PERRY, MICHAEL L., EASTMAN, Scott Alan, XIE, WEI
Priority to KR1020170024509A priority patent/KR20170113065A/en
Priority to EP17161778.0A priority patent/EP3223340B1/en
Priority to JP2017053854A priority patent/JP6951848B2/en
Priority to CN201710169177.8A priority patent/CN107230792B/en
Publication of US20170279130A1 publication Critical patent/US20170279130A1/en
Assigned to RAYTHEON TECHNOLOGIES CORPORATION reassignment RAYTHEON TECHNOLOGIES CORPORATION CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: UNITED TECHNOLOGIES CORPORATION
Assigned to RAYTHEON TECHNOLOGIES CORPORATION reassignment RAYTHEON TECHNOLOGIES CORPORATION CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: UNITED TECHNOLOGIES CORPORATION
Assigned to RAYTHEON TECHNOLOGIES CORPORATION reassignment RAYTHEON TECHNOLOGIES CORPORATION CORRECTIVE ASSIGNMENT TO CORRECT THE AND REMOVE PATENT APPLICATION NUMBER 11886281 AND ADD PATENT APPLICATION NUMBER 14846874. TO CORRECT THE RECEIVING PARTY ADDRESS PREVIOUSLY RECORDED AT REEL: 054062 FRAME: 0001. ASSIGNOR(S) HEREBY CONFIRMS THE CHANGE OF ADDRESS. Assignors: UNITED TECHNOLOGIES CORPORATION
Priority to US17/942,474 priority patent/US20230016898A1/en
Abandoned legal-status Critical Current

Abstract

A flow battery includes an electrochemical cell that has a first electrode, a second electrode spaced apart from the first electrode, and a separator layer arranged between the first electrode and the second electrode. The separator layer is formed of a polymer that has a polymer backbone with cyclic groups that are free of unsaturated nitrogen and one or more polar groups bonded between the cyclic groups.

Description

    BACKGROUND
  • Flow batteries, also known as redox flow batteries or redox flow cells, are designed to convert electrical energy into chemical energy that can be stored and later released when there is demand. As an example, a flow battery may be used with a renewable energy system, such as a wind-powered system, to store energy that exceeds consumer demand and later release that energy when there is greater demand.
  • A typical flow battery includes a redox flow cell that has a negative electrode and a positive electrode separated by an ion-exchange membrane. A negative fluid electrolyte (sometimes referred to as the anolyte) is delivered to the negative electrode and a positive fluid electrolyte (sometimes referred to as the catholyte) is delivered to the positive electrode to drive electrochemically reversible redox reactions. Upon charging, the electrical energy supplied causes a chemical reduction reaction in one electrolyte and an oxidation reaction in the other electrolyte. The separator prevents the electrolytes from freely and rapidly mixing but permits selected ions to pass through to complete the redox reactions. Upon discharge, the chemical energy contained in the liquid electrolytes is released in the reverse reactions and electrical energy can be drawn from the electrodes. Flow batteries are distinguished from other electrochemical devices by, inter alia, the use of externally-supplied, fluid electrolyte solutions that include reactants that participate in reversible electrochemical reactions.
  • SUMMARY
  • A flow battery according to an example of the present disclosure includes an electrochemical cell that has a first electrode, a second electrode spaced apart from the first electrode, and a separator layer arranged between the first electrode and the second electrode. The separator layer is formed of a polymer having a polymer backbone with aromatic groups that are free of unsaturated nitrogen and one or more polar groups bonded in the polymer backbone.
  • In a further embodiment of any of the foregoing embodiments, the one or more polar groups includes an atom selected from the group consisting of sulfur, oxygen, nitrogen, and combinations thereof.
  • In a further embodiment of any of the foregoing embodiments, the aromatic groups include nitrogen heterocycles.
  • In a further embodiment of any of the foregoing embodiments, the polymer backbone is free of unsaturated nitrogen.
  • In a further embodiment of any of the foregoing embodiments, the polymer includes at least one of adsorbed acid groups or aqueous electrolyte that is non-covalently bonded to the one or more polar groups.
