US20170073857A1 - Multilayer woven fibrous structure including a hollow tubular part, production method thereof and composite part comprising same - Google Patents
Multilayer woven fibrous structure including a hollow tubular part, production method thereof and composite part comprising same Download PDFInfo
- Publication number
- US20170073857A1 US20170073857A1 US15/361,278 US201615361278A US2017073857A1 US 20170073857 A1 US20170073857 A1 US 20170073857A1 US 201615361278 A US201615361278 A US 201615361278A US 2017073857 A1 US2017073857 A1 US 2017073857A1
- Authority
- US
- United States
- Prior art keywords
- layers
- warp yarns
- weft
- yarns
- warp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A fiber structure made as a single piece by multilayer weaving using a method including weaving warp yarns of at least a first set of layers of warp yarns with weft yarns including at least some that are woven with extra length so as to have warp yarn end portions available that extend beyond the zone of weaving, the warp yarn end portions being returned to be woven with warp yarns by being reinserted in layers of warp yarns, and a hollow, or tubular, portion being formed by looping the first woven set of layers of warp yarns back onto itself and applying traction to the ends of the reinserted weft yarns so that a fiber preform for a part including a hollow portion can be obtained as a single piece.
Description
- This application is a division of U.S. application Ser. No. 13/980,128 filed Jul. 17, 2013, the entire contents of which is incorporated herein by reference. U.S. application Ser. No. 13/980,128 is a 371 of International Application No. PCT/FR12/050087 filed Jan. 13, 2012, and claims the benefit of priority from prior French Application No. 11 50499 filed Jan. 21, 2011.
- The invention relates to making a fiber structure by multilayer weaving, and more particularly a fiber structure including at least one hollow portion, in particular a portion that is tubular or substantially tubular.
- The field of application is in particular that of making fiber structures for use in providing fiber preforms for composite material parts that are obtained by densifying fiber preforms with a matrix, or parts that are obtained by hot isostatic pressing or by forging and diffusion-welding preforms made of metallic fibers, and particularly, but not exclusively, parts for aviation turbine engines. Examples include:
-
- parts having at least one tubular portion secured to another portion such as a panel or a plate, the tubular portion being for enabling an element to be supported, guided, or hinged beside the panel; and
- parts such as hollow support arms or ducts that that may optionally be partitioned longitudinally in order to form a plurality of passages.
- Proposals have already been made to produce a fiber preform as a single piece from a multilayer woven structure in order to form a composite material part that is of complex shape.
- The terms “multilayer weaving” or “three-dimensional weaving” are used herein to mean a weaving process between a plurality of layers of warp yarns and a set of weft yarns, at least some of the weft yarns interlinking warp yarns belonging to different layers of warp yarns. Several multilayer weaves can be used, such as interlock weaves, in which weft yarns in a given weft column move in the same manner in a plane of the weave, or else multi-satin, multi-plain, or multi-twill weaves. Reference may be made to Document WO 2006/136755.
- It is known to make a multilayer woven structure that, on being shaped, makes it possible to obtain a preform having a shape that is close to the shape of a composite material part that is to be made. Reference may be made to Documents U.S. Pat. No. 7 241 112 and WO 2010/061139 that relate to making composite material blades for turbine engines.
- An object of the invention is to provide a method of making a structure that is woven as a single piece by multilayer weaving and that enables a fiber preform to be obtained for a composite material part having at least one hollow portion, in particular a portion that is tubular or substantially tubular, and that presents high mechanical strength.
- In a first aspect of the method, the method comprises:
-
- weaving warp yarns of at least a first set of layers of warp yarns with weft yarns including at least some weft yarns that are taken over a distance that is greater than the width of the first set of layers of warp yarns measured in the weft direction in order to have weft yarn end portions available that extend beyond the zone of weaving;
- returning the end portions of said weft yarns so as to weave them with warp yarns by reinserting them in layers of warp yarns; and
- forming said hollow portion by looping the first woven set of layers of warp yarns back onto itself and applying traction to the ends of the reinserted weft yarns.
- The free end portions of weft yarns may be reinserted in layers of warp yarns of a second set of layers of warp yarns, the first and second sets of layers of warp yarns being superposed and connected together over a fraction only of the width in the weft direction of the first set of warp yarns.
- In a variant, the free end portions of weft yarns may be reinserted in layers of warp yarns of the first set of layers of warp yarns at locations that are offset in the warp direction relative to the locations of their initial insertion.
