US20170197366A1 - Consolidating a build material substrate for additive manufacturing - Google Patents

Consolidating a build material substrate for additive manufacturing Download PDF

Info

Publication number
US20170197366A1
US20170197366A1 US15/321,002 US201415321002A US2017197366A1 US 20170197366 A1 US20170197366 A1 US 20170197366A1 US 201415321002 A US201415321002 A US 201415321002A US 2017197366 A1 US2017197366 A1 US 2017197366A1
Authority
US
United States
Prior art keywords
build material
substrate
layer
volume
powdered
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/321,002
Other languages
English (en)
Inventor
James Elmer Abbott, JR.
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hewlett Packard Development Co LP
Original Assignee
Hewlett Packard Development Co LP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hewlett Packard Development Co LP filed Critical Hewlett Packard Development Co LP
Assigned to HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P. reassignment HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ABBOTT, James Elmer, Jr
Publication of US20170197366A1 publication Critical patent/US20170197366A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/10—Processes of additive manufacturing
    • B29C64/165—Processes of additive manufacturing using a combination of solid and fluid materials, e.g. a powder selectively bound by a liquid binder, catalyst, inhibitor or energy absorber
    • B29C67/0081—
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/02—Small extruding apparatus, e.g. handheld, toy or laboratory extruders
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/25—Component parts, details or accessories; Auxiliary operations
    • B29C48/266—Means for allowing relative movements between the apparatus parts, e.g. for twisting the extruded article or for moving the die along a surface to be coated
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/25—Component parts, details or accessories; Auxiliary operations
    • B29C48/92—Measuring, controlling or regulating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/10—Processes of additive manufacturing
    • B29C64/171—Processes of additive manufacturing specially adapted for manufacturing multiple 3D objects
    • B29C64/182—Processes of additive manufacturing specially adapted for manufacturing multiple 3D objects in parallel batches
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/20—Apparatus for additive manufacturing; Details thereof or accessories therefor
    • B29C64/205—Means for applying layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/30—Auxiliary operations or equipment
    • B29C64/386—Data acquisition or data processing for additive manufacturing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/30—Auxiliary operations or equipment
    • B29C64/386—Data acquisition or data processing for additive manufacturing
    • B29C64/393—Data acquisition or data processing for additive manufacturing for controlling or regulating additive manufacturing processes
    • B29C67/0088—
    • B29C67/0092—
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y10/00—Processes of additive manufacturing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y30/00—Apparatus for additive manufacturing; Details thereof or accessories therefor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y50/00—Data acquisition or data processing for additive manufacturing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y50/00—Data acquisition or data processing for additive manufacturing
    • B33Y50/02—Data acquisition or data processing for additive manufacturing for controlling or regulating additive manufacturing processes
    • G—PHYSICS
    • G05—CONTROLLING; REGULATING
    • G05B—CONTROL OR REGULATING SYSTEMS IN GENERAL; FUNCTIONAL ELEMENTS OF SUCH SYSTEMS; MONITORING OR TESTING ARRANGEMENTS FOR SUCH SYSTEMS OR ELEMENTS
    • G05B19/00—Programme-control systems
    • G05B19/02—Programme-control systems electric
    • G05B19/18—Numerical control [NC], i.e. automatically operating machines, in particular machine tools, e.g. in a manufacturing environment, so as to execute positioning, movement or co-ordinated operations by means of programme data in numerical form
    • G05B19/4097—Numerical control [NC], i.e. automatically operating machines, in particular machine tools, e.g. in a manufacturing environment, so as to execute positioning, movement or co-ordinated operations by means of programme data in numerical form characterised by using design data to control NC machines, e.g. CAD/CAM
    • G05B19/4099—Surface or curve machining, making 3D objects, e.g. desktop manufacturing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C2948/00—Indexing scheme relating to extrusion moulding
    • B29C2948/92—Measuring, controlling or regulating
    • B29C2948/92504—Controlled parameter
    • B29C2948/92571—Position, e.g. linear or angular
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/40—Structures for supporting 3D objects during manufacture and intended to be sacrificed after completion thereof
    • G—PHYSICS
    • G05—CONTROLLING; REGULATING
    • G05B—CONTROL OR REGULATING SYSTEMS IN GENERAL; FUNCTIONAL ELEMENTS OF SUCH SYSTEMS; MONITORING OR TESTING ARRANGEMENTS FOR SUCH SYSTEMS OR ELEMENTS
    • G05B2219/00—Program-control systems
    • G05B2219/30—Nc systems
    • G05B2219/35—Nc in input of data, input till input file format
    • G05B2219/35134—3-D cad-cam
    • G—PHYSICS
    • G05—CONTROLLING; REGULATING
    • G05B—CONTROL OR REGULATING SYSTEMS IN GENERAL; FUNCTIONAL ELEMENTS OF SUCH SYSTEMS; MONITORING OR TESTING ARRANGEMENTS FOR SUCH SYSTEMS OR ELEMENTS
    • G05B2219/00—Program-control systems
    • G05B2219/30—Nc systems
    • G05B2219/49—Nc machine tool, till multiple
    • G05B2219/49007—Making, forming 3-D object, model, surface