  • In a further embodiment of any of the foregoing embodiments, the polymer includes polyetherimide (PEI).
  • In a further embodiment of any of the foregoing embodiments, the polymer includes polyamide-imide (PAI).
  • In a further embodiment of any of the foregoing embodiments, the polymer includes polyetheretherketone (PEEK).
  • In a further embodiment of any of the foregoing embodiments, the polymer includes polysulfone (PSF).
  • In a further embodiment of any of the foregoing embodiments, the polymer includes polyphenylene sulfide (PPS).
  • In a further embodiment of any of the foregoing embodiments, the polymer is selected from the group consisting of polyetherimide (PEI), polyamide-imide (PAI), polyetheretherketone (PEEK), polysulfone (PSF), polyphenylene sulfide (PPS), and combinations thereof.
  • A further embodiment of any of the foregoing embodiments includes a supply/storage system external of the electrochemical cell. The supply/storage system includes first and second vessels, first and second liquid electrolytes in, respectively, the first and second vessels, fluid lines connecting the first and second vessels to, respectively, the first electrode and the second electrode, and a plurality of pumps operable to circulate the first and second liquid electrolytes via the fluid lines between the first and second vessels and the electrochemical cell.
  • In a further embodiment of any of the foregoing embodiments, the separator layer has an area specific resistance of less than approximately 425 mΩ*cm2.
  • A separator layer for use in a flow battery, the separator layer being formed of a polymer having a polymer backbone with aromatic groups that are free of unsaturated nitrogen, wherein the separator layer has an area specific resistance of less than approximately 425 mΩ*cm2.
  • In a further embodiment of any of the foregoing embodiments, the separator layer has an area specific resistance of less than approximately 300 mΩ*cm2.
  • In a further embodiment of any of the foregoing embodiments, the polymer is selected from the group consisting of polyetherimide (PEI), polyamide-imide (PAI), polyetheretherketone (PEEK), polysulfone (PSF), polyphenylene sulfide (PPS), polystyrene (PS) and combinations thereof.
  • A flow battery according to an example of the present disclosure includes an electrochemical cell that has a first electrode, a second electrode spaced apart from the first electrode, and a separator layer arranged between the first electrode and the second electrode. The first electrode and the second electrode are configured to operate at a current density of greater than or equal to approximately 100 mA/cm2 and a supply/storage system external of the electrochemical cell. The supply/storage system includes first and second vessels, first and second liquid electrolytes in, respectively, the first and second vessels, fluid lines connecting the first and second vessels to, respectively, the first electrode and the second electrode, and a plurality of pumps operable to circulate the first and second liquid electrolytes via the fluid lines between the first and second vessels and the electrochemical cell. The separator layer is formed of a polymer having a polymer backbone with aromatic groups that are free of unsaturated nitrogen and one or more polar groups bonded in the polymer backbone.
  • A flow battery according to an example of the present disclosure includes an electrochemical cell that has a first electrode, a second electrode spaced apart from the first electrode, and a separator layer arranged between the first electrode and the second electrode. The separator layer is formed of a polymer having a polymer backbone with triazine groups.
  • In a further embodiment of any of the foregoing embodiments, the polymer backbone includes one or more polar groups bonded in the polymer backbone
  • In a further embodiment of any of the foregoing embodiments, the one or more polar groups includes an atom selected from the group consisting of sulfur, oxygen, nitrogen, and combinations thereof.
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • The various features and advantages of the present disclosure will become apparent to those skilled in the art from the following detailed description. The drawings that accompany the detailed description can be briefly described as follows.
  • FIG. 1 illustrates an example flow battery.
  • DETAILED DESCRIPTION
  • FIG. 1 schematically shows portions of an example flow battery 20 for selectively storing and discharging electrical energy. As an example, the flow battery 20 can be used to convert electrical energy generated in a renewable energy system to chemical energy that is stored until a later time when there is greater demand, at which time the flow battery 20 then converts the chemical energy back into electrical energy. The flow battery 20 can supply the electric energy to an electric grid, for example.
