US20170092752A1 - Iii-nitride semiconductors with recess regions and methods of manufacture - Google Patents
Iii-nitride semiconductors with recess regions and methods of manufacture Download PDFInfo
- Publication number
- US20170092752A1 US20170092752A1 US15/376,826 US201615376826A US2017092752A1 US 20170092752 A1 US20170092752 A1 US 20170092752A1 US 201615376826 A US201615376826 A US 201615376826A US 2017092752 A1 US2017092752 A1 US 2017092752A1
- Authority
- US
- United States
- Prior art keywords
- layer
- gate
- sublayer
- iii
- gate recess
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- This application is a non-provisional of and claims the benefit of priority to U.S. Ser. No. 62/298,824, filed on 23 Feb. 2016, entitled “III-Nitride Semiconductors with Recess Regions.”
- This application is also a Continuation-in-Part (CIP) of and claims the benefit of priority to U.S. Ser. No. 15/234,405, filed on 11 Aug. 2016, entitled “Semiconductor Structure with a Spacer Layer,” which itself is a non-provisional of and claims the benefit of priority to U.S. Ser. No. 62/203,438, filed on 11 Aug. 2015, entitled “Novel III-Nitride Structure with Spacer Layer,” and is also a Continuation-in-Part (CIP) of and claims the benefit of priority to U.S. Ser. No. 15/094,985, filed on 8 Apr. 2016, entitled “Semiconductor Structure and Etch Technique for Monolithic Integration of III-N Transistors,” issued as U.S. Pat. No. 9,502,535, on Nov. 22, 2016, which itself is a non-provisional of and claims the benefit of priority to U.S. Ser. No. 62/146,055, filed on 10 Apr. 2015, entitled “III-Nitride Integration Technology.” The entire disclosures of all cited applications are hereby incorporated by reference in their entireties herein.
- Described herein are semiconductor structures, and processes for forming semiconductor structures. Etching techniques are described for forming recesses in a semiconductor structure, such as gate recesses and/or ohmic recesses. Such structures and techniques can be used to produce high performance transistors for various uses such as in power electronics, power amplification and digital electronics.
- The statements in this section may serve as a background to help understand the invention and its application and uses, but may not constitute prior art.
- Compared with conventional power devices made of silicon, Group III-Nitride (III-N) semiconductors possess a number of excellent electronic properties that enable the fabrication of modern power electronic devices and structures for use in a variety of applications. Silicon's limited critical electric field and relatively high resistance make currently available commercial power devices, circuits, and systems bulky, heavy, with further constraints on operating frequencies. On the other hand, higher critical electric field and higher electron density and mobility of III-N materials allow high-current, high-voltage, high-power and/or high-frequency performances of improved power transistors that are greatly desirable for advanced transportation systems, high-efficiency electricity generation and conversion systems, and energy delivery networks. Such systems rely on efficient converters to step-up or step-down electric voltages, and use power transistors capable of blocking large voltages and/or carrying large currents. For example, power transistors with blocking voltages of more than 500V are used in hybrid vehicles to convert DC power from the batteries to AC power. Some other exemplary applications of power transistors include power supplies, automotive electronics, automated factory equipment, motor controls, traction motor drives, high voltage direct current (HVDC) electronics, lamp ballasts, telecommunication circuits and display drives.
- In spite of the enormous potential of III-N semiconductor devices for producing high-efficiency power electronics such as high power amplifiers and converters, a major factor that limit the performance and reliability of III-N high electron mobility transistors for high power and high frequency applications is high gate leakage current due to significant amount of surface defects and electron traps by surface or bulk trap states. In a conventional III-N transistor, a Schottky gate biased with a positive voltage during operation can have a gate leakage current as high as the drain current, leading to malfunction of the device. Gate leakage degradation at high electric fields are also commonly observed. Recently, gate leakage current and channel electric field management structures such as gate recesses, T-shaped and Γ-shaped gates, field-plates, and suitable passivation materials have been proposed and studied, some of which provide noticeable performance improvements. Nonetheless, further and significant reduction of gate leakage current are highly desirable for achieving high levels of reliability and stability under high-performance operations.
- Therefore, in view of the aforementioned practicalities and difficulties, there is an unsolved need for Group III-Nitride semiconductor structures, and for reducing device failure mechanisms, preventing high gate leakage currents, increasing breakdown voltages, and generally improving the reliability and stability of semiconductor devices fabricated thereon.
- The present invention provides semiconductor structures and methods for fabricating III-nitride transistors with recessed regions.
- In one aspect, one embodiment of the present invention is a multi-layer semiconductor structure for use in a III-Nitride (III-N) semiconductor device, comprising a channel layer, a barrier layer, a pair of ohmic electrodes, a gate electrode, and a first filler element. The channel layer comprises a first III-N material for providing electrical conduction. The barrier layer comprises a second III-N material. The pair of ohmic electrodes is disposed in ohmic recesses etched into the barrier layer, and the gate electrode is disposed in a gate recess etched into the barrier layer, in-between the pair of ohmic electrodes. The gate electrode is stepped to form a bottom stem and a bottom step within the gate recess. The first filler element is disposed at least below the bottom step of the gate electrode within the gate recess, and the first filler element comprises a first insulating material.
- In some embodiments of the present invention, the multi-layer semiconductor structure further comprises a second filler element disposed between the gate electrode and a sidewall of the gate recess, where the second filler element comprises a second insulating material, where the second filler element covers at least a portion of the sidewall of the gate recess, and where the second filler element is in contact with the first filler element. In some embodiments, the multi-layer semiconductor structure further comprises an air gap between a sidewall of the gate electrode and the second filler element.
- In some embodiments of the present invention, a top portion of the gate electrode exceeding a top level of the gate recess is shorter in length than the gate recess.
- In some embodiments of the present invention, the multi-layer semiconductor structure further comprises a gate dielectric layer disposed over the gate recess, above the first filler element and below the gate electrode within the gate recess.
- In some embodiments of the present invention, the barrier layer comprises a band-offset layer disposed above the channel layer, where the band-offset layer comprises a third III-N material, and where the band-offset layer has a wider bandgap than the channel layer. In some embodiments, the multi-layer semiconductor structure further comprises a passivation layer disposed on the barrier layer, where the gate recess is etched through the passivation layer. In some embodiments, the barrier comprises a sublayer that is n-type doped.
- In some embodiments of the present invention, the barrier layer comprises a spacer layer comprising a third III-N material, and a cap layer disposed on the spacer layer, the cap layer comprising at least two sublayers. Each sublayer is selectively etchable with respect to sublayers immediately below and above, each sublayer comprises a III-N material AlxInyGazN in which 0≦x≦1, 0≦y≦1, and 0≦z≦1, and at least one of the sublayers has a non-zero Ga content with 0<z≦1. In addition, a sublayer immediately above the spacer layer has a wider bandgap than the spacer layer, and a bottom of the gate recess is within or on a layer selected from the group consisting of the channel layer, the spacer layer, and one of the sublayers of the cap layer.
