US20140120145A1

US20140120145A1 - Formula and Process for Crosslinking Antimicrobials to Textiles

Info

Publication number: US20140120145A1
Application number: US13/661,579
Authority: US
Inventors: Joseph Giovanniello
Original assignee: Individual
Current assignee: SANIT TECHNOLOGIES LLC
Priority date: 2012-10-26
Filing date: 2012-10-26
Publication date: 2014-05-01
Also published as: US20160029620A1; US9924713B2; US20140186517A1; US9168322B2

Abstract

A process is described herein for applying antimicrobials to substrates such as fabrics. An antimicrobial-binder mixture is provided that includes an antimicrobial and a binder that includes guar gum in an aqueous solution, which is applied to the substrate. Once the substrate is cured, spikes formed by the antimicrobial are disposed on the fabric and function to rupture membranes of infectious agents.

Description

BACKGROUND

Healthcare-associated infections “in hospitals are a significant cause or morbidity and mortality in the United States.” R. Monina Klevens, et al., Estimating Health Care-Associated Infections and Deaths in U.S. Hospitals, 2002, Public Health Reports, 160-166 (March-April 2007). According to a study conducted by researchers at the CDC, Emory University School of Medicine, the Atlanta VA Medical Center, and the Atlanta VA Health Services Research and Development Center, during a one year period approximately 1.7 million people were infected by healthcare-associated infections in American hospitals, and slightly less than 100,000 of those infected died as a result. Id. (citing data from a study of the 2002 calendar year). These infections may be spread by, inter alia, hospital bedclothes and doctor clothing, such as scrubs.
One traditional approach to preventing the spread of healthcare-associated infections in hospitals is to treat fabrics used in hospitals with antimicrobial chemicals. Typically, these traditional treatments use silver salt antimicrobials to poison cell walls, DNA, and/or enzymes comprising the infectious agent.
These traditionally treated fabrics, however, suffer from numerous drawbacks. First, due to the process used to treat the substrates, the antimicrobial chemicals are applied in an uneven coating that wears off after a relatively low number of washes, thus greatly diminishing the effectiveness in preventing the spread of infectious agents. Second, because traditionally treated fabrics work by poisoning infectious agents, it is possible for the agents to develop resistance to the treatment. This results in the creation of a more dangerous infectious agent than the one originally targeted for destruction. Third, the silver salt antimicrobials used in traditional treatments require a substantial amount of contact time with an infectious agent to be effective in destroying the same. Fourth, traditional treatments may be easily neutralized by substances such as chlorine (which is commonly found in disinfectants such as bleach). This may result in the treatment losing its effectiveness to prevent infection from dangerous agents. Fifth, the silver salt antimicrobials have a tendency to leach into their surroundings. This may increase environmental risks, as well as health risks for the person coming in contact with the same. Further, traditional treatments are not always effective against the so-called “superbugs,” i.e. resistant infectious agents such as, for example, Methicillin-resistant Staphylococcus aureus (MRSA).
There is a significant need for an improved treatment for fabric and other substrates used in the medical field to prevent the spread of healthcare-associated infections. There is further a need for such treatment to destroy infectious agents without risk of increasing resistance or creating resistant agents. There is also a need for treatment to destroy dangerous resistant infectious agents that would not be destroyed with traditional treatments.

SUMMARY

The present application is directed at a method of applying an antimicrobial to a fabric. An antimicrobial-binder mixture is applied to the fabric. The binder comprises guar gum. The antimicrobial is characterized as an organo silane quaternary amine capable of forming spiked structures.
The present application is further directed at a treated fabric for preventing the spread of infectious agents. Such fabric includes a fabric and an antimicrobial-binder mixture secured to that fabric. The antimicrobial-binder mixture contains a binder comprised of guar gum and an antimicrobial that includes an organo silane quaternary amine having spiked structures.
The present application is also directed to a binder solution. The binder solution is aqueous and comprised guar gum.
The present application is further directed to a method of making a binder. Guar gum with water at a temperature in excess of 145° F. to form a guar gum-water mixture. The guar gum-water mixture is cooled to approximately 135-145° F. Ammonium sulfate and water are added to the guar gum-water mixture to form an ammonium sulfate-guar gum-water mixture. The temperature of this mixture is less than or equal to 145° F. Urea is mixed to the ammonium sulfate-guar gum-water mixture to form a urea-ammonium sulfate-guar gum-water mixture. Water and methyl acryloid are then added to the urea-ammonium sulfate-guar gum-water mixture to form the binder.