- In a second aspect of the method, in order to provide a woven structure having a longitudinally partitioned hollow portion, the method comprises:
-
- weaving warp yarns of a first set of layers of warp yarns with weft yarns including at least some that are inserted in layers of warp yarns of the first set of layers of warp yarns while being taken over a distance that is greater than the length of the first set of layers of warp yarns measured in the weft direction in order to have weft yarn end portions available that extend beyond the zone of weaving;
- weaving warp yarns of a second set of layers of warp yarns with weft yarns including at least some that are inserted in layers of warp yarns of the second set of layers of warp yarns while being taken over a distance that is greater than the length of the second set of layers of warp yarns measured in the weft direction in order to have weft yarn end portions available that extend beyond the zone of weaving, the first and second sets of layers of warp yarns being arranged one above another and being interlinked over a fraction only of their width in the weft direction;
- returning said weft yarn end portions so as to weave them with warp yarns by reinserting them in layers of warp yarns; and
- forming said partitioned hollow portion by looping the first and second sets of layers of warp yarns back onto themselves and applying traction to the ends of the reinserted weft yarns.
- Said end portions of weft yarn may be reinserted in layers of warp yarns of a third set of layers of warp yarns, the first, second, and third sets of warp yarns being superposed, and the first and second sets of layers of warp yarns being interlinked with the third set of layers of warp yarns over a fraction only of their width in the weft direction.
- In a variant, said end portions of weft yarn may be reinserted in layers of warp yarns of the first and second sets of layers of warp yarns at locations that are offset in the warp direction relative to the locations of their initial insertion.
- In any event, the hollow portion may be formed over a fraction only of the length of the woven structure in the warp direction.
- Thus, the invention is remarkable in that, in at least a portion of the woven structure that is to form a hollow portion, a set of warp yarns is woven with weft yarns presenting extra length enabling them to be reinserted in the warp in order to weave them once more with warp yarns. As a result, this set of warp yarns can be looped back onto itself so as to form the hollow portion in which weft yarns extend continuously all around the hollow portion, thereby conferring strong mechanical properties to the hollow portion of the part that is obtained after the woven structure has been shaped and densified.
- The invention also provides a woven fiber structure that is obtained as a single piece by multilayer weaving and comprising at least one hollow portion that is entirely defined by a multilayer woven wall made up of a plurality of layers of yarns interlinked by weaving throughout the thickness of the wall.
- In an embodiment, the fiber structure comprises a hollow portion together with another portion that is adjacent to the hollow portion and interlinked therewith by weaving.
- In an embodiment, the hollow portion is partitioned longitudinally.
- The invention also provides a composite material part presenting at least one hollow portion, in particular a portion that is tubular or substantially tubular, the part comprising a fiber reinforcing structure as defined above or obtained by a method as defined above, the fiber reinforcing structure being densified by a matrix.
- The invention can be better understood on reading the following description made by way of non-limiting indication and with reference to the accompanying drawings, in which:
-
FIG. 1 is a diagrammatic perspective view of a first part made of composite material comprising fiber reinforcement densified by a matrix; -
FIGS. 2 to 4 are very diagrammatic views showing successive steps in making a multilayer woven fiber structure for forming the fiber reinforcement of a part of the kind shown inFIG. 1 , in a first implementation of the invention; -
FIGS. 5A to 5D are successive weft planes in a portion of the fiber structure at the step ofFIG. 2 ; -
FIGS. 6A to 6D are successive weft planes in another portion of the fiber structure at the step ofFIG. 2 ; -
FIG. 7 shows a variant weave; -
FIGS. 8 and 9 are diagrammatic perspective views of a multilayer woven fiber structure and of a corresponding part made of composite material in a variant of the first implementation; -
FIGS. 10 and 11 are diagrammatic perspective views of a multilayer woven fiber structure and of a corresponding composite material part in another variant of the first implementation; -
FIG. 12 is a diagrammatic perspective view of a second part made of composite material comprising fiber reinforcement densified by a matrix; -
FIG. 13 is a highly diagrammatic view showing a step in making a multilayer woven fiber structure for forming the fiber reinforcement of a part of the kind shown inFIG. 12 , in a second implementation; -
FIGS. 14, 15, and 16 show weft planes in different portions of the fiber structure at the step ofFIG. 13 ; -
FIG. 17 is a highly diagrammatic view of a step in making a multilayer woven fiber structure in a variant of the second implementation; -
FIG. 18 is a diagrammatic perspective view of a third part made of composite material comprising fiber reinforcement densified by a matrix; -