Definitions

  • Additive manufacturing machines produce 3D (three-dimensional) objects by building up layers of material. Some additive manufacturing machines are commonly referred to as “3D printers” because they often use inkjet or other printing technology to apply some of the manufacturing materials. 3D printers and other additive manufacturing machines make it possible to convert a CAD (computer aided design) model or other digital representation of an object directly into the physical object.
  • 3D printers Some additive manufacturing machines are commonly referred to as “3D printers” because they often use inkjet or other printing technology to apply some of the manufacturing materials. 3D printers and other additive manufacturing machines make it possible to convert a CAD (computer aided design) model or other digital representation of an object directly into the physical object.
  • CAD computer aided design
  • FIGS. 1 and 2 are plan and section views, respectively, illustrating an in-process structure for two objects being manufactured using one example of a build material substrate.
  • FIGS. 3 and 4 show one example of the finished objects from the in-process structure illustrated in FIGS. 1 and 2 .
  • FIGS. 5 and 6 are plan views illustrating in-process structures for two objects being manufactured using other examples of a build material substrate.
  • FIG. 7 is a flow diagram illustrating one example of an additive manufacturing process.
  • FIGS. 8-12 are cross sections illustrating one example of an object being manufactured with the process of FIG. 7 .
  • FIG. 13 is a flow diagram illustrating one example of consolidating substrate material in the process shown in FIG. 7 .
  • FIG. 14 is a flow diagram illustrating another example of consolidating substrate build material in the process shown in in FIG. 7 .
  • FIG. 15 is a flow diagram illustrating one example of solidifying build material in the process shown in FIG. 7 .
  • FIG. 16 is a block diagram illustrating one example of a processor readable medium with instructions to form a build material substrate during the manufacture of a 3D object, using the process of FIG. 7 for example, such as might be used with the additive manufacturing machine of FIG. 17 or with the system of FIG. 18 .
  • FIG. 17 is a block diagram illustrating one example of an additive manufacturing machine implementing a controller with instructions to form a build material substrate, such as the one shown in FIGS. 1 and 2 , during manufacture of a 3D object.
  • FIG. 18 is a block diagram illustrating one example of an additive manufacturing system implementing a CAD computer program product with instructions to form a build material substrate, such as the one shown in FIGS. 1 and 2 , during manufacture of a 3D object.
  • Additive manufacturing machines make a 3D object through the solidification of one or more layers of a build material.
  • Additive manufacturing machines make objects based on data in a 3D model of an object created, for example, with a CAD computer program product. The model data is processed into slices each defining that part of a layer or layers of build material to be solidified.
  • thermal bonding is used to solidify a powdered build material.
  • the powdered build material substrate commonly referred to as a “powder bed”
  • the powdered build material substrate may be held at an elevated temperature to limit differential shrinkage of the edge of the first slices (formed in the first layers of build material) so that each slice stays flat during solidification. Heating the substrate increases power consumption and cost, and can alter the characteristics of the powder sufficient to render otherwise unused powder unfit for recycling back into the manufacturing process.
  • a thermal bonding process that uses nylon 12 powder for the build material, for example, it may be necessary to heat the powder substrate to as high as 150° C. to keep the edges of the object flat. Testing indicates that heating nylon 12 powder to temperatures above about 120° may make the powder unfit for reuse.
  • a new process has been developed to help stabilize the powdered build material substrate at a lower temperature.
  • powdered build material in the substrate is consolidated before layering the object slices.
  • the first layer of powdered build material is formed on the substrate.
  • Build material in the first layer within a perimeter of the consolidated volume of substrate is solidified in the desired pattern to form the first slice of the object.
  • the consolidated volume of substrate underlying the powder in the slice pattern during solidification provides a more stable base compared to an unconsolidated substrate.
  • Substrate may be consolidated, for example, by heating build material in the substrate to a temperature at least as high as the boiling point of a liquid binder but lower than a damaging temperature, and then applying the liquid binder to the heated volume of substrate.
  • a nylon 12 powdered build material heated to only about 100° C. and treated with a latex ink for the binder generates sufficient consolidation of the treated powder for a more stable base compared to unconsolidated nylon 12 powder. While the precise stabilization mechanism in the powder is not known, the nylon 12 powder exhibits more adhesion after water evaporates from the ink compared to untreated powder.
  • the treated powder is dry but not as fine grained as untreated powder.