DRAWINGS

FIG. 1 depicts a flow chart of one embodiment of a method for applying an antimicrobial to a fabric.

FIG. 2 depicts a flow chart of one embodiment of a method of making a binder.

FIG. 3 depicts a diagram from a Scanning Tunneling Microscope (STM) displaying an antimicrobial-binder composition bound to fabric.

DETAILED DESCRIPTION

Referring now to the drawings, wherein like reference numbers refer to like elements in each of the several views, FIG. 1 shows a flowchart of one embodiment of a method for applying an antimicrobial to fabric with via antimicrobial-binder mixture. FIG. 2 shows a flow chart of one embodiment of a method of making a binder that may be utilized with the methods and fabric described herein.
An aqueous binder solution may contain one or more components that form a binder to bind antimicrobials to substrates. One such aqueous binder solution that may be used with the method is comprised of guar gum. In some embodiments, the aqueous binder solution may further comprise ammonium sulfate, urea, and/or methyl acryloid. In one embodiment of an aqueous binder solution, the solution comprises approximately 1.5% guar gum by weight. In another embodiment of an aqueous binder solution, the aqueous binder solution may comprise 1.5% guar gum and approximately 2.0% ammonium sulfate by weight. In another embodiment of an aqueous binder solution, the solution may comprise approximately 1.5% guar gum, approximately 2.0% ammonium sulfate, approximately 0.9-1.0% urea, and approximately 1.75% methyl acryloid by weight.
A binder may be prepared for use in treating fabrics according to the methods herein. To prepare such a binder approximately 102 pounds (approximately 46.3 kg) is heated to a temperature greater than 145° F. (63° C.). Approximately 3.5 lbs (1.59 kg) of guar gum is mixed with the water (20). Thereafter, the mixture is cooled to between approximately 135-145° F. (57-63° C.) (22). Approximately 37.5 lbs (17 kg) of water is added to the mixture. The water is at a temperature less than or equal to 145° F. Approximately 4.5 lbs (2.04 kg) of ammonium sulfate is mixed therewith (24). After mixing the ammonium sulfate with the mixture, approximately 2 lbs (0.91 kg) of urea is mixed therewith (26). Once the mixing of the urea is complete, 75 lbs (34 kg) of water and 4 lbs (1.81 kg) of methyl acryloid is added to create a binder (28). This binder may then be used in methods to treat fabric substrates.
To treat fabrics, an antimicrobial is mixed with the binder and water (000). The percentages of antimicrobial and binder used in this mixture are predetermined. In some embodiments, the weight percentage of antimicrobial is approximately 2% to 3%, and the weight percentage of the binder is approximately 2% to 3%.
Antimicrobials that may be used include organo silane quarternary amines capable of forming a spiked structure. Typically, these molecules are comprised of a silane group (R), a carbon chain (C_xH_y), and a quarternary amine (NH₃). The molecules are arranged such that the silane group is attached to one end of the carbon chain, while the amine is attached to the other end of the carbon chain, forming a molecular spike (NH₃C_xH_yR). One example of an organo silane quarternary amine that may be used is NH₃C₁₈H₃₆R.
The quarternary amine structure of the molecular functions as the point of the spike. When this structure comes into contact with a cellular membrane, it pierces the same. The puncturing in the membrane brings about destruction of nutrient transport systems and structural integrity, leading to cell death. Of note, the amine point does not operate by poisoning the cells it comes into contact with. Rather, the amine point physically punctures the membranes of such cells.
After the antimicrobial and binder are mixed with water, the temperature of the mixture is adjusted to allow antimicrobial and binder to disperse within the water. In a preferred embodiment, the temperature is adjusted to one that permits even dispersion of the antimicrobial and binder within the water. Although this temperature will vary, in a preferred embodiment, the temperature is between approximately 37° C. (approximately 100° F.) and approximately 44° C. (approximately 110° F.).
A fabric or substrate is chosen to receive the antimicrobial and binder mixture. Fabrics suitable for receiving the antimicrobial and binder mixture include, but are not limited to, cotton, nylon, polyester, and combinations thereof. Fabrics or substrates comprising aluminum may also be utilized in some embodiments.
In some embodiments, the fabric may undergo preparation steps prior to application of the antimicrobial and binder mixture (100). For example, some fabrics could be cleaned prior to the application. Cleaning may be helpful to remove potentially harmful ions, such as silver ions, that may exist on the fabrics. In some embodiments, cleaning occurs by a process called scouring. For dark shade textile fabrics, scouring comprises treating the fabric with chemicals such as soda ash, mild soap, or sequestrian. For light shade textile fabrics, scouring comprises treatment with peroxide. Light shade textile fabrics may also be cleaned in some embodiments by bleaching.
After the antimicrobial-binder mixture and fabric are prepared, the antimicrobial-binder mixture is applied to the fabric (200). Any method of applying a mixture to fabric may be utilized. Examples of such methods include, but are not limited to, dipping applications and spraying applications. In a preferred embodiment, the application method allows for even distribution of the antimicrobial-binder mixture to the fabric. One application that permits even distribution is dipping. In an embodiment using dipping, the fabric is submersed into the antimicrobial-binder mixture. In some embodiments, the submersion lasts for approximately one to two minutes.
After application of the antimicrobial-binder mixture to the fabric, the mixture is cured onto the fabric (300). In some embodiments, curing occurs by treating the fabric to temperatures of approximately 275-350° C., and preferably between 275-300° C. The time of curing depends on the fabric being utilized. By means of example, a fabric comprising cotton often needs longer curing times than a nylon or polyester fabric. One of skill in the art appreciates that the curing process is well known.
Upon completion of the curing process, the fabric is chemically bound to the cured binder and antimicrobial. The antimicrobial and binder are present on the fabric at approximately a 1:1 ratio by weight. The binder binds the fabric to the antimicrobial, such that the antimicrobial is oriented in a spike structure that is exposed on the outer surface of the fabric. The quarternary amine portion of the spike structure is oriented distal to the treated fabric, with the quarternary amine forming the peak of the spike, while the silane group is oriented proximate the fabric, so as to form a silane bond with the same.
Due to those chemical bonds, the antimicrobial remains fixed to the fabric. The antimicrobial does not leach, and remains intact after numerous washings. Table 1 shows exemplar results of tests in which infectious agents were introduced to treated fabrics generated pursuant to the methods described herein. In each test, the treated fabric was washed up to fifty times. After a number of washes, the treated fabric was introduced to either staphylococcus auereus, which causes Staph infections, or klebsiella pneumonia, which causes bacterial pneumonia. In each test, the infectious agent populations were decreased by more than 99% when exposed to the treated fabric for twenty four hours.