FIGS. 19, 20, and 21 are highly diagrammatic views of successive steps in making a multilayer woven fiber structure for forming the fiber reinforcement of a part of the kind shown inFIG. 18 in a third implementation; -
FIGS. 22 and 23 show weft planes in two different portions of the fiber structure at the step ofFIG. 19 ; -
FIG. 24 is a diagrammatic perspective view of a fourth part made of composite material comprising fiber reinforcement densified by a matrix; -
FIGS. 25, 26, and 27 are highly diagrammatic views of successive steps in making a multilayer woven fiber structure to form the fiber reinforcement of a part of the kind shown inFIG. 24 , in a fourth implementation; -
FIGS. 28A to 28D show successive weft planes in the fiber structure at the step ofFIG. 25 ; and -
FIG. 29 is a diagrammatic perspective view of a fifth part made of composite material comprising fiber reinforcement densified by a matrix. - It should be observed that in
FIGS. 2, 13, 19, and 25 the non-woven portions of the fiber structure are not shown. -
FIG. 1 shows apart 10 made of composite material having fiber reinforcement densified by a matrix. Thepart 10 comprises a tubularhollow portion 11 forming a ring secured to aplate 12, thetubular portion 11 being connected to theplate 12 over a portion of its periphery and over its entire length. By way of example, thepart 10 may be used as a support or fastener part for an element inserted in thetubular portion 11, it being possible for theplate 12 to be fastened to a wall, e.g. by screws. - There follows a description of an embodiment of a fiber structure woven as a single piece by multilayer weaving so as to form, after shaping, a fiber preform suitable for constituting the fiber reinforcement of the
part 10, the description being made with reference toFIGS. 2, 3, 4, 5A to 5D, and 6A to 6D . -
FIG. 2 shows thefiber structure 100 at the weaving stage, prior to shaping. Thefiber structure 100 comprises a firstwoven portion 110 that is to form the portion of the fiber reinforcement that corresponds to thetubular portion 11 once it has been shaped by being looped onto itself, and a secondwoven portion 120 that is to form the portion of the fiber reinforcement that corresponds to theplate 12.FIGS. 5A to 5D show by way of example four successive weft planes in theportion 110, whileFIGS. 6A to 6D show by way of example four successive weft planes in theportion 120. - The weaving is performed with a
first set 112 of warp yarn layers C1, C2, C3 for theportion 110 and asecond set 122 of warp yarn layers C4, C5, C6 for thesecond portion 120. In theportion 110, the warp yarn layers extend in the weft direction (arrow T) over a distance corresponding substantially to the developed length of a circumference of thetubular portion 11. In theportion 120, the warp yarn layers extend in the weft direction over a distance corresponding substantially to the width of theplate 12. The set of layers ofwarp yarns - Two respective
first edges portions second edge 122 b of theportion 110 is situated beyond the oppositesecond edge 122 b of theportion 120. - For reasons of clarity,
FIG. 2 shows only the envelopes of thewoven portions first set 112 of layers of warp yarns are not shown, the wovenportion 110 extending in the warp direction over a distance that is substantially equal to the longitudinal dimension of thetubular portion 11, which distance is less than the length of theplate 12 in the example shown. - As shown in
FIGS. 5A to 5D , weaving is performed in theportion 110 with an interlock type weave, the layers of warp yarns being interlinked in each weft plane by weft yarns T1, T2 in a common column of weft yarns. The weft yarns T1, T2 are inserted with excess length so as to present end portions that extend beyond the weaving zone, i.e. beyond theedge 112 b. These end portions are of sufficient length to be capable of being returned to beside theedge 122 a and of being reinserted into layers of warp yarns in order to be woven with warp yarns. Thus, the weft yarn T1, after interlinking the warp yarns of the layers C1 and C2 is reused to interlink the warp yarns of the layer C4 in theset 122 with the warp yarns of the layer C3 of theset 112, thereby connecting together theportions FIG. 2 , the return of the end portions of the weft yarns initially woven with excess length is shown only for two yarns T1 and T2 in a single weft plane. - As shown in
FIGS. 6A to 6D , the weaving in theportion 120 is performed with the same interlock weave, for example, the layers of warp yarns being interlinked in each weft plane by weft yarns T3, T4. Each yarn T3 interlinks warp yarns of the layers C4 and C5, whereas each yarn T4 interlinks warp yarns of the layers C5 and C6. - In
FIGS. 5A to 5D , there can be seen the weft yarn T4 interlinking warp yarns of the layers C5 and C6. - The planes of
FIGS. 5A to 5D can be deduced from one another by moving in translation in the weft direction through a distance corresponding to one pitch step between the columns of warp yarns. The same applies to the planes shown inFIGS. 6A to 6D . - Naturally, the number of layers of warp yarns in the
sets - Furthermore, different interlock weave patterns may be adopted for the
portions - It should also be observed that only some of the weft yarns interlinking warp yarns in the
portion 110 need be woven with extra length in order to be reinserted into the warp, while other weft yarns may be woven conventionally over no more than the width of theportion 110 so that they are not reinserted into theportion 120. It is also possible to vary the number of warp yarns per column of warp yarns in theportion 110 in order to increase thickness locally. - After weaving, with the non-woven portions of the yarns being removed, the
