US20140287909A1 - Method of forming nano-pads of catalytic metal for growth of single-walled carbon nanotubes - Google Patents
Method of forming nano-pads of catalytic metal for growth of single-walled carbon nanotubes Download PDFInfo
- Publication number
- US20140287909A1 US20140287909A1 US14/297,840 US201414297840A US2014287909A1 US 20140287909 A1 US20140287909 A1 US 20140287909A1 US 201414297840 A US201414297840 A US 201414297840A US 2014287909 A1 US2014287909 A1 US 2014287909A1
- Authority
- US
- United States
- Prior art keywords
- nano
- catalytic metal
- pad
- photo
- resist
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Two methods of producing nano-pads of catalytic metal for growth of single walled carbon nanotubes (SWCNT) are disclosed. Both methods utilize a shadow mask technique, wherein the nano-pads are deposited from the catalytic metal source positioned under the angle toward the vertical walls of the opening, so that these walls serve as a shadow mask. In the first case, the vertical walls of the photo-resist around the opening are used as a shadow mask, while in the second case the opening is made in a thin layer of the dielectric layer serving as a shadow mask. Both methods produce the nano-pad areas sufficiently small for the growth of the SWCNT from the catalytic metal balls created after high temperature melting of the nano-pads.
Description
- This application is a continuation of U.S. patent application Ser. No. 13/401,220, filed Feb. 21, 2012, which is a continuation-in-part of U.S. patent application Ser. No. 12/986,429, filed Jan. 7, 2011, which is a continuation-in-part of U.S. patent application Ser. No. 12/011,044, filed Jan. 24, 2008, the contents of each of which is incorporated by reference herein for all purposes.
- The invention relates to a method of producing ultra-small pads of catalytic material for the growth of single walled semiconductor-type carbon nanotubes.
- The Carbon Nanotubes (CNT) are viewed to be a new key element for future electronics and photonics. In the CNT, such unique properties as quantization of the electron spectrum, ballistic electron propagation along the tube, current densities as high as 109 A/cm2, existence of the semiconductor phase, possibilities for n- and p-doping with a high carrier mobilities, as well as excellent thermal conductance, make the nanotubes a great candidate for future novel high-speed, high efficiency electronic and photonic devices.
- It is extremely important that all these outstanding properties are related to the semiconductor single walled carbon nanotubes (SWCNT), which are expected to be the building blocks for multiple semiconductor devices and circuits, with the properties far superior than those in the traditional semiconductor counterparts.
- The proof-of-concept design, wherein a single nanotube is placed on the substrate between the contacts, is utilized in essentially all publication on this topic, for both CMOS circuit (see e.g. V. Derycke et al. Nano Letters 1, p. 453, 2001) and individual transistors (see also E. Ungersboeck, et al., IEEE Transactions on nanotechnology, V4, p. 533, 2005). The drawback of this method is its impracticality for any scale of circuit integration: placement of multiple identical nanotubes to enhance the output current or to form new circuit elements requires a special micro-manipulator and thus precludes any possibility of IC mass manufacturing. The future success of CNT devices will rely on emergence of a cost efficient manufacturing process that will ensure a high-yield and cost efficiency above the modern FET and CMOS technologies.
- The present invention is related to this technology. It is based on the growth of a lithographically controlled nanotube array on a metal electrode normally to the electrode plane, followed by sequential deposition of dielectric and metal layers to produce a solid platform for attachment of a second contact to the nanotube tips, thereby forming source and drain electrodes. The transistor gate electrode is made as a third conductive layer sandwiched between the dielectric layers and placed somewhere in the middle of the nanotube length.