  • the untreated nylon 12 powder is not damaged by the lower temperature and, thus, may be recycled for reuse.
  • a processor readable medium with instructions for consolidating the powdered build material substrate during an additive manufacturing process may be implemented, for example, in a CAD computer program product, in an object model processor, or in the controller for the additive manufacturing machine.
  • a “binder” means a substance that consolidates or helps consolidate a powdered build material
  • a “liquid binder” means a binder in which the substance that consolidates or helps consolidate a powdered build material is liquid and/or the substance is carried in a liquid
  • a “coalescing agent” means a substance that causes or helps cause a build material to coalesce or solidify or to both coalesce and solidify
  • a “coalescence modifier agent” means a substance that modifies the effect of a coalescing agent
  • “consolidate” means to make stronger or more stable
  • “powder” means a dry substance made up of very small pieces of something
  • a “slice” means one or more slices of a multi-slice object or the object itself for a single slice object.
  • FIGS. 1 and 2 are plan and section views, respectively, illustrating a first object 10 and a second object 12 being manufactured using one example of a consolidated substrate volume 14 .
  • the finished objects 10 and 12 are shown in FIGS. 3 and 4 .
  • first object 10 is a single slice star and second object 12 is a three slice disc.
  • an in-process structure 16 is supported on a platform or other support 18 in an additive manufacturing machine (not shown).
  • Structure 16 includes a substrate 20 of build material on platform 18 .
  • Substrate 20 includes an unconsolidated volume 22 of powdered build material and a consolidated volume 14 of build material formed from unconsolidated powdered build material.
  • Star 10 is formed on substrate 20 in a first layer 24 of powdered build material that has been solidified in the shape of star 10 .
  • Disc 12 is formed on substrate 20 in first, second and thirds layers 24 , 26 , 28 of powder build material that have been successively solidified in the shape of disc 12 .
  • Any suitable powdered build material may be used, including for example metals, composites, ceramics, glass and polymers, and processed to make the desired solid object which may be hard or soft, rigid or flexible, elastic or inelastic.
  • the finished parts 10 , 12 shown in FIGS. 3 and 4 are obtained by “uncaking” layers of in-process structure 16 to separate the two objects 10 , 12 from substrate 20 and untreated build material in layers 24 - 28 . While two very simple objects 10 , 12 made with just a few layers of build material are shown to illustrate the use of a consolidated substrate volume 14 , a consolidated substrate volume may be used for complex objects manufactured in a single layer or in multiple layers.
  • Consolidated volume 14 is formed in substrate 20 with a perimeter 29 that will surround the first few slices of the object or objects to be formed on substrate 20 .
  • a rectangular consolidated volume 14 with a single perimeter surrounding both objects 10 and 12 is shown, other configurations for consolidated volume 14 are possible.
  • the perimeter 29 of each consolidated volume 14 corresponds to the shape of each object 10 , 12 .
  • the perimeter 29 of each consolidated volume 14 surrounds only the edge of each object 10 , 12 .
  • FIG. 7 is a flow diagram illustrating one example of an additive manufacturing process 100 .
  • FIGS. 8-12 are cross sections illustrating one example of an object 30 ( FIG. 10 ) being manufactured with process 100 of FIG. 7 .
  • a substrate 20 of unconsolidated powdered build material is formed at block 102 in FIG. 7 , as shown in FIG. 8 .
  • Substrate 20 may be formed on any suitable supporting structure such as a platform 18 shown in FIG. 1 , or on an underlying slice or object formed previously.
  • substrate 20 is formed with two layers of unconsolidated build material of equal thickness, such as might be formed with the same dispensing device used to form the subsequent slice layers. Other suitable configurations for substrate 20 are possible.
  • Powdered build material in substrate 20 is consolidated to form a consolidated volume 14 as shown in FIG. 9 (block 104 in FIG. 7 ).
  • a layer 24 of unconsolidated powdered build material is formed on substrate 20 as shown in FIG. 10 (block 106 in FIG. 7 ) and then powdered build material in layer 24 within a perimeter of consolidated substrate volume 14 is solidified in the desired pattern to form an object slice 30 , as shown in FIG. 11 (block 108 in FIG. 7 ).
  • Slice 30 is separated from substrate 20 , for example after the object is completed (block 110 in FIG. 7 ).
  • a single slice object 30 separating from substrate 20 is shown in FIG. 12 . While the exact stabilization mechanism is not known, testing suggests that consolidated substrate volume 14 under slice layer 24 provides a “restoring” force at the edge of the slice pattern to help hold slice 30 flat during solidification, compared to a slice formed on unconsolidated substrate.
  • FIG. 13 is a flow diagram illustrating one example of consolidating substrate build material at block 104 in FIG. 7 .
  • unconsolidated powdered build material in substrate 20 is heated to a temperature at least as high as the boiling point of a liquid binder but lower than a temperature damaging to the build material (block 112 ).
  • the liquid binder is applied to a heated volume of substrate 20 (block 114 ).