woven structure 100 is shaped as shown inFIG. 3 by looping theportion 110 onto itself while exerting traction on the ends of the reinserted weft yarns T1, T2. Theportion 110 may be shaped by rolling it up on a core. This obtains a hollow portion that is completely defined by a multilayer woven wall comprising a plurality of layers of yarns interlinked by weaving throughout the thickness of the wall. - In the tubular portion formed by looping the
portion 110, theedge 112 a forms astep 115. This may be eliminated by removing a few warp yarns and by cutting off the portions of weft yarns that are then left non-woven so that the inside face of the tubular portion formed by looping theportion 110 runs smoothly to a level corresponding to the top face of the portion 120 (FIG. 4 ). In a variant, instead of removing the warp yarns after weaving, it would be possible to form the set of layers of warp yarns for theportion 110 with a number of layers that increases progressively from theedge 112 a and over a distance in the weft direction that corresponds to the width of theset 120. This technique for varying thickness may be applied at any location in theportions -
FIG. 7 shows, by way of example, a weft plane in which theportion 110 of the fiber structure has a multi-satin type weave different from the interlock weave ofFIGS. 5A-5D and 6A-6D . - In the above-described implementation, the weft yarns initially woven with extra length are reinserted into the warp in the same weft plane as they were initially inserted. In a variant, this reinsertion of weft yarns initially woven with extra length could be performed in a different following weft plane, one that is not necessarily immediately adjacent to the weft plane corresponding to their initial insertion.
- During weaving, the end portions of the weft yarns woven with extra length may be returned, e.g. manually, to the weft yarn feed side in order subsequently to be reinserted and woven like the other weft yarns. The weaving is performed by means of a loom of the Jacquard type that is adapted to multilayer weaving, where such a loom is itself well known.
- Depending on the intended application, the part in which the multilayer woven structure forms the fiber reinforcement may be made of a composite material of the fiber and organic polymer type or it may be made of thermostructural composite material.
- With the first type of material, the fibers of the woven structure may in particular be fibers of carbon, of glass, of aramid, or of ceramic, while the matrix may be an organic resin, e.g. an epoxy, bismaleimide or polyimide polymer. A matrix-precursor resin may be impregnated immediately after weaving (at the step of
FIG. 2 ) prior to shaping the woven structure, with the pre-impregnated woven structure then being shaped by rolling theportion 110 around a core and being held in the desired shape by means of mold-forming tooling while the resin is polymerized. In a variant, the dry woven structure may be shaped by rolling theportion 110 around a core and it may then be held in the desired shape by means of mold-forming tooling into which the resin is injected by a method of the resin transfer molding (RTM) type. Both of those processes are well known. - With a composite material of the thermostructural type, the fibers of the woven structure may be made of carbon or of ceramic, while the matrix may be made of carbon or ceramic. For parts that are to be used in hot portions of an aviation turbine engine, it is preferable to select a ceramic matrix composite (CMC) material. It is well known how to make parts of complex shape out of thermostructural material. A first step of consolidation by a first matrix phase may be performed using a resin that is a precursor of the consolidating matrix of carbon or of ceramic. Impregnation may be performed immediately after weaving (at the step of
FIG. 2 ), and prior to shaping, or it may be performed after shaping, the woven structure then being held in shape in tooling. After the resin has been polymerized and pyrolyzed, a consolidated woven structure is obtained that conserves its shape without requiring supporting tooling. Densification can then be continued using a liquid technique (impregnation with a carbon or ceramic precursor resin, polymerization, and pyrolysis), or by a chemical vapor infiltration (CVI) technique. It is also possible for a fiber/matrix interphase coating to be formed beforehand. Reference may be in particular to documents US 2010/015428 and WO 2010/061139. - It is also possible to make a part from a woven structure made of metal or metal alloy tows and/or wires, e.g. made of titanium or titanium alloy, or to use composite yarns comprising a central core that is ceramic, e.g. made of fibers based on silicon carbide SiC, and coated in metal or metal alloy, e.g. in titanium or titanium alloy, or in boron.
- In a woven structure made of metal tows and/or wires or made of yarns coated in a metallic material, the making of the part may include an initial hot isostatic pressing (HIP) step or an initial step of isothermal forging under vacuum. Applying heat associated with pressure eliminates the empty spaces within the woven structure by plastic deformation and creep of the metal of the wires or of the coating of the yarns. The part is finally formed by diffusion welding under vacuum, where such a process combining HIP or isothermal vacuum forging with diffusion welding under a vacuum applied to a woven texture made of metal wires or of metal-coated yarns is itself known.