TABLE 1*

Agent	Initial	0 Washes	25 Washes	50 Washes

S. auereus	2.30 × 10⁹	<100	290	490
K. pneumonia	3.30 × 10⁸	<100	260	490

*values herein refer to colony forming units per milliliter (CFU/ml)

Unlike traditional treated fabrics, the treated fabrics generated pursuant to the methods described herein retain their ability to kill infectious agents after numerous washings.
Studies were also performed to determine the effectiveness of the novel treated fabrics in preventing infections. For example, Table 2 shows exemplar results of tests of the treated fabrics generated by the methods described herein. A control fabric and a treated fabric were both introduced to clostridium difficile, a species of harmful bacteria that is transmitted in hospitals and nursing homes. The introduced sample to each fabric had an anaerobic plate count of approximately 1,800,000.

TABLE 2*

Fabric	Initial	1 hour	12 hours	24 hours

Control	1,800,000	2,000,000	1,900,000	1,800,000
Treated		230,000	<100	<100

*values herein refer to anaerobic plate counts

As seen in Table 2, after one hour, the population of the harmful clostridium difficile bacteria reduced by over 87% percent on the treated fabric. After twelve hours, the population of the harmful clostridium difficile bacteria decreased by over 99%. The bacteria population on the untreated fabric, however, remained at or above the initial population. As seen from these results, the speed at which these fabrics kill harmful infectious agents is significantly faster than that of traditionally treated fabrics, which require at least twenty four hours of contact before becoming effective at killing such agents. Additional tests demonstrated that the treated fabrics prepared according to the methods disclosed herein are effective against viruses, such as H1N1, and superbugs, such as MRCA.
Although the present methods, compositions, and fabrics have been shown and described in considerable detail with respect to only a few/particular exemplary embodiments thereof, it should be understood by those skilled in the art that it is not intended to limit the methods, compositions, or fabrics to the embodiments since various modifications, omissions, and additions may be made to the disclosed embodiments without materially departing from the novel teachings and advantages described herein, particularly in light of the foregoing teachings.

Claims

What is claimed is:

1. A method of applying an antimicrobial to a fabric comprising

applying an antimicrobial-binder mixture to the fabric, wherein the binder of the antimicrobial-binder mixture comprises guar gum in an aqueous solution and the antimicrobial of the antimicrobial-binder mixture is characterized as an organo silane quaternary amine capable of forming spiked structures.