- In some embodiments of the present invention, the barrier layer comprises a bottom sublayer, a middle sublayer, and a top sublayer, where each sublayer comprises a III-N material AlxInyGazN in which 0≦x≦1, 0≦y≦1, and 0≦z≦1. Moreover, the bottom sublayer has a bandgap equal to or greater than that of the channel layer, the middle sublayer has a bandgap equal to or greater than that of the bottom sublayer, the top sublayer has a bandgap equal to or smaller than that of the middle sublayer, and a bottom of the gate recess is within or on a layer selected from the group consisting of the channel layer, and one of the sublayers of the barrier layer.
- In yet some embodiments of the present invention, the multi-layer semiconductor structure further comprises a back barrier layer disposed below the channel layer, where the back barrier layer comprises a III-N material AlxInyGazN in which 0≦x≦1, 0≦y≦1, and 0≦z≦1, and where the back barrier layer has a wider bandgap and/or an opposite polarization direction than the channel layer.
- In another aspect, one embodiment of the present invention is a method of fabricating a multi-layer semiconductor structure for use in a III-Nitride (III-N) semiconductor device. The method comprising steps of forming a channel layer comprising a first III-N material for providing electrical conduction; forming a barrier layer comprising a second III-N material; forming a pair of ohmic recesses by patterning and etching of the barrier layer; depositing a pair of ohmic electrodes in the pair of ohmic recesses respectively; forming a gate recess by patterning and etching of the barrier layer, where the gate recess is positioned in-between the pair of ohmic recesses; depositing a first filler layer covering a bottom of the gate recess, where the first filler layer comprises a first insulating material; recessing a recess through the filler layer, where a length of the recess through the filler layer is smaller than that of the gate recess, to form a first filler element at the bottom of the gate recess; and depositing a gate electrode in the gate recess, where the gate electrode is stepped by the first filler element to form a bottom stem and a bottom step within the gate recess.
- In some embodiments of the present invention, the method further comprises depositing a second filler element between the gate electrode and a sidewall of the gate recess, where the second filler element comprises a second insulating material, where the second filler element covers at least a portion of the sidewall of the gate recess, and where the second filler element is in contact with the first filler element. In some embodiments, a sidewall of the gate electrode is insulated by an air gap between the sidewall of the gate electrode and the second filler element.
- In some embodiments of the present invention, a top portion of the gate electrode exceeding a top level of the gate recess thus formed is shorter in length than the gate recess.
- In some embodiments of the present invention, the method further comprises depositing a gate dielectric layer over the gate recess, above the first filler element and below the gate electrode within the gate recess.
- In some embodiments of the present invention, the barrier layer comprises a band-offset layer formed above the channel layer, where the band-offset layer comprises a third III-N material, and where the band-offset layer has a wider bandgap than the channel layer.
- In some embodiments of the present invention, the barrier layer thus formed comprises a spacer layer comprising a third III-N material, and a cap layer disposed on the spacer layer, the cap layer comprising at least two sublayers. Each sublayer is selectively etchable with respect to sublayers immediately below and above, each sublayer comprises a III-N material AlxInyGazN in which 0≦x≦1, 0≦y≦1, and 0≦z≦1, and at least one of the sublayers has a non-zero Ga content with 0<z≦1. In addition, a sublayer immediately above the spacer layer has a wider bandgap than the spacer layer, and a bottom of the gate recess is within or on a layer selected from the group consisting of the channel layer, the spacer layer, and one of the sublayers of the cap layer.
- In some embodiments of the present invention, the barrier layer thus formed comprises a bottom sublayer, a middle sublayer, and a top sublayer, where each sublayer comprises a III-N material AlxInyGazN in which 0≦x≦1, 0≦y≦1, and 0≦z≦1. Moreover, the bottom sublayer has a bandgap equal to or greater than that of the channel layer, the middle sublayer has a bandgap equal to or greater than that of the bottom sublayer, the top sublayer has a bandgap equal to or smaller than that of the middle sublayer, and a bottom of the gate recess is within or on a layer selected from the group consisting of the channel layer, and one of the sublayers of the barrier layer.
- In some embodiments of the present invention, the method further comprises depositing a back barrier layer below the channel layer, where the back barrier layer comprises a III-N material AlxInyGazN in which 0≦x≦1, 0≦y≦1, and 0≦z≦1, and where the back barrier layer has a wider bandgap and/or an opposite polarization direction than the channel layer.
- Yet other aspects of the present invention include the semiconductor structures, processes and methods comprising the steps described herein, and also include the processes and modes of operation of the devices described herein. Other aspects and embodiments of the present invention will become apparent from the detailed description of the invention when read in conjunction with the attached drawings.
- The foregoing summary is provided by way of illustration and is not intended to be limiting.
- Embodiments of the present invention described herein are exemplary, and not restrictive. Embodiments will now be described, by way of examples, with reference to the accompanying drawings. In these drawings, each identical or nearly identical component that is illustrated in various figures is represented by a like reference character. For purposes of clarity, not every component is labeled in every drawing. The drawings are not necessarily drawn to scale, with emphasis instead being placed on illustrating various aspects of the techniques and devices described herein.
-
FIGS. 1, 2 and 3 show exemplary semiconductor structures each containing a recessed-gate transistor, according to several embodiments of the present invention, respectively. -
FIGS. 4, 5, and 6 show exemplary semiconductor structures each containing a recessed-gate transistor with a gate electrode stepped on the bottom, according to several embodiments of the present invention, respectively. -
FIG. 7 shows a multi-layer semiconductor structure with a plurality of dual layer barrier structures, according to one embodiment of the present invention. -
FIG. 8 shows a multi-layer semiconductor structure with a spacer layer and a cap layer comprising multiple selectively etchable sublayers, according to one embodiment of the present invention. -
FIGS. 9, 10, 11, and 12 show exemplary multi-layer semiconductor structures each containing a recessed-gate transistor with a gate electrode stepped on the bottom, according to several embodiments of the present invention, respectively. - In the following description, for purposes of explanation, numerous specific details are set forth in order to provide a thorough understanding of the invention. It will be apparent, however, to one skilled in the art that the invention can be practiced without these specific details. In other instances, structures, devices, activities, and methods are shown using schematics, use cases, and/or flow diagrams in order to avoid obscuring the invention. Although the following description contains many specifics for the purposes of illustration, anyone skilled in the art will appreciate that many variations and/or alterations to suggested details are within the scope of the present invention. Similarly, although many of the features of the present invention are described in terms of each other, or in conjunction with each other, one skilled in the art will appreciate that many of these features can be provided independently of other features. Accordingly, this description of the invention is set forth without any loss of generality to, and without imposing limitations upon, the invention.
- Broadly, embodiments of the present invention relate to multi-layer semiconductor structures and methods for fabricating such structures, with recessed gate regions and/or ohmic regions. Such multi-layer structures with recess regions may facilitate the monolithic integration of Group III-Nitride (III-N) transistors having different threshold voltages, while minimizing gate leakage current through the barrier layer, either below the gate region, through sidewalls of the gate recess, or at gate edges. The semiconductor structures described herein may be formed of compound semiconductor materials, such as III-V semiconductor materials, particularly Group III-Nitride (III-N) semiconductor materials.