  • a nylon 12 powdered build material is heated to about 100° C. and treated with Hewlett-Packard Company's HP881 Latex Ink, for example by dispensing ink on to the build material in the desired pattern with an inkjet printhead.
  • the treated nylon 12 powder exhibits more adhesion after water evaporates from the ink compared to untreated powder.
  • the consolidated powder is dry but not as fine grained as unconsolidated powder, and may appear clumpy.
  • the untreated nylon 12 powder is not damaged at temperatures below about 120° C. and, thus, may be recycled for reuse.
  • FIG. 14 is a flow diagram illustrating another example of consolidating substrate build material at block 104 in FIG. 7 .
  • a light-curable liquid binder is applied to an unheated, unconsolidated powdered build material in substrate 20 (block 116 ) and then exposed to light to consolidate a volume of the substrate where binder was applied to the build material (block 118 ).
  • block 116 unheated, unconsolidated powdered build material in substrate 20
  • FIG. 14 is a flow diagram illustrating another example of consolidating substrate build material at block 104 in FIG. 7 .
  • a light-curable liquid binder is applied to an unheated, unconsolidated powdered build material in substrate 20 (block 116 ) and then exposed to light to consolidate a volume of the substrate where binder was applied to the build material (block 118 ).
  • a polymer powdered build material at room temperature is treated with a UV (ultraviolet) curable ink such as Hewlett-Packard Company's HP HDR240 Scitex UV Curable Ink, for example by dispensing ink on to the build material in the desired pattern with an inkjet printhead, and then exposed to UV light to cure the ink and consolidate the polymer powder.
  • a UV curable ink such as Hewlett-Packard Company's HP HDR240 Scitex UV Curable Ink
  • FIG. 15 is a flow diagram illustrating one example of solidifying build material to form the object slice at block 108 in FIG. 7 .
  • a coalescing agent is selectively applied to powdered build material layer 26 in a pattern corresponding to slice 30 (block 120 ).
  • a coalescence modifier agent is selectively applied to layer 26 to help define the desired shape and characteristics of slice 30 (block 122 ).
  • a coalescence modifier agent modifies the effect of the coalescing agent and may be dispensed, for example, along the edge of the coalescence agent to help reduce the effects of lateral coalescence bleed and improve the definition of the edges of the slice.
  • a modifier agent is dispensed interspersed with the pattern of the coalescing agent to change the material characteristics of the slice.
  • the patterned parts of layer 26 are exposed to light to form slice 30 (block 124 in FIG. 15 ).
  • Suitable coalescing agents include pigments, dyes, polymers and other substances that have significant light absorption. Carbon black ink and light absorbing color inks commercially known as CM997A, CE039A and CE042A available from Hewlett-Packard Company are suitable coalescing agents with the appropriate light source.
  • Suitable coalescence modifier agents may separate individual particles of the build material to prevent the particles from joining together and solidifying as part of the slice.
  • this type of coalescence modifier agent include colloidal, dye-based, and polymer-based inks, as well as solid particles that have an average size less than the average size of particles of the build material.
  • the molecular mass of the coalescence modifier agent and its surface tension should be such that it enables the agent to penetrate sufficiently into the build material to achieve the desired mechanical separation.
  • a salt solution may be used as a coalescence modifier agent.
  • inks commercially known as CM996A and CN673A available from Hewlett-Packard Company may be used as a coalescence modifier agent.
  • Suitable coalescence modifier agents may act to modify the effects of a coalescing agent by preventing build material from reaching temperatures above its melting point during heating.
  • a fluid that exhibits a suitable cooling effect may be used as this type of coalescence modifier agent.
  • energy applied to the build material may be absorbed evaporating the fluid to help prevent build material from reaching its melting point.
  • a fluid with a high water content may be a suitable coalescence modifier agent.
  • coalescence modifier agent may be used.
  • An example of a coalescence modifier agent that may increase the degree of coalescence may include, for example, a plasticizer.
  • Another example of a coalescence modifier agent that may increase the degree of coalescence may include a surface tension modifier to increase the wettability of particles of build material.
  • FIG. 16 is a block diagram illustrating a processor readable medium 32 with instructions 34 to consolidate build material in the substrate during the manufacture of a 3D object.
  • a processor readable medium 32 is any non-transitory tangible medium that can embody, contain, store, or maintain instructions for use by a processor.
  • Processor readable media include, for example, electronic, magnetic, optical, electromagnetic, or semiconductor media. More specific examples of suitable processor readable media include a hard drive, a random access memory (RAM), a read-only memory (ROM), memory cards and sticks and other portable storage devices.