  • The flow battery 20 includes a fluid electrolyte 22 that has an electrochemically active species 24 that functions in a redox pair with regard to an additional fluid electrolyte 26 that has an electrochemically active species 28. The electrochemically active species 24/28 include ions of elements that have multiple, reversible oxidation states in a selected liquid solution, such as but not limited to, aqueous solutions or dilute aqueous acids, such as 1-5M sulfuric acid. In some examples, the multiple oxidation states are non-zero oxidation states, such as for transition metals including but not limited to vanadium, iron, manganese, chromium, zinc, molybdenum and combinations thereof, and other elements including but not limited to sulfur, cerium, lead, tin, titanium, germanium and combinations thereof. In some examples, the multiple oxidation states can include the zero oxidation state if the element is readily soluble in the selected liquid solution in the zero oxidation state. Such elements can include the halogens, such as bromine, chlorine, and combinations thereof. The electrochemically active species 24/28 could also be organic molecules that contain groups that undergo electrochemically reversible reactions, such as quinones.
  • The first fluid electrolyte 22 (e.g., the negative electrolyte) and the second fluid electrolyte 26 (e.g., the positive electrolyte) are contained in a supply/storage system 30 that includes first and second vessels 32/34 and pumps 35. The fluid electrolytes 22/26 are delivered using the pumps 35 to at least one electrochemical cell 36 of the flow battery 20 through respective feed lines 38 and are returned from the cell 36 to the vessels 32/34 via return lines 40. The feed lines 38 and the return lines 40 connect the vessels 32/34 with first and second electrodes 42/44. Multiple cells 36 can be provided as a stack.
  • The cell 36 includes the first electrode 42, the second electrode 44 spaced apart from the first electrode 42, and a separator layer 46 arranged between the first electrode 42 and the second electrode 44. For example, the electrodes 42/44 are porous carbon structures, such as carbon paper or felt. The electrodes 42/44 may each be configured for operation at relatively high current densities, such as but not limited to, current density greater than or equal to approximately 100 mA/cm2.
  • In general, the cell or cells 36 can include bipolar plates, manifolds and the like for delivering the fluid electrolytes 22/26 through flow field channels to the electrodes 42/44. The bipolar plates can be carbon plates, for example. It is to be understood however, that other configurations can be used. For example, the cell or cells 36 can alternatively be configured for flow-through operation where the fluid electrolytes 22/26 are pumped directly into the electrodes 42/44 without the use of flow field channels.
  • The fluid electrolytes 22/26 are delivered to the cell 36 to either convert electrical energy into chemical energy or, in the reverse reaction, convert chemical energy into electrical energy that can be discharged. The electrical energy is transmitted to and from the cell 36 through an electric circuit 48 that is electrically coupled with the electrodes 42/44.
  • The separator layer 46 prevents the fluid electrolytes 22/26 from freely and rapidly mixing but permits selected ions to pass through to complete the redox reactions while electrically isolating the electrodes 42/44. In this regard, the fluid electrolytes 22/26 are generally isolated from each other during normal operation, such as in charge, discharge and shutdown states.
  • In particular, due to the highly oxidative and acidic environment in flow batteries in comparison to gaseous fuel cells, there are only a few materials (e.g., perfluorosulfonic acid) that are useful as a separator layer or ion exchange membrane. Materials that may be effective in the less severe environment of a gaseous fuel cell are degraded by the oxidative and acidic environment in flow batteries and suffer from inadequate ion conductivity (e.g., proton conductivity) and/or ion selectivity (e.g., blocking permeation of vanadium or other electrochemically active ion species that can reduce energy efficiency). In this regard, as discussed further below, the disclosed separator layer 46 is formed of a polymer that may be stable in the oxidative and acidic environment in the flow battery 20 and that may have good ion conductivity and ion selectivity, among other properties.
  • In addition to ion conductivity and ion selectivity, the separator layer 46 has properties such as ionic resistance, area specific resistance, and electric conductivity and resistivity. The ionic resistance is measured, in ohms (Ω), between the opposed surfaces of the separator layer 46. The ionic resistance is a function of the thickness of the separator layer 46, the cross-sectional area, and the bulk resistivity. The (ionic) area specific resistance is a function of the ionic resistance and cross-sectional area. The area specific resistance can be calculated, in units of amperes per area squared, by the equation RAS=R*A, where RAS is the area specific resistance, R is ionic resistance, and A is cross-sectional area.