- The threshold voltage of a transistor is a gate voltage past which the transistor is turned from an on-state to an off-state, or vice versa. Gate and/or ohmic recesses formed with specific, controllable depths can lead to desired or targeted threshold voltages, thus enabling the production of normally-off field effect transistors, and the integration of Enhancement-mode (E-mode) and Depletion-mode (D-mode) transistors on a common substrate. In addition, gate recesses have been used in nitride semiconductor-based high-electron-mobility transistors (HEMTs) to reduce short channel effects, improve current gain cut-off frequency, and improve device performance in various manners. Nonetheless, the recessing process may induce surface damages and cause etch-based variations that significantly contribute to increased gate leakage current, thus comprising device characteristics, reliability, and stability.
- Described herein are semiconductor structures and processes for forming semiconductor structures to precisely control etching depth, produce low defect density on recessed surfaces, and significantly reduce gate leakage current by the use of insulating filler elements and air gaps within gate recesses. In particular, some embodiments of the present invention modify a gate edge profile within a gate recess by stepping the bottom of a gate electrode using at least one filler element during the fabrication process, and by further shielding or insulating the recessed and stepped gate electrode from enclosing semiconductor materials using additional filler elements and/or air gaps that partially or fully cover the gate electrode within the gate recess.
- Further described herein are multi-layer semiconductor structures and techniques that exploit etching selectivity between different III-N semiconductor materials. For example, GaN can be selectively etched over materials such as AlN, AlGaN, InAlN and AlInGaN with high Al content using a dry etching technique. More generally, iterations between a selective dry etching step and a selective or non-selective wet etching step may be used to achieve precise control of recess depth and to produce a surface with a low density of defect states.
- With reference to the figures, embodiments of the present invention are now described in detail.
-
FIG. 1 shows a cross-section view of anexemplary semiconductor structure 100 containing a recessed-gate transistor with a gate electrode orgate contact 110 insulated fromsidewalls gate recess 120 byair gaps FIG. 2 shows anexemplary semiconductor structure 200 containing a recessed-gate transistor with agate contact 210 insulated fromsidewalls gate recess 220 byfiller elements FIG. 3 , on the other hand, shows anexemplary semiconductor structure 300 containing a recessed-gate transistor with agate contact 310 insulated fromsidewalls gate recess 320 byair gaps - Each of
semiconductor structures substrate 102, abuffer layer 104, achannel layer 106, and abarrier layer 150. In some embodiments, each layer may have a thickness of at least 0.2 nanometers (nm), andchannel layer 106 may have a thickness between 1 nm and 10,000 nm or 10 μm. In some embodiments, each layer may have a thickness between 0.5 nm and 40 nm. In some embodiments,barrier layer 150 may include two or more sublayers, where each sublayer may be etchable by different etching techniques, where some sublayers may serve as etch stops to sublayers immediately above, and where each sublayer may possess bandgap properties the help improve threshold voltages when used in a field-effect transistor. - In
semiconductor structures 100 shown inFIG. 1 ,gate recess 120 is etched intobarrier layer 150, where abottom 125 ofgate recess 120 is positioned withinbarrier layer 150. In some embodiments, thickness of the semiconductor material between the gate recess andchannel layer 106 is between 0.5 nm and 40 nm. In some embodiments, thickness of the semiconductor material between the gate recess andchannel layer 106 is within 10 nm.Gate electrode 110 is disposed ingate recess 120, in-between sourceohmic electrode 126 and drainohmic electrode 128, each disposed in ohmic recesses etched intobarrier layer 150.Air gaps gate electrode 110 frombarrier layer 150, thus reducing gate leakage through the sidewalls of the gate recess, and help increase device breakdown voltage. In this example, the lateral lengths or “thickness” ofair gaps air gaps top portion 112 ofgate electrode 110, exceeding a top level ofgate recess 120, may be no greater in length thangate recess 120, where the length ofgate recess 120 is represented by LGR, as indicated in the cross-section view shown inFIG. 1 . In this particular example, bothgate electrode 110 andgate recess 120 are shown to be rectangular in cross section, and uniform in lateral length. In embodiments where eithergate electrode 110 orgate recess 120 is further recessed, stepped, or otherwise modified to be nonuniform in shape, gate length LG may be measured as the largest lateral distance between two sidewalls ofgate electrode 110, while gate recess length LGR may be measured as the largest lateral distance between two sidewalls ofgate recess 120. - In
semiconductor structure 200 shown inFIG. 2 ,gate recess 220 is etched intobarrier layer 150, where abottom 225 ofgate recess 220 is positioned withinbarrier layer 150.Gate contact 210 is disposed ingate recess 220, which in turn is positioned in-between ohmic recesses etched intobarrier layer 150.Filler elements gate contact 210 andsidewalls gate recess 220, respectively. In this example, each filler element covers a sidewall ofgate recess 220. In some embodiments, a filler element may partially fill the space betweengate contact 210 and a sidewall ofgate recess 220, towards the bottom, such that an air gap exists above the filler elements withingate recess 220. In some embodiments, each filler element may comprise more than one insulating material. In some embodiments, each filler element may comprise one or more components, where each component is made of one or more insulating materials. - In
semiconductor structure 300 shown inFIG. 3 ,gate recess 320 is etched intobarrier layer 150, and a lower portion ofgate recess 320 is stepped, so a bottom 325 ofgate recess 320 is onchannel layer 106.Gate contact 310 is disposed ingate recess 320 and through the lower stepped portion. In this example,air gaps gate contact 310 andsidewalls gate recess 320 partially insulategate contact 310 frombarrier layer 150. - Although pairs of air gaps are shown in
FIG. 1 andFIG. 3 , and a pair of filler elements is shown inFIG. 2 , in some other embodiments not shown explicated herein, a single air gap or a single filler element may be present, between the gate contact and the sidewall towards the drain ohmic contact, to reduce gate-drain leakage current. - Examples of materials that may form the
semiconductor structure 100 will now be described. - In some embodiments, a semiconductor material with a lattice constant different from that of