- In the above-described implementation, a multilayer woven structure is made in order to fabricate a part that presents a plate secured to a hollow tubular portion extending over a fraction only of the length of the plate.
-
FIG. 8 shows a multilayer woven fiber structure at a weaving stage that differs from that ofFIG. 2 in that it has a wovenportion 110 a in addition to theportion 110 and similar thereto, thewoven portions portion 120. After theportions kind 10 a shown inFIG. 9 that presents aplate 12 secured to two tubularhollow portions -
FIG. 10 shows a multilayer woven fiber structure at the weaving stage that differs from that ofFIG. 2 in that theportions portion 110 has been looped onto itself, a fiber preform is obtained (FIG. 11 ) that presents an essentially tubular hollow shape that is entirely defined by a multilayer woven wall having a plurality of layers of yarns interlinked by weaving throughout the thickness of the wall. Such a preform may for example be used to form a hollow arm of an intermediate casing in an aviation turbine engine. -
FIG. 12 shows anotherpart 20 comprising a hollow tubular portion forming aring 21 secured to aplate 22 and suitable for being used for the same purposes as thepart 10 ofFIG. 1 , for example. It should be observed that the end faces of thetubular portion 12 are not perpendicular to the longitudinal direction of theportion 22. - An embodiment of a fiber texture woven as a single piece by multilayer weaving and, after shaping, forming a fiber preform for the
part 20 is described below with reference toFIGS. 13 to 16 . -
FIG. 13 shows thefiber structure 200 at the weaving stage, prior to shaping. Thefiber structure 200 comprises two wovenportions portion 220 is to form the portion of the fiber preform that corresponds to theplate 22 and it presents oppositelongitudinal edges portion 210 extends in the weft direction (arrow T) fromedge 222 a to anopposite edge 212 b over a distance that makes it possible, after being looped, to co-operate with a segment of theportion 220 to form the portion of the fiber preform that corresponds to theannular portion 21. In the warp direction, theportion 210 extends over a distance that is shorter in comparison with theportion 220.FIG. 13 shows only the envelopes of thewoven portions -
FIG. 14 shows a weft plane in theportion 220, in front of the location of theportion 210. Weaving is performed with aset 212 of layers of warp yarns C1 to C4 that are interlinked by weft yarns T1, T2, and T3 in a given column of weft yarns, the weave being of the interlock type, for example. -
FIG. 15 shows a weft plane in theportion 210. Over the total distance in the weft direction of the touchingportions FIG. 14 . The yarns T4, T5, and T6 are woven with extra length so as to present end portions that extend beyond the weaving zone. These end portions are of sufficient length to be capable of being returned to beside theedge 222 a and of being reinserted into the warp in order to be woven with warp yarns. - The free end portions of the weft yarns woven with extra length are reinserted into the layers of warp yarns C1 to C4 of the
set 212 at respective locations that are offset rearwards in the warp direction. As shown inFIG. 13 , the end portions of the weft yarns of the first weft plane of the wovenportion 210 are reinserted into the layers of warp yarns, e.g. to form a first weft plane of theportion 220 following the last weft plane in theportion 210. The procedure is repeated in similar manner for the weft yarns (not shown inFIG. 13 ) of all of the other weft planes of theportion 210.FIG. 16 shows such a weft plane in theportion 210 with warp yarns interwoven with the end portions of the weft yarns T4, T5, and T6 ofFIG. 15 . In this example, the offset in the warp direction of the end portions of the weft yarns that are reinserted is implemented over a distance that corresponds to the dimension of theportion 210 in the warp direction. As a function in particular of the ability of theportion 210 to deform while it is being looped over, this offset may be made over some other distance, e.g. a shorter distance. In the latter case, the first weft yarns woven with extra length in theportion 210 are reinserted into this same portion, and the extra lengths are determined accordingly. - Naturally, the number of layers of warp yarns in the
portions - After weaving, the non-woven portions of the yarns are removed and the
woven structure 200 is shaped by looping theportion 210 so as to bring itsedge 212 b against theedge 222 a of theportion 220 while applying traction on the ends of the reinserted weft yarns. This produces a fiber preform having a shape close to that of thepart 20 and having a hollow portion that is defined entirely by a multilayer woven wall comprising a plurality of layers of yarns that are interlinked by weaving throughout the thickness of the wall. The shaping of thefiber structure 200 by means of tooling in order to obtain a fiber preform for thepart 20, and the treatment of the fiber preform in order to obtain the desired part may be performed in the same manner as that described above for the first implementation. - In the implementation of
FIG. 13 , the end portions of the weft yarns that are woven with extra length in theportion 210 are reinserted into the layers of warp yarns at locations that are offset rearwards in the warp direction. - In a variant, this reinsertion may be performed at locations that are offset forwards in the warp direction.