  • Instructions 34 include instructions to consolidate powdered build material in the substrate, shown at block 104 in FIG. 7 . Instructions 34 may also include other manufacturing instructions, for example instructions to form, solidify and separate shown at blocks 106 , 108 and 110 in FIG. 7 .
  • Processor readable medium 32 with instructions 34 may be implemented, for example, in a CAD computer program product, in an object model processor, or in a controller for an additive manufacturing machine. Control data to consolidate powdered build material in the substrate can be generated, for example, by processor readable instructions on the source application, usually a CAD computer program product, in an object model processor, or by processor readable instructions on the additive manufacturing machine.
  • FIG. 17 is a block diagram illustrating one example of an additive manufacturing machine 36 implementing a controller 38 with instructions 34 to consolidate a substrate volume during the manufacture of a 3D object.
  • machine 36 includes controller 38 , a support 18 , a build material layering device 40 , a binder dispenser 42 , a coalescing agent dispenser 44 , a heater 46 and a light source 48 .
  • the in-process object structure is supported on support 18 during manufacturing.
  • support 18 may support the in-process structure during uncaking.
  • support 18 is movable at the urging of controller 38 to compensate for the changing thickness of the in-process structure, for example as layers of build material are added during manufacturing.
  • Build material layering device 40 layers build material on support 18 and on the in-process structures and may include, for example, a device to dispense the build material and a blade or roller to distribute the build material uniformly to the desired thickness for each layer.
  • Binder dispenser 42 dispenses binder selectively at the direction of controller 38 on to substrate build material in a pattern that will surround the first slices of an object supported on the substrate during manufacturing.
  • Coalescing agent dispenser 44 dispenses coalescing agent selectively at the direction of controller 38 on to build material, usually in a pattern corresponding to a slice.
  • Manufacturing machine 36 may include a heater 46 if it is desired to heat the substrate.
  • Manufacturing machine 36 includes a light source 48 to apply light energy to solidify build material treated with coalescing agent.
  • Controller 38 represents the processor (or multiple processors), the associated memory (or multiple memories) and instructions, and the electronic circuitry and components needed to control the operative elements of machine 36 .
  • controller 38 includes a memory 50 having a processor readable medium 32 with instructions 34 and a processor 52 to read and execute instructions 34 .
  • controller 38 would receive control data and other instructions from a CAD program to make an object (e.g., blocks 102 , 106 , 108 and 110 in FIG. 7 ) and execute local instructions 34 to consolidate part of the substrate (e.g., block 104 in FIG. 7 ) as part of the process of making the object.
  • consolidation instructions 34 may be embodied in a processor readable medium 32 separate from controller 38 , for example as part of a CAD computer program product shown in FIG. 18 .
  • an additive manufacturing system 54 includes an additive manufacturing machine 36 operatively connected to a CAD computer program product 56 with the instructions to consolidate parts of the substrate during manufacture of the object.
  • CAD program 56 includes processor readable medium 32 with instructions 34 .
  • Any suitable connection between machine 36 and CAD program 56 may be used to communicate instructions and control data to machine 36 including, for example, a wired link, a wireless link, and a portable connection such as a flash drive or compact disk.
  • additive manufacturing machine 36 includes a coalescence modifier agent dispenser 58 . Inkjet printheads or another suitable dispenser 58 dispenses coalescence modifier agent selectively on to build material at the direction of controller 38 executing instructions from CAD program 58 .
  • Light source 48 applies light energy to build material formed on or over the substrate to cause the solidification of portions of the build material according to where coalescing agent has been delivered or has penetrated.
  • light source 48 is an infra-red (IR) or near infra-red light source, a halogen light source, or a light emitting diode.
  • Light source 48 may be a single light source or an array of multiple light sources.
  • light source 48 is configured to apply light energy in a substantially uniform manner simultaneously to the whole surface of a layer of build material.
  • light source 48 is configured to apply energy to only a select areas of the whole surface of a layer of build material. In these examples light source 48 may be moved or scanned across the layer of build material such that a substantially equal amount of energy is applied to the selected areas or across the whole surface of a layer of build material.
  • the combination of build material, coalescing and coalescence modifier agents, and light energy may be selected for an object slice so that (1) build material with no coalescing agent does not coalesce when the energy is applied, (2) build material with only coalescing agent solidifies when energy is applied; or (3) build material with both agents undergo a modified degree of coalescence between no coalescence and solidification with or without the application of energy.