substrate 102 may be formed oversubstrate 102, wheresubstrate 102 is suitable for III-Nitride semiconductor epitaxial growth. In some embodiments,buffer layer 104 may be included betweensubstrate 102 and the overlying semiconductor material to accommodate a difference in lattice constant.Substrate 102 may include a group IV, III-V, or II-VI semiconductor material such as silicon, germanium, or ZnO for example. Other typical substrates include SiC, Sapphire, Si, and bulk GaN. The semiconductor material formed oversubstrate 102 may include a compound semiconductor material, such as a III-V semiconductor material (e.g., a III-N material). Suitable techniques for accommodating a lattice mismatch betweensubstrate 102 and a semiconductor material of a different lattice constant using abuffer layer 104 are understood by those of ordinary skill in the art, and will not be detailed herein. In some embodiments, asubstrate 102 having a suitable lattice constant for the formation of overlying compound semiconductor material(s) may be used, andbuffer layer 104 may be omitted. For example,substrate 102 may be a GaN substrate, a ZnO substrate or another substrate of a material with a lattice constant similar to that of a compound semiconductor material to be formed thereon. The techniques described herein are not limited as tosubstrate 102 orbuffer layer 104. In addition, although not shown explicitly inFIG. 1 , in some embodiments, a nucleation layer may be disposed betweensubstrate 102 andbuffer layer 104; in some other embodiments,buffer layer 104 may include the nucleation layer or a nucleation region at the interface withsubstrate 102. -
Substrate 102 and the layers of semiconductor materials formed thereon may be monocrystalline, and may have any suitable crystallographic orientation. Compound semiconductor materials, if included insubstrate 102 or an overlying layer, may have any suitable composition at the face of the semiconductor material. If a III-N material is included, it may have an N-face composition or a group III face composition. For example, GaN may be grown either N-face/N-polar, Ga-face/Ga-polar or in non-polar orientations. -
Channel layer 106 may be formed of a semiconductor material suitable for formation of a channel therein, to provide electrical conduction. In some embodiments,channel layer 106 may include a III-V semiconductor material, such as a III-N semiconductor material. In some embodiments,channel layer 106 may include gallium nitride (GaN). In some embodiments, a nitride semiconductor material may be used such as BwAlxInyGazN, for example, in which w, x, y and z each has a suitable value between zero and one (inclusive), and w+x+y+z=1. Exemplary materials for the formation ofchannel layer 106 include, but are not limited to, GaN, InN, AlGaN, AlInN, InGaN, and AlInGaN. - In some embodiments, a semiconductor heterostructure may be formed in the
semiconductor structure 100. For example, in some embodiments abarrier layer 150 comprising Bw1Alx1Iny1Gaz1N and achannel layer 106 comprising Bw2Alx2Iny2Gaz2N may be formed, where a semiconductor material ofbarrier layer 150 has a larger bandgap and/or polarization than that ofchannel layer 106. However, the techniques described herein are not limited as to the formation of heterostructures. - As implicitly implied above, in some embodiments, each layer formed over
substrate 102, includingbuffer layer 104,channel layer 106, andbarrier layer 150 may comprise more than one materials, including III-N materials. For example,buffer layer 104 may comprise an AlN/GaN superlattice. In some embodiments, a portion or one or more regions ofbuffer layer 104 orchannel 106 may be GaN. Such regions may be located at layer interfaces, or at positions particularly defined with respect to desired gate or ohmic contact regions. For example, the nucleation layer as described before may be included as part ofbuffer layer 104 at the interface withsubstrate 102. In yet some other embodiments, one or more layers formed over substrate 2 may be doped with a suitable dopant. - As discussed above, in some embodiments,
barrier layer 150 may be formed having two or more layers or sublayers, as shall be discussed further with respect toFIGS. 7 and 8 . For example,barrier layer 150 may include one or more “dual-layer” barrier structures each having an upper barrier layer of a first semiconductor material that is etchable using a first etching technique and a lower barrier layer of a second semiconductor material that is etchable using a second etching technique. For example, the upper barrier layer may include a semiconductor material selectively etchable in a dry etching process, such as GaN, or another nitride semiconductor material such as BwAlxInyGazN, in which w, x, y and z each has a suitable value between zero and one (inclusive), and w+x+y+z=1, and the composition is such that the nitride semiconductor material is selectively etchable using a dry etching process. As another example, the upper barrier layer may include a semiconductor material such as BwAlxInyGazN in which x is less than 0.25. In yet some other embodiments,barrier layer 150 may comprise an odd number of sublayers. - Any sublayer of
barrier layer 150 orbarrier layer 150 itself may be doped or undoped. Doping of a sublayer may supply carriers to channellayer 106 underneath. After gate recessing, one or more doped regions may be formed below the gate, between the gate and the source and/or between the gate and the drain, outside of the gate-recess. A doped region may be polarization doped or may include dopants such as n-type dopants or p-type dopants. A doped region may have any suitable doping concentration and distribution. For example, dopants may be provided at the lower surface ofbarrier 150, the upper surface ofbarrier layer 150, a lower surface or an upper surface of a sublayer withinbarrier 150, and/or in another location. The doping profile may be uniform or non-uniform. The doping concentration may be at least 1016 cm−3. In some embodiments, a delta-doping profile may be used. In addition, any suitable doping technique may be used, such as implantation or diffusion. In some embodiments, ay sublayer ofbarrier layer 150 may be doped during its formation (e.g., growth). In some embodiments, the doping type may be of the same type as that of carriers in the channel region. For example, the doping type may be n-type for an n-channel transistor and p-type for a p-channel transistor. In some embodiments, a doped region may be highly doped. - The reference herein to BwAlxInyGazN or a “BwAlxInyGazN material” refers to a semiconductor material having nitride and one or more of boron, aluminum, indium and gallium. Examples of BwAlxInyGazN materials include binary, ternary, and quaternary compounds such as GaN, AlN, AlGaN, AlInGaN, InGaN, and BAlInGaN, by way of illustration. Examples of BwAlxInyGazN materials also include compounds with relatively percentages in which w, x, y and z each has a suitable value between zero and one (0≦w≦1, 0≦x≦1, 0≦y≦1, and 0≦z≦1), and w+x+y+z=1. A BwAlxInyGazN material may include other materials besides nitride, boron, aluminum, indium and/or gallium as well. For example, a BwAlxInyGazN material may be doped with a suitable dopant such as silicon and germanium. Furthermore, in the present disclosure, the terms “BwAlxInyGazN material” and “III-N material” are used interchangeably to represent nitride-based compound semiconductor materials, unless otherwise specified or limited.