- Still in a variant, and as shown in
FIG. 17 , theportion 210 may be made up of two superposedwoven subportions portion 210 a and woven with extra length have their ends reinserted into layers of warp yarns at locations that are offset rearwards in the warp direction. The weft yarns T7, T8, and T9 initially situated in the same plane as the yarns T4, T5, and T6, interlinking layers of warp yarns in theportion 210 b and woven with extra length, have their ends reinserted into layers of warp yarns at locations that are offset forwards in the warp direction. After weaving, the subportions 210 a and 210 b are bent over so as to form two loops diverging from each other in the warp direction from a common origin along theedge 222 b of theportion 220. -
FIG. 18 shows yet anotherpart 30 having two tubularhollow portions 31 forming two rings secured to apanel 32 in the vicinity of an edge thereof, the tubular portions being spaced part from each other and having substantially a same axis. Thepart 30 may be used for example as a door or a cap that pivots about a pin engaged in thetubular portions 31. - An embodiment of a fiber structure woven as a single piece by multilayer weaving and that serves, after shaping, to form a fiber preform for the
part 30 is described below with reference toFIGS. 19, 20, 21, 22 , and 23. -
FIG. 19 shows thefiber structure 300 at the weaving stage, before shaping. Thefiber structure 300 has two firstwoven portions 310 that, after shaping by being looped back onto themselves, are to form the portions of the fiber reinforcement that correspond to thetubular portions 31, and a secondwoven portion 320 that is to form the portion of the fiber reinforcement that corresponds to thepanel 32. InFIG. 19 , only the envelopes of the woven portions are shown for greater clarity. Theportion 320 presents two oppositelongitudinal edges portion 310 is superposed on theportion 320 and presentslongitudinal edges edges 312 a substantially coincide with theedge 322 a, while theedges 312 b are set back from theedge 322 b, theportions 310 extending in the weft direction (arrow T) over a distance that corresponds to the developed length of a circumference of atubular portion 31, this distance in the example shown being less than the size of theportion 320. It should also be observed that eachportion 310 is connected to theportion 320 over only a fraction d of its size in the weft direction from theedges non-interlinked zone 313 is arranged between eachportion 310 and theportion 320. -
FIG. 22 shows a weft plane in the wovenstructure 300 where aportion 310 is superposed on theportion 320. The weaving is performed with afirst set 312 of layers of warp yarns C1 to C3 for theportion 310 and asecond set 322 of layers of warp yarns C4 to C6 for theportion 320. A weft yarn T1 interlinks the warp yarns of the layers C1 and C2, while a weft yarn T2 interlinks the warp yarns of the layers C2 and C3. A weft yarn T3 interlinks warp yarns of the layers C3 and C4 over the distance d only so as to leave thenon-interlinked zone 313. - The weft yarns T1 and T2 are inserted with extra length so as to present end portions that extend beyond the weaving zone, i.e. beyond the
edge 312 b. These end portions are of a length that is sufficient to enable them to be returned to side of theedge 322 a and to be reinserted in the warp in order to be woven with warp yarns. Thus, the weft yarn T1, after interlinking warp yarns of the layers C1 and C2 is reused to interlink warp yarns of the layers C4 and C5 of thesecond set 322 of layers of warp yarns. Similarly, after interlinking warp yarns of the layers C2 and C3, the weft yarn T2 is reused for interlinking warp yarns of the layers C5 and C6 of thesecond set 322 of layers of warp yarns. Only one weft plane is shown, the others being deduced therefrom by offsetting through one pitch step between columns of warp yarns. InFIG. 19 , the return of only two weft yarns T1 and T2 is shown. -
FIG. 23 shows a weft plane in theportion 320 of the woven structure outside its superposition with theportion 310. A weft yarn T4 interlinks warp yarns of the layers C4 and C5, while a weft yarn T5 interlinks warp yarns of the layers C5 and C6 in the same manner as the reinserted portions of the yarns T1 and T2 inFIG. 22 . A single weft plane is shown, the others being deduced therefrom by offsetting to one pitch step between columns of warp yarns. - In the example shown in
FIGS. 22 and 23 , the weaving is performed with an interlock weave. Other weaves could naturally be used. The weaves may differ between firstly theportions 310 and secondly theportions 320, and they may also differ between theportions 310. In addition, the number of layers of warp yarns in theportions portion 310, it should also be observed that only some of the weft yarns need be woven initially with extra length. - After weaving, the non-woven portions of the yarns are removed and the woven structure can be shaped as shown in