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Mechanical Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Optics & Photonics (AREA)
  • Health & Medical Sciences (AREA)
  • Clinical Laboratory Science (AREA)
  • Human Computer Interaction (AREA)
  • General Physics & Mathematics (AREA)
  • Automation & Control Theory (AREA)
US15/321,002 2014-07-16 2014-07-16 Consolidating a build material substrate for additive manufacturing Abandoned US20170197366A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2014/046892 WO2016010536A1 (en) 2014-07-16 2014-07-16 Consolidating a build material substrate for additive manufacturing

Publications (1)

Publication Number Publication Date
US20170197366A1 true US20170197366A1 (en) 2017-07-13

Family

ID=55078868

Family Applications (2)

Application Number Title Priority Date Filing Date
US15/321,002 Abandoned US20170197366A1 (en) 2014-07-16 2014-07-16 Consolidating a build material substrate for additive manufacturing
US15/526,948 Expired - Fee Related US10688716B2 (en) 2014-07-16 2015-02-27 Consolidating a build material for additive manufacturing

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/526,948 Expired - Fee Related US10688716B2 (en) 2014-07-16 2015-02-27 Consolidating a build material for additive manufacturing

Country Status (3)

Country Link
US (2) US20170197366A1 (de)
EP (1) EP3186068A4 (de)
WO (2) WO2016010536A1 (de)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11299644B2 (en) 2017-11-30 2022-04-12 Hewlett-Packard Development Company, L.P. Anti-coalescing agent for three-dimensional printing
US12121964B2 (en) 2023-05-04 2024-10-22 James J. Myrick Processes, compositions and systems for 2D and 3D printing

Families Citing this family (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11192306B2 (en) 2016-02-08 2021-12-07 Hewlett-Packard Development Company, L.P. Build layer temperature control
US11020905B2 (en) 2016-03-24 2021-06-01 Hewlett-Packard Development Company, L.P. Accuracy improvement and surface finishing using fusing agent and detailing agent
CN109070464A (zh) * 2016-05-12 2018-12-21 惠普发展公司，有限责任合伙企业 3d打印定义过程
CN106042748A (zh) * 2016-05-30 2016-10-26 陕西科技大学 一种龙泉青瓷堆积法制造方法
RU2646086C1 (ru) * 2016-07-01 2018-03-01 федеральное государственное автономное образовательное учреждение высшего образования "Санкт-Петербургский национальный исследовательский университет информационных технологий, механики и оптики" (Университет ИТМО) Способ получения трехмерных объектов
WO2018017062A1 (en) * 2016-07-19 2018-01-25 Hewlett-Packard Development Company, L.P. Additive manufacturing including selective heating
BR112018072273B1 (pt) 2016-07-21 2022-05-03 Hewlett-Packard Development Company, L.P Impressora tridimensional e método para controlar a operação de uma impressora tridimensional
US20190152155A1 (en) * 2016-07-27 2019-05-23 Hewlett-Packard Development Company, L.P. 3d printing
WO2018022034A1 (en) * 2016-07-27 2018-02-01 Hewlett-Packard Development Company, L.P. Forming three-dimensional (3d) electronic parts
US11148227B2 (en) 2016-07-29 2021-10-19 Hewlett-Packard Development Company, L.P. Laser melting of build materials
CN113895032A (zh) * 2017-04-09 2022-01-07 惠普发展公司，有限责任合伙企业 增材制造
EP3648912A4 (de) * 2017-07-06 2021-01-20 Hewlett-Packard Development Company, L.P. Dreidimensionales (3d) drucken
US11628627B2 (en) 2017-07-18 2023-04-18 Hewlett-Packard Development Company, L.P. Additive manufacturing process to disguise physical characteristics of item
EP3687769B1 (de) 2017-11-17 2023-12-27 Hewlett-Packard Development Company, L.P. Ein dielektrisches mittel und ein verfahren zum dreidimensionalen drucken
US20210129432A1 (en) * 2017-12-20 2021-05-06 Hewlett-Packard Development Company, L.P. Additive manufacturing devices and methods
CN111819065A (zh) 2018-03-09 2020-10-23 惠普发展公司，有限责任合伙企业 虚拟对象体积
US11383448B2 (en) 2018-03-28 2022-07-12 Hewlett-Packard Development Company, L.P. Generating objects in additive manufacturing utilizing a predefined portion within a threshold distance of a wall of fabrication chamber
US20210008805A1 (en) * 2018-04-06 2021-01-14 Hewlett-Packard Development Company, L.P. Additive manufacturing system
WO2019194836A1 (en) * 2018-04-06 2019-10-10 Hewlett-Packard Development Company, L.P. Configuring an additive manufacturing system
US11072039B2 (en) 2018-06-13 2021-07-27 General Electric Company Systems and methods for additive manufacturing
WO2020122876A1 (en) * 2018-12-11 2020-06-18 Hewlett-Packard Development Company, L.P. Part packing based on agent usage
US20220063202A1 (en) * 2019-01-15 2022-03-03 Hewlett-Packard Development Company, L.P. Additive manufacturing parts
US11577463B2 (en) 2019-03-15 2023-02-14 Hewlett-Packard Development Company, L.P. Patterns on objects in additive manufacturing
US11938681B2 (en) 2019-03-15 2024-03-26 Hewlett-Packard Development Company, L.P. Coloured object generation
WO2020204899A1 (en) * 2019-03-29 2020-10-08 Hewlett-Packard Development Company, L.P. Separation of objects for additive manufacturing
WO2020209871A1 (en) * 2019-04-12 2020-10-15 Hewlett-Packard Development Company, L.P. Resonator-based object pose determination
US20220080670A1 (en) * 2019-04-30 2022-03-17 Hewlett-Packard Development Company, L.P. Colored object generation
WO2020222794A1 (en) * 2019-04-30 2020-11-05 Hewlett-Packard Development Company, L.P. Colored object generation
US20220250319A1 (en) * 2019-08-05 2022-08-11 Hewlett-Packard Development Company, L.P. Additive manufacturing with laser arrays
US20230401364A1 (en) * 2020-10-23 2023-12-14 Hewlett-Packard Development Company, L.P. Agent map generation
WO2022231601A1 (en) * 2021-04-29 2022-11-03 Hewlett-Packard Development Company, L.P. 3d printing decaking stations