- In this particular example shown in
FIG. 1 , gate contact orgate electrode 110 is placed in the recessedgate region 120, making direct contact tobarrier layer 150 at the bottom of the gate recess.Gate contact 110 may be made from materials such as metals, metal compounds, polycrystalline semiconductors, or any other suitable conductive material. Ohmic contacts orelectrodes channel layer 106.Ohmic electrodes channel layer 106, so electrical current flows between the ohmic electrodes laterally via the channel layer.Gate electrode 110 controls the current flow in thechannel layer 106 underneath the gate recess. Depending on the thickness of the barrier layer below the gate contact, and the gate electrode's work-function, the transistor shown inFIG. 1 may be either a normally-off device having no free electrons in the channel layer underneath the gate region with no gate bias voltage, or a normally-on device having free electrons in the channel layer underneath the gate region with no gate bias voltage. In some embodiments, ohmic electrodes are in contact with at least part of the side-walls of the ohmic recesses. In addition, the depth of ohmic recesses may be the same as that of the gate recess, deeper than that of the gate recess, as shown inFIG. 1 , or shallower than that of the gate recess. The ohmic recess depth forsource 126 and drain 128 may be the same or different. - A process of forming a transistor in the
semiconductor structures FIGS. 1, 2, 3 , using two or more etching steps is discussed in parent application Ser. No. 15/234,405, the entire disclosure of which is hereby incorporated by reference in its entirety herein. -
FIG. 4 shows a cross-section view of anexemplary semiconductor structure 400 containing a recessed-gate transistor with agate contact 410 stepped on the bottom and insulated fromsidewalls gate recess 420 byfiller elements FIG. 5 shows anexemplary semiconductor structure 500 containing a recessed-gate transistor with agate contact 510 stepped on the bottom and insulated from the sidewalls of the gate recess byair gaps filler elements FIG. 6 shows anexemplary semiconductor structure 600 containing a recessed-gate transistor with agate contact 610 stepped on the bottom and insulated fromsidewalls gate recess 620 byfiller elements gate dielectric layer 690, according to yet another embodiment of the present invention. Again, each ofsemiconductor structures substrate 102, abuffer layer 104, achannel layer 106, and abarrier layer 150, comprising semiconductor materials as described with respect toFIGS. 1 to 3 . - In
semiconductor structure 400 shown inFIG. 4 ,gate recess 420 is etched intobarrier layer 150, where abottom 425 ofgate recess 420 is withinbarrier layer 150.Gate contact 410 is disposed withingate recess 420, in-between source and drain ohmic contacts recessed intobarrier layer 150. A lower portion ofgate contact 410 is stepped to form abottom stem 414 and twobottom steps gate recess 420. In other words, gate edge profiles ofgate contact 410 is modified inFIG. 4 through the stepping process to increase an overall surface area around the bottom of the gate electrode. In some embodiments, multiple steps may be formed at the bottom ofgate contact 420, on one side or on both sides, through the use of multiple filler elements formed using one or more selective etching steps. Furthermore, in some embodiments,gate contact 410 may be stepped to form a bottom stem and asingle bottom step 416, on the side towards the drain ohmic contact, to reduce gate-drain leakage current. InFIG. 4 , each ofbottom step gate contact 410. Alternatively, a bottom step may be viewed as a cornered volume of the stepped portion ofgate contact 410. - In addition, in this example, a non-stepped
middle portion 413 ofgate contact 410, located abovebottom steps top portion 412 ofgate contact 410, wheretop portion 412 exceeds a top level ofgate recess 420. In some embodiments,top portion 412 may be no greater in length than non-steppedmiddle portion 413. In some embodiments,top portion 412 may be no greater in length thangate recess 420. In yet some embodiments,top portion 412 may be wider in length than non-steppermiddle portion 413, orgate recess 420, to form a T-shaped or F-shaped gate top, which may also be viewed as a gate electrode with one or more field plate extensions. - Furthermore, in this example,
filler element 484 is of a L-shape, whilefiller element 487 is of a laterally-inverted L-shape.Filler element 484 coversbottom step 415 and the sidewall ofgate contact 410 on the side of the source ohmic contact.Filler element 484 also covers or is in contact withsidewall 422 ofgate recess 420 on the side of the source ohmic contact. Similarly,filler element 487 coversbottom step 416 and the sidewall ofgate contact 410 on the side of the drain ohmic contact.Filler element 487 is further in contact withsidewall 424 ofgate recess 420 on the side of the drain ohmic contact. Alternatively, in this embodiment, each of 484 and 487 may be viewed as a filler element group consisting of multiple filler elements or filler components. For example,group 484 may be viewed as a combination of afirst filler element 485 disposed belowbottom step 415, and asecond filler element 486 disposed betweengate contact 410 andsidewall 422. In addition,filler elements bottom step 415 is thus fully covered, or enclosed, by a combination of thefirst filler element 485 and thesecond filler element 486. Same applies tofiller elements group 487. In various embodiments, each constituting filler element such as 485, 486, 488, and 489 may comprise one or more insulating materials, possibly layered or stacked either laterally or vertically. Iffiller elements filler element 484. Moreover, in some other embodiments,filler elements gate recess 420, and may further be extended laterally to fully or partially cover a top surface ofbarrier layer 150, or any other semiconductor layers placed thereon. -
FIG. 5 shows another embodiment of the present invention, whereair gaps gate contact 510 fromsidewalls gate recess 520 withinbarrier layer 150. In this example, L-shapedfiller elements gate contact 520, are in direct contact and covered by such filler elements. -
FIG. 6 shows another embodiment of the present invention where agate dielectric layer 690 is disposed within and overgate recess 620, directly abovefiller elements gate contact 610 within the gate recess, thus insulatinggate contact 610 frombarrier layer 150.Dielectric layer 690 is also in contact with the vertical components offiller elements Gate dielectric layer 690 may be formed by oxidization of the surfaces of III-Nitride semiconductors inside the gate recess region, or by deposition of any suitable dielectric material, such as SiO2, Al2O3, and SiN. In addition, although not shown explicitly, in some embodiments,gate dielectric layer 690 may be formed underneath thegate contact 610 only, where the sidewalls ofgate contact 610 may be insulated by filler elements or air gaps from sidewalls ofgate recess 620. - While
FIGS. 1-6 provide exemplary embodiments of semiconductor structures comprising a barrier layer with or without sublayers,FIG. 7 shows an exemplary multi-layer semiconductor structure with abarrier layer 750 having a plurality of dual layer barrier structures, on which transistors with bottom steps may be formed, according to one embodiment of the present invention. In different embodiments, any suitable number of “dual-layer” barrier structures may be included. For example, as illustrated inFIG. 7 , asemiconductor structure 700 may include a first dual-layer barrier structure 757 and a second dual-layer barrier structure 753, each having an upper barrier sublayer and a lower barrier sublayer. The upper and lower barrier sublayers are indicated inFIGS. 7 as 758 and 756, respectively, for dual-layer barrier structure 757, and indicated as 754 and 752, respectively, for dual-layer barrier structure 753. Dual-layer barrier structures barrier layer 750 may include one or both of a band-offsetlayer 730 and a carrier-donor layer 760. Apassivation layer 770 may be further included in thesemiconductor structure 700 abovebarrier layer 750. Each barrier sublayer may be formed using materials and processes similar for barrier sublayers as discusses with respect tosemiconductor structures FIGS. 1 to 3 . For example, each layer or sublayer shown inFIG. 7 may comprise a III-N material BwAlxInyGazN. Moreover, a gate recess or an ohmic recess may be formed through one or more of thebarrier sublayers - In one illustrative embodiment where
barrier layer 750 comprises dual-layer structures layer 758, then a second etching process (e.g., a wet etching process) may be performed to remove a region oflayer 756. Then, the first etching process (e.g., a dry etching process) may be performed to remove a region oflayer 754, and the second etching process (e.g., a wet etching process) may be performed to remove a region oflayer 752. A bottom-stepped gate contact may be formed in the gate recess by first depositing a filler layer covering the bottom the gate recess, then recessing through the filler layer, wherein a length of the second recess through the filler layer is shorter than that of the first recess, to form one or more filler elements at the bottom of the gate recess. Source and drain regions with or without ohmic recesses may be formed as well. - In embodiments where each or any combination of a band-offset
layer 730, a carrier-donor layer 760, and apassivation layer 770 may be included in thesemiconductor structure 700, similar etching techniques may be performed to form gate and/or ohmic recesses through the passivation layer, and one or more sublayers ofbarrier layer 750. The techniques described herein are not limited in this respect, as band-offsetlayer 730, carrier-donor layer 760, andpassivation layer 770 may be optional. - Structures and techniques described herein are not limited to techniques for forming a gate-recess. Such techniques may be used any other application where a damage-free, uniform and/or reproducible etch is desired, or where bottom-stepped electrodes are needed. One example is the formation of ohmic recesses to reduce ohmic contact resistance and/or to form gold-free ohmic contacts. Another example is the formation of one or more recesses and/or electrodes to access an n-doped layer in a GaN light emitting diode or laser. A further example is the formation of one or more recesses and/or electrodes to access the base and/or collector layers in a III-N bipolar transistor.