  • As an example, the separator layer 46 is formed of a polymer that has a polymer backbone with aromatic groups that are free of (i.e., exclude) unsaturated nitrogen and that has one or more polar groups that are bonded within the polymer backbone. Such polar groups may be located between the cyclic groups, but are not limited to such locations. The aromatic groups may provide the separator layer 46 with good chemical stability in the oxidative and acidic environment of the flow battery 20, while the polar groups may provide permanent dipoles that are non-covalently bonded to adsorbed acid groups and/or aqueous electrolyte that serve to facilitate ion conductivity. As examples, the one or more polar groups can include, but are not limited to, groups that have one or more high electronegative atoms selected from sulfur, oxygen, nitrogen, and combinations thereof. In further examples, the polar groups include one or more of the chemical structures: C—O—C, C═O, N—C═O, S═O, S═O═S, or C—S.
  • In further examples, the aromatic groups of the polymer backbone include six-carbon atom rings and/or aromatic groups with nitrogen heterocycles. Since the aromatic groups are free of unsaturated nitrogen, the nitrogen heterocycles are also free of unsaturated nitrogen. Although not limited, such nitrogen heterocycles may include a five-atom ring that has one nitrogen atom and four carbon atoms. As will be appreciated, other aromatic groups and aromatic groups with nitrogen heterocycles according to Hückel's rule may additionally or alternatively be used.
  • Furthermore, the flow battery 20 generally operates at much lower temperatures (e.g., less than 100° C., but typically less 50° C.) than some types of fuel cells (e.g., greater than 200° C.). Thus, the selected polymer need not have the high temperature stability that is required in fuel cell membranes. For instance, the glass transition temperature of the selected polymer need only be greater than the expected operating temperature of the flow battery 20 (greater than 50° C. or 100° C.).
  • In further examples, the polymer of the separator layer 46 is selected from polyetherimide (PEI), polyamide-imide (PAI), polyetheretherketone (PEEK), polysulfone (PSF), polyphenylene sulfide (PPS), or combinations thereof. It is to be understood that the example polymers herein include the molecular formula of the polymer and any isomers based upon the formula. Additionally, a combination could be in the form of blends, alloys, and co-, ter-, quatrenary- (etc.) polymers, where at least a portion of the component is of the polymers listed subsequently. Shown below are example structures of the polymer of the separator layer 46, with adsorbed acid groups or aqueous electrolyte, represented at “A,” that are non-covalently bonded to the one or more of the polar groups:
  • Polyetherimide:
  • Figure US20170279130A1-20170928-C00001
  • Polyamide-Imide:
  • Figure US20170279130A1-20170928-C00002
  • Polyetheretherketone:
  • Figure US20170279130A1-20170928-C00003
  • Polysulfone:
  • Figure US20170279130A1-20170928-C00004
  • Polyphenylene Sulfide:
  • Figure US20170279130A1-20170928-C00005
  • In another example, the separator layer 46 is formed of a polymer that has a polymer backbone with triazine groups. A triazine group is a nitrogen heterocycle that includes three nitrogen atoms in an aromatic ring. In further examples, the polymer backbone may also include one or more polar groups as discussed herein above that are bonded within the polymer backbone. The triazine groups may provide the separator layer 46 with good chemical stability in the oxidative and acidic environment of the flow battery 20, while the polar groups may provide permanent dipoles that are non-covalently bonded to adsorbed acid groups and/or aqueous electrolyte that serve to facilitate ion conductivity.
  • In further examples, the separator layer 46 has a thickness of less than approximately 125 micrometers or less than 100 micrometers, based on the flow battery 20 operating at an average current density above approximately 100 mA/cm2 (e.g., greater than 200 mA/cm2). In a further example, the area specific resistance is less than approximately 425 mΩ*cm2, based on the flow battery 20 operating at an average current density above approximately 100 mA/cm2 (e.g., greater than 200 mA/cm2). In further examples, the separator layer 46 has an area specific resistance of less than approximately 425 mΩ*cm2 and the polymer of the separator layer 46 is selected from polyetherimide (PEI), polyamide-imide (PAI), polyetheretherketone (PEEK), polysulfone (PSF), polyphenylene sulfide (PPS), polystyrene, or combinations thereof.