- Such a technology was described in the U.S. Pat. No. 7,851,784 filed by A. Kastalsky, where several nanotube array devices and methods for their fabrication have been disclosed. Shown in
FIG. 1 as a Prior Art, is the drawing from this patent wherein the CNT FET consists of thenanotube 57 grown normally to the substrate, and thegate electrode 51 is attached to the sidewall of everynanotube 57 in the array through a layer ofinsulator 54. The key element is themetal layer 51 in the middle of the nanotube length, sandwiched between two insulator layers 52 and 53. During deposition of the first insulator layer 52, a thin layer of insulation material will also be deposited on the nanotube walls, thereby forming agate insulator layer 54 around each nanotube. It is then followed by deposition of thegate metal layer 51 and the insulator layer 53. After polishing of the insulator layer 53 and exposure of the nanotube tips, the top metal layer 55 (the drain electrode) is deposited to complete the structure. Such a design of the CNT transistor, with the nanotube buried within sequentially deposited insulating and metal layers, allows realization of the planar technology for commercial manufacturing of the CNT-based devices and integration circuits. - The above described device technology requires vertical growth of the semiconductor type SWCNT. Typically, they are 1-3 nm in diameter, and are CVD grown from tiny spheres of the catalytic metals, such as Ni, Fe, Cd, formed after melting the nano-pads deposited on the original contact electrode. The nano-pads are designed to be a few nm in diameter to produce a SWCNT. This is a rather challenging job since the current best resolution e-beam lithography can produce pads of only about 20 nm in diameter. For the smallest reliable thickness of the catalytic layer of 0.5 nm, this results in a sphere diameter of about 6-7 nm, which is too large for making SWCNT. There is therefore a necessity to reduce the metal pad diameter below the modern e-beam capabilities. One of such possibilities was disclosed in the US Patent Application No. 2011/0186,808 where a 20 nm opening made by e-beam lithography was designed to be further reduced down to a few nm in diameter using the photo-resist melting procedure. At temperatures elevated above 90° C., the photo-resist is known to soften and behave like a viscous fluid moving toward the opening center thereby shrinking the aperture. After deposition of an about 0.5 nm-thick catalytic metal layer and then metal lift-off, the metal pads with the diameter defined by the reduced aperture will be formed. The resultant effect of shrinking the opening depends on several factors, such as temperature, photoresist thickness and its properties, and duration of the procedure. All these factors must be kept under strict control to obtain the desirable type of the nanotubes with uniform properties over the nanotube array.
- The disclosed according to the present invention technique also relates to forming nano-pads of the catalytic metal. Unlike the above discussed method, relying on the photo-resist softening, the present invention is based on a “shadow mask” for the catalytic metal deposition, when the metal evaporation source is positioned under the angle relative to the plane of the openings, while the photo-resist height around the aperture serves as a shadow mask.
- Two different shadow mask processes are disclosed, according to the present invention. In one case, the photo-resist itself, having the thickness close to the opening diameter, is utilized as the shadow mask. In the second case, prior to forming the opening, a 20-30 nm-thin layer of insulator is deposited on the original metal contact. The 20 nm opening in the photo-resist is then made using the e-beam lithography, and the insulator is etched within the aperture to expose the bottom contact metal layer. Then photo-resist is removed and the remaining insulator layer around the hole serves as the shadow mask. In both cases, the original opening is made on the metal contact in the shape of a 20×20 nm2 square, and the resultant shadow mask deposition process creates a small metal square pad in one of the corners of the original opening.
- The disclosure and analysis of these two shadow mask techniques for obtaining nano-pads of catalytic material are the main objects of the present invention.
-
FIG. 1 . The cross-sectional view of the CNT transistor with vertically grown nanotubes (Prior Art). -
FIG. 2 . The processing steps for forming nano-pads with photo-resist as a shadow mask. -
FIG. 3 . The processing steps for forming nano-pads with dielectric layer as a shadow mask. -
FIG. 4 Illustration of the beam broadening at the metal deposition plane for shadow mask process. - Both invented methods rely on formation of a barrier serving as a shadow mask for the angled metal deposition, thereby limiting the area of the metal pad within the e-beam produced original opening. The resultant metal pad area depends on the barrier height and angle of the shadow mask, i.e. the angle between the direction from the opening to the metal source and the substrate plane. The most desirable situation arises when the barrier height is close to the opening side, and the angle of metal evaporation is about 45°. In both cases discussed, the original opening represents a square with the minimal for e-beam lithography side of about 20 nm, while the beam of the metal evaporation is directed along one of the diagonals of the square. The above mentioned opening in the photo-resist is formed on the contact layer preliminary deposited on the substrate.