-
FIG. 8 shows anothermulti-layer semiconductor structure 800 further extending the “dual layer”barrier structure 700 shown inFIG. 7 , wherebarrier layer 880 comprises aspacer layer 832 and acap layer 850 having multiple selectively etchable sublayers, according to one embodiment of the present invention. In different embodiments, bothmulti-layer semiconductor structure 700 andmulti-layer semiconductor structure 800 may be used for fabricating transistors having different threshold voltages (VT) and bottom-stepped gate contacts. The threshold voltage of a transistor is a gate voltage past which the transistor is turned from an on-state to an off-state, or vice versa.Semiconductor structure 800 may include asubstrate layer 802, abuffer layer 804, achannel layer 806, a band-offsetlayer 830, aspacer layer 832, acap layer 850, acarrier donor layer 860, and apassivation layer 870. Each ofsubstrate layer 802,buffer layer 804, andchannel layer 806 may be formed using materials and processes similar forsubstrate layer 102,buffer layer 104, andchannel layer 106, respectively, according to descriptions of embodiments shown inFIGS. 1-6 .Cap layer 850 may be formed using materials and processes similar forbarrier sublayers FIG. 7 , or similar for barrier sublayers as discusses with respect to semiconductor structures shown inFIGS. 1-6 . Compared with previously disclosed semiconductor structures such as 100, 200, 400, or 700, each of semiconductor layers abovechannel layer 806, including band-offsetlayer 830,spacer layer 832, sublayers ofcap layer 850, and carrier-donor layer 860, may be viewed as a sublayer withingeneral barrier layer 880. Each or any barrier sublayer as disclosed herein may be optional. - Instead of pairs of upper and lower barrier layers,
cap layer 850 comprises a plurality of n selectively etchable sublayers, such assublayer 851 with thickness t1,sublayer 852 with thickness t2,sublayer 858 with thickness tn−1, andsublayer 859 with thickness t, where n may be any even or odd integer greater than or equal to two, according to various embodiments of the present invention. For example, amulti-layer barrier 880 with acap layer 850 having n=4 sublayers, a band-offset layer, and a carrier-donor layer, gives rise to theillustrative semiconductor structure 700 shown inFIG. 7 . Thickness t1, t2, . . . , tn may be between 2 angstroms and 500 nanometers, and may or may not be the same in various embodiments of the present invention. For example, tn may be greater than or equal to the total thickness of all other sublayers. In another example, all odd-numbered or odd sublayers may be grown to a first thickness, while all even-numbered or even sublayers may be grown to a second thickness. - In some embodiments, each i-th sublayer (1≦i<n) of
cap layer 850 is selectively etchable with respect to the (i+1)-th sublayer below using some etching technique, thus the (i+1)-th sublayer below may serve as an etch stop for the i-th sublayer under the given etching technique. The n-th sublayer may further be selectively etchable with respect to band-offsetlayer 830,spacer layer 832, or any layer disposed directly below and/or in contact with the n-th sublayer.Spacer layer 832 may or may not be selectively etchable over band-offsetlayer 830. In some embodiments, each sublayer is selectively etchable with respect to both the sublayer above and the sublayer below using some etching technique, such as dry etching, wet etching, or a combination of dry etching and wet etching. For example, selectively etchable sublayers may be classified into two types. All odd sublayers counting from thefirst sublayer 851 may be formed of a material that is selectively etchable with respect to even sublayers by a first etching technique, such as dry etching, while all even sublayers counting from thesecond sublayer 852 may be formed of a material that is selectively etchable with respect to odd sublayers by a second etching technique, such as wet etching, or vice versa. The n-th sublayer may further be selectively etchable with respect to band-offsetlayer 830,spacer layer 832, or any layer disposed directly below and/or in contact with the n-th sublayer, using a dry etch process, a wet etch process or a combination thereof. The n-th sublayer may be etched at a faster rate the layer below, and the selectivity of the etch process may be greater than 3:1, such that the n-th sublayer is etched at a rate greater than three times as high as the rate at which layer below is etched.Spacer layer 832 may or may not be selectively etchable oversublayer 859 and/or band-offsetlayer 830. Band-offsetlayer 830 may or may not be selectively etchable oversublayer 859 and/orspacer layer 832. Each of the odd sublayers may have the same structure, composition, and/or thickness. Alternatively, each of the odd sublayers may have a different structure, composition, and/or thickness. Similarly, each of the even sublayers may have the same structure, composition, and/or thickness, or a different structure, composition, and/or thickness. In yet some other embodiments, each sublayer may be selectively etchable with respect to a selected subset of all other sublayers, using one or more etching techniques. For example, in some embodiments, selectively etchable sublayers may be classified into three types, where each type is repeated every three sublayers, and where each type is selectively etchable over the other two types using one or more etching techniques. - More specifically, selective etchability of sublayers within
cap layer 850 may be achieved by alternating sublayer material between two or more types of compositions. In some embodiments, all odd sublayers counting from thefirst sublayer 851 may include or comprise a semiconductor material that is selectively etchable in a dry etching process, such as GaN, or another nitride semiconductor material BwAlxInyGazN, in which w, x, y and z each has a suitable value between zero and one inclusive (0≦w, x, y, z≦1), and the composition is such that the nitride semiconductor material is selectively etchable using a dry etching process. In one example, odd sublayers may be formed of a semiconductor material BwAlxInyGazN where x is less than 0.25. In different embodiments, the values of w, x, y, and z may or may not add to 1. In some embodiments, odd sublayers may be formed of a semiconductor material AlxInyGazN in which x, y, and z each has a suitable value between zero and one inclusive (0≦x, y, z≦1), and where the values of x, y, and z may or may not add to 1. Similarly, all even sublayers counting from thesecond sublayer 852 may include or comprise a semiconductor material that is selectively etchable in a wet etching process, such as AlN, or another nitride semiconductor material BwAlxInyGazN, in which w, x, y and z each has a suitable value between zero and one inclusive (0≦w, x, y, z≦1), and the composition is such that the nitride semiconductor material is selectively etchable using a wet etching process. The values of w, x, y, and z may or may not add to 1. In one example, even sublayers may be formed of a semiconductor material BwAlxInyGazN where x is greater than 0.5. In some embodiments, even sublayers may be formed of a semiconductor material AlxInyGazN in which x, y, and z each has a suitable value between zero and one inclusive (0≦x, y, z≦1), and where the values of x, y, and z may or may not add to 1. In those embodiments, at least one of the selectively etchable sublayers may have a non-zero Ga content (0<z≦1) that makes the layer growth process easier. When consecutive, adjacent or continuous sublayers ofcap layer 850 have their material compositions alternate between GaN and AlN, fluorine-based chemicals may be used to dry etch GaN without etching AlN, while tetramethylammonium hydroxide (TMAH) may be used to wet etch AlN without etching GaN. In some embodiments, odd layers may include or comprise a semiconductor material that is selectively etchable in a wet etching process, such as AlN, while even layers may include or comprise a semiconductor material that is selectively etchable in a dry etching process, such as GaN. - The reference herein to BwAlxInyGazN, “BwAlxInyGazN material,” or “III-N material” refers to a semiconductor material having nitride and one or more of boron, aluminum, indium and gallium. An AlxInyGazN material is a BwAlxInyGazN material where w=0. Examples of BwAlxInyGazN materials include, but are not limited to, GaN, AlN, AlGaN, AlInGaN, InGaN, and BAlInGaN, Al0.15Ga0.85N, and Al0.65Ga0.35N, by way of illustration. A BwAlxInyGazN material may include other materials besides nitride, boron, aluminum, indium and/or gallium. For example, a BwAlxInyGazN material may be doped with a suitable dopant such as silicon or germanium.