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020145213A1 (en) * 2001-04-10 2002-10-10 Junhai Liu Layer manufacturing of a multi-material or multi-color 3-D object using electrostatic imaging and lamination
US20060208388A1 (en) * 1999-11-05 2006-09-21 Z Corporation Material systems and methods of three-dimensional printing
US20110107967A1 (en) * 2003-07-25 2011-05-12 Loughborough University Enterprises Limited Method and apparatus for combining particulate material

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5348693A (en) 1991-11-12 1994-09-20 Advanced Cardiovascular Systems, Inc. Formation of three dimensional objects and assemblies
US6596224B1 (en) * 1996-05-24 2003-07-22 Massachusetts Institute Of Technology Jetting layers of powder and the formation of fine powder beds thereby
WO2001038061A1 (en) 1999-10-26 2001-05-31 University Of Southern California Process of making a three-dimensional object
US6376148B1 (en) * 2001-01-17 2002-04-23 Nanotek Instruments, Inc. Layer manufacturing using electrostatic imaging and lamination
US6986654B2 (en) * 2002-07-03 2006-01-17 Therics, Inc. Apparatus, systems and methods for use in three-dimensional printing
DE102004020452A1 (de) * 2004-04-27 2005-12-01 Degussa Ag Verfahren zur Herstellung von dreidimensionalen Objekten mittels elektromagnetischer Strahlung und Auftragen eines Absorbers per Inkjet-Verfahren
US7389154B2 (en) 2004-09-29 2008-06-17 Hewlett-Packard Development Company, L.P. Fabricating a three-dimensional object
JP2009508723A (ja) * 2005-09-20 2009-03-05 ピーティーエス ソフトウェア ビーブイ 三次元物品を構築する装置及び三次元物品を構築する方法
DE102007033434A1 (de) 2007-07-18 2009-01-22 Voxeljet Technology Gmbh Verfahren zum Herstellen dreidimensionaler Bauteile
DE102010042230A1 (de) 2010-10-08 2012-04-12 Eos Gmbh Electro Optical Systems Verfahren zum Beschichten von Objekten, insbesondere solchen Objekten, die durch ein generatives Fertigungsverfahren hergestellt wurden
EP2529694B1 (de) * 2011-05-31 2017-11-15 Ivoclar Vivadent AG Verfahren zur generativen Herstellung von Keramikformkörpern durch 3D-Inkjet-Drucken
WO2013113372A1 (en) 2012-01-31 2013-08-08 Hewlett-Packard Development Company, L.P. Techniques for three-dimensional printing
DE102012013318A1 (de) 2012-07-06 2014-01-09 Eos Gmbh Electro Optical Systems Verfahren und Vorrichtung zum schichtweisen Herstellen eines dreidimensionalen Objekts
US8888480B2 (en) * 2012-09-05 2014-11-18 Aprecia Pharmaceuticals Company Three-dimensional printing system and equipment assembly
WO2014138386A1 (en) 2013-03-06 2014-09-12 University Of Louisville Research Foundation, Inc. Powder bed fusion systems, apparatus, and processes for multi-material part production
US9403725B2 (en) 2013-03-12 2016-08-02 University Of Southern California Inserting inhibitor to create part boundary isolation during 3D printing
US9626489B2 (en) * 2013-03-13 2017-04-18 Intertrust Technologies Corporation Object rendering systems and methods
ES2745763T3 (es) * 2013-12-23 2020-03-03 The Exone Co Métodos y sistemas para la impresión en tres dimensiones utilizando múltiples fluidos aglutinantes
TW201609934A (zh) * 2014-07-01 2016-03-16 精工愛普生股份有限公司 三維造形用組合物、三維造形物之製造方法及三維造形物