FIG. 20 by looping theportions 310 onto themselves while exerting traction on the ends of the reinserted weft yarns T1 and T2. This produces hollow portions, each of which is completely defined by a multilayer woven wall having a plurality of layers of yarns interlinked by weaving throughout the thickness of the wall. In the tubular portions formed by looping back theportion 310, theedges 312 a form steps 315. These may be eliminated or avoided in the same manner as that described above with reference toFIGS. 3 and 4 so as to end up with a fiber preform of the kind shown inFIG. 21 . - The shaping of the
fiber structure 300 by means of tooling in order to obtain a fiber preform for thepart 30 and the treatment of that preform in order to obtain the desired part may be performed in the manner descried above for the first implementation. -
FIG. 24 also shows anotherpart 40 having ahollow portion 41 of substantially tubular shape with apartition 42 subdividing the inside volume of thehollow portion 41 over its entire length. Such a partitioned hollow part may be used for example as an intermediate casing arm in an aviation turbine engine that presents two separate ducts for passing different functions, e.g. a radial shaft transmitting mechanical power to an accessory gearbox (AGB) on one side of thepartition 42, and an electrical connection on the other side, or indeed tubes for conveying fluid. Thepartition 42 may also serve merely to stiffen thepart 40. - There follows a description of an embodiment of a fiber structure woven as a single piece by multilayer weaving that, after shaping, forms a fiber preform for the
part 40, the description being given with reference toFIGS. 25, 26, 27, and 28A to 28D . -
FIG. 25 shows thefiber structure 400 at the weaving stage, prior to shaping. Thefiber structure 400 comprises a firstwoven portion 410 that, after being shaped by being looped back onto itself, is to form a major fraction of the portion of the fiber reinforcement that corresponds to thetubular portion 41, a secondwoven portion 420 that, after shaping by being looped back onto itself, is to form the portion of the fiber reinforcement that corresponds to thepartition 42, and a thirdwoven portion 430. - By way of example,
FIGS. 28A to 28D show four successive weft planes in the wovenstructure 400. - Weaving is performed with a
first set 412 of layers of warp yarns C5, C6, C7 for theportion 410, asecond set 422 of layers of warp yarns C8, C9, C10 for theportion 420, and athird set 432 of warp yarns C1, C2, C3, C4 for theportion 430. In theportion 410, the layers of warp yarns extend in a weft direction (arrow T) over a width corresponding substantially to the developed length of a circumference of thetubular portion 11. In theportion 420, the layers of warp yarns extend in the weft direction over a width that is less than the width of theportion 410 but that is sufficient, after looping, to form the portion of the fiber reinforcement that corresponds to thepartition 42. In theportion 430, the layers of warp yarns extend in the weft direction over an even smaller width. The sets of layers ofwarp yarns longitudinal edges woven portions portion 410 is connected to the wovenportion 430 over its entire width, while the wovenportion 420 is connected to the wovenportion 420 over a fraction only of its width starting from theedge 422 a, thereby leaving anon-interlinked zone 413 between theportions portions portion 430. InFIG. 25 , and for reasons of clarity, only the envelopes of thewoven portions - As shown in
FIGS. 28A to 28D , in a given weft column, weft yarns T1, T2 interlink warp yarns of the layers of warp yarns C5, C6, C7, while a weft yarn T3 interlinks warp yarns of the layers of warp yarns C7 and C8, and weft yarns T4, T5 interlink warp yarns of the layers of warp yarns C8, C9, and C10. - The weft yarns T1 and T2 are inserted with extra lengths so as to present end portions that extend beyond the weaving zone, i.e. beyond the
longitudinal edge 412 b of the wovenportion 410 remote from theedge 412 a. These end portions are of a length that is sufficient to enable them to be brought back to beside theedge 432 a and to be reinserted into the layers of warp yarns in theportion 430. Thus, the weft yarn T1, after interlinking warp yarns of the layers C5 and C6 is reused to interlink warp yarns of the layers C1 and C2, while the weft yarn T2, after interlinking warp yarns of the layers C6 and C7 is reused to interlink warp yarns of the layers C2 and C3. - The weft yarn T3 interlinks warp yarns of the layers C7 and C8 over a limited distance from the
edges non-interlinked zone 413 between thewoven portions - The weft yarns T4 and T5 are inserted with extra length so as to present end portions that extend beyond the weaving zone, i.e. beyond the
longitudinal edge 422 b of the wovenportion 420 remote from theedge 422 a. These end portions are of a length that is sufficient to enable them to be brought back to beside theedge 432 a and to be reinserted into layers of warp yarns in theportion 430. Thus, the warp yarn T4, after interlinking warp yarns of the layers C8 and C9 is reused to interlink warp yarns of the layer C3 and C4, while the weft yarn T5, after interlinking warp yarns of the layers C9 and C10 is reused to interlink warp yarns of the layers C4 and C5. - The return of the end portions of the weft yarns initially woven with extra lengths is shown in