- In some embodiments, selective etchability of sublayers within
cap layer 850 is achieved by alternating aluminum content or composition of adjacent or consecutive sublayers between a relatively high value or percentage and a relatively low value or percentage. In other words, selective etchability may be achieved by alternating between Al-light and Al-rich sublayers, or adjusting the value of x for material BwAlxInyGazN or AlxInyGazN as described above. In one example, consecutive or adjacent sublayers ofcap layer 850 may have Al contents alternating between less than 0.5 inclusive and greater than 0.5 exclusive, less than 0.5 exclusive and greater than 0.5 inclusive, or less than 0.5 exclusive and greater than 0.5 exclusive. In other examples, consecutive or adjacent sublayers ofcap layer 850 may have Al content alternate between less than 0.25 and greater than 0.5, less than 0.35 and greater than 0.5, or less than 0.35 and greater than 0.65, inclusive or exclusive. In some embodiments, at least one of the plurality of selectively etchable sublayers has an Al content great than 0.5. In addition, at least one of the selectively etchable sublayers may have a non-zero Ga content (0<z≦1). Moreover, B, Al, In, and Ga compositions in each type of sublayers may not necessarily be the same. For example, when n is odd,first sublayer 851 and n-th sublayer 859 may have x=0.1 and x=0.2 respectively, whilesecond layer 852 and (n−1)-th sublayer 858 may have x=0.6 and x=0.7 respectively. Similarly, when n is even,first sublayer 851 and (n−1)-th sublayer 858 may have x=0.1 and x=0.2 respectively, whilesecond sublayer 852 and n-th sublayer 859 may have x=0.6 and x=0.7 respectively. - In some embodiments, each layer or sublayer of
multi-layer semiconductor structure 800 may comprise a III-N material BwAlxInyGazN, andoptional spacer layer 832 may comprise a III-N material with a zero Al content in the form of BwInyGazN, including materials such as GaN and InGaN.Spacer layer 832, or any other sublayer ofbarrier 880 may also be n-type doped. - In some embodiments, one or more layers or sublayers shown in
FIG. 8 may comprise III-N materials such as GaN, AlN, AlGaN, InAlN, and AlInGaN. For example,channel layer 806 may comprise GaN, band-offsetlayer 830 may comprise AlGaN,spacer layer 832 may comprise GaN, andcap layer 850 may comprise alternating layers of GaN and AlN. In some embodiments, band-offsetlayer 830 may comprise a III-N material with a non-zero Al content. In some embodiments, band-offsetlayer 830 may comprise a III-N material AlxInyGazN in which x+y+z=1, 0<x≦1, 0≦y≦1, and 0≦z≦1. In yet some embodiments, band-offsetlayer 830 may comprise a III-N material AlxGazN in which x+z=1, 0.05<x≦0.4, and 0.6≦z≦0.95. - In some embodiments, band-offset
layer 830 may have a wider bandgap or a higher conduction band edge thanchannel layer 806 below andspacer layer 832 above. In addition,spacer layer 832 may have a narrower bandgap or a lower conduction band edge thansublayer 859 immediately above. A spacer layer with a narrower bandgap makes the net polarization charge at the interface between the spacer layer and the band-offset layer negative as the polarization of the spacer layer is smaller than that of the band-offset layer, thus helping to improve the threshold voltages when themulti-layer structure 800 withspacer layer 832 is used in a field-effect transistor. - In yet some embodiments,
barrier layer 880 may comprise a bottom sublayer, a middle sublayer, and a top sublayer, where the bottom sublayer may have an equal or wider bandgap thanchannel layer 806 below, the middle sublayer may have an equal or wider bandgap than the bottom sublayer, while the top sublayer may have an equal or narrower bandgap than the middle sublayer. For example, such bottom, middle and top sublayers may correspond to band-offsetlayer 830,spacer layer 832, andsublayer 859 shown inFIG. 8 , respectively. In some embodiments, the bottom sublayer comprises Alx1Gaz1N, the middle sublayer comprises AlN, and the top sublayer comprises Alx2Gaz2N. The middle sublayer may serve as an etch stop for the top sublayer. - Furthermore,
optional spacer layer 832 shown inFIG. 800 may have a thickness less than or equal to 20 nm, and/or greater than or equal to 0.2 nm. In various embodiments, thickness of a layer or sublayer may refer to an average, maximum, or medium vertical distance measured between points on an upper interface and a lower interface of the layer or sublayer. - Additionally, a
back barrier layer 805 may be inserted betweenchannel layer 806 andbuffer layer 830 in some embodiments, where the added back barrier layer may comprise a III-N material AlxInyGazN in which 0≦x≦1, 0≦y≦1, and 0≦z≦1, such as InN, AlN, InGaN, AlGaN, InAlN, and InAlGaN. The thickness ofback barrier layer 805 may be between 1 nm and 5 μm, but less than a critical thickness before which backbarrier layer 805 may crack due to mechanical stress.Back barrier layer 805 may have a wider bandgap thanchannel layer 806, a stronger polarization in the c-axis, or a negative polarization in the c-axis than that of the channel layer, so electrons in the channel layer may be better confined. -
FIGS. 9, 10, 11, and 12 show non-limiting exemplarymulti-layer semiconductor structures structure 700 shown inFIG. 7 , orstructure 800 shown inFIG. 8 , according to different embodiments of the present invention, respectively. In these exemplary structures, any of a bottom surface of the gate recess, a bottom surface of each filler element, or a bottom surface of a bottom stem of the stepped gate may be positioned within or on a sublayer in the multi-layer semiconductor structure disclosed herein, including, but are not limited to, a channel layer, or any sublayer of a barrier layer, where the barrier layer may comprise any combination of a band-offset layer, a spacer layer, a cap layer with selectively etchable sublayers, a carrier-donor layer, and any other suitable semiconductor layers. In other words,FIGS. 9, 10, 11, and 12 provide illustrative examples of relative positions of filler elements, gate recess, and gate bottom steps within the gate recess, in different permutations or variations. - More specifically,
FIGS. 9 and 10 show two exemplarymulti-layer semiconductor structures filler elements structure 800 shown inFIG. 8 , but without an explicit carrier-donor layer such aslayer 860, according to two separate embodiments of the present invention. Similar to the transistor structure shown inFIG. 4 , bothgate electrodes filler elements spacer layer 832. In addition, abottom surface 915 ofgate contact 910 shown inFIG. 9 is positioned onspacer layer 832. By comparison, abottom surface 1015 ofgate contact 1010 shown inFIG. 10 is positioned on band-offsetlayer 830. In both cases, the bottom surface of the gate contact may be viewed as the bottom surface of the gate recess as well. In various embodiments, a bottom of the gate contact or the gate recess may be positioned anywhere within or on a sublayer in the multi-layer semiconductors structures disclosed herein, including, but are not limited to, a channel layer, or any sublayer of a barrier layer, where the barrier layer may comprise any combination of a band-offset layer, a spacer layer, a cap layer with selectively etchable sublayers, a carrier-donor layer, or any other suitable semiconductor layers. In addition, each offiller elements passivation layer 870, may comprise the same insulating material aspassivation layer 870. Each offiller elements passivation layer 870, for example, using conformal deposition techniques. - By comparison, in