  • In a further example, the area specific resistance of the separator layer 46 is less than approximately 300 mΩ*cm2, based on the flow battery 20 operating at an average current density above approximately 100 mA/cm2 (e.g., greater than 200 mA/cm2) and the use of aqueous electrolytes 22/26. In a further example, the ion conductivity of the separator layer 46 is greater than or equal to 0.05 S/cm.
  • In an additional example, the separator layer 46 has an electronic area specific resistance of greater than approximately 1×104 Ω*cm2. Electronic area specific resistance is similar to ionic area specific resistance but utilizes electric resistance rather than ionic resistance in the calculation. In a further example, the separator layer 46 has a per-cycle selectivity of greater than 99.995% based on use of dissimilar electrolytes 22/26. Per-cycle selectivity is defined as the number of moles of desired ion passed over a full charge/discharge cycle divided by the sum of the number of moles of desired ion passed and the number of moles of reactant or other species that can lead to degradation or a loss of current efficiency per charge/discharge cycle.
  • The separator layer 46 can be fabricated using a technique that is capable of producing a relatively uniform, thin layer of the polymer. Example techniques may include, but are not limited to, solution casting, blade coating, spin coating, dip molding, melt pressing, extruding, and sol-gel processing.
  • In additional examples, the fabrication technique is adapted to adjust a balance between ion conductivity and selectivity. For example, where the polymer in an as-fabricated state has low ion conductivity and high selectivity, the technique may be adapted to sacrifice a portion of the selectivity in order to obtain better conductivity. In this regard, the separator layer 46 can be fabricated with a controlled porosity. The porosity permits greater uptake of acid groups (e.g., acid electrolyte), which may non-covalently bond at the permanent dipoles of the polar groups of the polymer to increase ion conductivity. While such porosity enhances conductivity, it may also decrease selectivity by providing greater free volume through which electrochemically active ions can migrate.
  • One example of an adapted fabrication technique includes inclusion of a sacrificial additive, such as powder and/or liquid additives, in a solution casting material. The sacrificial additive is mixed into and dispersed through the solution casting material. Upon casting and drying/curing, the additive remains in the separator layer 46. However, the additive is active with regard to the liquid electrolyte used in the flow battery 20 such that the additive either dissolves or reacts once exposed to the liquid electrolyte. The reaction or dissolution serves to remove the additive from the separator layer 46, thereby leaving a controlled porosity in the separator layer 46 for uptake of acid groups from the electrolyte. As examples, the additive may include, but is not limited to, oxalic acid, polyethylene glycol, or combinations thereof. The separator layer 46 may this be fabricated in a “dry” state without any adsorbed liquid electrolyte and subsequently installed into the flow battery 20 in the dry state, which facilitates greater toleration of stresses from handling and compression during installation.
  • The reaction or dissolution of the powder may consume protons from the liquid electrolyte; however, the effect on the liquid electrolyte will be low and can be accounted for in initially formulating the liquid electrolyte to have a higher concentration of the active species that are affected.
  • Although a combination of features is shown in the illustrated examples, not all of them need to be combined to realize the benefits of various embodiments of this disclosure. In other words, a system designed according to an embodiment of this disclosure will not necessarily include all of the features shown in any one of the FIGURES or all of the portions schematically shown in the FIGURES. Moreover, selected features of one example embodiment may be combined with selected features of other example embodiments.
  • The preceding description is exemplary rather than limiting in nature. Variations and modifications to the disclosed examples may become apparent to those skilled in the art that do not necessarily depart from this disclosure. The scope of legal protection given to this disclosure can only be determined by studying the following claims.

Claims (20)

What is claimed is:
1. A flow battery comprising:
an electrochemical cell including a first electrode, a second electrode spaced apart from the first electrode, and a separator layer arranged between the first electrode and the second electrode,
wherein the separator layer is formed of a polymer having a polymer backbone with aromatic groups that are free of unsaturated nitrogen and one or more polar groups bonded in the polymer backbone.