-
FIG. 2 shows the processing steps when a thin layer of the photo-resist serves as a shadow mask. The processing begins from deposition of thecontact layer 31 on thesubstrate 30,FIG. 2 a. Then asmall opening 34 in the shape of a square is made within the photo-resist 32,FIG. 2 b, wherein the distance d1 defines the diagonal of the square, while the barrier height is determined by the photo-resist thickness R. It is followed by the angled catalytic metal deposition of the layer 36 from thesource 35, seeFIG. 2 c, shifted to the right from theopening 34 and directed along the diagonal of the square thereby forming the deposition angle .theta. After photo-resist removal,FIG. 2 d, a small nano-pad of thecatalytic layer 37 remains on theoriginal contact layer 31, the length of the diagonal d.sub.2 being controlled by both the barrier height R and the angle of evaporation θ. -
FIG. 2 e shows an enlarged top view of the nano-pad 37 inside the e-beam produced opening 34. The dashed line of the length d1 is the diagonal of the square. It lies in the plane which is normal to the drawing plane and intersects the center of themetal source 35. The final metal nano-pad 37 has a diagonal of the length d2 and the area (d2′)2, while theoriginal opening area 34 is (d1′)2. This implies that the effect of catalytic metal shrinking produced by shadow mask processing is determined by the ratio (d2)2/(d1)2. After the heat treatment and melting thecatalytic metal pad 37 of thickness 1,FIG. 2 c, the metal layer coalesces into aball 38 of the diameter d.sub.3, seeFIG. 2 f. The diameter d3 should be less than 5 nm to grow the SWCNT, see e.g. A.-C. Dupuis, Progress in Material Science, 50 (2005), 929-961. Simple estimates shows that for a realistic thickness of 1=0.5 nm, the length d2′ of the side of the square 37 should be in this case close to or smaller than 3 nm. Shown inFIG. 2 g, is the nanotube 39 vertically grown with the assistance of thecatalytic ball 38. - The above discussed shadow mask method relies on the barrier for catalytic method deposition created by the wall of the photo-resist 32 after forming the
opening 34. The accuracy of this method, i.e. uniformity of the final metal nano-pad areas over the substrate depends on the uniformity of the thickness R of the photo-resistlayer 32, seeFIG. 2 b. For the photo-resist thickness R of ca. 20 nm the issue of uniformity may become critical. It is therefore preferable to replace the photo-resist as the shadow mask layer with the dielectric layer whose thickness can be made more controllable and uniform. -
FIG. 3 shows the processing steps for this case. The processing is almost identical to that of the photo-resist-based shadow mask. The only difference is deposition of a thin dielectric layer 33 prior to the photo-resistcoating 32, seeFIG. 3 b. After forming anopening 34 in both photo-resist and dielectric layers the photo-resist layer is removed,FIG. 3 c, so that the dielectric layer 33 provides the shadow mask barrier. After angled deposition of the catalytic metal layer 36, the shadow mask dielectric layer 33 is selectively etched, together with the lift-off of the metal layer 36, and remaining nano-pad 37, seeFIG. 3 d, is then used for further processing,FIGS. 3 e and 3 f. - The parameters affecting resolution of the invented methods are the diameter of the metal source and its proximity to the opening: if the metal source is too large and/or is located too close to the opening, the metal beam passing the shadow mask barrier will be broadened, thereby reducing the deposition accuracy and limiting the capability of the discussed methods. It is therefore desirable to make the beam cross-section at the deposition plane much smaller than the length of diagonal d.sub.2 of the nano-
pad square 37, seeFIG. 2 e. -
FIG. 4 shows a 3-dimensional box of the shadow mask and the metal source. The cube 42 with the side length d1′ illustrates theopening 34 surrounded by four vertical walls of height R and the nano-pad 37 with the square side d2′. The metal source of diameter D is positioned at the distance L from the right top apex of the cube where the beam enters the cube. The length t along the intersection of the beam with theplane 37 defines the beam broadening, while the length r is the distance which the beam passes inside the cube. Simple estimates show that the length t can be expressed as τ≈r·D/L. For the distance L=60 cm, the beam diameter D=1 cm and the distance inside the cube r=30 nm, one obtains t.about.0.5 nm. To further reduce the distance t, one can narrow the beam width using theslit 40 with theslit opening 41. For instance, the reduction of the beam width to 1 mm yields the distance τ≈0.05 nm, which is sufficiently small to be neglected.