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20060208388A1 (en) * 1999-11-05 2006-09-21 Z Corporation Material systems and methods of three-dimensional printing
US20020145213A1 (en) * 2001-04-10 2002-10-10 Junhai Liu Layer manufacturing of a multi-material or multi-color 3-D object using electrostatic imaging and lamination
US20110107967A1 (en) * 2003-07-25 2011-05-12 Loughborough University Enterprises Limited Method and apparatus for combining particulate material

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11299644B2 (en) 2017-11-30 2022-04-12 Hewlett-Packard Development Company, L.P. Anti-coalescing agent for three-dimensional printing
US12110362B2 (en) 2017-11-30 2024-10-08 Hewlett-Packard Development Company, L.P. Three-dimensional printing
US12121964B2 (en) 2023-05-04 2024-10-22 James J. Myrick Processes, compositions and systems for 2D and 3D printing

Also Published As

Publication number Publication date
WO2016010536A1 (en) 2016-01-21
WO2016010590A1 (en) 2016-01-21
EP3186068A1 (de) 2017-07-05
US10688716B2 (en) 2020-06-23
EP3186068A4 (de) 2018-03-07
US20170326791A1 (en) 2017-11-16

Similar Documents

Publication Publication Date Title
US20170197366A1 (en) Consolidating a build material substrate for additive manufacturing
RU2693131C2 (ru) Формирование трехмерного объекта
TWI583538B (zh) 產生三維物件之技術
CN107206667A (zh) 生成三维对象
WO2016186609A1 (en) Three-dimensional printing systems
US10486373B2 (en) Penetration barrier for additive manufacturing
CN114474725A (zh) 用于增材制造的光照
EP3197667B1 (de) Prozessorlesbares medium und verfahren für additive fertigung
US10766246B2 (en) Additive manufacturing
CN107530954A (zh) 三维对象的聚结剂浓度和连续色调密度
US11155029B2 (en) Three dimensional (3D) printing using fusing and detailing agents
CN105916661A (zh) 生成三维对象
US20210370597A1 (en) Additive manufacturing
EP3362256A1 (de) Baumaterialzuführung zur generativen fertigung
CN107530966B (zh) 生成具有目标表面粗糙度的三维物体
CN113811437B (zh) 三维打印机及选择性固化构建材料的连续层的方法
JP6546306B2 (ja) 三次元物体の生成
JP2019089348A (ja) 付加製造
WO2017127113A1 (en) Layering powdered build material for additive manufacturing
WO2021216059A1 (en) Modify property of 3d parts to cause different nozzle usages

Legal Events

Date Code Title Description
AS Assignment

Owner name: HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P., TEXAS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:ABBOTT, JAMES ELMER, JR;REEL/FRAME:040934/0494

Effective date: 20140716

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: EX PARTE QUAYLE ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO EX PARTE QUAYLE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NOTICE OF ALLOWANCE MAILED -- APPLICATION RECEIVED IN OFFICE OF PUBLICATIONS

STPP Information on status: patent application and granting procedure in general

Free format text: AWAITING TC RESP., ISSUE FEE NOT PAID

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO PAY ISSUE FEE