FIG. 25 only for the weft warps T1, T2, T4, and T5 in a single weft plane. - The weft planes of
FIGS. 28A to 28D can be deduced from one another by offsetting through one pitch step between columns of warp yarns. - These figures show an interlock type weave. Other types of weave could naturally be used. The weaves of the
portions portion portions portions - After weaving, the non-woven portions of the yarns are removed, and the
woven structure 400 is shaped as shown inFIG. 26 (end view) by looping back onto themselves thewoven portions portions - In the tubular portions formed by looping back the
portions edges FIGS. 3 and 4 ) in order to obtain the shape shown inFIG. 27 (end view). - Shaping by means of tooling in order to obtain a fiber preform for the
part 40, and processing of the preform in order to obtain the desired part may be performed as described above for the first implementation. - In the implementation of
FIGS. 24-27 and 28A-28D , the weft yarns woven with extra length in theportions portion 430 in the same weft plane. In a variant, the end portions of the weft yarns of a given weft plane woven with extra length in theportion 410 may be reinserted in a following weft plane in order to be woven with warp yarns of thesame portion 410. In similar manner, the end portions of the weft yarns of a given weft plane woven with extra length in theportion 420 may be reinserted into a following weft plane in order to be woven with warp yarns of thesame portion 420. - Naturally, in applying a weaving principle similar to that described above, it is possible to make a multiply-partitioned hollow part, i.e. a part having a plurality of longitudinal partitions subdividing its inside volume.
- In addition, in the part, the partition or at least one of the partitions when there are two or more partitions, may extend over a length that is less than the length of the hollow portion, the portion of the fiber structure corresponding to the or each partition of reduced length, such as the
portion 420 inFIG. 25 , then being woven over a shorter distance in the warp direction compared with the other portions of the fiber structure. -
FIG. 29 shows yet anotherpart 50 that can be obtained from a structure woven as a single piece by multilayer weaving in accordance with the invention. Thepart 50 comprises a tubularhollow portion 51 secured to anotherportion 52 that is curved about an axis other than the axis of theportion 51, e.g. that is perpendicular thereto. By way of example, such a part may be used as a bellcrank. To obtain thepart 50, it is possible to use a woven structure such as thestructure 100 ofFIG. 2 , the portion of the fiber preform corresponding to thehollow portion 51 being obtained by looping back onto itself theportion 110 of thefiber structure 100, and the portion of the fiber preform corresponding to theportion 52 being obtained by curving theportion 120 of thefiber structure 100.
Claims (5)
1. (canceled)
2. A method of making a structure woven as a single piece by multilayer weaving and including at least one hollow portion that is longitudinally partitioned, the method comprising:
weaving warp yarns of a first set of layers of warp yarns with weft yarns including at least some that are inserted in layers of warp yarns of the first set of layers of warp yarns while being taken over a distance that is greater than a length of the first set of layers of warp yarns measured in a weft direction to have weft yarn end portions available that extend beyond a zone of weaving;
weaving warp yarns of a second set of layers of warp yarns with weft yarns including at least some that are inserted in layers of warp yarns of the second set of layers of warp yarns while being taken over a distance that is greater than a length of the second set of layers of warp yarns measured in the weft direction to have weft yarn end portions available that extend beyond the zone of weaving, the first and second sets of layers of warp yarns being arranged one above another and being interlinked over a fraction only of their width in the weft direction;
returning the weft yarn end portions so as to weave them with warp yarns by reinserting them in layers of warp yarns; and
forming the partitioned hollow portion by looping the first and second sets of layers of warp yarns back onto themselves and applying traction to the ends of the reinserted weft yarns.
3. A method according to claim 2 , wherein the free end portions of the weft yams are reinserted in layers of warp yarns of a third set of layers of warp yarns, the first, second, and third sets of warp yarns being superposed, and the first and second sets of layers of warp yarns being interlinked with the third set of layers of warp yarns over a fraction only of their width.
4. A method according to claim 2 , wherein the end portions of the weft yarns are reinserted in layers of warp yams of the first and second sets of layers of warp yams at locations that are offset in the warp direction relative to locations of their initial insertion.
5. A method according to claim 2 , wherein the hollow portion is formed over a fraction only of the length of the woven structure in the warp direction.