2. The method of claim 1, wherein the binder further comprises ammonium sulfate.

3. The method of claim 2, wherein the binder further comprises urea and methyl acryloid.

4. The method of claim 1, wherein the antimicrobial-binder mixture comprises at least 2% antimicrobial and at least 2% binder by weight.

5. The method of claim 1, wherein after applying the antimicrobial-binder mixture to the fabric, the antimicrobial forms spiked structures on the fabric that function to rupture membranes of infectious agents.

6. The method of claim 1, wherein the antimicrobial includes a quaternary amine, a carbon chain, and a silane group, and wherein the carbon chain is bound at one end to the quarternary amine and bound at the other end to the silane group.

7. The method of claim 6, wherein the antimicrobial is oriented such that the silane group is proximate to the fabric while the quarternary amine is distal to the fabric.

8. The method of claim 6, wherein the antimicrobial forms a spiked structure with the quaternary amine forming the peak of the spike.

9. The method of claim 6, wherein the antimicrobial is characterized by the formula NH₃C₁₈H₃₆R, where R is a silane group.

10. The method of claim 6, wherein the silane group is bound to the binder.

11. The method of claim 1, wherein applying the antimicrobial-binder mixture includes:

adjusting the temperature of the antimicrobial-binder mixture to a temperature of approximately 100° F.-110° F.;

administering the antimicrobial-binder mixture to the fabric; and

curing the antimicrobial-binder mixture while the mixture is on the fabric.

12. The method of claim 11, wherein administering the antimicrobial-binder mixture to the fabric comprises dipping the fabric in or spraying the fabric with the antimicrobial-binder mixture.

13. The method of claim 11, further including removing existing chemicals from the fabric prior to administering the antimicrobial-binder mixture to the fabric.

14. A treated fabric for preventing the spread of infectious agents, the fabric comprising (a) a fabric; and (b) an antimicrobial-binder mixture secured to the fabric, the antimicrobial-binder mixture containing a binder comprising guar gum, and an antimicrobial that includes an organo silane quaternary amine having spiked structures.

15. The treated fabric of claim 14, wherein the binder further comprises ammonium sulfate.

16. The treated fabric of claim 15, wherein the binder further comprises urea and methyl acryloid.

17. The treated fabric of claim 14, wherein the antimicrobial-binder mixture comprises antimicrobial and binder in an approximately 1:1 ratio by weight.

18. The treated fabric of claim 14, wherein the spiked structures formed by the organo silane quaternary amine are bound to and exposed on an outer surface of the fabric.

19. The treated fabric of claim 14, wherein the antimicrobial includes a quaternary amine, a carbon chain, and a silane group, and wherein the carbon chain is bound at one end to the quarternary amine and bound at the other end to the silane group.

20. The treated fabric of claim 14, wherein the antimicrobial is oriented such that the silane group is proximate to the fabric while the quarternary amine is distal to the treated fabric.

21. The treated fabric of claim 14, wherein the antimicrobial forms a spiked structure with the quaternary amine forming the peak of the spike.

22. The treated fabric of claim 14, wherein the antimicrobial is characterized by the formula NH₃C₁₈H₃₆R, where R is a silane group.

23. The treated fabric of claim 14, wherein the silane group is bound to the binder.

24. The treated fabric of claim 14, wherein the fabric comprises a woven or non-woven fabric.

25. The treated fabric of claim 14, wherein the fabric is comprised at least in part by cotton, nylon, polyester, or a combination thereof.

26. The treated fabric of claim 14, wherein the fabric comprises aluminum.

27. An aqueous binder solution, the aqueous binder solution comprising guar gum, ammonium slufate, urea, and methyl acryloid.

28. The aqueous binder solution of claim 27, wherein the aqueous binder solution is characterized by comprising approximately 1.5% guar gum by weight, approximately 2% ammonium sulfate by weight, approximately 0.9-1.0% urea by weight, and approximately 1.75% methyl acryloid by weight.

29. A method of making a binder, the method comprising

mixing guar gum with water to form a guar gum-water mixture, wherein the water is at a temperature in excess of 145° F.;

cooling the guar gum-water mixture to approximately 135-145° F.;

mixing ammonium sulfate and water to the guar gum-water mixture to form an ammonium sulfate-guar gum-water mixture, wherein the water is at a temperature less than or equal to 145° F.;

mixing urea to the ammonium sulfate-guar gum-water mixture to form a urea-ammonium sulfate-guar gum-water mixture; and

adding water and methyl acryloid to the urea-ammonium sulfate-guar gum-water mixture to form the binder.