Claims (8)
1. A method of producing the nano-pads of catalytic metal for growth of the Single Walled Carbon Nanotubes (SWCNT) using a shadow mask technique, in which the original opening in the photo-resist deposited on the substrate is used to create the nano-pad of catalytic metal of a much smaller area than that of said original opening, wherein the walls of said original opening in the photo-resist serve as a shadow mask for the angled deposition of said nano-pads of catalytic metal, when the catalytic metal source is positioned under an angle to the direction normal to the substrate plane, so that said angle and the said walls of said original opening control the area of the nano-pads.
2. The method of claim 1 , wherein said original opening in the photo-resist has a shape of the square, which is oriented toward said catalytic metal source in such a manner that the plane normal to the substrate plane goes through said catalytic metal source and intersects the substrate plane along one of the diagonals of said original square, so that the resultant nano-pad also has the shape of the square located in one of the corners of said original opening, farthest to said catalytic metal source.
3. The method of claim 1 , which includes the following processing steps: deposition of the contact pad on the substrate; deposition of a thin layer of the photo-resist and patterning; making the original opening in the photo-resist; angled deposition of said catalytic metal layer to form the nano-pad; removal of the photo-resist, so that only said nano-pad of catalytic metal remains on said contact pad; high-temperature treatment of the nano-pad layer to selectively melt the nano-pad metal and form a spherical ball.
4. The method of claim 2 , wherein the area of said square of the original opening in the photo-resist is about 20×20 nm2, while the walls of said original opening in the photo-resist are about 20 nm high.
5. The method of producing the nano-pads of catalytic metal for growth of the SWCNT using a shadow mask technique, in which the original opening is formed in a thin dielectric layer deposited on the contact layer to create the nano-pad of catalytic metal of a much smaller area than that of said original opening, wherein the walls of said original opening in the said dielectric layer serve as a shadow mask for the angled deposition of said nano-pads of catalytic metal, when the catalytic metal source is positioned under an angle to the direction normal to the substrate plane, so that said angle and the height of the walls of said original opening determine the size of the nano-pads.
6. The method of claim 5 , wherein said original opening in the dielectric has a shape of the square, said square being oriented toward said catalytic metal source in such a manner that the plane normal to the substrate plane goes through said catalytic metal source and intersects the substrate plane along one of the diagonals of said original square, so that resultant said nano-pad also has the shape of the square.
7. The method of claim 5 , which includes the following processing steps: deposition of the contact pad on the substrate; deposition of a thin layer of the dielectric deposition of the photo-resist and patterning; making the original opening in the photo-resist; making the original opening in the dielectric; removal of the photo-resist, angled deposition of said catalytic metal layer to form the nano-pad, removal of the dielectric layer and metal lift-off, so that only said nano-pad of catalytic metal remains on said contact pad; high-temperature treatment of the nano-pad layer to melt the nano-pad metal and form a spherical ball.
8. The method of claim 5 , wherein the area of said original opening in the dielectric is about 20×20 nm2, while the walls of said original opening in the dielectric are about 20 nm high.