2. The flow battery as recited in claim 1, wherein the one or more polar groups includes an atom selected from the group consisting of sulfur, oxygen, nitrogen, and combinations thereof.
3. The flow battery as recited in claim 1, wherein the aromatic groups include nitrogen heterocycles.
4. The flow battery as recited in claim 1, wherein the polymer backbone is free of unsaturated nitrogen.
5. The flow battery as recited in claim 1, wherein the polymer includes at least one of adsorbed acid groups or aqueous electrolyte that is non-covalently bonded to the one or more polar groups.
6. The flow battery as recited in claim 1, wherein the polymer includes polyetherimide (PEI).
7. The flow battery as recited in claim 1, wherein the polymer includes polyamide-imide (PAI).
8. The flow battery as recited in claim 1, wherein the polymer includes polyetheretherketone (PEEK).
9. The flow battery as recited in claim 1, wherein the polymer includes polysulfone (PSF).
10. The flow battery as recited in claim 1, wherein the polymer includes polyphenylene sulfide (PPS).
11. The flow battery as recited in claim 1, wherein the polymer is selected from the group consisting of polyetherimide (PEI), polyamide-imide (PAI), polyetheretherketone (PEEK), polysulfone (PSF), polyphenylene sulfide (PPS), and combinations thereof.
12. The flow battery as recited in claim 1, further comprising a supply/storage system external of the electrochemical cell, the supply/storage system including first and second vessels, first and second liquid electrolytes in, respectively, the first and second vessels, fluid lines connecting the first and second vessels to, respectively, the first electrode and the second electrode, and a plurality of pumps operable to circulate the first and second liquid electrolytes via the fluid lines between the first and second vessels and the electrochemical cell.
13. The flow battery as recited in claim 1, wherein the separator layer has an area specific resistance of less than approximately 425 mΩ*cm2.
14. A separator layer for use in a flow battery, the separator layer being formed of a polymer having a polymer backbone with aromatic groups that are free of unsaturated nitrogen, wherein the separator layer has an area specific resistance of less than approximately 425 mΩ*cm2.
15. The separator layer as recited in claim 14, wherein the separator layer has an area specific resistance of less than approximately 300 mΩ*cm2.
16. The separator layer as recited in claim 14, wherein the polymer is selected from the group consisting of polyetherimide (PEI), polyamide-imide (PAI), polyetheretherketone (PEEK), polysulfone (PSF), polyphenylene sulfide (PPS), polystyrene (PS) and combinations thereof.
17. A flow battery comprising:
an electrochemical cell including a first electrode, a second electrode spaced apart from the first electrode, and a separator layer arranged between the first electrode and the second electrode, and the first electrode and the second electrode are configured to operate at a current density of greater than or equal to approximately 100 mA/cm2; and
a supply/storage system external of the electrochemical cell, the supply/storage system including first and second vessels, first and second liquid electrolytes in, respectively, the first and second vessels, fluid lines connecting the first and second vessels to, respectively, the first electrode and the second electrode, and a plurality of pumps operable to circulate the first and second liquid electrolytes via the fluid lines between the first and second vessels and the electrochemical cell,
wherein the separator layer is formed of a polymer having a polymer backbone with aromatic groups that are free of unsaturated nitrogen and one or more polar groups bonded in the polymer backbone.
18. A flow battery comprising:
an electrochemical cell including a first electrode, a second electrode spaced apart from the first electrode, and a separator layer arranged between the first electrode and the second electrode,
wherein the separator layer is formed of a polymer having a polymer backbone with triazine groups.
19. The flow battery as recited in claim 18, wherein the polymer backbone includes one or more polar groups bonded in the polymer backbone
20. The flow battery as recited in claim 19, wherein the one or more polar groups includes an atom selected from the group consisting of sulfur, oxygen, nitrogen, and combinations thereof.
US15/079,239 2016-03-24 2016-03-24 Separator layer for flow battery Abandoned US20170279130A1 (en)