FIG. 11 , each offiller elements layer 830, while a bottom surface of the gate contact is also positioned on band-offsetlayer 830. InFIG. 12 ,filler elements spacer layer 832,filler elements layer 830, and a bottom surface of the gate contact is also positioned on band-offsetlayer 830. Each of the filler elements as shown inFIGS. 9 to 11 may comprise the same of different insulating materials. - To fabricate recessed-gate transistors with bottom-stepped gate contacts as shown in
FIGS. 9 to 12 , epitaxial growth of multiple semiconductor layers and selective etching of sublayers maybe performed. As an example, a fabrication process is discussed below. - To form
semiconductor structure 900 shown inFIG. 9 , epitaxial growth ofbuffer layer 804 may first take place onsubstrate layer 802. Subsequently, layers 806, 830, 832, and 850 may be grown successively overbuffer layer 804, andpassivation layer 870 may be formed thereon. A photoresist mask may then be used to pattern for gate and ohmic recesses, where either wet etching or dry plasma etching may be formed to removepassivation layer 870. The etching oflayer 870 may be stopped on the surface ofbarrier layer 850. For example, SF6-based plasma can selectively etchpassivation layer 870 over III-Nitridesemiconductor barrier layer 850. - Depending on the desired recess depth and the number of sublayers within,
barrier layer 850 may be further etched in the gate recess region, using one or more selective-etching techniques. Moreover, in some embodiments, a bottom sublayer ofbarrier layer 850 may be selectively etchable overspacer layer 832. For example, dry plasma containing BCl3 and SF6 gases may be used to selectively etch a bottom sublayer ofbarrier layer 850 containing less Al content thanspacer layer 832, wherespacer layer 832 may serve as an etch stop. To formsemiconductor structure 1000 shown inFIG. 10 ,spacer layer 832 may be further etched. In some embodiments,spacer layer 832 may be selectively etchable over band-offsetlayer 830. For example,spacer 832 may have higher Al content than band-offsetlayer 830, and may be wet etched using tetramethylammonium hydroxide or potassium hydroxide at elevated temperature, where the etch stops on band-offsetlayer 830. Similarly, time-etching or digital etching techniques may be employed to achieve desired recess depths. - In some exemplary embodiments, a conformal deposition of a filler layer covering the sidewalls of the gate recess may be performed, with non-isotropic plasma etching of the filler layer and selectivity over
spacer layer 832 to formfiller elements bottom surface 915, andfiller elements filler elements passivation layer 870 comprises the same material as the filler elements, the same deposition step may be used, followed by a subsequent recess step through the insulating material, to formpassivation layer 870,filler elements filler elements FIG. 12 . - A gate electrode as shown in
FIG. 9 may be deposited in the gate region covering the gate recess after the formation of the filler elements, with or without additional air gaps. Moreover, additional dielectric and metal layers may be formed over the device shown inFIG. 9 using standard back-end processes. - Ohmic recesses as shown in
FIG. 9 may have the same or different depth as the game recess. More specifically, ohmic recesses may be etched through at least thepassivation layer 870. In different embodiments, ohmic recesses may be formed before, after, or at the same time as the gate recess. Ohmic contacts or electrodes may be formed by depositing metals such as titanium and aluminum in the ohmic regions, covering the ohmic recesses, and by annealing the ohmic metal between 400° C. and 1000° C. Alternatively, ohmic contacts may be formed by implantation of n-type dopants such as Si, Ge or other suitable n-type dopants in the ohmic regions and subsequent activation of the dopants by annealing between 900° C. and 1400° C. After ohmic implantation and activation, ohmic metal may be deposited covering at least a part of the implantation region with optional ohmic metal annealing to form the ohmic contacts. - Use of ordinal terms such as “first,” “second,” “third,” etc., in the claims to modify a claim element does not by itself connote any priority, precedence, or order of one claim element over another or the temporal order in which acts of a method are performed, but are used merely as labels to distinguish one claim element having a certain name from another element having a same name (but for use of the ordinal term) to distinguish the claim elements.
- Also, the phraseology and terminology used herein is for the purpose of description and should not be regarded as limiting. The use of “including,” “comprising,” or “having,” “containing,” “involving,” and variations thereof herein, is meant to encompass the items listed thereafter and equivalents thereof as well as additional items. For example, an apparatus, structure, device, layer, or region recited as “including,” “comprising,” or “having,” “containing,” “involving,” a particular material is meant to encompass at least the material listed and any other elements or materials that may be present. The partially open-ended phrase “consisting essentially of” is meant to encompass essentially the material listed and does not preclude the presence of relatively small quantities of other materials, including the presence of dopants.
- Various aspects of the apparatus and techniques described herein may be used alone, in combination, or in a variety of arrangements not specifically discussed in the embodiments described in the foregoing description and is therefore not limited in its application to the details and arrangement of components set forth in the foregoing description or illustrated in the drawings. For example, aspects described in one embodiment may be combined in any manner with aspects described in other embodiments. In other words, although the present invention has been described with reference to specific exemplary embodiments, it will be evident that the various modification and changes can be made to these embodiments without departing from the broader scope of the invention. Accordingly, the specification and drawings are to be regarded in an illustrative sense rather than in a restrictive sense. It will also be apparent to the skilled artisan that the embodiments described above are specific examples of a single broader invention which may have greater scope than any of the singular descriptions taught. There may be many alterations made in the descriptions without departing from the scope of the present invention.
Claims (24)